CN110157352A - A kind of Novel free glue is included to repair tyre cement and its application method - Google Patents
A kind of Novel free glue is included to repair tyre cement and its application method Download PDFInfo
- Publication number
- CN110157352A CN110157352A CN201910520052.4A CN201910520052A CN110157352A CN 110157352 A CN110157352 A CN 110157352A CN 201910520052 A CN201910520052 A CN 201910520052A CN 110157352 A CN110157352 A CN 110157352A
- Authority
- CN
- China
- Prior art keywords
- parts
- tire
- agent
- coupling agent
- tyre cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of included reparation tyre cements of Novel free glue, its raw material is as follows in parts by weight: 60-80 parts of rubber, 3-5 parts of reinforcing filler, 1-2 parts of antiaging agent, 1-2 parts of softening agent, 5-9 parts of silane coupling agent, 5-9 parts of titanate coupling agent, 6-8 parts of aluminate coupling agent, 4-5 parts of boric acid ester coupler, 10-12 parts of vulcanizing agent, 7-9 parts of tetraisopropyl titanate, 15-20 parts of nano material, the present invention in rubber raw materials by being added reinforcing filler, antiaging agent, softening agent, silane coupling agent, titanate coupling agent, aluminate coupling agent, boric acid ester coupler, vulcanizing agent, tetraisopropyl titanate and nano material, not only improve the bond properties of material, and tyre damage position can be repaired, the addition of nano material, improve the benefit The extreme pressure property and wear-resisting property of tire glue, improve the reparation stability to damaged mouth position, and surface will form a hard and bright and clean protection film layer, extend the repairing performance of damaged mouth position.
Description
Technical field
The present invention relates to tyre cement technical field, specially a kind of Novel free glue is included to repair tyre cement, while this hair
It is bright to further relate to a kind of included application method for repairing tyre cement of Novel free glue.
Background technique
Automobile tire is one of important component of automobile, it is directly contacted with road surface and automotive suspension mitigates vapour jointly
Vehicle suffered impact when driving, guarantees that automobile has good driving comfort and ride performance；Guarantee that wheel and road surface have
Good adhesion；Improve traction property, braking and the passability of automobile；The weight that subject automobile, all due to automobile tire
It is rubber product, encounters the sharp iron plate of comparison and nail is easy to stab or directly puncture.
Existing tire repair method mostly uses adhesive tape method tire patching, mushroom nail tire patching and patch tire patching method, existing patch
In tire patching method, tyre cement does not have the repair function to damaged mouth, causes the method service life of patch tire patching not grown, Er Qiechang
After time use, it is easy to which fall off abrasion, and using effect is bad.
Summary of the invention
The purpose of the present invention is to provide a kind of included reparation tyre cement of Novel free glue and its application methods, are not only promoted
The bond properties of material, and tyre damage position can be repaired, and the addition of nano material, improve the benefit
The extreme pressure property and wear-resisting property of tire glue improve the reparation stability to damaged mouth position, while the tyre cement is for a long time
After use, surface will form a hard and bright and clean protection film layer, further extend the toolability of damaged mouth position
Can, to solve the problems mentioned in the above background technology.
To achieve the above object, the invention provides the following technical scheme: a kind of Novel free glue is included to repair tyre cement,
Raw material is as follows in parts by weight: 60-80 parts of rubber, 3-5 parts of reinforcing filler, and 1-2 parts of antiaging agent, 1-2 parts of softening agent, silane
5-9 parts of coupling agent, 5-9 parts of titanate coupling agent, 6-8 parts of aluminate coupling agent, 4-5 parts of boric acid ester coupler, vulcanizing agent 10-12
Part, 7-9 parts of tetraisopropyl titanate, 15-20 parts of nano material.
Preferably, the rubber is any one material in natural rubber and synthetic rubber.
Preferably, the reinforcing filler is the mixture of carbon black, clay, magnesium carbonate and barium carbonate, wherein carbon black, pottery
The mixing match of soil, magnesium carbonate and barium carbonate is 2:1:1:1.
