CN109880200A - A kind of self-priming chemical pump rubber seal - Google Patents
A kind of self-priming chemical pump rubber seal Download PDFInfo
- Publication number
- CN109880200A CN109880200A CN201910178291.6A CN201910178291A CN109880200A CN 109880200 A CN109880200 A CN 109880200A CN 201910178291 A CN201910178291 A CN 201910178291A CN 109880200 A CN109880200 A CN 109880200A
- Authority
- CN
- China
- Prior art keywords
- self
- rubber seal
- chemical pump
- ultra micro
- priming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of self-priming chemical pump rubber seals, are related to chemical industry pump technical field, are made of following component: tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber, Lanthanum Stearate modified powdered carbon, white carbon black, chlorinated paraffin, anti-aging agent, sulphur, surfactant;The present invention carries out rational proportion by the raw material to self-priming chemical pump rubber seal, the self-priming chemical pump rubber seal haveing excellent performance can be made, it is acted synergistically by each component, the chemical pump of preparation has excellent tensile strength, hardness and brittleness temperature with rubber seal, can adapt to the working environment of Various Complex.
Description
Technical field
The invention belongs to chemical industry pump technical fields, and in particular to a kind of self-priming chemical pump rubber seal.
Background technique
Currently, existing self-priming chemical pump includes that the components self-priming chemical pump such as the pump housing, connecting cylinder, machine barrel, shaft is mainly used
Water, industrial and mineral plumbing etc. are sent in farmland treegarden irrigation, underground water lift, water tower, needs water being transported to eminence from lower, in use
The leakproofness of water pump directly affects the service life of water pump, and installation gland seal device, existing bearing arrangement are usually required in shaft
Multiple sealing rings are generallyd use, however existing sealing ring is easy to wear can generate gap and influence leakproofness.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of self-priming chemical pump rubber seal is provided.
The present invention is achieved by the following technical solutions:
A kind of self-priming chemical pump rubber seal, is made of following component by weight: tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber
112-115, Lanthanum Stearate modified powdered carbon 22-26, white carbon black 6-7, chlorinated paraffin 4.5-4.9, anti-aging agent 1.2-1.5, sulphur 1-
2, surfactant 0.5-1.5;
The preparation method of the modified powdered carbon of the Lanthanum Stearate the following steps are included:
(1) pine is crushed to 500 mesh, obtains pine point, then impregnated 55-60min with ethyl alcohol alkali mixed solution, then carry out
Filtering, cleaning, drying to constant weight, obtains pretreatment pine powder;
(2) pretreatment pine powder obtained above is placed in twin-screw extruder and carries out expanding treatment, then by gained
Puffing material pulverizes, and obtains ultra micro pine powder;
(3) ultra micro pine powder obtained above and fatty acid loss water sorbit ester, petroleum ether are added by 10:1:50 mass ratio
Into reaction kettle, 80 DEG C are heated to, with 1500r/min revolving speed stirring 2 hours, is then filtered, it is dry to constant weight, changed
Property ultra micro pine powder;
(4) Lanthanum Stearate of its quality 1.5% will be added in modified ultra micro pine powder obtained above, after mixing, then in nitrogen
Charing process is carried out under gas atmosphere, until after modified ultra micro pine powder carbonizes completely, then grinding is carried out 1 hour to get Lanthanum Stearate
Modified powdered carbon.
Further, the tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber the preparation method comprises the following steps:
88 parts of nitrile rubber, 3 parts of tetrahydrofurfuryl amine, 1.2 parts of 2- vinyl naphthalene, 8 parts of sericite in powder are added to mixing by weight
In machine, temperature is increased to 135 DEG C, insulation reaction 40min, is then further continued for being heated to 168 DEG C, then add maleimide 2.8
Part with 0.2 part of benzoyl peroxide, insulation reaction 2 hours, then discharge, cooling, washing, drying to constant weight to get four
Hydrogen chaff amine modified butadiene acrylonitrile rubber.
Further, the sericite in powder granularity is 800 mesh.
Further, the anti-aging agent is antioxidant MB.
Further, the surfactant is neopelex.
Further, ethyl alcohol, alkali, water mixing mass ratio are 20:10:50 in the ethyl alcohol alkali mixed solution.
Further, the alkali is sodium hydroxide.
Further, the ultra micro pine Powder Particle Size is 1300 mesh.
