CN111098573A - 一种双面9h柔韧纤维膜 - Google Patents
一种双面9h柔韧纤维膜 Download PDFInfo
- Publication number
- CN111098573A CN111098573A CN202010017329.4A CN202010017329A CN111098573A CN 111098573 A CN111098573 A CN 111098573A CN 202010017329 A CN202010017329 A CN 202010017329A CN 111098573 A CN111098573 A CN 111098573A
- Authority
- CN
- China
- Prior art keywords
- fiber
- sided
- double
- fibers
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于保护膜技术领域，具体涉及一种双面9H柔韧纤维膜，包括有机树脂层、二氧化硅层和加硬层，所述加硬层位于有机树脂层的两侧，所述二氧化硅层位于所述有机树脂层和所述加硬层之间，所述有机树脂层由50‑70%的纤维、15‑20%二氧化硅和余量的助剂组成，所述加硬层由有机硅基树脂和/或有机硅基树脂，经过紫外辐射或热固化处理而成；本发明的9H柔韧纤维膜结构，主要解决现市面所用膜片，表面硬度、柔韧、爆裂、耐刮伤、抗油污、易清洁等不良现象，大大提升消费者对本产品的使用体验。
Description
技术领域
本发明属于保护膜技术领域，具体涉及一种双面9H柔韧纤维膜。
背景技术
柔韧纤维膜，主要应运于电子产品屏幕保护膜，改善解决现市面膜片表面硬度、柔韧、爆裂、耐刮伤、抗油污、易清洁等不良现象，现市场膜片，主要还是PET膜，其表面硬度均在3H至6H内，且表面易刮伤（花）、抗油污差、无防爆效果。
发明内容
本发明提供了一种双面9H柔韧纤维膜，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种双面9H柔韧纤维膜，包括有机树脂层、二氧化硅层和加硬层，所述加硬层位于有机树脂层的两侧，所述二氧化硅层位于所述有机树脂层和所述加硬层之间，所述有机树脂层由70%的纤维、15-20%二氧化硅和余量的助剂组成，所述加硬层由有机硅基树脂和/或有机硅基树脂，经过紫外辐射或热固化处理而成。
优选的，所述有机硅基树脂通过紫外线吸收剂、附着促进剂或增韧剂进行改性。
优选的，所述纤维包括有机纤维和合成纤维，有机纤维为聚对苯二甲酸乙二醇酯纤维、聚丙烯腈纤维、聚酰胺纤维、聚丙烯纤维、芳香族聚酰胺纤维、超高分子量聚乙烯纤维、聚对苯撑苯并双恶唑纤维或聚酰亚胺纤维中的一种，合成纤维为聚丙烯纤维、聚丙烯腈纤维或聚乙烯醇缩甲醛纤维中的一种。
优选的，所述有机树脂为聚碳酸酯、丙烯腈-丁二烯-苯乙烯共聚物、聚酰胺12或尼龙12。
优选的，所述紫外线吸收剂为邻羟基苯甲酸苯酯、2-2ˊ-羟基-5ˊ-甲基苯基苯并三氮唑、2，4-二羟基二苯甲酮、2-羟基-4-甲氧基二苯甲酮或2-羟基-4-正辛氧基二苯甲酮中的一种。
