CN111916848A - Method for manufacturing lead-acid storage battery - Google Patents

Method for manufacturing lead-acid storage battery Download PDF

Info

Publication number
CN111916848A
CN111916848A CN202010818144.3A CN202010818144A CN111916848A CN 111916848 A CN111916848 A CN 111916848A CN 202010818144 A CN202010818144 A CN 202010818144A CN 111916848 A CN111916848 A CN 111916848A
Authority
CN
China
Prior art keywords
acid
density
sulfuric acid
battery
acid solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010818144.3A
Other languages
Chinese (zh)
Inventor
杨新新
周刚
程志明
陈�胜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chaowei Power Group Co Ltd
Original Assignee
Chaowei Power Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to CNPCT/CN2020/073065 priority Critical
Priority to PCT/CN2020/073066 priority patent/WO2021142853A1/en
Priority to CNPCT/CN2020/073066 priority
Priority to PCT/CN2020/073065 priority patent/WO2021142852A1/en
Priority to CN2020103854358 priority
Priority to CN202010385435 priority
Application filed by Chaowei Power Group Co Ltd filed Critical Chaowei Power Group Co Ltd
Publication of CN111916848A publication Critical patent/CN111916848A/en
Pending legal-status Critical Current

Abstract

The invention relates to a method for manufacturing a storage battery, which comprises the following steps: step 1: adding a first-density sulfuric acid solution into a lead-acid storage battery, wherein the density of the first-density sulfuric acid solution is 1.04g/cm 3-1.28 g/cm 3; step 2, electrifying to form; and 3, adding a second density sulfuric acid solution into the battery through an acid adding kettle, wherein the density of the second density sulfuric acid solution is 1.25-1.6 g/cm3, the density of the second density sulfuric acid solution is greater than that of the first density sulfuric acid solution, and the acid adding kettle can store a certain amount of acid liquor. The manufacturing method of the storage battery can accurately obtain the capacity of the lead-acid storage battery and realize flexible production.

