CN110154202A - A kind of gauge stuff terrace and decorated gypsum board and preparation method thereof - Google Patents

A kind of gauge stuff terrace and decorated gypsum board and preparation method thereof Download PDF

Info

Publication number
CN110154202A
CN110154202A CN201910314413.XA CN201910314413A CN110154202A CN 110154202 A CN110154202 A CN 110154202A CN 201910314413 A CN201910314413 A CN 201910314413A CN 110154202 A CN110154202 A CN 110154202A
Authority
CN
China
Prior art keywords
parts
main
gypsum
powder
decorated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910314413.XA
Other languages
Chinese (zh)
Other versions
CN110154202B (en
Inventor
何晶
张建龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JINGMEN QIANNIANJIAN HEALTH CARE TECHNOLOGY CO LTD
Original Assignee
JINGMEN QIANNIANJIAN HEALTH CARE TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JINGMEN QIANNIANJIAN HEALTH CARE TECHNOLOGY CO LTD filed Critical JINGMEN QIANNIANJIAN HEALTH CARE TECHNOLOGY CO LTD
Priority to CN201910314413.XA priority Critical patent/CN110154202B/en
Publication of CN110154202A publication Critical patent/CN110154202A/en
Application granted granted Critical
Publication of CN110154202B publication Critical patent/CN110154202B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of gauge stuff terrace and decorated gypsum boards and preparation method thereof, the method includes (1) floral designs design decorative pattern gypsic horizons as needed to manufacture mold, coloured plaster mill base is molded into the decorative pattern gypsic horizon manufacture mold, obtains chromatic pattern plaster block to absolutely dry;(2) the chromatic pattern plaster block that step 1 obtains is put into ground or board mould, main gypsum casting material is molded into the ground or board mould, be frozen into main gypsic horizon to get gauge stuff terrace or decorated gypsum board crude product is arrived;(3) after being placed at room temperature for 2~6h, band water is polished, so that the main gypsum casting material being covered on the chromatic pattern plaster block is washed out by water;Or place to absolutely dry, sander is polished into powder, and blows or sucks to remove powder;The phenomenon that main gypsic horizon combines together with chromatic pattern plaster block, is not in layering in the gauge stuff terrace or decorated gypsum board.

