CN111470826A - Novel wood-like furniture and preparation method thereof - Google Patents

Novel wood-like furniture and preparation method thereof Download PDF

Info

Publication number
CN111470826A
CN111470826A CN202010100864.6A CN202010100864A CN111470826A CN 111470826 A CN111470826 A CN 111470826A CN 202010100864 A CN202010100864 A CN 202010100864A CN 111470826 A CN111470826 A CN 111470826A
Authority
CN
China
Prior art keywords
percent
furniture
water
negative oxygen
superplasticizer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010100864.6A
Other languages
Chinese (zh)
Inventor
王文博
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yangzhou Boyeda New Building Materials Technology Co ltd
Original Assignee
Yangzhou Boyeda New Building Materials Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yangzhou Boyeda New Building Materials Technology Co ltd filed Critical Yangzhou Boyeda New Building Materials Technology Co ltd
Priority to CN202010100864.6A priority Critical patent/CN111470826A/en
Publication of CN111470826A publication Critical patent/CN111470826A/en
Pending legal-status Critical Current

Abstract

The invention discloses novel wood-like furniture and a preparation method thereof, and belongs to the technical field of wood-like furniture. The wood-like furniture is composed of a fabric and a middle material, and a product is obtained by steam curing and forming; the fabric is a mixture of various raw materials in inorganic cementing materials, natural colored sand, toner, short fibers, superplasticizers, retarders, titanium dioxide, negative oxygen ions, fine saw dust materials or water, and the medium materials are a mixture of various raw materials in inorganic cementing materials, superplasticizers, negative oxygen ions, polyphenyl granules, coarse saw dust materials, retarders or water. The invention adopts the matching process of various color systems such as cementing materials, natural colored sand, toner and the like to manufacture the furniture with the wood grain effects similar to silicification, pear flower wood, red sandalwood and the like, and has the advantages of ornamental value, practicability, natural and real natural color, vivid image, difficult fading and color change, good weather resistance, difficult shedding and cracking, long quality guarantee period and capability of saving a large amount of wood resources.

Description

Novel wood-like furniture and preparation method thereof
Technical Field
The invention belongs to the technical field of wood-like furniture, and particularly relates to novel wood-like furniture and a preparation method thereof.
Background
With the development of the furniture industry in China, the pursuit of beauty and environmental performance of the furniture by people at present is improved, the competition and research of the furniture industry are carried out by grasping the core of the two points, the furniture materials owned in the market at present are respectively composite boards and solid boards, the composite boards have the defects of organic adhesion and molding, the released formaldehyde is harmful to human bodies, the solid boards belong to renewable resources, the price is relatively high, and the design and color are uncontrollable.
Disclosure of Invention
The technical problem to be solved by the invention is to provide novel wood-like furniture, which adopts natural color sand and toner to match with various colors, has natural and real natural color, is vivid in image, is not easy to fade or change color, is not easy to fall off or crack, has long quality guarantee period, and can save a large amount of wood resources. The invention aims to solve another technical problem of providing a preparation method of novel wood-like furniture, wherein the raw materials are paved and then steamed until the raw materials are solidified, the preparation method is simple, the size of the product can be customized according to the requirement, and the repeatability is good; products with complex structures can be molded at one time; the surface is smooth and clean without secondary modification.
In order to solve the problems, the technical scheme adopted by the invention is as follows:
the novel wood-like furniture is composed of a fabric and a middle material, wherein the fabric is a mixture of multiple raw materials of an inorganic cementing material, natural colored sand, toner, short fibers, a superplasticizer, a retarder, titanium dioxide, negative oxygen ions, a fine saw dust material or water, and the middle material is a mixture of multiple raw materials of the inorganic cementing material, the superplasticizer, the negative oxygen ions, polyphenyl particles, a coarse saw dust material, the retarder or water.
According to the novel wood-like furniture, the inorganic cementing material is sulphoaluminate cement; the toner is any one of yellow iron oxide, red iron oxide, black iron oxide or green iron oxide; the short fiber is polypropylene fiber.