Description

Method for manufacturing lead-acid storage battery
Technical Field
The invention relates to the field of storage batteries.
Background
In the process of present lead-acid storage battery manufacturing, the process of internalization formation of battery is all required, the internalization formation method of present battery, for preventing that the acidizing fluid is not enough, all adopt rich solution to become, full acidification becomes promptly, also has the opening about the present acidification kettle, overlaps on the battery acidification hole all the time during the use, and can not separate between the battery, so can not seal and independently store the acidizing fluid yet, can't accurately obtain required battery capacity through ration acidification in the production process, more can't carry out flexible production according to the battery capacity of needs.
Disclosure of Invention
In order to solve the technical problem, the invention provides a method for manufacturing a storage battery, which comprises the following steps: step 1: adding a first-density sulfuric acid solution into a lead-acid storage battery, wherein the density of the first-density sulfuric acid solution is 1.04g/cm 3-1.28 g/cm 3; step 2, electrifying to form; and 3, adding a second density sulfuric acid solution into the battery through an acid adding kettle, wherein the density of the second density sulfuric acid solution is 1.25-1.6 g/cm3, the density of the second density sulfuric acid solution is greater than that of the first density sulfuric acid solution, and the acid adding kettle can store a certain amount of acid liquor.
Further, in the step 2, the electrification formation is the complete formation, and in the step 3, a second density sulfuric acid solution is added into the battery after the complete formation through an acid adding pot.
Further, the quantificationThe volume of the second density sulfuric acid solution added is related to the second density sulfuric acid solutionV0Is the final sulfuric acid volume, p0Is the final sulfuric acid density, ω0Is the final sulfuric acid mass fraction, V1Is the volume of sulfuric acid added for the first time, p1Is the sulfuric acid density, omega, of the first addition of acid1Is the mass fraction of sulfuric acid of the first addition of acid, rho2Is the sulfuric acid density, omega, of the second addition of acid2Is the mass fraction of the sulfuric acid added for the second time,m0m is the mass of pure sulfuric acid precipitated in the formation process1The loss of quality of the electrolyzed water in the formation process.
Furthermore, the acid adding kettle capable of storing a fixed amount of acid liquid comprises a kettle body, wherein an acid injection port, a leakage-proof valve, an acid discharge port and a drain valve are arranged on the kettle body, the leakage-proof valve is used for sealing or opening the acid injection port, and the drain valve is used for sealing or opening the acid discharge port.
Further, the leakage-proof valve comprises a sealing element and an elastic body, wherein the elastic body is positioned at the lower part of the sealing element, and the elastic body pushes the sealing element to seal the acid injection port.
The manufacturing method of the storage battery can accurately obtain the capacity of the lead-acid storage battery and realize flexible production.
Drawings
FIG. 1 is a schematic view of a lead acid battery acid addition kettle of the present invention;
fig. 2 is another schematic diagram of the lead-acid battery acid adding kettle of the invention.
Detailed Description
The invention is further described with reference to specific examples.
The manufacturing method of the storage battery comprises the following steps: step 1, adding a sulfuric acid solution with a first density into a lead-acid storage battery to be formed, wherein the first density is preferably 1.04g/cm 3-1.28 g/cm 3; step 2, electrifying to form; and 3, adding a second density sulfuric acid solution into the battery, wherein the second density is preferably 1.25-1.6 g/cm3(25 ℃), and the capacity of the formed sulfuric acid solution with the first density is lower, so that the density of the added sulfuric acid solution with the second density is higher than that of the sulfuric acid solution with the first density in order to achieve the required battery capacity, and manufacturers can add the sulfuric acid solutions with the second densities and different volumes according to different use conditions, thereby providing greater convenience for producing batteries with different capacities and different purposes. The density of the added sulfuric acid can be accurately determined, the situation that the added density is too low to reach the capacity and the energy is wasted due to too high density is avoided, and the production efficiency in the production process is improved. In addition, the conversion rate of the lead dioxide at the end of the electrified formation in the step 2 is between 75 and 92 percent, and the sulfuric acid is added in the step 3. The first addition of the low-density sulfuric acid solution can be 1 addition of the low-density sulfuric acid solution or multiple additions of the low-density sulfuric acid solution, and when the low-density sulfuric acid solution is added multiple times, the volume of the low-density sulfuric acid solution added at the next time is preferably larger than that of the low-density sulfuric acid solution added at the previous time. The second addition of the high-density sulfuric acid solution can be 1 addition of the high-density sulfuric acid solution or multiple additions of the high-density sulfuric acid solution, and when the high-density sulfuric acid solution is added multiple times, the volume of the high-density sulfuric acid solution added at the next time is preferably smaller than that of the high-density sulfuric acid solution added at the previous time.
The final sulfuric acid volume V can be determined according to the design capacity of the battery0Volume of increased weight V after acidificationtFinal sulfuric acid density p0Final sulfuric acid mass fraction omega0The mass of pure sulfuric acid which is introduced into the lead plaster in the plaster mixing process and is separated out in the formation process is m0Volume V of sulfuric acid of the first addition1First addition of acid sulfuric acid density rho1Mass fraction omega of the first acid addition1Loss mass m of electrolyzed water in formation process1. According to the law of mass conservation of pure sulfuric acid before and after formation: mass rho of pure sulfuric acid added in first acid addition1V1ω1Adding the mass rho of pure sulfuric acid added by the second acid adding2V2ω2Plus the mass m of pure sulfuric acid introduced into the lead paste during the paste-mixing process and precipitated during the formation process0Should equal the mass of sulfuric acid p of the final cell0V0ω0. Only water is electrolyzed in the formation process to reduce, and pure sulfuric acid is not reduced.
ρ0V0ω0=ρ1V1ω12V2ω2+m0(formula 1)