Preferably, the nano material is silica and titanium dioxide mixing material, wherein silica and titanium dioxide
The mixing match of titanium is 1:1.
Preferably, the rubber sequentially adds reinforcing filler, antiaging agent, softening agent, silane after smashing and grinding
Coupling agent, titanate coupling agent, aluminate coupling agent, boric acid ester coupler, vulcanizing agent, tetraisopropyl titanate and nano material are mixed
After conjunction uniformly, this is made through hot melt, extrusion, sizing and exempts from the included reparation tyre cement of glue, and is exempting from the included reparation tyre cement of glue
Tire patching film is made in upper be pasted on tyre cement using sizing gummed paper.
The present invention also provides a kind of included application methods for repairing tyre cement of Novel free glue, include the following steps:
S1: tire dismantling, the wheel where damaged tire are dismantled, and lower tire is taken off, and take off most handy bamboo clappers sled when tire
After playing one side, tire both sides can gently be taken off down to intermediate pressure as far as possible, and when operation prevents violence from tire both sides are staved pair
Tire causes secondary injury；
S2: damaged mouth cleaning finds the damaged mouth position of tire, the foreign matter around cut is cleaned out, and rinses broken
Damage mouth, naturally dry；
S3: grinding process grinds off the oxide layer on surface by grinding process around damaged mouth in tire, and it is new to expose internal layer
Fresh rubber layer；
S4: the material after cleaning polishing is removed the damaged mouth after grinding process and the rubber residues of surrounding clean；
S5: pasting tyre cement, by the breaking of polish of being attached to of the included adhesive surface side for repairing tyre cement of Novel free glue
Position is damaged, 2-3min around tire patching film is pressed lightly on；
S6: after pasting completely, the included sizing gummed paper repaired on tyre cement of Novel free glue is torn it down and is got rid of, and will
It is cleaned out around tyre cement, again by tire according to on automobile, that is, completing the included tyre cement of repairing of the Novel free glue
It uses.
Preferably, automobile tire position is jacked up using jack when being dismantled in the step S1 and is operated.
Preferably, grinding process mode is polished using sand paper in the step S3, what the specification of sand paper used
Specification is 800-1200 mesh.
Compared with prior art, the beneficial effects of the present invention are: the included reparation of the strict control of the present invention Novel free glue
Tyre cement and its application method carry the accounting for repairing each component of formula of tyre cement by strict control Novel free glue,
By the way that reinforcing filler, antiaging agent, softening agent, silane coupling agent, titanate coupling agent, Aluminate are added in rubber raw materials
Coupling agent, boric acid ester coupler, vulcanizing agent, tetraisopropyl titanate and nano material not only improve the bond properties of material, and
And tyre damage position can be repaired, and the addition of nano material, improve the extreme pressure property of the tyre cement and resistance to
Performance is ground, improves the reparation stability to damaged mouth position, while after the tyre cement long-time use, surface will form one
A hard and bright and clean protection film layer, further extends the repairing performance of damaged mouth position.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
A kind of Novel free glue provided by the invention is included to repair tyre cement, data in base-material composition and specific embodiment
Accounting, such as the following table 1:
Embodiment 1
A kind of Novel free glue is included to repair tyre cement, and raw material is as follows in parts by weight: 60 parts of rubber, reinforcing filler
3 parts, 1 part of antiaging agent, 1 part of softening agent, 5 parts of silane coupling agent, 5 parts of titanate coupling agent, 6 parts of aluminate coupling agent, boric acid
4 parts of ester coupling agent, 10 parts of vulcanizing agent, 7 parts of tetraisopropyl titanate, 15 parts of nano material, the rubber is natural rubber and synthesis
Any one material in rubber, the reinforcing filler are the mixture of carbon black, clay, magnesium carbonate and barium carbonate, wherein charcoal
The mixing match of black, clay, magnesium carbonate and barium carbonate is 2:1:1:1, and the nano material is that silica and titanium dioxide are mixed
Condensation material, wherein the mixing match of silica and titanium dioxide is 1:1, and the rubber sequentially adds after smashing and grinding
Reinforcing filler, antiaging agent, softening agent, silane coupling agent, titanate coupling agent, aluminate coupling agent, boric acid ester coupler,
Vulcanizing agent, tetraisopropyl titanate and nano material after mixing, are made this through hot melt, extrusion, sizing and exempt from the included reparation of glue
Tyre cement, and be pasted on tyre cement on exempting from the included reparation tyre cement of glue using sizing gummed paper and tire patching film is made.
