CN110193755A - A kind of carbon fibre composite grinding processing method - Google Patents
A kind of carbon fibre composite grinding processing method Download PDFInfo
- Publication number
- CN110193755A CN110193755A CN201910398045.1A CN201910398045A CN110193755A CN 110193755 A CN110193755 A CN 110193755A CN 201910398045 A CN201910398045 A CN 201910398045A CN 110193755 A CN110193755 A CN 110193755A
- Authority
- CN
- China
- Prior art keywords
- carbon fibre
- grinding
- fibre composite
- processing method
- face
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to carbon fibre composite technical fields of mechanical processing, a kind of carbon fibre composite grinding processing method, using vertical type numerically controlled machine, by applying cup type skive, vertical end face corase grinding and fine grinding carried out to carbon fibre composite square plate surface, including the cooling face to be processed of clamping workpiece, cleaning, corase grinding workpiece surface, fine grinding workpiece surface, cleaning is cooling dries up and detect machined surface.Processing technology of the present invention is simple, and clamping fast and stable, easy to operate, tool wear is small, high in machining efficiency, the treatment of surfaces of components finish is good, stress is small, it is not damaged, without layering tearing etc. manufacturing deficiencies.
Description
Technical field
The invention belongs to carbon fibre composite technical field of mechanical processing more particularly to a kind of carbon fibre composite plates
Grinding processing method.
Background technique
Carbon fibre composite has many advantages, such as that light-weight, intensity is high, good rigidity and antifatigue, is widely used in aviation
The industrial circles such as space flight, defence and military and communications and transportation.Carbon fibre composite is made of carbon fiber and resin, is deposited between the two
In complicated interaction relationship, the features such as making material there are anisotropy, additivity, big high rigidity and brittleness, ratio one is processed
As material difficulty it is big.
Currently, most of carbon fibre composite part is to manufacture to complete by straight forming, but produce preferably to be promoted
Moral character energy usually also needs to carry out the following process such as milling, grinding, drilling to it.Drilling can only process hole, and milling, grinding are usual
For plane machining.Wherein Milling Process Part Surface Roughness is in 3.2 microns, and vibration cutting is severe, abrasion condition is serious,
Need frequent tool changing;Traditional grinding mode is mostly Horizontal surface wheel, and grinding temperature is high, easily causes Surface Burning in Grinding, table
Face stress is big, and low efficiency.In addition, the accurate grinding processing technology about carbon fibre composite plate, domestic and international rarely seen correlation
Report.
It therefore, is current machine with regard to how efficient grinding goes out the carbon fibre composite plate part of great surface quality
Tool processing technique field engineering problem urgently to be resolved.
Summary of the invention
To solve the above problems, the present invention provides a kind of carbon fibre composite plate grinding processing method, including it is following
Step:
The processing method uses vertical type numerically controlled machine, by applying cup type skive, to carbon fibre composite side
Shape planar surface carries out vertical end face corase grinding and fine grinding;
Step 1: the carbon fibre composite plate blank clamping being ready for is fixed on platen;
Step 2: by cooling tube to the comprehensive spray cooling liquid of workpiece work surface, surface impurity is washed away, is mentioned simultaneously
Preceding cooling down workpiece;
Step 3: vertical end face corase grinding is carried out to carbon fibre composite plate using cup type skive;
Step 4: after the completion of corase grinding, by adjusting grinding parameter, continue to refine;
Step 5: after fine grinding, cleaning drying, and its surface is detected with contact surface roughometer.
When corase grinding, the speed of mainshaft is 3000~5500rpm, and feed speed is 150~300mm/min, and emery wheel feed amount is
0.1~0.3mm.
When fine grinding, the speed of mainshaft is 5500~7500rpm, and feed speed is 50~200mm/min, and emery wheel feed amount is
0.01~0.05mm.
The clamping tooling can be common tiger's jaw fixture or vacuum chuck.
The cup type skive is composed of knife handle, cutter hub and bistrique three parts, wherein knife handle and cutter hub by
It is 120#~240# that the manufacture of common stainless steel material is manufactured by diamond into, diamond grit at, end face grinding head, and the mill
Head bottom face outer edge has one 30 °~45 ° of chamfering.
When the vertical end face corase grinding and fine grinding, cup type skive central axis and grinding workpiece surface are hung down
Directly, emery wheel grinding-head bottom face is contacted with grinding workpiece surface, and grinding wheel high speed rotation while moves in the horizontal direction, to grind off
Surface surplus.
The corase grinding and fine grinding tool path pattern is two-way round-trip form.
The beneficial effects of the present invention are:
Using carbon fibre composite plate grinding processing method provided by the present invention, by application by stainless steel and Buddha's warrior attendant
The cup type skive that stone is composed carries out two-way round-trip vertical end face high-speed grinding to workpiece made of carbon fiber composite,
Spray cooling liquid, the grinding mode simultaneously in grinding process, can effectively avoid tool wear, piece surface burn, surface
The problems such as stress is excessive, layering is torn and burr, processing technology is simple, and easy to operate, high in machining efficiency, processing quality stabilization can
It leans on.
Detailed description of the invention
Fig. 1 is carbon fibre composite plate grinding schematic diagram;
Fig. 2 is carbon fibre composite plate grinding rear surface roughness measurement result figure.