The novel wood-like furniture is characterized in that the fabric is composed of 43% -47% of inorganic cementing materials, 37.1% -41.1% of natural colored sand, 1.6% -2.6% of toner, 0.1% -0.2% of short fibers, 1.3% -1.4% of superplasticizer, 0.08% -0.12% of retarder, 0.008% -0.012% of titanium dioxide, 0.35% -0.41% of negative oxygen ions and 11% -12% of water, the particle size of the natural colored sand is 20-40 meshes or 80-120 meshes, and the percentages refer to the percentage of the usage amount of the raw materials in the total mass of the fabric; the medium material consists of 73.4 to 77.5 percent of inorganic cementing material, 2.18 to 2.35 percent of superplasticizer, 0.28 to 0.45 percent of negative oxygen ion, 18.8 to 20.22 percent of water and 2.48 to 2.69 percent of polyphenyl granules, and the percentages refer to the percentage of the amount of the raw material in the total mass of the medium material.
The novel wood-like furniture is characterized in that the fabric is composed of 43% -47% of inorganic cementing materials, 37.1% -41.1% of natural colored sand, 1.6% -2.6% of toner, 0.1% -0.2% of short fibers, 1.3% -1.4% of superplasticizer, 0.08% -0.12% of retarder, 0.008% -0.012% of titanium dioxide, 0.35% -0.41% of negative oxygen ions and 11% -12% of water, the particle size of the natural colored sand is 20-40 meshes or 80-120 meshes, and the percentages refer to the percentage of the usage amount of the raw materials in the total mass of the fabric; the middle material consists of 66.88 to 70.64 percent of inorganic cementing material, 1.97 to 2.23 percent of superplasticizer, 9.38 to 10.41 percent of coarse saw powder material, 0.14 to 0.19 percent of retarder, 0.62 to 0.73 percent of negative oxygen ion and 18.8 to 20.22 percent of water, wherein the grain diameter of the coarse saw powder material is 10 to 60 meshes, and the percentages refer to the percentage of the consumption of the raw material in the total mass of the middle material.
The novel wood-like furniture is characterized in that the fabric is composed of 70% -74% of inorganic cementing materials, 2.3% -2.7% of fine saw dust materials, 0.23% -0.27% of short fibers, 3% -3.4% of toner, 2.12% -2.2% of superplasticizer, 0.15% -0.19% of retarder, 0.7% -0.75% of negative oxygen ions and 18.75% -18.79% of water, the particle size of the fine saw dust materials is 60-100 meshes, and the percentages refer to the percentage of the usage amount of the raw materials in the total mass of the fabric; the medium material consists of 73.4 to 77.5 percent of inorganic cementing material, 2.18 to 2.35 percent of superplasticizer, 0.28 to 0.45 percent of negative oxygen ion, 18.8 to 20.22 percent of water and 2.48 to 2.69 percent of polyphenyl granules, and the percentages refer to the percentage of the amount of the raw material in the total mass of the medium material.
The novel wood-like furniture is characterized in that the fabric is composed of 70% -74% of inorganic cementing materials, 2.3% -2.7% of fine saw dust materials, 0.23% -0.27% of short fibers, 3% -3.4% of toner, 2.12% -2.2% of superplasticizer, 0.15% -0.19% of retarder, 0.7% -0.75% of negative oxygen ions and 18.75% -18.79% of water, the particle size of the fine saw dust materials is 60-100 meshes, and the percentages refer to the percentage of the usage amount of the raw materials in the total mass of the fabric; the middle material consists of 66.88 to 70.64 percent of inorganic cementing material, 1.97 to 2.23 percent of superplasticizer, 9.38 to 10.41 percent of coarse saw powder material, 0.14 to 0.19 percent of retarder, 0.62 to 0.73 percent of negative oxygen ion and 18.8 to 20.22 percent of water; the particle size of the coarse saw dust material is 10-60 meshes, and the percentages refer to the percentage of the consumption of the raw material in the total mass of the medium material.
