CN110306343A - A kind of preparation process of uvioresistant textile cloth - Google Patents
A kind of preparation process of uvioresistant textile cloth Download PDFInfo
- Publication number
- CN110306343A CN110306343A CN201910532232.4A CN201910532232A CN110306343A CN 110306343 A CN110306343 A CN 110306343A CN 201910532232 A CN201910532232 A CN 201910532232A CN 110306343 A CN110306343 A CN 110306343A
- Authority
- CN
- China
- Prior art keywords
- cloth
- uvioresistant
- time
- dyes
- altogether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to textile cloth technical fields, more particularly to a kind of preparation process of uvioresistant textile cloth, the purpose of the present invention is to provide a kind of preparation processes of uvioresistant textile cloth for improving production uvioresistant textile cloth efficiency, a kind of preparation process of uvioresistant textile cloth, include the following steps: that (1) cloth weaves: cloth is woven from by acrylic fibers warp thread and terylene weft yarn；(2) cloth uvioresistant and the total bath process of dyeing: uvioresistant is prepared using organic dyestuff and uvioresistant finishing agent and dyes bath foam altogether, the content that uvioresistant dyes organic dyestuff in bath foam altogether is 1.5%-3%, the additive amount of uvioresistant finishing agent is 15g/L-25g/L, will be woven after cloth immerse 100 DEG C -120 DEG C of uvioresistant and dye and impregnate 28min-40min in bath foam altogether；(3) cloth pads: by treated, cloth pad for the first time, and padding the time is 20s-35s, pick-up 55%-70%, and the cloth after padding for the first time is padded for the second time, and padding the time is 15s-35s, pick-up 45%-60%.
Description
Technical field
The invention belongs to textile cloth technical field more particularly to a kind of preparation processes of uvioresistant textile cloth.
Background technique
With the continuous development of science and technology, people have recognized a kind of sightless light --- ultraviolet light, and with its quilt
After being confirmed as one of cutaneum carcinoma inducement, people is made to recognize the fearful degree of ultraviolet light deeply, however in real life, by
Contain ultraviolet light in sunlight, so that ultraviolet light is nearly ubiquitous, therefore people especially pay attention to the protection of ultraviolet light,
But have to long-time exposure in the case where direct sunlight under the pressure of various reasons people, since skin receives largely
Ultraviolet light and cause to tan severely, cloth as protection people's skin one of defence line, anti-ultraviolet performance is increasingly by people
Concern, the textile cloth with anti-ultraviolet function is constantly subjected to the extensive favor of people, however existing uvioresistant
Dyeing and anti-ultraviolet radiation treatment technique are independently run in the preparation process of textile cloth, so that existing uvioresistant
The preparation process of line textile cloth is excessively cumbersome, and the efficiency for producing uvioresistant textile cloth is lower.
Summary of the invention
For the problems in background, the purpose of the present invention is to provide a kind of raising production uvioresistant textile cloth effects
The preparation process of the uvioresistant textile cloth of rate.
To achieve the above object, the present invention provides the following technical solutions:
A kind of preparation process of uvioresistant textile cloth, includes the following steps:
(1) cloth weaves: cloth is woven from by acrylic fibers warp thread and terylene weft yarn；
(2) it cloth uvioresistant and dyes bath process altogether: being prepared using organic dyestuff with uvioresistant finishing agent anti-
Ultraviolet light dyes bath foam altogether, and the content that the uvioresistant dyes organic dyestuff described in bath foam altogether is 1.5%-3%, described
The additive amount of uvioresistant finishing agent is 15g/L-25g/L, will be woven after cloth immerse 100 DEG C -120 DEG C of uvioresistant
It dyes in bath foam altogether and impregnates 28min-40min；
(3) cloth pads: by treated, cloth pad for the first time, and padding the time is 20s-35s, and pick-up is
55%-70% is padded the cloth after padding for the first time for the second time, and padding the time is 15s-35s, pick-up 45%-
60%；
(4) cloth sizing fixation: by treated, cloth uses 115 DEG C -150 DEG C of temperature to dry cloth, so
Afterwards by the cloth after drying in 200 DEG C of -230 DEG C of baking 90s-130s.