Description

A kind of gauge stuff terrace and decorated gypsum board and preparation method thereof
Technical field
The present invention relates to plastering technical field more particularly to a kind of gauge stuff terrace and decorated gypsum board and its systems Preparation Method.
Background technique
Gypsum is a kind of widely used industrial materials and construction material, can be used for gypsum building products, cement retarder, Modelling, medical food additive, gas washing in SA production, filler, paint filler etc..In recent years, gypsum material and gypsum system Product in the decoration and finishing of architecture indoor using more, especially in the decoration and finishing of home dwelling.With apply other Same type of material is compared, and plastering has the characteristics that quality is relatively light, intensity is higher, fire protecting performance is good, with this material Manufactured plate, flame-retardant grade are level-one, are one of the preferred materials of various environment indoor decoratings.However it is existing Some gypsum sheet materials are whole white, pattern-free, color, and intensity is still to be improved as bottom plate or decorated wall surface.
Summary of the invention
It is an object of the invention to overcome the defect of the prior art, a kind of gauge stuff terrace and decorated gypsum board are provided And preparation method thereof, the phenomenon that main gypsic horizon combines together with chromatic pattern plaster block, is not in layering.
The present invention is implemented as follows:
It is an object of the present invention to provide a kind of preparation methods of gauge stuff terrace, include the following steps:
The preparation of step 1, chromatic pattern plaster block: floral designs design decorative pattern gypsic horizon as needed manufactures mold, Coloured plaster mill base is molded into the decorative pattern gypsic horizon manufacture mold, obtains chromatic pattern plaster block to absolutely dry;
The casting of step 2, gauge stuff terrace: the chromatic pattern plaster block that step 1 obtains is put into ground to be decorated In, main gypsum casting material is cast on ground to be decorated, the main gypsum casting material Self-leveling is in ground and is wrapped in coloured silk Around color patterned plaster block, it is frozen into main gypsic horizon, obtains gauge stuff terrace crude product;
The post-processing of step 3, gauge stuff terrace: after being placed at room temperature for 2~6h, band water is polished, so that being covered on the coloured silk Main gypsum casting material on color patterned plaster block is washed out by water to get gauge stuff terrace finished product is arrived;Or it places to absolutely dry, polishing The main gypsic horizon being covered on the chromatic pattern plaster block is polished into powder by machine, and is blown or sucked and arrived with removing powder Gauge stuff terrace finished product.
The second object of the present invention is to provide the gauge stuff terrace that the method is prepared.
The three of the object of the invention are to provide a kind of preparation method of decorated gypsum board, include the following steps:
The preparation of step 1, chromatic pattern plaster block: floral designs design decorative pattern gypsic horizon as needed manufactures mold, Coloured plaster mill base is molded into the decorative pattern gypsic horizon manufacture mold, obtains chromatic pattern plaster block to absolutely dry;
The casting of step 2, decorated gypsum board: prepare board mould, the chromatic pattern plaster block that step 1 obtains is put into plate In material mold, main gypsum casting material is molded into the board mould, board mould described in the main gypsum casting material Self-leveling It is interior and be wrapped in around chromatic pattern plaster block, main gypsic horizon is frozen into get to decorated gypsum board crude product;
The post-processing of step 3, decorated gypsum board: after the decorated gypsum board crude product that step 2 obtains is placed at room temperature for 2~6h, Band water is polished, so that the main gypsum casting material being covered on the chromatic pattern plaster block is washed out to arrive gauge stuff by water Board finished product;Or place the decorated gypsum board crude product that step 2 obtains to absolutely dry, sander will be covered on the chromatic pattern gypsum Main gypsic horizon on block is polished into powder, and blows or sucks and arrive gauge stuff board finished product to remove powder.
The fourth object of the present invention is to provide the decorated gypsum board that the method is prepared.
Preferably, the coloured plaster mill base in the step 1 based on parts by weight include 80~95 parts of alpha gypsum powder, it is aqueous 4~10 parts of mill base, 0.5~1 part of dispersing agent, 0.5~1 part of retarder and 0.5~2 part of water-reducing agent;
The main gypsum casting material includes 50~85 parts of alpha gypsum powder, 4~10 parts of aqueous color paste, dispersion based on parts by weight 0.5~1 part of agent, 0.5~1 part of retarder, 0.5~2 part of water-reducing agent and 10~40 parts of added material;The added material includes jade One of mountain flour, white marble powder, granite powder, sandstone powder are a variety of.
The retarder is sodium citrate;The dispersing agent is one of sodium pyrophosphate, Sodium Polyacrylate;The diminishing Agent is lignin sulfonic acid sodium salt.
Compared with prior art, the invention has the advantages that and effect:
The present invention provides a kind of gauge stuff terrace and decorated gypsum board, the main gypsum casting material cast in step 2 with Step 1 obtains closely connecting between chromatic pattern plaster block, and since main material is gypsum, cohesive force, adhesive force are high, main gypsum The phenomenon that main gypsic horizon that casting material is formed combines together with chromatic pattern plaster block, is not in layering;And utilize gypsum The characteristic of Self-leveling is not in rugged situation, so that the gauge stuff terrace or decorated gypsum board finally obtained is flat Whole beauty;It is placed at room temperature for after 2~6h band water again in step 3 to polish, is the face because applicants have discovered that when being placed at room temperature for 2~6h Vibration will not occur for color, because its water content is higher when decorated gypsum board crude product is placed at room temperature for 2~6h, main gypsic horizon is full in water Other pigment will not be absorbed with state.Gauge stuff terrace and decorated gypsum board be that step 2 is different, wherein gauge stuff Level ground is directly to cast on the ground;Decorated gypsum board need to cast in a mold, and decorated gypsum board obtained can be used for filling On pool and floor treatment.Wherein chromatic pattern plaster block may be designed to various pierced patterns, meet the needs of consumer.It is colored The color of decorative pattern plaster block and main gypsic horizon can all be colour, can also be colour with chromatic pattern plaster block, and main gypsic horizon Color be white.