The novel wood-like furniture is characterized in that the fabric is composed of 70.4% -72.5% of inorganic cementing material, 3.35% -3.72% of fine saw dust material, 0.22% -0.27% of short fiber, 3.04% -3.25% of toner, 2.1% -2.18% of superplasticizer, 0.14% -0.21% of retarder, 0.69% -0.75% of negative oxygen ion and 18.1% -18.85% of water, the particle size of the fine saw dust material is 60-100 meshes, and the percentages refer to the percentage of the usage amount of the raw material in the total mass of the fabric; the medium material consists of 73.4 to 77.5 percent of inorganic cementing material, 2.18 to 2.35 percent of superplasticizer, 0.28 to 0.45 percent of negative oxygen ion, 18.8 to 20.22 percent of water and 2.48 to 2.69 percent of polyphenyl granules, and the percentages refer to the percentage of the amount of the raw material in the total mass of the medium material.
The novel wood-like furniture is characterized in that the fabric is composed of 70.4% -72.5% of inorganic cementing material, 3.35% -3.72% of fine saw dust material, 0.22% -0.27% of short fiber, 3.04% -3.25% of toner, 2.1% -2.18% of superplasticizer, 0.14% -0.21% of retarder, 0.69% -0.75% of negative oxygen ion and 18.1% -18.85% of water, the particle size of the fine saw dust material is 60-100 meshes, and the percentages refer to the percentage of the usage amount of the raw material in the total mass of the fabric; the middle material consists of 66.88 to 70.64 percent of inorganic cementing material, 1.97 to 2.23 percent of superplasticizer, 9.38 to 10.41 percent of coarse saw powder material, 0.14 to 0.19 percent of retarder, 0.62 to 0.73 percent of negative oxygen ion and 18.8 to 20.22 percent of water, wherein the grain diameter of the coarse saw powder material is 10 to 60 meshes, and the percentages refer to the percentage of the consumption of the raw material in the total mass of the middle material.
According to the preparation method of the novel wood-like furniture, the fabric and the middle material are laid in a mold, and then primary maintenance is carried out; after the primary curing is finished, the mould is separated, and secondary curing is carried out, so that the wood-like furniture is finally obtained; the primary curing is curing for 24 hours at the temperature of 25-30 ℃, and the humidity is more than or equal to 85 percent; the secondary curing is curing for 48 hours at 25-30 ℃ with the humidity more than or equal to 85 percent.
Has the advantages that: compared with the prior art, the invention has the advantages that:
(1) the invention adopts the matching process of various color systems such as cementing materials, natural colored sand, toner and the like to manufacture the furniture with the wood grain effects similar to silicification, pear flower wood, red sandalwood and the like, and has the advantages of ornamental value, practicability, natural and real natural color, vivid image, difficult fading and color change, good weather resistance, difficult shedding and cracking, long quality guarantee period and capability of saving a large amount of wood resources.
(2) In order to ensure the diversification of colors, the fabric adopts three color series to form combined colors, the types of the colors can be increased or reduced by replacing the toner, the middle materials are mainly used for filling, the raw materials are steamed after being paved until being solidified, the product size can be customized according to the requirement, and the repeatability is good; products with complex structures can be molded at one time; the surface is smooth and clean without secondary modification.
(3) The raw materials for producing the product are inorganic cementing materials, formaldehyde does not exist in performance, the appearance effect is controllable, and the defects of furniture materials are overcome.
Drawings
FIG. 1 is a schematic diagram of a first product prepared in example 1.
Detailed Description
In order to make the aforementioned objects, features and advantages of the present invention comprehensible, embodiments accompanied with examples are described in detail below.
Example 1
A novel wood-like furniture is composed of a fabric and a middle material, wherein the fabric is composed of 45% of sulphoaluminate cement, 39.4% of natural colored sand (with the particle size of 20-40 meshes), 2.1% of iron oxide yellow, 0.15% of polypropylene fiber, 1.35% of a superplasticizer, 0.10% of a retarder, 0.010% of titanium dioxide, 0.39% of negative oxygen ions and 11.5% of water, and the percentages are percentages of the usage amount of the raw materials in the total mass of the fabric; the medium material consists of 75.3 percent of inorganic gelled material, 2.26 percent of superplasticizer, 0.35 percent of negative oxygen ion, 19.50 percent of water and 2.59 percent of polyphenyl granules, and the percentages all refer to the percentage of the consumption of the raw material in the total mass of the medium material; laying the fabric and the middle materials into a mold, then carrying out primary curing, and separating from the mold after the primary curing is finished to carry out secondary curing to obtain a product I; the primary curing is curing for 24 hours at 30 ℃ and the humidity is 90 percent; the secondary curing is curing at 25 ℃ for 48h with the humidity of 90%.
