CN110170531B - 一种型材轧制的润滑方法 - Google Patents
一种型材轧制的润滑方法 Download PDFInfo
- Publication number
- CN110170531B CN110170531B CN201910529221.0A CN201910529221A CN110170531B CN 110170531 B CN110170531 B CN 110170531B CN 201910529221 A CN201910529221 A CN 201910529221A CN 110170531 B CN110170531 B CN 110170531B
- Authority
- CN
- China
- Prior art keywords
- lubricating
- rolling
- lubricating liquid
- roller
- volume percentage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
技术领域
本发明属于型材轧制领域,尤其涉及一种型材轧制的润滑方法。
背景技术
目前,润滑轧制技术在热轧带钢、冷轧领域有广泛的应用,好处是:1、减少轧制过程中轧辊与轧件之间的摩擦系数,减少电能消耗;2、降低轧制力;3、减少轧辊消耗,提高作业率;4、改善轧后产品表面质量等。但润滑轧制技术在型材的轧制中还没有成熟应用,原因是型材在轧制过程中采用润滑技术后变形复杂,润滑效果影响因素多,不易控制产品尺寸规格。
发明内容
为克服现有技术的不足,本发明的目的是提供一种型材轧制的润滑方法,提高产品表面质量,减少轧辊铁皮粘着。
为实现上述目的,本发明通过以下技术方案实现:
一种型材轧制的润滑方法,采用全孔型润滑方式,将润滑液通过喷嘴对轧辊润滑,润滑液体积百分浓度范围3%-11%,流量范围0.8-1.2m3/h;润滑液压力范围为3-6公斤力;
型材轧制速度、润滑液体积百分浓度、喷射流量的关系:
式(1)中:A是润滑液体积百分浓度;V是轧制速度,单位m/s;Q是喷射流量,单位L/h。
与现有技术相比,本发明的有益效果是:
型材轧制的润滑方法是由润滑液喷射浓度,流量,压力,喷射部位及钢轨轧制速度得到型材最佳的润滑方式,提高了产品表面质量,降低了辊耗、电耗;减少轧辊铁皮粘着,提高轧制节奏,提高生产率。
附图说明
图1是润滑液喷射装置的示意图。
图中:1-上轧辊 2-上喷嘴 3-上辊系横梁 4-下辊系横梁 5-下喷嘴 6-下轧辊 7-型材。
具体实施方式
下面结合说明书附图对本发明进行详细地描述,但是应该指出本发明的实施不限于以下的实施方式。
实施例
见图1,在UF轧机上、下辊系横梁3、4处分别固定上、下喷嘴2、5,上、下喷嘴2、5各布置两个扇形水嘴,扇形水嘴将上、下轧辊1、6全覆盖,以达到全孔型喷射的目的。
采用现场净环水管线供水,流量控制阀控制水流量;原液采用泵电机变频调速方式,通过控制电机转速从而控制原液流量。
采用原液及水在混合器中混合成一定浓度润滑液,润滑液通过扇形水嘴喷射到上、下轧辊1、6表面,实现对型材7润滑目的。
给定润滑液流量及轧制速度,并计算出润滑液体积百分浓度及对应的原液供应量,从而控制相应流量的原液。
设定润滑液体积百分浓度范围3%-11%,流量范围0.8-1.2m3/h。混合液压力范围为3-6公斤力。
钢轨轧制过程润滑系统参数设定;供水压力范围:0.3-0.7Mpa;水流量范围:15-20L/min;原液输出压力范围:0.6-1.5Mpa;原液输出流量范围:0.2-2L/min;混合后润滑液浓度范围为1%-11%。调整参数时保证原液压力大于供水压力。
根据试验结果:润滑液流量1000L/h,轧制速度3.5m/s,浓度3%,在此条件下为最优性价比。
本发明是由润滑液喷射浓度,流量,压力,喷射部位及钢轨轧制速度得到型材最佳的润滑方式,提高了产品表面质量,降低了辊耗、电耗;减少轧辊铁皮粘着,提高轧制节奏,提高生产率。将润滑液喷射在轧辊上,再利用润滑液对型材润滑,实现了全孔型润滑,提高了型材表面质量。
Claims (1)