According to the mass conservation law of the battery before and after formation: adding the first sulfuric acid mass rho before formation1V1Adding the mass rho of sulfuric acid added for the second time after formation2V2Subtracting the mass m of the electrolyzed water in the formation process1Should be equal to the weight gain rho before and after formation0Vt
ρ0Vt=ρ1V12V2-m1(formula 2)
Equation 2, in conjunction with equation 1, will be given by2V2And (4) replacing.
And (3) obtaining the mass fraction of the sulfuric acid added for the second time:
finding out the mass fraction omega of the sulfuric acid according to the comparison table of the density and the mass fraction of the sulfuric acid2Corresponding density ρ2
The volume of the second addition of sulfuric acid was:
example 1
The semi-finished product of the battery with 6-DZF-20 glue sealed off line is taken, the method is adopted for acid addition and formation, and the sample preparation process is as follows:
1) adding acid for the first time, namely adding a sulfuric acid solution with the first density of 1.07g/cm3 into the lead storage battery to be added with acid for 140ml, wherein the acid can be added for multiple times, namely 60ml for the first time and 80ml for the next time. And adding acid by using a vacuum acid adding machine.
2) And (3) placing the battery subjected to the first acid adding in a water bath, connecting a charging wire clamp, starting a charger, and performing the process according to the process in the table 1.
TABLE 16-DZF-20 Process
Step (ii) of Means for Current (A) Time (h) Electric quantity (Ah)
1 Charging of electricity 0.4 0.5 0.2
2 Charging of electricity 0.8 0.5 0.4
3 Charging of electricity 1.6 0.5 0.8
4 Charging of electricity 3 0.5 1.5
5 Charging of electricity 3.5 0.875 3.0625
6 Charging of electricity 4 14 56
7 Charging of electricity 3 2.88 8.64
8 Charging of electricity 6.3 8.94 56.322
9 Standing still Standing for 1 hour 1
10 Charging of electricity 5.7 2.2 12.54
11 Standing still Standing for 1 hour 1
12 Charging of electricity 5.1 2.5 12.75
3) And (5) when the formation is finished and the charge capacity reaches 126Ah, and the content of PbO2 reaches about 88%, completely forming, namely completely forming, and finishing the conversion of the basic lead sulfate and the lead oxide. The battery capacity at this time was 4 AH.
4) To achieve a battery with a battery capacity of 20AH, a second density of acid used only as an energy material was initially added to the battery. The density and volume of the second addition of acid were calculated as follows:
a. according to the design capacity of the battery, the final volume V of sulfuric acid for the design of the battery is determined0167.69ml, increased in volume V after acidificationt161.13ml, final sulfuric acid density ρ01.360g/cm3, and finding out the mass fraction omega of the sulfuric acid according to the comparison table of the density and the mass fraction of the sulfuric acid0=45.3%;
b. The mass of pure sulfuric acid introduced into the lead plaster in the plaster mixing process and separated out in the formation process is m0=16.49g;
c. Volume V of sulfuric acid of the first addition1=140ml,Density of sulfuric acid rho11.07g/cm3 and mass fraction ω19.3 percent; d. loss mass m of electrolyzed water in formation process130 g; e. the mass fraction of the sulfuric acid added for the second time is as follows:
finding out the mass fraction omega of the sulfuric acid according to the comparison table of the density and the mass fraction of the sulfuric acid2Corresponding density ρ2=1.65g/cm3
f. The volume of the second addition of sulfuric acid was:
the acid can be added in multiple times, 40ml for the first time and 20ml for the second time.
The addition of the acid at the second density to the cell is initiated. Acid is added by adopting an acid adding machine, and acid liquor is added into an acid adding kettle capable of quantitatively storing the acid liquor. And connecting an acid adding kettle with a battery injection hole, and quantitatively injecting acid liquid with a second density into the battery, wherein the acid density of the second density is 1.65g/cm3, and the adding amount of the acid with the second density is 60 ml. After the acid addition was complete, the procedure of Table 1 was continued.
5) Acid extraction is avoided after the formation is finished.
Example 2
The semi-finished product of the battery with 6-DZF-20 glue sealed off line is taken, the method is adopted for acid addition and formation, and the sample preparation process is as follows:
1) adding acid for the first time, namely adding a sulfuric acid solution with a first density and a density of 1.17g/cm3 into the lead storage battery to be added, wherein the acid volume is 145ml, and the acid can be added for multiple times, namely 60ml for the first time and 85ml for the next time. And adding acid by using a vacuum acid adding machine.
2) And (3) placing the battery subjected to the first acid addition in a water bath, connecting a charging wire clamp, starting a charger, and performing the process according to the process 1 in the table.
3) And (3) when the formation is finished and the charge amount reaches 126Ah, and the content of PbO2 reaches about 81 percent, partially forming, namely incomplete conversion of basic lead sulfate and lead oxide. The battery capacity at this time was 6 AH.
4) To achieve a cell capacity of 20AH, a second density of acid is initially added to the cell. The density and volume of the second addition of acid were calculated as follows:
a. according to the design capacity of the battery, the final volume V of sulfuric acid for the design of the battery is determined0167.69ml, increased in volume V after acidificationt161.13ml, final sulfuric acid density ρ01.360g/cm3, and finding out the mass fraction omega of the sulfuric acid according to the comparison table of the density and the mass fraction of the sulfuric acid0=45.3%;
b. The mass of pure sulfuric acid introduced into the lead plaster in the plaster mixing process and separated out in the formation process is m0=16.49g;
c. Volume V of sulfuric acid of the first addition1145ml sulfuric acid density p11.17g/cm3 and mass fraction ω122.9%; d. loss mass m of electrolyzed water in formation process1=30g;
e. The mass fraction of the sulfuric acid added for the second time is as follows:
finding out the mass fraction omega of the sulfuric acid according to the comparison table of the density and the mass fraction of the sulfuric acid2Corresponding density ρ2=1.50g/cm3
f. The volume of the second addition of sulfuric acid was:
the acid can be added in multiple times, 30ml for the first time and 23ml for the last time.
And adding acid with the second density into the battery, adding the acid by using an acid adding machine, and adding the acid into an acid adding pot capable of quantitatively storing the acid. And connecting the acid adding kettle with the battery liquid injection hole, and quantitatively injecting acid liquid with a second density into the battery. The second density acid had a density of 1.50g/cm3 and 53ml of the second density acid was added. After the acid addition was complete, the procedure of Table 1 was continued.
