CN1099788A - 多产烯烃的裂化催化剂 - Google Patents
多产烯烃的裂化催化剂 Download PDFInfo
- Publication number
- CN1099788A CN1099788A CN 93116615 CN93116615A CN1099788A CN 1099788 A CN1099788 A CN 1099788A CN 93116615 CN93116615 CN 93116615 CN 93116615 A CN93116615 A CN 93116615A CN 1099788 A CN1099788 A CN 1099788A
- Authority
- CN
- China
- Prior art keywords
- catalyzer
- zeolite
- molecular sieve
- pulp
- zsm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种多产C3-C5烯烃的裂化催化剂,是由10-50m%晶胞常数≤2.450nm的Y型沸石、2-40m%选自P、RE、Ca、Mg、H、Al等改性的ZSM-5沸石,β沸石及其混合物、20-80m%由高岭土和铝粘结剂组成的半合成载体组成。其制备方法是:将预先制得的分子筛浆液与载体浆液混合搅拌、干燥、成型即得产品。使用该催化剂不仅能提高C3-C5烯烃的收率,其中iC4=+iC5=的产率达10-13m%,同时还可以使汽油产率保持在35-42m%左右。
Description
本发明涉及一种裂化催化剂,具体地说是关于一种多产C3-C5烯烃的裂化催化剂。
随着石油化工工业的发展,催化裂化工艺不仅是提供轻质油品的重要手段,同时也是提供烯烃等基本有机化工原料的一种加工方式。随着汽油配方的重新调整,汽油中要求有一定的氧含量,MTBE、TAME等含氧化合物将逐步添加到汽油中,作为它们的原料-iC= 4和iC= 5,其需求量必将日益增加,因此,有必要改进裂化催化剂对C3-C5烯烃的选择性。据美国专利3758403报导,在Y型分子筛催化剂中添加ZSM-5,可以提高汽油的辛烷值,同时也能提高C3-C5烯烃的产率,但提高幅度不大。CN 1043520A公开了一种生产低碳烯烃的裂解催化剂,主要用来生产丙烯和丁烯,该催化剂包含75-100m%的ZSM-5和0-25m%的Y型沸石。美国专利4911823公开了一种β沸石催化裂化蜡含量至少为20m%的重烷烃油的方法,用该方法可以获得高辛烷值的汽油,同时还可以增加i-C= 4的产量。
本发明的目的是制备一种能多产C3-C5烯烃的裂化催化剂,该催化剂既能提高其中C4-C5异构烯烃的含量,也能够使汽油产率维持相当水平。
本发明所说的催化剂是由10-50m%晶胞常数≤2.450nm的Y型沸石、2-40m%的其它分子筛、以及20-80m%的载体组成。所说的其它分子筛选自P、RE、Ca、Mg、H、Al等改性的ZSM-5,β沸石及其混合物,还可以是不改性的ZSM-5和β沸石的混合物。也可以选自丝光沸石等高硅沸石。所说的载体是由高岭土和铝粘结剂组成的半合成载体,还可以选自氧化铝、氧化硅、硅铝胶及其混合物。
本发明所说的铝粘结剂是指铝溶胶、拟薄水铝石及其混合物。
本发明所说的粘结剂中也可以含少量其它诸如Sn、Ti、Mg、Zr、P、Mn、Cr等元素。
本发明所说的β沸石选自Hβ、Pβ、REβ。
本发明所说催化剂的制备方法是:将予先制得的分子筛浆液与载体浆液混合、搅拌、干燥、成型,即得产品。根据该催化剂的组成配比,其制备步骤包括:
1、分子筛浆液的制备:将Y型沸石及其它分子筛以及脱离子水混合打浆,制成固含量为20-40m%的分子筛浆液;