Example 2
A novel wood-like furniture is composed of a fabric and a middle material, wherein the fabric is composed of 45% of sulphoaluminate cement, 39.4% of natural colored sand (with the particle size of 80-120 meshes), 2.1% of iron oxide yellow, 0.15% of polypropylene fiber, 1.35% of a superplasticizer, 0.10% of a retarder, 0.010% of titanium dioxide, 0.39% of negative oxygen ions and 11.5% of water, and the percentages are percentages of the usage amount of the raw materials in the total mass of the fabric; the medium material consists of 67.71 percent of sulphoaluminate cement, 2.09 percent of superplasticizer, 9.89 percent of coarse saw dust material (the grain diameter is 10-60 meshes), 0.16 percent of retarder, 0.67 percent of negative oxygen ion and 19.48 percent of water, and the percentages all refer to the percentage of the consumption of the raw material in the total mass of the medium material; laying the fabric and the middle materials into a mold, then carrying out primary curing, and separating from the mold after the primary curing is finished to carry out secondary curing to obtain a second product; the primary curing is curing for 24 hours at 30 ℃ and the humidity is 85 percent; the secondary curing is curing at 25 ℃ for 48h with the humidity of 90%.
Example 3
A novel wood-like furniture is composed of a fabric and a middle material, wherein the fabric is composed of 72.22% of sulphoaluminate cement, 2.5% of fine saw dust (with the particle size of 60-100 meshes), 0.25% of polypropylene fiber, 3.2% of iron oxide red, 2.16% of a superplasticizer, 0.17% of a retarder, 0.73% of negative oxygen ions and 18.77% of water, and the percentages are percentages of the usage amount of the raw materials in the total mass of the fabric; the medium material consists of 75.3 percent of sulphoaluminate cement, 2.26 percent of superplasticizer, 0.35 percent of negative oxygen ions, 19.50 percent of water and 2.59 percent of polyphenyl granules, and the percentages all refer to the percentage of the consumption of the raw materials in the total mass of the medium material; laying the fabric and the middle materials into a mold, then carrying out primary curing, and separating from the mold after the primary curing is finished to carry out secondary curing to obtain a third product; the primary curing is curing for 24 hours at 26 ℃ and the humidity is 90 percent; (ii) a The secondary curing is curing at 30 ℃ for 48h with the humidity of 88%.
Example 4
A novel wood-like furniture is composed of a fabric and a middle material, wherein the fabric is composed of 72.22% of sulphoaluminate cement, 2.5% of fine saw dust (with the particle size of 60-100 meshes), 0.25% of polypropylene fiber, 3.2% of iron oxide black, 2.16% of a superplasticizer, 0.17% of a retarder, 0.73% of negative oxygen ions and 18.77% of water, and the percentages are percentages of the usage amount of the raw materials in the total mass of the fabric; the medium material consists of 67.71 percent of sulphoaluminate cement, 2.09 percent of superplasticizer, 9.89 percent of coarse saw dust material (the grain diameter is 10-60 meshes), 0.16 percent of retarder, 0.67 percent of negative oxygen ion and 19.48 percent of water, and the percentages all refer to the percentage of the consumption of the raw material in the total mass of the medium material; laying the fabric and the middle materials into a mold, then carrying out primary curing, and separating from the mold after the primary curing is finished to carry out secondary curing to obtain a product IV; the primary curing is curing for 24 hours at 28 ℃ with the humidity of 89 percent; the secondary curing is curing at 25 ℃ for 48h with 85% humidity.
Example 5
A novel wood-like furniture comprises a fabric and a middle material, wherein the fabric is composed of sulphoaluminate cement 71.5%; 3.55% of fine saw powder (with the grain diameter of 60-100 meshes); 0.25% of polypropylene fiber; 3.16% of iron oxide green; 2.14 percent of superplasticizer; 0.18 percent of retarder; 0.72 percent of negative oxygen ions; 18.50 percent of water, wherein the percentages refer to the percentage of the raw materials in the total mass of the fabric; the medium material consists of 75.3 percent of sulphoaluminate cement, 2.26 percent of superplasticizer, 0.35 percent of negative oxygen ions, 19.50 percent of water and 2.59 percent of polyphenyl granules, and the percentages all refer to the percentage of the consumption of the raw materials in the total mass of the medium material; laying the fabric and the middle materials into a mold, then carrying out primary curing, and separating from the mold after the primary curing is finished to carry out secondary curing to obtain a fifth product; the primary curing is curing for 24 hours at 30 ℃ and the humidity is 85 percent; the secondary curing is curing at 25 ℃ for 48h with the humidity of 90%.