In figure: 1 carbon fibre composite plate, 2 cup type skives, 3 frock clamps, 4 workbench, 5 cooling tubes, n master
Axis revolving speed, aeThe amount of feeding, V grinding wheel feed speed and direction.
Specific embodiment
Technical solution of the present invention is described further with reference to the accompanying drawing, but required protection scope does not limit to
In described:
The present invention provides a kind of carbon fibre composite plate grinding processing method, comprising the following steps:
Step 1: the carbon fibre composite square plate blank 1 that will be ready for is fixed by common 3 clamping of tiger's jaw fixture
In on platen 4;
Step 2: by cooling tube 5 to the comprehensive spray cooling liquid of 1 work surface of workpiece, surface impurity is washed away, simultaneously
The effect of cooling down workpiece 1 in advance can be played;
Step 3: the cup type skive 2 that by granularity be 240#, bottom end surface chamfer is 45 ° is mounted on R5030 and stands
On formula main shaft of numerical control machine tool, keep grinding wheel central axis vertical with 1 surface of carbon fibre composite plate, main shaft drives grinding wheel rotation,
It feeds down simultaneously, makes end surface of diamond grinding wheel cutting edge contact workpiece, then move grinding, while spray cooling liquid along the direction V,
By way of two-way feed, the corase grinding to carbon fibre composite plate 1 is completed.Speed of mainshaft n is when being wherein ground
5000rpm, the grinding wheel amount of feeding down aeIt is 250mm/min for 0.2mm, feed speed V;
Step 4: after the completion of corase grinding, adjusting grinding parameter, and wherein speed of mainshaft n is set as 6000rpm, grinding wheel downwards into
Give amount aeIt is set as 0.02mm, feed speed V is set as 150mm/min, then continues essence by the processing tool path pattern of corase grinding
Mill;
Step 5: after fine grinding, tiger's jaw fixture 3 is unclamped, carbon fibre composite plate 1 is taken out, with deionized water to it
Surface after grinding is cleaned, and is then dried up, and is finally detected using contact surface roughometer to its surface, surface
Roughness measurement result is Ra0.526 μm, and the results are shown in attached figure 2.
Technical solution of the present invention is walked using vertical cross grinding with two-way back and forth by developing cup type skive
The processing method of knife solves grinding burn, tool wear, surface stress existing for carbon fibre composite plate traditional diamond-making technique
The problems such as excessive, part layering tearing and burr, grinding surface roughness is at 0.6 micron hereinafter, better than common process essence
Degree, it is high in machining efficiency.
Claims (8)
1. a kind of carbon fibre composite grinding processing method, it is characterised in that the following steps are included:
The processing method uses vertical type numerically controlled machine, by applying cup type skive, stands to carbon fibre composite
Formula end face corase grinding and fine grinding;
Step 1: carbon fibre composite plate blank clamping to be processed is fixed on platen;
Step 2: by cooling tube to the comprehensive spray cooling liquid of carbon fibre composite plate blank work surface, table is washed away
Face impurity, while carbon fibre composite plate blank is cooled down in advance;
Step 3: vertical end face corase grinding is carried out to carbon fibre composite plate blank using cup type skive;
When corase grinding, the speed of mainshaft be 3000~5500rpm, feed speed be 150~300mm/min, emery wheel feed amount be 0.1~
0.3mm;
Step 4: after the completion of corase grinding, by adjusting grinding parameter, continue to refine;
Step 5: after fine grinding, cleaning drying, and its surface is detected with contact surface roughometer;
When fine grinding, the speed of mainshaft be 5500~7500rpm, feed speed be 50~200mm/min, emery wheel feed amount be 0.01~
0.05mm。
2. carbon fibre composite grinding processing method according to claim 1, which is characterized in that the cup type Buddha's warrior attendant
Stone sand wheel is combined by knife handle, cutter hub and bistrique three parts, and wherein knife handle and cutter hub are manufactured by common stainless steel material into end face mill
Head is by diamond manufacture at diamond grit is 120#~240#, and the bistrique bottom face outer edge has one 30 °~45 °
Chamfering.
3. carbon fibre composite grinding processing method according to claim 1 or 2, which is characterized in that described is vertical
When end face corase grinding and fine grinding, cup type skive central axis and ground carbon fibre composite plate blank surface hang down
Directly, cup type skive bistrique bottom face is contacted with ground carbon fibre composite plate blank surface, cup type boart boart
It is moved in the horizontal direction while taking turns high speed rotation, to grind off surface surplus.
4. carbon fibre composite grinding processing method according to claim 1 or 2, which is characterized in that the clamping
Tooling used is common tiger's jaw fixture or vacuum chuck.
5. carbon fibre composite grinding processing method according to claim 3, which is characterized in that used in the clamping
Tooling be common tiger's jaw fixture or vacuum chuck.
6. according to claim 1, carbon fibre composite grinding processing method described in 2 or 5, which is characterized in that described is thick
Mill and fine grinding tool path pattern are two-way round-trip form.
7. carbon fibre composite grinding processing method according to claim 3, which is characterized in that the corase grinding and essence
Mill tool path pattern is two-way round-trip form.
8. carbon fibre composite grinding processing method according to claim 4, which is characterized in that the corase grinding and essence
Mill tool path pattern is two-way round-trip form.