CN110372313A - Granite powder stone material and preparation method thereof - Google Patents
Granite powder stone material and preparation method thereof Download PDFInfo
- Publication number
- CN110372313A CN110372313A CN201910695015.7A CN201910695015A CN110372313A CN 110372313 A CN110372313 A CN 110372313A CN 201910695015 A CN201910695015 A CN 201910695015A CN 110372313 A CN110372313 A CN 110372313A
- Authority
- CN
- China
- Prior art keywords
- parts
- stone material
- granite
- stone
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to stone material fields, especially granite powder stone material and preparation method thereof.The parts by weight of each raw material of the stone material are as follows: the parts by weight of each raw material of stone material are as follows: 20-80 parts of kaolin, 30-80 parts of granite granulated slag, 0.6-7 parts of sodium metasilicate, 0.4-5 parts of water.The present invention is primary raw material using kaolin, granite stone powder, binder, processed to fire.Granite waste stone dust dioxide-containing silica is high, mainly by mineral compositions such as quartz, feldspar and a small amount of micas.The stone material being prepared into using granite waste stone dust, had not only realized the resource utilization of waste stone dust, but also expanded the source of stone material, solved the problems, such as that rock material resource is in short supply, promoted environmentally friendly production model.
Description
Technical field
The present invention relates to stone material fields, especially granite powder stone material and preparation method thereof.
Background technique
Granite will carry out the requirement that cutting is just able to satisfy people, but many granulated slags can be generated in cutting process, due to powder
The partial size very little of slag is not used as the coarse-fine aggregate of concrete, so being just poured into farmland, not only pollutes environment, Er Qiezao
At very big waste, because there is the nearly 30% granite granulated slag water that can be cooled to take away in cutting process.Discarded mountain flour meeting
Irreversible environmental pollution is caused, the life of the periphery inhabitation people is seriously endangered.And among the existing manufacturing, these are useless
The mountain flour of abandoning can not be to handle and utilize.
Summary of the invention
In order to solve the deficiencies in the prior art described in background technique, the present invention provides a kind of granite powder stone material and its systems
Preparation Method is primary raw material using kaolin, granite stone powder, binder, processed to fire.Granite waste stone dust dioxy
SiClx content is high, mainly by mineral compositions such as quartz, feldspar and a small amount of micas.The stone material being prepared into using granite waste stone dust,
Not only the resource utilization of waste stone dust had been realized, but also has expanded the source of stone material, has solved the problems, such as that rock material resource is in short supply, had been promoted
Environmentally friendly production model.
The technical solution adopted by the present invention to solve the technical problems is:
A kind of granite powder stone material, the parts by weight of each raw material of the stone material are as follows:
20-80 parts of kaolin, 30-80 parts of granite granulated slag, 0.6-7 parts of sodium metasilicate, 0.4-5 parts of water.
Specifically, described kaolin 20-70 parts, 30-70 parts of granite granulated slag, 0.6-6 parts of sodium metasilicate, 0.4-4 parts of water.
Specifically, described kaolin 20-75 parts, 30-75 parts of granite granulated slag, 0.6-5 parts of sodium metasilicate, 0.4-3 parts of water.
A kind of preparation method of granite powder stone material, comprising the following steps:
A. it after smashing kaolin, granite granulated slag to pieces, is proportionally added into blender and is stirred mixing, obtain mixture
One；
B. then sodium metasilicate and water are proportionally added in mixture one and are stirred mixing, obtain mixture two；
C. mixture two is put into vibration-extrusion in stone material mold to form, obtains stone material；
D., the stone material of extrusion forming is cut into the plate of various criterion size with makita 4100NH；
E. the plate of well cutting is air-dried at aeration-drying, after surface is whitened, is put into kiln road and is sintered 24 hours
Obtain finished product stone material.
Specifically, the partial size of kaolin and granite powder after smashing to pieces is respectively less than 1mm.
Specifically, the time being stirred is 20~60 minutes.
Specifically, the time being stirred is 20~60 minutes.
The beneficial effects of the present invention are: passing through kaolin, flower the present invention provides a kind of granite powder stone material and preparation method thereof
Hilllock Rock Powder, binder etc. are primary raw material, processed to fire.Granite waste stone dust dioxide-containing silica is high, mainly by
The mineral compositions such as quartz, feldspar and a small amount of mica.The stone material being prepared into using granite waste stone dust had both realized the money of waste stone dust
Sourceization utilizes, and expands the source of stone material, solves the problems, such as that rock material resource is in short supply, promotes environmentally friendly production mould
Formula.
