CN110092918A - 自溶型沥青乳化剂及制备方法 - Google Patents
自溶型沥青乳化剂及制备方法 Download PDFInfo
- Publication number
- CN110092918A CN110092918A CN201910480719.2A CN201910480719A CN110092918A CN 110092918 A CN110092918 A CN 110092918A CN 201910480719 A CN201910480719 A CN 201910480719A CN 110092918 A CN110092918 A CN 110092918A
- Authority
- CN
- China
- Prior art keywords
- sodium
- polyoxyethylene ether
- solubilizer
- inorganic
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种无需机械研磨的自溶型沥青乳化剂及制备方法,原料及质量比如下:阴离子表面活性剂5~15%、非离子表面活性剂2~6%、木质素10~25%、无机增溶剂15~20%、阴离子调节剂5~8%、水余量;所述阴离子表面活性剂为油酸钠、松香酸钠、双十二烷基羧酸钠、十六烷基苯磺酸钠及十二烷基硫酸钠中的2~3种;所述非离子表面活性剂为壬基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚、斯潘、吐温及脂肪酸聚氧乙烯醚中的1~2种;所述无机增溶剂为硫酸氢钠、磷酸三钠及三聚磷酸钠中的1~2种;所述阴离子调节剂包括氢氧化钠、氢氧化钾、胍、胆碱中的1~2种。
Description
技术领域
本发明涉及一种沥青乳化剂,尤其是一种无需机械研磨的自溶型沥青乳化剂及制备方法。
背景技术
沥青乳化剂能够吸附在沥青颗粒与水界面,显著降低沥青与水界面的自由能,进而把油水两相连接起来,使沥青成为均匀而稳定的乳浊液并具有无毒、无臭、不易燃、原料价廉易得及便于冷施工等优点。然而现有沥青乳化剂必需通过专业胶体磨设备才能够将沥青乳化,不仅设备投资高,而且因不能将设备置于施工现场,故不能现用现配。由于乳化沥青稳定性差无法长期储存,故需耗费大量人力物力实现乳化沥青的转场,进一步加大成本。
发明内容
本发明的技术解决方案是:一种自溶型沥青乳化剂,其特征在于原料及质量比如下:阴离子表面活性剂5~15%、非离子表面活性剂2~6%、木质素10~25%、无机增溶剂15~20%、阴离子调节剂5~8%、水余量;
所述阴离子表面活性剂为油酸钠、松香酸钠、双十二烷基羧酸钠、十六烷基苯磺酸钠及十二烷基硫酸钠中的2~3种;
所述非离子表面活性剂为壬基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚、斯潘、吐温及脂肪酸聚氧乙烯醚中的1~2种;
所述无机增溶剂为硫酸氢钠、磷酸三钠、三聚磷酸钠中的1~2种;
所述阴离子调节剂包括氢氧化钠、氢氧化钾、胍、胆碱中的1~2种。
一种上述自溶型沥青乳化剂的制备方法,其特征在于依次按照如下步骤进行:
a. 将木质素与水按比例混合均匀;
b. 加入阴离子调节剂,混合搅拌;
c. 加入无机增溶剂、非离子表面活性剂及阴离子表面活性剂,持续搅拌至温度为20~30℃。
本发明不需要专业乳化设备进行机械研磨,只在施工现场人工搅拌,即可将基质沥青乳化,节省了专业胶体磨设备投入及转场费用,保证了乳化沥青稳定性,确保了施工质量。
具体实施方式
实施例1:
本发明自溶型沥青乳化剂,原料及质量比如下:油酸钠10%、十六烷基苯磺酸5%、壬基酚聚氧乙烯醚2%、斯潘4%、木质素(造纸废液提炼的植物纤维)23%、硫酸氢钠15%、氢氧化钠5%、水余量。
制备方法依次按照如下步骤进行:
a. 将木质素与水按比例混合均匀;
b. 加入氢氧化钠,混合搅拌;此期间发生大量的热,同时有少量的氨气溢出;
c. 依次加入磷酸三钠、十六烷基苯磺酸钠、壬基酚聚氧乙烯醚、斯潘及油酸钠,持续搅拌至温度为20℃。
实施例2:
本发明自溶型沥青乳化剂,原料及质量比如下:松香酸钠5%、双十二烷基羧酸钠5%、脂肪醇聚氧乙烯醚2%、吐温4%、木质素(造纸废液提炼的植物纤维)10%、三聚磷酸钠20%、氢氧化纳2%、胆碱6%及水余量。
制备方法依次按照如下步骤进行:
a. 将木质素与水按比例混合均匀;
b. 加入氢氧化钠和胆碱,混合搅拌;此期间发生大量的热,同时有少量的氨气溢出;
c. 依次加入松香酸钠、十二烷基羧酸钠、脂肪醇聚氧乙烯醚、吐温及三聚磷酸钠,持续搅拌至温度为25℃。
实施例3:
本发明自溶型沥青乳化剂,原料及质量比如下:十二烷基硫酸钠5%、松香酸钠5%、双十二烷基羧酸钠2%、壬基酚聚氧乙烯醚5%、木质素(造纸废液提炼的植物纤维)20%、三聚磷酸钠7.5%、磷酸三钠10.5%、氢氧化钾5%及水余量。
制备方法依次按照如下步骤进行:
a. 将木质素与水按比例混合均匀;
b. 加入氢氧化钾,混合搅拌;此期间发生大量的热,同时有少量的氨气溢出;
c. 依次加入十二烷基硫酸钠、松香酸钠、双十二烷基羧酸钠、壬基酚聚氧乙烯醚、三聚磷酸钠、磷酸三钠,持续搅拌至温度为30℃。
使用时,将实施例1、实施例2或实施例3按照水的重量1~2%,制成水乳液并加温到50~70℃,再以质量比为20~70%与110~130℃沥青混合搅拌均匀即可。
Claims (2)
1.一种自溶型沥青乳化剂,其特征在于原料及质量比如下:阴离子表面活性剂5~15%、非离子表面活性剂2~6%、木质素10~25%、无机增溶剂15~20%、阴离子调节剂5~8%、水余量;
所述阴离子表面活性剂为油酸钠、松香酸钠、双十二烷基羧酸钠、十六烷基苯磺酸钠及十二烷基硫酸钠中的2~3种;
所述非离子表面活性剂为壬基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚、斯潘、吐温及脂肪酸聚氧乙烯醚中的1~2种;
所述无机增溶剂为硫酸氢钠、磷酸三钠及三聚磷酸钠中的1~2种;
所述阴离子调节剂包括氢氧化钠、氢氧化钾、胍、胆碱中的1~2种。
2.一种如权利要求1所述自溶型沥青乳化剂的制备方法,其特征在于依次按照如下步骤进行:
a. 将木质素与水按比例混合均匀;
b. 加入阴离子调节剂,搅拌均匀;
c. 加入无机增溶剂、非离子表面活性剂及阴离子表面活性剂,持续搅拌至温度为20~30℃。