When prepared by the Novel free glue included reparation tyre cement, technological parameter temperature data see the table below 2:
| Process | Hot melt | It squeezes out | Sizing |
| Temperature (DEG C) | 130-150 | 130-150 | 0-110 |
The present invention also provides a kind of included application methods for repairing tyre cement of Novel free glue, include the following steps:
S1: tire dismantling, the wheel where damaged tire are dismantled, and lower tire is taken off, and take off most handy bamboo clappers sled when tire
After playing one side, tire both sides can gently be taken off down to intermediate pressure as far as possible, and when operation prevents violence from tire both sides are staved pair
Tire causes secondary injury；
S2: damaged mouth cleaning finds the damaged mouth position of tire, the foreign matter around cut is cleaned out, and rinses broken
Damage mouth, naturally dry；
S3: grinding process grinds off the oxide layer on surface by grinding process around damaged mouth in tire, and it is new to expose internal layer
Fresh rubber layer；
S4: the material after cleaning polishing is removed the damaged mouth after grinding process and the rubber residues of surrounding clean；
S5: pasting tyre cement, by the breaking of polish of being attached to of the included adhesive surface side for repairing tyre cement of Novel free glue
Position is damaged, 2min around tire patching film is pressed lightly on；
S6: after pasting completely, the included sizing gummed paper repaired on tyre cement of Novel free glue is torn it down and is got rid of, and will
It is cleaned out around tyre cement, again by tire according to on automobile, that is, completing the included tyre cement of repairing of the Novel free glue
It uses.
Automobile tire position is jacked up using jack when being dismantled in the step S1 and is operated, is beaten in the step S3
Mill processing mode is polished using sand paper, and the specification that the specification of sand paper uses is 800 mesh.
Embodiment 2
A kind of Novel free glue is included to repair tyre cement, and raw material is as follows in parts by weight: 70 parts of rubber, reinforcing filler
4 parts, 1.5 parts of antiaging agent, 1.5 parts of softening agent, 7 parts of silane coupling agent, 7 parts of titanate coupling agent, 7 parts of aluminate coupling agent,
4.5 parts of boric acid ester coupler, 11 parts of vulcanizing agent, 8 parts of tetraisopropyl titanate, 17.5 parts of nano material, the rubber is natural rubber
Any one material in glue and synthetic rubber, the reinforcing filler are the mixing of carbon black, clay, magnesium carbonate and barium carbonate
Object, wherein the mixing match of carbon black, clay, magnesium carbonate and barium carbonate is 2:1:1:1, and the nano material is silica and two
Titanium oxide mixing material, wherein the mixing match of silica and titanium dioxide be 1:1, the rubber by smashing and grinding after,
Sequentially add reinforcing filler, antiaging agent, softening agent, silane coupling agent, titanate coupling agent, aluminate coupling agent, boric acid
Ester coupling agent, vulcanizing agent, tetraisopropyl titanate and nano material after mixing, are made this through hot melt, extrusion, sizing and exempt from glue
It is included to repair tyre cement, and be pasted on tyre cement on exempting from the included reparation tyre cement of glue using sizing gummed paper and tyre cement is made
Piece.