In order to improve the anti-uv-ray of cloth, it further includes organic nickel polymerization in bath foam altogether that the uvioresistant, which dyes,
Object, crosslinking agent and bleeding agent, the content that every liter of uvioresistant dyes organic nickel polymer in bath foam altogether is 18-28g, crosslinking agent
Content be 3g-5.5g, the content of bleeding agent is 1-2g.
In order to improve cloth dyeing efficiency, and the effect of anti-ultraviolet radiation treatment is improved, the uvioresistant dyeing bath altogether
It further include dispersing agent in liquid, the content that every liter of uvioresistant dyes dispersing agent in bath foam altogether is 2-5mL.
Compared with prior art, the beneficial effects of the present invention are as follows: the preparation work of new structural uvioresistant textile cloth
Skill by cloth uvioresistant and dyes bath process altogether, can realize while dyeing at the uvioresistant to textile cloth
Reason, the process flow of " woven fabric-dyeing-sizing-cleaning-drying-anti-ultraviolet radiation treatment-pads-shaping and drying " is reduced to
" woven fabric-uvioresistant and dyeing are bathed altogether-pads-shaping and drying ", and can be by anti-purple by 200 DEG C -230 DEG C of baking
The thawing of outside line pulvis sticks on cloth, so that the cloth satisfaction prepared by this technique is not easy decoloration and long-acting uvioresistant
Function, improve production uvioresistant textile cloth efficiency.
Specific embodiment
In order to be more clearly understood that technical solution of the present invention, the present invention is carried out in conjunction with following instance further detailed
Explanation.It should be appreciated that specific embodiment described herein is only used to explain invention, it is not intended to limit the present invention.
Embodiment 1
A kind of preparation process of uvioresistant textile cloth, includes the following steps:
(1) cloth weaves: cloth is woven from by acrylic fibers warp thread and terylene weft yarn；
(2) it cloth uvioresistant and dyes bath process altogether: being prepared using organic dyestuff with uvioresistant finishing agent anti-
Ultraviolet light dyes bath foam altogether, and the content that the uvioresistant dyes organic dyestuff described in bath foam altogether is 1.5%, the anti-purple
The additive amount of outside line finishing agent is 15g/L, will be woven after cloth immerse 100 DEG C of uvioresistant and dye and impregnate in bath foam altogether
30min；
(3) cloth pads: treated cloth pad for the first time, padding the time is 20s, pick-up 55%,
Cloth after padding for the first time is padded for the second time, padding the time is 15s, pick-up 45%；
(4) cloth sizing fixation: by treated, cloth uses 115 DEG C of temperature to dry cloth, then will dry
Cloth after dry is in 200 DEG C of baking 130s.
Embodiment 2
A kind of preparation process of uvioresistant textile cloth, includes the following steps:
(1) cloth weaves: cloth is woven from by acrylic fibers warp thread and terylene weft yarn；
(2) it cloth uvioresistant and dyes bath process altogether: being prepared using organic dyestuff with uvioresistant finishing agent anti-
Ultraviolet light dyes bath foam altogether, and the content that the uvioresistant dyes organic dyestuff described in bath foam altogether is 2%, the uvioresistant
The additive amount of line finishing agent is 20g/L, will be woven after cloth immerse 110 DEG C of uvioresistant and dye and impregnate in bath foam altogether
35min；
(3) cloth pads: treated cloth pad for the first time, padding the time is 25s, pick-up 65%,
Cloth after padding for the first time is padded for the second time, padding the time is 20s, pick-up 55%；
(4) cloth sizing fixation: by treated, cloth uses 130 DEG C of temperature to dry cloth, then will dry
Cloth after dry is in 220 DEG C of baking 110s.
Embodiment 3
A kind of preparation process of uvioresistant textile cloth, includes the following steps:
(1) cloth weaves: cloth is woven from by acrylic fibers warp thread and terylene weft yarn；
(2) it cloth uvioresistant and dyes bath process altogether: being prepared using organic dyestuff with uvioresistant finishing agent anti-
Ultraviolet light dyes bath foam altogether, and the content that the uvioresistant dyes organic dyestuff described in bath foam altogether is 3%, the uvioresistant
The additive amount of line finishing agent is 25g/L, will be woven after cloth immerse 120 DEG C of uvioresistant and dye and impregnate in bath foam altogether
40min；
(3) cloth pads: treated cloth pad for the first time, padding the time is 35s, pick-up 70%,
Cloth after padding for the first time is padded for the second time, padding the time is 35s, pick-up 60%；
(4) cloth sizing fixation: by treated, cloth uses 150 DEG C of temperature to dry cloth, then will dry
Cloth after dry is in 230 DEG C of baking 90s.