2、载体浆液的制备:将高岭土、粘结剂和脱离子水混合搅拌打浆,如果粘结剂是拟薄水铝石还需用盐酸酸化、老化,制得载体浆液,其中盐酸的加入量占拟薄水铝石中Al2O3灼基量的15-30m%;
3、将分子筛浆液加到载体浆液中搅拌10-30分钟,然后进行干燥、成型,制得催化剂产品。
本发明所说的催化剂与已有技术制得的催化剂(活性组分为Y型沸石+ZSM-5)比较,当催化剂中分子筛的总含量相同、并且在进行催化裂化反应时,转化率相近的情况下、使用本发明所说的催化剂,C= 3-C= 5的产率达30-35m%以上,比已有技术高2-6个百分点,iC= 4+iC= 5产率达10-13m%,比已有技术高1-3个百分点,同时还能使汽油产率保持在35-42m%左右。
下面的实施例将对本发明作进一步说明。
(一)本发明所用的分析测试方法:
1、Na2O含量:火焰原子吸收光谱法。
2、Fe含量:原子吸收光谱法。
3、晶胞常数ao:X光衍射法。
(二)本发明实例中所用原料的产地、规格:
1、DASY沸石:周村催化剂厂生产的Y型沸石,Na2O 1.0m%,晶胞常数ao=2.444nm;
2、ZSM-5:周村催化剂厂生产,SiO2/Al2O3=62,Na2O 0.08m%;
3、β沸石:石油三厂,SiO2/Al2O3=25,Na2O 0.86m%;
4、RSY:周村催化剂厂生产的一种Y型沸石,晶胞常数ao=2.450nm;
5、高岭土:中国高岭土公司生产;
6、铝溶胶:周村催化剂厂生产,Al2O3含量21m%,Al/Cl(m)=1.15-1.25,Fe含量为0.025-0.07m%;
7、拟薄水铝石:山东铝厂,β三水Al2O3<5m%;
8、磷酸:北京化工厂,化学纯,浓度85m%;
9、氨水:秦皇岛市化学试验厂,化学纯,25m%;
10、NH4Cl:北京红星化工厂,化学纯;
11、RECl3:上海跃龙化工厂,打火石规格,Ce2O3>45m%;
12、盐酸:化学纯,北京化学试剂二厂,浓度36m%。
(三)本发明实例中,其它原料的制备:
1、HD沸石的制备:将350克NH4Cl用11.5立升脱离子水溶解,制成NH4Cl溶液。取DASY沸石700克,用NH4Cl溶液在90-95℃交换1小时,过滤,用脱离子水冲洗滤饼,直至无Cl-,将湿滤饼在空气中于600℃焙烧2小时,即得HD沸石,其晶胞常数ao=2.438nm,Na2O含量为0.41m%。
2、Hβ沸石的制备:取β沸石176克,用634毫升0.3N的HCl在90℃处理1小时,过滤,用脱离子水洗至Cl-,滤饼在100-110℃干燥,最后在550℃焙烧2小时,制得Hβ沸石,Na2O含量0.23m%。
实例1
PZ分子筛的制备:将330毫升浓度为85m%的磷酸用30立升脱离子水稀释,加入263毫升氨水,然后加入3公斤ZSM-5分子筛于95℃交换1小时,过滤,制得PZ分子筛。
取DASY分子筛1.5公斤和PZ分子筛混合,加脱离子水6.1公斤球磨30分钟,制成分子筛浆液。
将7公斤高岭土加到3.57公斤铝溶胶和16公斤脱离子水中,搅拌30分钟,加入盐酸1.3公斤,搅拌30分钟,再加入12.3公斤Al2O3含量为36.6m%的拟薄水铝石,混合搅拌40分钟,在60℃老化1小时,制得载体浆液。将分子筛浆液加到老化后的载体浆液中,搅拌20分钟,进行喷雾干燥,制得催化剂A。其组成配比见表1。
实例2
分子筛浆液的制备,将DASY分子筛1.5公斤、ZSM-52.3公斤、β沸石0.8公斤混合,加入脱离子水8.4公斤球磨1小时,制得分子筛浆液。
将17公斤铝溶胶与8.1公斤高岭土混合搅拌1.5小时,然后加入分子筛浆液,搅拌30分钟,喷雾干燥,制得催化剂B。其组成配比见表1。
实例3
将15克ZSM-5分子筛、10克Hβ分子筛和10克RSY分子筛与37克水混合搅拌,制得分子筛浆液。
将58.2克高岭土与68克铝溶胶混合搅拌制得载体浆液,然后加入上述分子筛浆液混合搅拌,在110℃干燥,制得催化剂C,其组成配方见表1。