Detailed description of the invention
Fig. 1 is a kind of structural schematic diagram for decorated gypsum board that the embodiment of the present invention 1 provides;
In figure, 1, chromatic pattern plaster block;2, main gypsic horizon.
Specific embodiment
Embodiment 1
It one, include chromatic pattern as shown in Figure 1, the present embodiment provides a kind of gauge stuff terrace and decorated gypsum boards Plaster block 1 and main gypsic horizon 2, the main gypsic horizon 2 are wrapped in around chromatic pattern plaster block 1, the chromatic pattern gypsum 2 integrally connected of block 1 and main gypsic horizon.
Two, the preparation method of the gauge stuff terrace and decorated gypsum board, includes the following steps:
The preparation of step 1, chromatic pattern plaster block: floral designs design decorative pattern gypsic horizon as needed manufactures mold Coloured plaster mill base is molded into described by (the hollow out decorative pattern that the decorative pattern in Fig. 1 is also designed to other various needs) Decorative pattern gypsic horizon manufactures mold, obtains chromatic pattern plaster block to absolutely dry (being typically greater than equal to 15 days);
Coloured plaster mill base includes 92 parts of alpha gypsum powder, 6 parts of aqueous color paste, 0.8 part of dispersing agent, slow setting based on parts by weight 0.7 part of agent and 1 part of water-reducing agent.
Step 2, casting:
The casting of gauge stuff terrace: the chromatic pattern plaster block that step 1 obtains is put into ground to be decorated, will be led Gypsum casting material is cast on ground to be decorated, and the main gypsum casting material Self-leveling is in ground and is wrapped in chromatic pattern stone Around cream block, it is frozen into main gypsic horizon, obtains gauge stuff terrace crude product;
The casting of decorated gypsum board: prepare board mould, the chromatic pattern plaster block that step 1 obtains is put into board mould In, main gypsum casting material is molded into the board mould, board mould described in the main gypsum casting material Self-leveling is interior and wraps It is rolled in around chromatic pattern plaster block, is frozen into main gypsic horizon, obtain decorated gypsum board crude product;
The main gypsum casting material include based on parts by weight 82 parts of alpha gypsum powder, 6 parts of aqueous color paste, 0.8 part of dispersing agent, 0.7 part of sodium citrate, 1 part of water-reducing agent and 15 parts of granite powder;
Step 3, post-processing: after being placed at room temperature for 2~6h, band water is polished, so that being covered on the chromatic pattern plaster block Main gypsum casting material washed out by water;Or place to absolutely dry, sander will be covered on the chromatic pattern plaster block Main gypsic horizon is polished into powder, and blows or sucks to remove powder.
Embodiment 2
Coloured plaster mill base described in step 1 includes 95 parts of alpha gypsum powder, aqueous color paste based on parts by weight in the present embodiment 4 parts, 0.5 part of dispersing agent, 0.5 part of sodium citrate and 0.5 part of water-reducing agent.
Main gypsum casting material described in step 2 includes 85 parts of alpha gypsum powder, 4 parts of aqueous color paste, dispersion based on parts by weight 0.5 part of agent, 0.5 part of retarder, 0.5 part of water-reducing agent and 10 parts of white marble powder.
Remaining step is the same as embodiment 1.
Embodiment 3
Coloured plaster mill base described in step 1 includes 80 parts of alpha gypsum powder, aqueous color paste based on parts by weight in the present embodiment 10 parts, 1 part of dispersing agent, 1 part of sodium citrate and 2 parts of water-reducing agent.
Main gypsum casting material described in step 2 includes 60 parts of α gypsum, 10 parts of aqueous color paste, dispersion based on parts by weight 1 part of agent, 1 part of retarder, 2 parts of water-reducing agent and 40 parts of sandstone powder;Remaining step is the same as embodiment 1.
Embodiment 4
Coloured plaster mill base described in step 1 includes 85 parts of alpha gypsum powder, aqueous color paste based on parts by weight in the present embodiment 10 parts, 1 part of dispersing agent, 1 part of sodium citrate and 2 parts of water-reducing agent.
Main gypsum casting material described in step 2 includes 50 parts of alpha gypsum powder, aqueous color paste 10 part, point based on parts by weight 1 part of powder, 1 part of retarder, 2 parts of water-reducing agent and 20 parts of added material;The additive includes 5 parts of jade powder and 15 parts of flower Hilllock rock powder.Remaining step is the same as embodiment 1.
Comparative example
Coloured plaster mill base and main gypsum casting material contain only the α gypsum and aqueous color paste of equivalent in the comparative example, Remaining step is the same as embodiment 4.Specifically: the coloured plaster mill base includes 85 parts of alpha gypsum powder, aqueous color paste based on parts by weight 10 parts.Main gypsum casting material described in step 2 includes 50 parts of alpha gypsum powder, 10 parts of aqueous color paste based on parts by weight.
Experimental example
The hardness and strength of the resulting decorated gypsum board of embodiment 1- embodiment 4 are measured, as shown in table 1.
Table 1
Group Intensity (MPa) Enhancing degree (%) Hardness Hardening degree (%)
Embodiment 1 5.36 14.52 25.82 36.54
Embodiment 2 5.07 8.33 22.15 17.13
Embodiment 3 5.22 11.54 23.57 24.64
Embodiment 4 5.81 24.15 28.16 48.92
Comparative example 1 4.68 / 18.91 /
To sum up show a kind of decorated gypsum board and gauge stuff terrace provided by the invention and preparation method thereof, this method The phenomenon that making winner's gypsic horizon combine together with chromatic pattern plaster block, be not in layering.And decorated gypsum board and ornamental stone Hardness, the intensity of cream terrace are big, and decorated gypsum board obtained can be used in decoration and floor treatment.
Described is only presently preferred embodiments of the present invention, is not intended to limit the invention, it is all in spirit of the invention and Within principle, any modification, equivalent replacement, improvement and so on should all include within protection scope of the present invention.