Present invention discloses a kind of preparation process of uvioresistant textile cloth, using uvioresistant finishing agent with it is organic
The uvioresistant that dyestuff is prepared jointly dyes bath foam altogether, realizes anti-ultraviolet radiation treatment and dyeing while carrying out, shortens work
Skill process, and ensure that the uvioresistant textile cloth being prepared is not easy decoloration and long-acting anti-ultraviolet function, in turn
Reduce the Meteorological of equipment, and improves the preparation efficiency of uvioresistant textile cloth.
In description in this article, unless otherwise indicated, the meaning of " plurality " is two or more；Term " on ",
The orientation or positional relationship of "lower", "left", "right", "inner", "outside", " front end ", " rear end ", the instructions such as " head ", " tail portion " is
Orientation or positional relationship shown in being based on, is merely for convenience of description of the present invention and simplification of the description, rather than indication or suggestion institute
The device or element of finger must have a particular orientation, be constructed and operated in a specific orientation, therefore should not be understood as to this hair
Bright limitation.In description in this article, it should be noted that unless otherwise clearly defined and limited, term " connected ",
" connection " shall be understood in a broad sense, for example, it may be being fixedly connected, may be a detachable connection, or be integrally connected；It can be with
It is mechanical connection, is also possible to be electrically connected, can be directly connected, it can also be indirectly connected through an intermediary.For ability
For the those of ordinary skill in domain, the concrete meaning of above-mentioned term in the present invention can be understood with concrete condition.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, without necessarily requiring or implying between these entities or operation
There are any actual relationship or orders.Moreover, the terms "include", "comprise" or its any other variant are intended to
Cover non-exclusive inclusion, so that the process, method, article or equipment for including a series of elements not only includes that
A little elements, but also including other elements that are not explicitly listed, or further include for this process, method, article or
The intrinsic element of equipment.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright specification and content is applied directly or indirectly in other relevant technologies
Field is included within the scope of the present invention.
Claims (3)
1. a kind of preparation process of uvioresistant textile cloth, which comprises the steps of:
(1) cloth weaves: cloth is woven from by acrylic fibers warp thread and terylene weft yarn；
(2) uvioresistant cloth uvioresistant and the total bath process of dyeing: is prepared using organic dyestuff and uvioresistant finishing agent
Line dyes bath foam altogether, and the content that the uvioresistant dyes organic dyestuff described in bath foam altogether is 1.5%-3%, the uvioresistant
The additive amount of line finishing agent be 15g/L-25g/L, will be woven after cloth immerse 100 DEG C -120 DEG C uvioresistant dyeing altogether bath
28min-40min is impregnated in liquid；
(3) cloth pads: by treated, cloth pad for the first time, and padding the time is 20s-35s, pick-up 55%-
70%, the cloth after padding for the first time is padded for the second time, padding the time is 15s-35s, pick-up 45%-60%；
(4) cloth sizing fixation: by treated, cloth uses 115 DEG C -150 DEG C of temperature to dry cloth, then will
Cloth after drying is in 200 DEG C of -230 degrees Celsius of baking 90s-130s.
2. a kind of preparation process of uvioresistant textile cloth according to claim 1, it is characterised in that: the uvioresistant
It further includes organic nickel polymer, crosslinking agent and bleeding agent in bath foam altogether that line, which dyes, and every liter of uvioresistant dyes organic in bath foam altogether
The content of nickel polymer is 18-28g, the content of crosslinking agent is 3g-5.5g, the content of bleeding agent is 1-2g.
3. a kind of preparation process of uvioresistant textile cloth according to claim 1, it is characterised in that: the uvioresistant
It further includes dispersing agent in bath foam altogether that line, which dyes, and the content that every liter of uvioresistant dyes dispersing agent in bath foam altogether is 2-5mL.