实例4
Pβ沸石的制备:将4公斤β沸石加入到由440毫升浓度为85m%的磷酸及40立升脱离子水配制的磷酸溶液中,在搅拌下缓缓加入350毫升氨水,在90℃交换1小时,过滤,进行固液分离,制得Pβ沸石。
将Pβ沸石与800克DASY沸石混合,加入4200毫升脱离子水进行球磨,制得分子筛浆液。
将7公斤高岭土加入到16立升脱离子水中,搅拌30分钟,得到均匀的土浆液,再加入浓度为36m%的盐酸1300克,搅拌30分钟,加入16.6公斤Al2O3含量为36.6m%的拟薄水铝石,于60℃老化3.5小时,制得载体浆液,然后加入分子筛浆液,搅拌15分钟,进行喷雾干燥,制得催化剂D,其组成配方见表1。
实例5
REβ分子筛的制备:β分子筛10克用320毫升RECl3溶液(RECl3浓度为2.35克/立升)在90℃交换1小时,过滤,滤饼在100℃干燥4小时,最后在550℃焙烧2小时,制得REβ分子筛。
将19.9克HD分子筛、10克REβ分子筛和45克脱阳离子水混合,制成分子筛浆液。
将69.9克高岭土与71.4克铝溶胶混合均匀,加入分子筛浆液,混合搅拌15分钟,然后置于干燥箱内,在100℃干燥20小时,制得催化剂E,其组成配方见表1。
对比例1
将33克HD分子筛、53克ZSM-5分子筛与128克脱离子水混合搅拌,制成分子筛浆液。
将597克脱离子水与145克高岭土混合搅拌30分钟,加入盐酸10克,搅拌30分钟,再加入136.6克Al2O3含量为36.6m%的拟薄水铝石搅拌30分钟,升温至60℃保持1小时,冷却至室温,加入分子筛浆液搅拌15分钟,然后在110℃干燥,制得对比催化剂F,其组成配方见表1。
实例6
对本发明催化剂A-E以及对比例催化剂F进行微活评价,评价条件:反应温度520℃、重量空速16小时-1,催化剂4.0克,原料为胜利蜡油,馏程范围227-475℃,比重0.8652,残炭0.04m%,催化剂评价前予先进行水蒸气减活,条件为:800℃、常压、100%水蒸气处理4小时,评价结果见表2。
由表2可以看出:本发明所说的催化剂A、B、D与用已有技术制得的分子筛含量与其相同的催化剂F比较,在转化率相近的情况下,使用本发明催化剂C= 3-C= 5产率达30-35m%以上,比已有技术高2-6个百分点,iC= 4+iC= 5产率达10-13m%,比已有技术高1-3个百分点,同时还能保持汽油产率在35-42m%左右。
Claims (6)
1、一种多产C3-C5烯烃的裂化催化剂,其特征在于该催化剂是由10-50m%晶胞常数≤2.450nm的Y型沸石、2-40m%选自P、RE、Ca、Mg、H、Al等改性的ZSM-5,β沸石及其混合物、20-80m%由高岭土和铝粘结剂组成的半合成载体组成。
2、根据权利要求1所说的催化剂,其特征在于根据本发明所述催化剂的组成比例,该催化剂的制备方法为:
(1)将Y型沸石及其它分子筛以及脱离子水混合打浆,制成固含量为20-40m%的分子筛浆液;
(2)将高岭土、铝粘结剂和脱离子水混合搅拌、打浆,如果粘结剂是拟薄水铝石,还需用盐酸酸化、老化,制得载体浆液,其中盐酸的加入量占拟薄水铝石中Al2O3灼基量的15-30m%;
(3)将分子筛浆液加到载体浆液中,搅拌10-30分钟,然后进行干燥、成型,制得催化剂产品。
3、根据权利要求1所说的催化剂,其特征在于所说的除Y型沸石以外的其它分子筛,还可以是不改性的ZSM-5和β沸石的混合物。
4、根据权利要求1所说的催化剂,其特征在于所说的β沸石选自Hβ、Pβ、REβ。
5、根据权利要求1所说的催化剂,其特征在于所说的铝粘结剂可以是铝溶胶、拟薄水铝石及其混合物。
6、根据权利要求1所说的催化剂,其特征在于所说的改性ZSM-5沸石是P-ZSM5和RE-ZSM5。