CN1101345C - 高折射率玻璃 - Google Patents
高折射率玻璃 Download PDFInfo
- Publication number
- CN1101345C CN1101345C CN98802074A CN98802074A CN1101345C CN 1101345 C CN1101345 C CN 1101345C CN 98802074 A CN98802074 A CN 98802074A CN 98802074 A CN98802074 A CN 98802074A CN 1101345 C CN1101345 C CN 1101345C
- Authority
- CN
- China
- Prior art keywords
- glass
- cao
- zro
- tio
- sio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及折射率大于1.880,阿贝数大于或等于30.4,密度大于4.1的玻璃,其化学组成以氧化物为基准的重量%表示如下:SiO2:6-9,B2O3:15-19,并且SiO2+B2O3<26,Nb2O5:12至<20.5,ZrO2:8-10,TiO2:7-11,La2O3:23-32,并且ZrO2+TiO2+La2O3≥44,CaO:8至<13,SrO:0-2,BaO:0-2,MgO:0-2,Y2O3:0-5,WO3:0-5,ZnO:0-5,并且CaO+SrO+BaO+MgO+ZnO≥9,Li2O+Na2O+K2O:0-2,其它为0-1。
Description
本发明涉及折射率大于1.880,阿贝数大于或等于30.4,密度小于4.1的玻璃。
眼科用途对这类玻璃是很感兴趣的,尤其是校正视力度数较高的情况,高折射率可以减小玻璃的厚度。适中的密度和较高的阿贝数还可以使佩戴者感觉舒适。
而且,玻璃生产简便并且生产成本低也是有利的。为此目的,原料成本低,析晶倾向低,都是要求的要素。
现有技术领域
具备上述光学性能和类似密度的玻璃已为人们所知,但是就其生产成本和抗析晶性能而论,它们还不能令人满意。
欧洲专利B-570,687描述了具有下面组成的玻璃,该组成以氧化物为基准的%(重量)表示:
SiO2 5-8
B2O3 15-21
ZrO2 3-10
TiO2 7-17
Nb2O5 20.5-26
并且ZrO2+TiO2+Nb2O5 29-45
La2O3 19-23
Y2O3 0-9
CaO 8-16
SrO 0-5
BaO 0-5
MgO 0-5
并且CaO+SrO+BaO+MgO 8-16
ZnO 0-5
Li2O 0-2
Na2O 0-2
K2O 0-2
并且Li2O+Na2O+K2O 0-2
这类玻璃的折射率大于1.88。阿贝数大于29,密度小于4.1,380-800nm的积分透射大于79%(厚度为10毫米时)。
然而这类玻璃有两大缺陷:
-与很低的液相线粘度相关的非常高的析晶倾向。液相线温度在1150℃左右;在此温度,粘度仅为几泊。
-Nb2O5的含量高(20.5-26),使原料的成本非常高。
已知还有组成与本发明玻璃相似的其它一些玻璃。
日本专利A-3-5340(1991)描述了折射率为1.83-1.88的玻璃,其组成以%(重量)表示如下:
SiO2 20-14
B2O3 8-25
并且SiO2+B2O3 22-29
CaO 13-25
MgO 0-10
并且CaO+MgO 13-25
La2O3 15-28
BaO+SrO+ZnO 0-12
并且La2O3+BaO+SrO+ZnO 15-28
ZrO2 1-9
TiO2 6-15
Nb2O5 6-20
并且ZrO2+TiO2+Nb2O5 24-38
K2O+Na2O+Li2O 0-3
尽管上述专利提到的玻璃,其折射率最大可为1.88,但是在其实施例中所述玻璃的最高折射率仅达到1.8725,其具体描述的绝大多数玻璃折射率还要低得多。而且,现有技术的这些玻璃中CaO含量比本发明的玻璃高得多。
德国专利C-4,242,859提出权利要求的是一些高折射率玻璃,其组成界定的范围很宽,接近本发明的玻璃,但与本发明显著的不同是ZrO2含量较低(<8%),并且必须含有氟。其所述的五个具体实施例不同于本发明,在涉及一个或多个组分的其它组成上有差别。
本发明的界定