The present invention also provides a kind of included application methods for repairing tyre cement of Novel free glue, include the following steps:
S1: tire dismantling, the wheel where damaged tire are dismantled, and lower tire is taken off, and take off most handy bamboo clappers sled when tire
After playing one side, tire both sides can gently be taken off down to intermediate pressure as far as possible, and when operation prevents violence from tire both sides are staved pair
Tire causes secondary injury；
S2: damaged mouth cleaning finds the damaged mouth position of tire, the foreign matter around cut is cleaned out, and rinses broken
Damage mouth, naturally dry；
S3: grinding process grinds off the oxide layer on surface by grinding process around damaged mouth in tire, and it is new to expose internal layer
Fresh rubber layer；
S4: the material after cleaning polishing is removed the damaged mouth after grinding process and the rubber residues of surrounding clean；
S5: pasting tyre cement, by the breaking of polish of being attached to of the included adhesive surface side for repairing tyre cement of Novel free glue
Position is damaged, 2.5min around tire patching film is pressed lightly on；
S6: after pasting completely, the included sizing gummed paper repaired on tyre cement of Novel free glue is torn it down and is got rid of, and will
It is cleaned out around tyre cement, again by tire according to on automobile, that is, completing the included tyre cement of repairing of the Novel free glue
It uses.
Automobile tire position is jacked up using jack when being dismantled in the step S1 and is operated, is beaten in the step S3
Mill processing mode is polished using sand paper, and the specification that the specification of sand paper uses is 1000 mesh.
Embodiment 3
A kind of Novel free glue is included to repair tyre cement, and raw material is as follows in parts by weight: 80 parts of rubber, reinforcing filler
5 parts, 2 parts of antiaging agent, 2 parts of softening agent, 9 parts of silane coupling agent, 9 parts of titanate coupling agent, 8 parts of aluminate coupling agent, boric acid
5 parts of ester coupling agent, 12 parts of vulcanizing agent, 9 parts of tetraisopropyl titanate, 20 parts of nano material, the rubber is natural rubber and synthesis
Any one material in rubber, the reinforcing filler are the mixture of carbon black, clay, magnesium carbonate and barium carbonate, wherein charcoal
The mixing match of black, clay, magnesium carbonate and barium carbonate is 2:1:1:1, and the nano material is that silica and titanium dioxide are mixed
Condensation material, wherein the mixing match of silica and titanium dioxide is 1:1, and the rubber sequentially adds after smashing and grinding
Reinforcing filler, antiaging agent, softening agent, silane coupling agent, titanate coupling agent, aluminate coupling agent, boric acid ester coupler,
Vulcanizing agent, tetraisopropyl titanate and nano material after mixing, are made this through hot melt, extrusion, sizing and exempt from the included reparation of glue
Tyre cement, and be pasted on tyre cement on exempting from the included reparation tyre cement of glue using sizing gummed paper and tire patching film is made.
The present invention also provides a kind of included application methods for repairing tyre cement of Novel free glue, include the following steps:
S1: tire dismantling, the wheel where damaged tire are dismantled, and lower tire is taken off, and take off most handy bamboo clappers sled when tire
After playing one side, tire both sides can gently be taken off down to intermediate pressure as far as possible, and when operation prevents violence from tire both sides are staved pair
Tire causes secondary injury；
S2: damaged mouth cleaning finds the damaged mouth position of tire, the foreign matter around cut is cleaned out, and rinses broken
Damage mouth, naturally dry；
S3: grinding process grinds off the oxide layer on surface by grinding process around damaged mouth in tire, and it is new to expose internal layer
Fresh rubber layer；
S4: the material after cleaning polishing is removed the damaged mouth after grinding process and the rubber residues of surrounding clean；
S5: pasting tyre cement, by the breaking of polish of being attached to of the included adhesive surface side for repairing tyre cement of Novel free glue
Position is damaged, 3min around tire patching film is pressed lightly on；
S6: after pasting completely, the included sizing gummed paper repaired on tyre cement of Novel free glue is torn it down and is got rid of, and will
It is cleaned out around tyre cement, again by tire according to on automobile, that is, completing the included tyre cement of repairing of the Novel free glue
It uses.
Automobile tire position is jacked up using jack when being dismantled in the step S1 and is operated, is beaten in the step S3
Mill processing mode is polished using sand paper, and the specification that the specification of sand paper uses is 1200 mesh.