Specific embodiment
The application is blended the granite granulated slag cooperation multiple material generated during Granite-cutting, it is final resulting
A kind of granite powder stone material, compression strength average value are 100-300Mpa, and therefore, the application not only solves granite granulated slag
Pollution problem has achieved the purpose that turn waste into wealth, and meets the needs of state guarantee environment purpose.
Embodiment one:
A kind of granite powder stone material, the parts by weight of each raw material of the stone material are as follows:
20-80 parts of kaolin, 30-80 parts of granite granulated slag, 0.6-7 parts of sodium metasilicate, 0.4-5 parts of water.
Embodiment two:
A kind of granite powder stone material, the parts by weight of each raw material of the stone material are as follows:
20-70 parts of kaolin, 30-70 parts of granite granulated slag, 0.6-6 parts of sodium metasilicate, 0.4-4 parts of water.
Embodiment three:
A kind of granite powder stone material, the parts by weight of each raw material of the stone material are as follows:
20-75 parts of kaolin, 30-75 parts of granite granulated slag, 0.6-5 parts of sodium metasilicate, 0.4-3 parts of water.Stone material the preparation method comprises the following steps:
(1), material is smashed to pieces
Kaolin, granite granulated slag are smashed to pieces, control partial size is less than 1mm:
(2), ingredient mixes
It will be stirred 20~60 minutes under material room temperature that step (1) is smashed to pieces, obtain mixture 1；
(3), it stirs
Sodium metasilicate and water are added in the resulting mixture 1 of step (2), room temperature whisks mixing 20~60 minutes, obtains mixture
2:
(4) stone material forms
The resulting mixture 2 of step (3) is put into vibration-extrusion molding in stone material mold:
(5), stone material is cut
The stone material of step (4) extrusion forming is cut into the plate of various criterion size on makita 4100NH:
(6), it air-dries and bakes
Step (5) resulting standard plate is air-dried at aeration-drying, after surface is whitened, is put into 800-1200 degrees Celsius
It is sintered 5-24 hours in kiln road, up to a kind of granite powder Novel stone of the invention.
Above-mentioned resulting granite granulated slag Novel stone is by being sintered common Stone Strength test (GB/T 2542-2003)
Method measure its average strength be 100-300MPa.The compression strength average value for meeting the stone material of national regulation is not less than
The requirement of 100MPa, to illustrate that granite powder debris material of the invention its intensity after being mixed with granite granulated slag meets state
The compression strength requirement of stone material as defined in family, and granite is the waste abandoned, it is not necessary to cost, to reduce stone material
Production cost, and solve problem of environmental pollution, realizing turns waste into wealth.
Taking the above-mentioned ideal embodiment according to the present invention as inspiration, through the above description, relevant staff completely may be used
Without departing from the scope of the technological thought of the present invention', to carry out various changes and amendments.The technical model of this invention
It encloses and is not limited to the contents of the specification, it is necessary to which the technical scope thereof is determined according to the scope of the claim.
Claims (7)
1. a kind of granite powder stone material, which is characterized in that the parts by weight of each raw material of the stone material are as follows: 20-80 parts of kaolin,
30-80 parts of granite granulated slag, 0.6-7 parts of sodium metasilicate, 0.4-5 parts of water.
2. granite powder stone material according to claim 1 and preparation method thereof, which is characterized in that the kaolin 20-70
Part, 30-70 parts of granite granulated slag, 0.6-6 parts of sodium metasilicate, 0.4-4 parts of water.
3. granite powder stone material according to claim 1 and preparation method thereof, which is characterized in that the kaolin 20-75
Part, 30-75 parts of granite granulated slag, 0.6-5 parts of sodium metasilicate, 0.4-3 parts of water.
4. a kind of preparation method of granite powder stone material according to claim 1 or 2 or 3, which is characterized in that including following
Step:
A. it after smashing kaolin, granite granulated slag to pieces, is proportionally added into blender and is stirred mixing, obtain mixture
One；
B. then sodium metasilicate and water are proportionally added in mixture one and are stirred mixing, obtain mixture two；
C. mixture two is put into vibration-extrusion in stone material mold to form, obtains stone material；
D., the stone material of extrusion forming is cut into the plate of various criterion size with makita 4100NH；
E. the plate of well cutting is air-dried at aeration-drying, after surface is whitened, is put into kiln road and is sintered 24 hours
Obtain finished product stone material.
5. the preparation method of granite powder stone material according to claim 4, which is characterized in that the height in step a, after smashing to pieces
The partial size of ridge soil and granite powder is respectively less than 1mm.
6. the preparation method of granite powder stone material according to claim 4, which is characterized in that in step a, be stirred
Time is 20~60 minutes.
7. the preparation method of granite powder stone material according to claim 4, which is characterized in that in step b, be stirred
Time is 20~60 minutes.