优选的，所述附着促进剂为氰基乙酰氧基类湿附着力促进剂、乙酰乙酸类促进剂或脲环类湿附着力促进剂中的一种。
优选的，所述增韧剂为聚乙烯醇缩丁醛、聚醚砜或聚苯醚酮中的一种。
与现有技术相比，本发明的有益效果是：
本发明的9H柔韧纤维膜结构，主要解决现市面所用膜片，表面硬度、柔韧、爆裂、耐刮伤、抗油污、易清洁等不良现象，大大提升消费者对本产品的使用体验。
附图说明
附图用来提供对本发明的进一步理解，并且构成说明书的一部分，与本发明的实施例一起用于解释本发明，并不构成对本发明的限制。在附图中：
图1为本发明的结构示意图。
图中：1、第一加硬层；2、有机树脂层；3、第二加硬层。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
请参阅图1，本发明提供以下技术方案：一种双面9H柔韧纤维膜，包括有机树脂层2、二氧化硅层和加硬层，所述加硬层位于有机树脂层2的两侧（第一加硬层1和第二加硬层3），所述二氧化硅层位于所述有机树脂层和所述加硬层之间，所述有机树脂层由70%的纤维、15-20%二氧化硅和余量的助剂组成，所述加硬层由有机硅基树脂和有机硅基树脂，经过紫外辐射处理而成。
具体的，所述有机硅基树脂通过紫外线吸收剂、附着促进剂和增韧剂进行改性。
具体的，所述纤维包括有机纤维和合成纤维，有机纤维为聚对苯二甲酸乙二醇酯纤维、聚丙烯腈纤维、聚酰胺纤维、聚丙烯纤维、芳香族聚酰胺纤维、超高分子量聚乙烯纤维、聚对苯撑苯并双恶唑纤维或聚酰亚胺纤维中的一种，合成纤维为聚丙烯纤维、聚丙烯腈纤维或聚乙烯醇缩甲醛纤维中的一种。
具体的，所述有机树脂为聚碳酸酯、丙烯腈-丁二烯-苯乙烯共聚物、聚酰胺12或尼龙12。
具体的，所述紫外线吸收剂为邻羟基苯甲酸苯酯、2-2ˊ-羟基-5ˊ-甲基苯基苯并三氮唑、2，4-二羟基二苯甲酮、2-羟基-4-甲氧基二苯甲酮或2-羟基-4-正辛氧基二苯甲酮中的一种。
具体的，所述附着促进剂为氰基乙酰氧基类湿附着力促进剂、乙酰乙酸类促进剂或脲环类湿附着力促进剂中的一种。
具体的，所述增韧剂为聚乙烯醇缩丁醛、聚醚砜或聚苯醚酮中的一种。
实施例2
请参阅图1，本发明提供以下技术方案：一种双面9H柔韧纤维膜，包括有机树脂层、二氧化硅层2和加硬层，所述加硬层位于有机树脂层2的两侧（第一加硬层1和第二加硬层3），所述二氧化硅层位于所述有机树脂层和所述加硬层之间，所述有机树脂层由60%的纤维、15-20%二氧化硅和余量的助剂组成，所述加硬层由有机硅基树脂和/或有机硅基树脂，经过热固化处理而成。
具体的，所述有机硅基树脂通过附着促进剂和增韧剂进行改性。
具体的，所述纤维包括有机纤维和合成纤维，有机纤维为聚对苯二甲酸乙二醇酯纤维、聚丙烯腈纤维、聚酰胺纤维、聚丙烯纤维、芳香族聚酰胺纤维、超高分子量聚乙烯纤维、聚对苯撑苯并双恶唑纤维或聚酰亚胺纤维中的一种，合成纤维为聚丙烯纤维、聚丙烯、腈纤维或聚乙烯醇缩甲醛纤维中的一种。
具体的，所述二氧化硅为纤维，有机树脂为溶液合成，合成柔韧的纤维体。
具体的，所述有机树脂为聚碳酸酯、丙烯腈-丁二烯-苯乙烯共聚物、聚酰胺12或尼龙12。
具体的，所述附着促进剂为氰基乙酰氧基类湿附着力促进剂、乙酰乙酸类促进剂或脲环类湿附着力促进剂中的一种。