本发明涉及的玻璃,折射率大于1.880,阿贝数大于或等于30.4,密度小于4.1,其化学组成以氧化物为基准的%(重量)表示如下:
SiO2 6-9
B2O3 15-19
并且SiO2+B2O3 <26
Nb2O5 12至<20.5
ZrO2 8-10
TiO2 7-11
La2O3 23-32
并且ZrO2+TiO2+La2O3 ≥44
Y2O3 0-5
WO3 0-5
CaO 8至<13
SrO 0-2
BaO 0-2
MgO 0-2
ZnO 0-5
并且CaO+SrO+BaO+MgO+ZnO ≥9
Li2O+Na2O+K2O 0-2
其它 0-1
较好的玻璃,其化学组成以氧化物为基准的%(重量)表示如下:
SiO2 6.5-8
B2O3 15.5-19
并且SiO2+B2O3 <26
Nb2O5 15-18.5
ZrO2 ≥8-9
TiO2 9-11
La2O3 25-30
并且ZrO2+ TiO2+La2O3 ≥44
CaO 11至<13
ZnO 0-5
并且CaO+ZnO ≥12
其它 0-1
更好的玻璃,其化学组成以氧化物为基准的%(重量)表示如下:
SiO2 6.5-8
B2O3 15.5-19
并且SiO2+B2O3 <26
Nb2O5 15-18.5
ZrO2 ≥8-9
TiO2 9-10.5
La2O3 25至<28
并且ZrO2+TiO2+La2O3 ≥44
CaO 12至<13
其它 0-1
与欧洲专利B-570,687所述的玻璃相比,上述玻璃由于降低了Nb2O5含量,可以显著降低原料成本。
本发明玻璃的阿贝数比欧洲专利B-570,687的玻璃高得多。事实上阿贝数已经达到30.4-31.3范围,而欧洲专利B-570,687中,其实施例玻璃的阿贝数在29.6-30.6范围。观察到的本发明玻璃析晶倾向下降,是与下一事实有关,即欧洲专利B-570,687中的玻璃,其发生析晶的主要结晶相为铌含量高的一种复合氧化物。降低铌的含量可以降低析晶倾向,产生的晶体数目和晶体成长速度都显著下降。最好的组成还具有较低的液相线温度。
如果Nb2O5含量小于12%,不可能获得大于1.88的折射率。
由于同样原因,ZrO2、TiO2和La2O3含量必须分别至少为8%、7%和23%,这三种元素的总含量必须至少为44%。
ZrO2含量大于10%,会引起严重的析晶。
La2O3含量大于32%,会导致过大的密度。
玻璃的颜色对TiO2含量非常敏感;由于这个原因,这种元素含量应限于11%以下。
碱土金属氧化物和ZnO也有助于达到高折射率。虽然它们对提高折射率的作用没有上述元素大。它们具有对色散影响较小的优点。碱土金属氧化物减小了富铌相析晶的危险。这些氧化物中以用CaO为宜,因为它提高密度的作用小于BaO或ZnO。而且还观察到,对抗析晶来说,CaO比MgO更合适。CaO含量需在8-13%之间。
SiO2和B2O3是必需的玻璃生成剂。若SiO2和B2O3的含量分别小于6%和15%,玻璃的析晶就很严重,是不能接受的。若这两种氧化物的总含量大于26%就不能达到要求的折射率。
可以加入少量碱金属氧化物,帮助熔化。然而,其总量必需限制在2%以下,因为这些元素会降低玻璃的粘度,特别是液相线粘度。组成中最好没有这些元素。
还可以加入常用的精炼剂,如As2O3、Sb2O5、氟化物、溴化物或氯化物,只要它们的总量不超过1%。
如果使用相当纯的原料,例如Fe2O3含量小于10ppm的那些原料,玻璃就只会微弱着色。如果需要,可加入脱色剂。还可加入常用的着色元素,例如过渡金属氧化物或稀土金属氧化物使色玻璃着色。
在上述组成范围的玻璃,其析晶性能和密度得到优化。
本发明用表1所列出的非限制性实施例进行说明。
所有比例均以%(重量)表示。尽管所有这些实施例为实验室试验,但采用通常的熔化和成型方法,可以工业化生产本发明的玻璃。
每次试验中,将3000克原料在铂坩埚中熔化1小时。然后成型为1厘米厚的玻璃棒。以60℃/小时速度进行退火。
用10毫米厚的抛光样品测得380-800nm的积分透射,从而确定玻璃的颜色。
采用下面的试验评价析晶倾向:对每种组成,将一些小玻璃片放在铂坩埚中,分别在1096℃、1112℃和1125℃重新处理5分钟。肉眼观察比较其结晶程度,对每种玻璃的评价列为1-4级:4级玻璃有最大的析晶倾向,1级玻璃的析晶倾向最小。
实施例1属最佳。实施例2、3和4属较佳。实施例8不在本发明范围内,因为它的Nb2O5含量太高,其析晶倾向太大,不能接受。