5) Acid extraction is avoided after the formation is finished.
Example 3
The semi-finished product of the battery with 6-DZF-20 glue sealed off line is taken, the method is adopted for acid addition and formation, and the sample preparation process is as follows:
1) adding acid for the first time, namely adding a sulfuric acid solution with the first density of 1.28g/cm3 into the lead storage battery to be added with acid for the first time, wherein the acid adding volume is 155ml, and the acid can be added for multiple times, namely 60ml for the first time and 95ml for the last time. And adding acid by using a vacuum acid adding machine.
2) And (3) placing the battery subjected to the first acid adding in a water bath, connecting a charging wire clamp, starting a charger, and performing the process according to the process in the table 1.
3) And (5) when the formation is finished and the charge amount reaches 126Ah, and the content of PbO2 reaches about 77%, partially forming, namely, the conversion of basic lead sulfate and lead oxide is not finished. At this time, the battery capacity is 13 AH.
4) To achieve a cell capacity of 20AH, a second density of acid is initially added to the cell. The density and volume of the second addition of acid were calculated as follows:
a. according to the design capacity of the battery, the final volume V of sulfuric acid for the design of the battery is determined0167.69ml, increased in volume V after acidificationt161.13ml, final sulfuric acid density ρ01.360g/cm3, and finding out the mass fraction omega of the sulfuric acid according to the comparison table of the density and the mass fraction of the sulfuric acid0=45.3%;
b. The mass of pure sulfuric acid introduced into the lead plaster in the plaster mixing process and separated out in the formation process is m0=16.49g;
c. Volume V of sulfuric acid of the first addition1155ml, sulfuric acid density ρ11.28g/cm3 and mass fraction ω136.4%; d. loss mass m of electrolyzed water in formation process1=30g;
e. The mass fraction of the sulfuric acid added for the second time is as follows:
finding out the mass fraction omega of the sulfuric acid according to the comparison table of the density and the mass fraction of the sulfuric acid2Corresponding density ρ2=1.21g/cm3
f. The volume of the second addition of sulfuric acid was:
the acid can be added in multiple times, 32ml for the first time and 10ml for the second time.
And adding acid with the second density into the battery, adding the acid by using an acid adding machine, and adding the acid into an acid adding kettle capable of quantitatively storing the acid. And connecting the acid adding kettle with the battery liquid injection hole, and quantitatively injecting acid liquid with a second density into the battery. The second density acid had a density of 1.21g/cm3 and was added in an amount of 42ml of the second density acid. After the acid addition was complete, the procedure of Table 1 was continued.
5) Acid extraction is avoided after the formation is finished.
The invention relates to a method for manufacturing a storage battery, wherein the step 3 of adding a second-density sulfuric acid solution can be performed by an acid adding pot capable of storing a certain amount of acid liquor, as shown in figures 1 and 2, the invention provides the acid adding pot, which comprises a pot body 1, wherein the upper part of the pot body is provided with an acid injection port 4, the lower part of the acid injection port 4 is connected with a leakage-proof valve 5, and the upper part in the leakage-proof valve 5 is provided with a sealing piece, such as: the rubber seals the valve body 9, and the lower part is provided with an elastomer, such as a rubber marble 10. When acid is injected into the kettle body 1, the acid liquor is connected with the acid injection port 4 through the acid injection nozzle of the acid adding machine and presses the rubber sealing valve body 9 downwards, so that the rubber ball 10 is extruded and deformed, a gap is formed between the rubber sealing valve body 9 and the top cover of the kettle body 1, and the acid liquor is injected into the kettle body 1. After the acid adding is finished, the acid injection nozzle of the acid adding machine is removed, the rubber marble 10 recovers deformation, the rubber sealing valve body 9 is jacked up to realize sealing with the top cover of the kettle body 1, and the acid liquor is stored in the kettle body 1. The lower part of the kettle body 1 is provided with a rubber acid discharge port 7, a pull rod drain valve 6 is arranged in the kettle body 1 and can move up and down, the lower end of the pull rod drain valve 6 seals the kettle body 1 through a sealing rubber ring 11 arranged in the lower part of the kettle body 1, and the upper end of the pull rod drain valve 6 penetrates through an opening in the upper end of the kettle body 1 and seals the kettle body 1 through a sealing rubber ring 8 arranged in the opening. The top ends of a plurality of pull rod drain valves 6 are connected through a cross rod 2, and a travel limit sleeve 3 is arranged to limit the linear movement of the pull rod drain valves 6, and the travel limit sleeve 3 is fixed on the kettle body 1. When acid liquor is discharged from the kettle body 1, the rubber acid discharge port 5 is connected to an acid injection nozzle on the top of a common acid adding kettle or an acid injection nozzle of a battery middle cover, the pull rod drain valve 6 is pulled upwards, the lower end is separated from the sealing rubber ring 11, and the acid liquor is discharged. After acid is discharged, the pull rod drain valve 6 is pressed downwards, so that the lower end of the pull rod is sealed with the sealing rubber ring 11, and acid can be repeatedly injected into the kettle body 1. In this embodiment, the pull rod type drain valve 6 moves linearly, and may rotate as necessary, or other ways to seal and open the drain opening may be implemented. The pot body 1 of the invention can be arranged into a plurality of bodies according to the requirement.
The acid adding kettle provided by the invention can store acid liquor quantitatively, and can be applied to the process of formation and quantitative acid addition of a lead-acid storage battery. Quantitatively adding part of acid liquor into the acid adding kettle by using an acid adding machine, and hermetically storing and transferring the acid liquor in the kettle. During or after the formation process, the acid adding kettle is sleeved on a battery according to the process requirements, and acid liquor stored in the kettle is added into the battery to realize quantitative acid addition, so that acid pumping can be avoided, and the required capacity after formation can be realized by selecting proper sulfuric acid density.
The above-described embodiments are only preferred embodiments of the present invention, and are not intended to limit the present invention in any way, and other variations and modifications may be made without departing from the spirit of the invention as set forth in the claims.