具体的，所述增韧剂为聚乙烯醇缩丁醛、聚醚砜或聚苯醚酮中的一种。
实施例3
请参阅图1，本发明提供以下技术方案：一种双面9H柔韧纤维膜，包括有机树脂层、二氧化硅层2和加硬层，所述加硬层位于有机树脂层2的两侧（第一加硬层1和第二加硬层3），所述二氧化硅层位于所述有机树脂层和所述加硬层之间，所述有机树脂层由50%的纤维、15-20%二氧化硅和余量的助剂组成，所述加硬层由有机硅基树脂和/或有机硅基树脂，经过紫外辐射或热固化处理而成。
具体的，所述有机硅基树脂通过紫外线吸收剂、附着促进剂或增韧剂进行改性。
具体的，所述纤维包括有机纤维和合成纤维，有机纤维为聚对苯二甲酸乙二醇酯纤维、聚丙烯腈纤维、聚酰胺纤维、聚丙烯纤维、芳香族聚酰胺纤维、超高分子量聚乙烯纤维、聚对苯撑苯并双恶唑纤维或聚酰亚胺纤维中的一种，合成纤维为聚丙烯纤维、聚丙烯腈纤维或聚乙烯醇缩甲醛纤维中的一种。
具体的，所述有机树脂为聚碳酸酯、丙烯腈-丁二烯-苯乙烯共聚物、聚酰胺12或尼龙12。
具体的，所述紫外线吸收剂为邻羟基苯甲酸苯酯、2-2ˊ-羟基-5ˊ-甲基苯基苯并三氮唑或2，4-二羟基二苯甲酮中的一种。
具体的，所述附着促进剂为氰基乙酰氧基类湿附着力促进剂、乙酰乙酸类促进剂或脲环类湿附着力促进剂中的一种。
具体的，所述增韧剂为聚乙烯醇缩丁醛、聚醚砜或聚苯醚酮中的一种。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (7)
1.一种双面9H柔韧纤维膜，其特征在于：包括有机树脂层、二氧化硅层和加硬层，所述加硬层位于有机树脂层的两侧，所述二氧化硅层位于所述有机树脂层和所述加硬层之间，所述有机树脂层由50-70%的纤维、15-20%二氧化硅和余量的助剂组成，所述加硬层由有机硅基树脂和/或有机硅基树脂，经过紫外辐射或热固化处理而成。
2.根据权利要求1所述的一种双面9H柔韧纤维膜，其特征在于：所述有机硅基树脂通过紫外线吸收剂、附着促进剂或增韧剂进行改性。
3.根据权利要求1所述的一种双面9H柔韧纤维膜，其特征在于：所述纤维包括有机纤维和合成纤维，有机纤维为聚对苯二甲酸乙二醇酯纤维、聚丙烯腈纤维、聚酰胺纤维、聚丙烯纤维、芳香族聚酰胺纤维、超高分子量聚乙烯纤维、聚对苯撑苯并双恶唑纤维或聚酰亚胺纤维中的一种，合成纤维为聚丙烯纤维、聚丙烯腈纤维或聚乙烯醇缩甲醛纤维中的一种。
4.根据权利要求1所述的一种双面9H柔韧纤维膜，其特征在于：所述有机树脂为聚碳酸酯、丙烯腈-丁二烯-苯乙烯共聚物、聚酰胺12或尼龙12。
5.根据权利要求2所述的一种双面9H柔韧纤维膜，其特征在于：所述紫外线吸收剂为邻羟基苯甲酸苯酯、2-2ˊ-羟基-5ˊ-甲基苯基苯并三氮唑、2，4-二羟基二苯甲酮、2-羟基-4-甲氧基二苯甲酮或2-羟基-4-正辛氧基二苯甲酮中的一种。
6.根据权利要求2所述的一种双面9H柔韧纤维膜，其特征在于：所述附着促进剂为氰基乙酰氧基类湿附着力促进剂、乙酰乙酸类促进剂或脲环类湿附着力促进剂中的一种。
7.根据权利要求2所述的一种双面9H柔韧纤维膜，其特征在于：所述增韧剂为聚乙烯醇缩丁醛、聚醚砜或聚苯醚酮中的一种。