Example 6
A novel wood-like furniture comprises a fabric and a middle material, wherein the fabric is composed of sulphoaluminate cement 71.5%; 3.55% of fine saw powder (with the grain diameter of 60-100 meshes); 0.25% of polypropylene fiber; 3.16% of iron oxide red; 2.14 percent of superplasticizer; 0.18 percent of retarder; 0.72 percent of negative oxygen ions; 18.50 percent of water, wherein the percentages refer to the percentage of the raw materials in the total mass of the fabric; the medium material consists of 67.71 percent of sulphoaluminate cement, 2.09 percent of superplasticizer, 9.89 percent of coarse saw dust material (the grain diameter is 10-60 meshes), 0.16 percent of retarder, 0.67 percent of negative oxygen ion and 19.48 percent of water, and the percentages all refer to the percentage of the consumption of the raw material in the total mass of the medium material; laying the fabric and the middle materials into a mold, then carrying out primary curing, and separating from the mold after the primary curing is finished to carry out secondary curing to obtain a product six; the primary curing is curing for 24 hours at 26 ℃ and the humidity is 90 percent; the secondary curing is curing at 30 ℃ for 48h with the humidity of 88%.
The wood-like products have natural and real natural colors, are vivid in image, are not easy to fade or change color, are good in weather resistance, are not easy to fall off or crack, are long in shelf life, and can save a large amount of wood resources. The size of the product can be customized according to the needs of customers, and the repeatability is good; products with complex structures can be molded at one time; the surface is smooth and clean without secondary modification.

Claims (9)

1. The novel wood-like furniture is characterized by comprising a fabric and a middle material, wherein the fabric is a mixture of inorganic cementing materials, natural colored sand, toner, short fibers, superplasticizers, retarders, titanium dioxide, negative oxygen ions, fine saw dust materials or various raw materials in water, and the middle material is a mixture of inorganic cementing materials, superplasticizers, negative oxygen ions, polyphenyl particles, coarse saw dust materials, retarders or various raw materials in water.
2. The novel wood-like furniture according to claim 1, wherein the inorganic cementitious material is sulphoaluminate cement; the toner is any one of yellow iron oxide, red iron oxide, black iron oxide or green iron oxide; the short fiber is polypropylene fiber.
3. The novel wood-like furniture according to claim 1 or 2, characterized in that the fabric is composed of 43% -47% of inorganic gelled material, 37.1% -41.1% of natural color sand, 1.6% -2.6% of toner, 0.1% -0.2% of short fiber, 1.3% -1.4% of superplasticizer, 0.08% -0.12% of retarder, 0.008% -0.012% of titanium dioxide, 0.35% -0.41% of negative oxygen ion and 11% -12% of water, wherein the particle size of the natural color sand is 20-40 meshes or 80-120 meshes; the middle material consists of 73.4 to 77.5 percent of inorganic gelled material, 2.18 to 2.35 percent of superplasticizer, 0.28 to 0.45 percent of negative oxygen ion, 18.8 to 20.22 percent of water and 2.48 to 2.69 percent of polyphenyl granules.
4. The novel wood-like furniture according to claim 1 or 2, characterized in that the fabric is composed of 43% -47% of inorganic gelled material, 37.1% -41.1% of natural color sand, 1.6% -2.6% of toner, 0.1% -0.2% of short fiber, 1.3% -1.4% of superplasticizer, 0.08% -0.12% of retarder, 0.008% -0.012% of titanium dioxide, 0.35% -0.41% of negative oxygen ion and 11% -12% of water, wherein the particle size of the natural color sand is 20-40 meshes or 80-120 meshes; the middle material consists of 66.88 to 70.64 percent of inorganic cementing material, 1.97 to 2.23 percent of superplasticizer, 9.38 to 10.41 percent of coarse saw powder material, 0.14 to 0.19 percent of retarder, 0.62 to 0.73 percent of negative oxygen ion and 18.8 to 20.22 percent of water, and the particle size of the coarse saw powder material is 10 to 60 meshes.