表I
1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | |
SiO2 | 7.3 | 7.3 | 7.3 | 7.3 | 7.3 | 7.3 | 7.3 | +7.3 |
B2O3 | 16.85 | 16.65 | 16.65 | 17.15 | 16.65 | 17.65 | 18.15 | 16.65 |
CaO | 12.5 | 12.5 | 12.5 | 12 | 12 | 10.5 | 9 | 14 |
ZnO | 2.5 | |||||||
TiO2 | 9.6 | 10.1 | 9.6 | 9.6 | 8.6 | 9.6 | 9.6 | 8.6 |
ZrO2 | 8.2 | 8.2 | 8.5 | 8.7 | 8.2 | 8.2 | 8.2 | 8.2 |
Nb2O5 | 18 | 15.95 | 16.9 | 17.7 | 18.2 | 17.7 | 17.7 | 21.2 |
La2O3 | 27.5 | 29.25 | 28.5 | 27.5 | 29 | 29 | 27.5 | 24 |
As2O3 | 0.05 | 0.05 | 0.05 | 0.05 | 0.05 | 0.05 | 0.05 | 0.05 |
SiO2-B2O3 | 24.15 | 23.95 | 23.95 | 24.45 | 23.95 | 24.95 | 25.45 | 23.95 |
TiO2+ZrO2+La2O3 | 45.3 | 47.55 | 46.6 | 45.8 | 45.8 | 46.8 | 45.3 | 40.8 |
CaO+ZnO | 12.5 | 12.5 | 12.5 | 12 | 12 | 10.5 | 11.5 | 14 |
折射率 | 1.884 | 1.885 | 1.885 | 1.884 | 1.883 | 1.884 | 1.883 | 1.883 |
阿贝数 | 30.8 | 31.3 | 31.3 | 31 | 31.3 | 30.8 | 30.5 | 30.4 |
密度 | 4.03 | 4.06 | 4.05 | 4.03 | 4.07 | 4.05 | 4.05 | 3.98 |
透射 | 80.8 | 80.8 | 81.1 | 81.4 | 81.1 | 80.5 | 81.4 | 80.6 |
析晶倾向 | 2 | 1 | 2 | 2 | 2 | 3 | 1 | 4 |
液相线温度(℃) | 1112-1140 | 1123-1139 | 1143-1162 | 1143-1162 | 1130-1139 | 1152-1161 | 1139-1164 | 1149-1161 |
Claims (3)
1.折射率大于1.880,阿贝数大于或等于30.4,密度小于4.1的玻璃,其化学组成以氧化物为基准的重量%表示如下:
SiO2 6-9
B2O3 15-19
并且SiO2+B2O3 <26
Nb2O5 12至<20.5
ZrO2 8-10
TiO2 7-11
La2O3 23-32
并且ZrO2+TiO2+La2O3 ≥44
Y2O3 0-5
WO3 0-5
CaO 8至<13
SrO 0-2
BaO 0-2
MgO 0-2
ZnO 0-5
并且CaO+SrO+BaO+MgO+ZnO ≥9
Li2O+Na2O+K2O 0-2
其它 0-1。
2.如权利要求1所述的玻璃,其特征在于,所述的玻璃具有下列以氧化物为基准的重量%表示的化学组成:
SiO2 6.5-8
B2O3 15.5-19
并且SiO2+B2O3 <26
Nb2O5 15-18.5
ZrO2 ≥8-9
TiO2 9-11
La2O3 25-30
并且ZrO2+TiO2+La2O3 ≥44
CaO 11至<13
ZnO 0-5
并且CaO+ZnO ≥12
其它 0-1。
3.如权利要求2所述的玻璃,其特征在于,所述的玻璃具有下列以氧化物为基准的重量%表示的化学组成:
SiO2 6.5-8
B2O3 15.5-19
并且SiO2+B2O3 <26
Nb2O5 15-18.5
ZrO2 ≥8-9
TiO2 9-10.5
La2O3 25至<28
并且ZrO2+TiO2+La2O3 ≥44
CaO 12至<13
其它 0-1。