In summary: the strict control of the present invention Novel free glue is included to repair tyre cement and its application method, by tight
Lattice control the accounting of each component of the included formula for repairing tyre cement of Novel free glue, are filled out by the way that reinforcement is added in rubber raw materials
Fill agent, antiaging agent, softening agent, silane coupling agent, titanate coupling agent, aluminate coupling agent, boric acid ester coupler, vulcanization
Agent, tetraisopropyl titanate and nano material not only improve the bond properties of material, but also can carry out to tyre damage position
It repairs, and the addition of nano material, improves the extreme pressure property and wear-resisting property of the tyre cement, improve to damaged mouth position
Reparation stability, while after the tyre cement long-time use, surface will form a hard and bright and clean protection film layer,
Further extend the repairing performance of damaged mouth position.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of Novel free glue is included to repair tyre cement, it is characterised in that: its raw material is as follows in parts by weight: rubber 60-80
Part, 3-5 parts of reinforcing filler, 1-2 parts of antiaging agent, 1-2 parts of softening agent, 5-9 parts of silane coupling agent, titanate coupling agent 5-9
Part, 6-8 parts of aluminate coupling agent, 4-5 parts of boric acid ester coupler, 10-12 parts of vulcanizing agent, 7-9 parts of tetraisopropyl titanate, nanometer material
15-20 parts of material.
2. a kind of Novel free glue according to claim 1 is included to repair tyre cement, it is characterised in that: the rubber is day
Any one material in right rubber and synthetic rubber.
3. a kind of Novel free glue according to claim 1 is included to repair tyre cement, it is characterised in that: the reinforcement and filler
Agent is the mixture of carbon black, clay, magnesium carbonate and barium carbonate, and wherein the mixing match of carbon black, clay, magnesium carbonate and barium carbonate is
2:1:1:1.
4. a kind of Novel free glue according to claim 1 is included to repair tyre cement, it is characterised in that: the nano material
For silica and titanium dioxide mixing material, wherein the mixing match of silica and titanium dioxide is 1:1.
5. a kind of Novel free glue according to claim 1 is included to repair tyre cement, it is characterised in that: the rubber passes through
After smashing and grinding, reinforcing filler, antiaging agent, softening agent, silane coupling agent, titanate coupling agent, Aluminate are sequentially added
Coupling agent, boric acid ester coupler, vulcanizing agent, tetraisopropyl titanate and nano material after mixing, through hot melt, extrusion, sizing
This is made and exempts from the included reparation tyre cement of glue, and is pasted onto tyre cement using sizing gummed paper on tyre cement exempting from glue included repair
On tire patching film is made.
6. a kind of included application method for repairing tyre cement of Novel free glue according to claim 1, it is characterised in that: packet
Include following steps:
S1: tire dismantling, the wheel where damaged tire are dismantled, and lower tire is taken off, and most handy bamboo clappers levers up one when taking off tire
Bian Hou, tire both sides can gently be taken off down to intermediate pressure as far as possible, and when operation prevents violence from tire both sides are staved to tire
Cause secondary injury；
S2: damaged mouth cleaning is found the damaged mouth position of tire, the foreign matter around cut is cleaned out, and rinse damaged mouth,
Naturally dry；
S3: grinding process grinds off the oxide layer on surface by grinding process around damaged mouth in tire, and it is fresh to expose internal layer
Rubber layer；
S4: the material after cleaning polishing is removed the damaged mouth after grinding process and the rubber residues of surrounding clean；
S5: pasting tyre cement, and the included adhesive surface side for repairing tyre cement of Novel free glue is attached to the damaged position polished
It sets, presses lightly on 2-3min around tire patching film；
S6: after pasting completely, the included sizing gummed paper repaired on tyre cement of Novel free glue being torn it down and is got rid of, and by tire patching
It is cleaned out around glue, again by tire according to on automobile, that is, completing the included use for repairing tyre cement of the Novel free glue.
7. a kind of included application method for repairing tyre cement of Novel free glue according to claim 6, it is characterised in that: institute
It states to jack up automobile tire position using jack when dismantling in step S1 and operate.
8. a kind of included application method for repairing tyre cement of Novel free glue according to claim 6, it is characterised in that: institute
It states grinding process mode in step S3 to polish using sand paper, the specification that the specification of sand paper uses is 800-1200 mesh.