5. The novel wood-like furniture according to claim 1 or 2, characterized in that the facing material is composed of inorganic gelled material 70% -74%, fine saw dust 2.3% -2.7%, short fiber 0.23% -0.27%, toner 3% -3.4%, superplasticizer 2.12% -2.2%, retarder 0.15% -0.19%, negative oxygen ion 0.7% -0.75% and water 18.75% -18.79%; the particle size of the fine saw dust material is 60-100 meshes; the middle material consists of 73.4 to 77.5 percent of inorganic gelled material, 2.18 to 2.35 percent of superplasticizer, 0.28 to 0.45 percent of negative oxygen ion, 18.8 to 20.22 percent of water and 2.48 to 2.69 percent of polyphenyl granules.
6. The novel wood-like furniture according to claim 1 or 2, characterized in that the shell fabric is composed of 70% -74% of inorganic gelled material, 2.3% -2.7% of fine saw dust material, 0.23% -0.27% of short fiber, 3% -3.4% of toner, 2.12% -2.2% of superplasticizer, 0.15% -0.19% of retarder, 0.7% -0.75% of negative oxygen ion and 18.75% -18.79% of water, wherein the particle size of the fine saw dust material is 60-100 meshes; the middle material consists of 66.88 to 70.64 percent of inorganic cementing material, 1.97 to 2.23 percent of superplasticizer, 9.38 to 10.41 percent of coarse saw powder material, 0.14 to 0.19 percent of retarder, 0.62 to 0.73 percent of negative oxygen ion and 18.8 to 20.22 percent of water; the particle size of the coarse saw dust material is 10-60 meshes.
7. The novel wood-like furniture according to claim 1 or 2, characterized in that the shell fabric is composed of inorganic gelled material 70.4% -72.5%, fine saw dust 3.35% -3.72%, short fiber 0.22% -0.27%, toner 3.04% -3.25%, superplasticizer 2.1% -2.18%, retarder 0.14% -0.21%, negative oxygen ion 0.69% -0.75% and water 18.1% -18.85%, and the particle size of the fine saw dust is 60-100 meshes; the middle material consists of 73.4 to 77.5 percent of inorganic gelled material, 2.18 to 2.35 percent of superplasticizer, 0.28 to 0.45 percent of negative oxygen ion, 18.8 to 20.22 percent of water and 2.48 to 2.69 percent of polyphenyl granules.
8. The novel wood-like furniture according to claim 1 or 2, characterized in that the shell fabric is composed of inorganic gelled material 70.4% -72.5%, fine saw dust 3.35% -3.72%, short fiber 0.22% -0.27%, toner 3.04% -3.25%, superplasticizer 2.1% -2.18%, retarder 0.14% -0.21%, negative oxygen ion 0.69% -0.75% and water 18.1% -18.85%; the particle size of the fine saw dust material is 60-100 meshes; the middle material consists of 66.88 to 70.64 percent of inorganic cementing material, 1.97 to 2.23 percent of superplasticizer, 9.38 to 10.41 percent of coarse saw powder material, 0.14 to 0.19 percent of retarder, 0.62 to 0.73 percent of negative oxygen ion and 18.8 to 20.22 percent of water, and the particle size of the coarse saw powder material is 10 to 60 meshes.
9. The method for preparing the novel wood-like furniture according to claim 1 or 2, wherein the shell fabric and the middle material are laid in a mold and then are cured for one time; after the primary curing is finished, the mould is separated, and secondary curing is carried out, so that the wood-like furniture is finally obtained; the primary curing is curing for 24 hours at the temperature of 25-30 ℃, and the humidity is more than or equal to 85 percent; the secondary curing is curing for 48 hours at 25-30 ℃ with the humidity more than or equal to 85 percent.
CN202010100864.6A 2020-02-18 2020-02-18 Novel wood-like furniture and preparation method thereof Pending CN111470826A (en)