Claims (5)

1. A method for manufacturing a lead-acid battery, characterized by comprising the steps of: step 1: adding a first-density sulfuric acid solution into a lead-acid storage battery, wherein the density of the first-density sulfuric acid solution is 1.04g/cm 3-1.28 g/cm 3; step 2, electrifying to form; and 3, adding a second density sulfuric acid solution into the battery through an acid adding kettle, wherein the density of the second density sulfuric acid solution is 1.25-1.6 g/cm3, the density of the second density sulfuric acid solution is greater than that of the first density sulfuric acid solution, and the acid adding kettle can store a certain amount of acid liquor.
2. The method for manufacturing a lead-acid storage battery according to claim 1, wherein in the step 2, the electrification formation is a complete formation, and in the step 3, a second-density sulfuric acid solution is added into the battery after the complete formation through an acid adding pot.
3. A method of manufacturing a lead-acid battery according to claim 1 or 2, characterized in that the volume of the dosed sulfuric acid solution of second density is related to the sulfuric acid solution of second densityV0Is the final sulfuric acid volume, p0Is the final sulfuric acid density, ω0Is the final sulfuric acid mass fraction, V1Is the volume of sulfuric acid added for the first time, p1Is the sulfuric acid density, omega, of the first addition of acid1Is the mass fraction of sulfuric acid of the first addition of acid, rho2Is the sulfuric acid density, omega, of the second addition of acid2Is the mass fraction of the sulfuric acid added for the second time,m0m is the mass of pure sulfuric acid precipitated in the formation process1The loss of quality of the electrolyzed water in the formation process.
4. The method for manufacturing a lead-acid storage battery as defined in claim 1 or 2, wherein said acid adding pot capable of storing a fixed amount of acid liquid comprises a pot body, said pot body is provided with an acid filling port, a leakage-proof valve, an acid discharging port and a drain valve, said leakage-proof valve is used for sealing or opening said acid filling port, and said drain valve is used for sealing or opening said acid discharging port.
5. The method of claim 4, wherein the leak-proof valve comprises a sealing member and an elastic member, the elastic member is located at a lower portion of the sealing member, and the elastic member pushes the sealing member to seal the acid injection port.
CN202010818144.3A 2020-01-19 2020-08-14 Method for manufacturing lead-acid storage battery Pending CN111916848A (en)