Claims (10)

1. a kind of preparation method of gauge stuff terrace, which comprises the steps of:
The preparation of step 1, chromatic pattern plaster block: floral designs design decorative pattern gypsic horizon as needed manufactures mold, will be color Colored stone cream mill base is molded into the decorative pattern gypsic horizon manufacture mold, obtains chromatic pattern plaster block to absolutely dry;
The casting of step 2, gauge stuff terrace: the chromatic pattern plaster block that step 1 obtains is put into ground to be decorated, will Main gypsum casting material is cast on ground to be decorated, and the main gypsum casting material Self-leveling is in ground and is wrapped in chromatic pattern Around plaster block, it is frozen into main gypsic horizon, obtains gauge stuff terrace crude product;
The post-processing of step 3, gauge stuff terrace: after being placed at room temperature for 2~6h, band water is polished, so that being covered on the colored flower Main gypsum casting material on line plaster block is washed out by water to get gauge stuff terrace finished product is arrived;Or it places to absolutely dry, sander general The main gypsic horizon being covered on the chromatic pattern plaster block is polished into powder, and blows or sucks and arrive decoration to remove powder Gypsum terrace finished product.
2. preparation method as described in claim 1, which is characterized in that the coloured plaster mill base in the step 1 is with parts by weight Number meter includes 80~95 parts of alpha gypsum powder, 4~10 parts of aqueous color paste, 0.5~1 part of dispersing agent, 0.5~1 part of retarder and diminishing 0.5~2 part of agent.
3. preparation method as described in claim 1, which is characterized in that the main gypsum casting material includes α based on parts by weight 50~85 parts of land plaster, 4~10 parts of aqueous color paste, 0.5~1 part of dispersing agent, 0.5~1 part of retarder, 0.5~2 part of water-reducing agent and 10~40 parts of added material;The added material includes one of jade powder, white marble powder, granite powder, sandstone powder or more Kind.
4. preparation method as described in claim 1, which is characterized in that the decorated gypsum board crude product room that will will be obtained in step 3 After temperature places 4h, then band water is polished.
5. the gauge stuff terrace that a kind of any method of claim 1-4 is prepared.
6. a kind of preparation method of decorated gypsum board, which comprises the steps of:
The preparation of step 1, chromatic pattern plaster block: floral designs design decorative pattern gypsic horizon as needed manufactures mold, will be color Colored stone cream mill base is molded into the decorative pattern gypsic horizon manufacture mold, obtains chromatic pattern plaster block to absolutely dry;
The casting of step 2, decorated gypsum board: prepare board mould, the chromatic pattern plaster block that step 1 obtains is put into plate mould In tool, main gypsum casting material is molded into the board mould, in board mould described in the main gypsum casting material Self-leveling and It is wrapped in around chromatic pattern plaster block, is frozen into main gypsic horizon, obtain decorated gypsum board crude product;
The post-processing of step 3, decorated gypsum board: after the decorated gypsum board crude product that step 2 obtains is placed at room temperature for 2~6h, band water Polishing so that the main gypsum casting material being covered on the chromatic pattern plaster block by water wash out to get to decorated gypsum board at Product;Or place the decorated gypsum board crude product that step 2 obtains to absolutely dry, sander will be covered on the chromatic pattern plaster block Main gypsic horizon be polished into powder, and blow or suck to remove powder to get to gauge stuff board finished product.
7. preparation method as claimed in claim 6, which is characterized in that the coloured plaster mill base in the step 1 is with parts by weight Number meter includes 80~95 parts of alpha gypsum powder, 4~10 parts of aqueous color paste, 0.5~1 part of dispersing agent, 0.5~1 part of retarder and diminishing 0.5~2 part of agent.
8. preparation method as claimed in claim 6, which is characterized in that the main gypsum casting material includes α based on parts by weight 50~85 parts of land plaster, 4~10 parts of aqueous color paste, 0.5~1 part of dispersing agent, 0.5~1 part of retarder, 0.5~2 part of water-reducing agent and 10~40 parts of added material;The added material includes one of jade powder, white marble powder, granite powder, sandstone powder or more Kind.
9. preparation method as claimed in claim 6, which is characterized in that the decorated gypsum board crude product room that will will be obtained in step 3 After temperature places 4h, then band water is polished.
10. the decorated gypsum board that a kind of any method of claim 6-9 is prepared.
CN201910314413.XA 2019-04-18 2019-04-18 Decorative gypsum terrace, decorative gypsum board and preparation method thereof Active CN110154202B (en)