The utility model has the advantages that the present invention carries out rational proportion by the raw material to self-priming chemical pump rubber seal, can make
The self-priming chemical pump rubber seal that must be had excellent performance, is acted synergistically by each component, the chemical pump rubber seal of preparation
Part has excellent tensile strength, hardness and brittleness temperature, can adapt to the working environment of Various Complex, service life obtains
It greatly ensures, by acting synergistically in sulphur and tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber, so that the linear high score in rubber material
Son becomes net high-polymer, forms fine and close network structure, improves the performance for thinking rubber seal, then passes through Lanthanum Stearate again
Modified powdered carbon is evenly dispersed wherein, combines on the macromolecular chain of net high-polymer, not only plays profit to rubber seal
Sliding, antifriction effect, while the coefficient of friction between dynamic rubber seal and mechanical part can be reduced, frictional heat generation is reduced,
To reduce the operating temperature of sealing element, rubber heat-proof aging degree is reduced, improves seal durability, also, the system that rubs
After number reduces, the frictional force or friction torque that the dynamic rubber seal and mechanical part of relative motion are shown in reduce, to reduce
Power loss reaches energy-saving and environment-friendly purpose, and tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber makes intermolecular Electronic interactions,
Mobility, the plasticity of rubber are improved by reducing the active force between rubber molecule, meanwhile, nitrile rubber sealing can be improved
The resistance to low temperature of part, the modified powdered carbon of Lanthanum Stearate can be the Physical Network lineations between rubber after being distributed to nitrile rubber molecule centre
It opens, to have the function that improve low temperature resistant.
Specific embodiment
Embodiment 1
A kind of self-priming chemical pump rubber seal, is made of following component by weight: tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber
112, Lanthanum Stearate modified powdered carbon 22, white carbon black 6, chlorinated paraffin 4.5, anti-aging agent 1.2, sulphur 1, surfactant 0.5;
The preparation method of the modified powdered carbon of the Lanthanum Stearate the following steps are included:
(1) pine is crushed to 500 mesh, obtains pine point, then impregnated 55-60min with ethyl alcohol alkali mixed solution, then carry out
Filtering, cleaning, drying to constant weight, obtains pretreatment pine powder;
(2) pretreatment pine powder obtained above is placed in twin-screw extruder and carries out expanding treatment, then by gained
Puffing material pulverizes, and obtains ultra micro pine powder;
(3) ultra micro pine powder obtained above and fatty acid loss water sorbit ester, petroleum ether are added by 10:1:50 mass ratio
Into reaction kettle, 80 DEG C are heated to, with 1500r/min revolving speed stirring 2 hours, is then filtered, it is dry to constant weight, changed
Property ultra micro pine powder;
(4) Lanthanum Stearate of its quality 1.5% will be added in modified ultra micro pine powder obtained above, after mixing, then in nitrogen
Charing process is carried out under gas atmosphere, until after modified ultra micro pine powder carbonizes completely, then grinding is carried out 1 hour to get Lanthanum Stearate
Modified powdered carbon.
Further, the tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber the preparation method comprises the following steps:
88 parts of nitrile rubber, 3 parts of tetrahydrofurfuryl amine, 1.2 parts of 2- vinyl naphthalene, 8 parts of sericite in powder are added to mixing by weight
In machine, temperature is increased to 135 DEG C, insulation reaction 40min, is then further continued for being heated to 168 DEG C, then add maleimide 2.8
Part with 0.2 part of benzoyl peroxide, insulation reaction 2 hours, then discharge, cooling, washing, drying to constant weight to get four
Hydrogen chaff amine modified butadiene acrylonitrile rubber.
Further, the sericite in powder granularity is 800 mesh.
Further, the anti-aging agent is antioxidant MB.
Further, the surfactant is neopelex.
Further, ethyl alcohol, alkali, water mixing mass ratio are 20:10:50 in the ethyl alcohol alkali mixed solution.
Further, the alkali is sodium hydroxide.
Further, the ultra micro pine Powder Particle Size is 1300 mesh.
Embodiment 2
A kind of self-priming chemical pump rubber seal, is made of following component by weight: tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber
115, Lanthanum Stearate modified powdered carbon 26, white carbon black 7, chlorinated paraffin 4.9, anti-aging agent 1.5, sulphur 2, surfactant 1.5;
The preparation method of the modified powdered carbon of the Lanthanum Stearate the following steps are included:
(1) pine is crushed to 500 mesh, obtains pine point, then impregnated 55-60min with ethyl alcohol alkali mixed solution, then carry out
Filtering, cleaning, drying to constant weight, obtains pretreatment pine powder;
(2) pretreatment pine powder obtained above is placed in twin-screw extruder and carries out expanding treatment, then by gained
Puffing material pulverizes, and obtains ultra micro pine powder;
(3) ultra micro pine powder obtained above and fatty acid loss water sorbit ester, petroleum ether are added by 10:1:50 mass ratio
Into reaction kettle, 80 DEG C are heated to, with 1500r/min revolving speed stirring 2 hours, is then filtered, it is dry to constant weight, changed
Property ultra micro pine powder;
(4) Lanthanum Stearate of its quality 1.5% will be added in modified ultra micro pine powder obtained above, after mixing, then in nitrogen
Charing process is carried out under gas atmosphere, until after modified ultra micro pine powder carbonizes completely, then grinding is carried out 1 hour to get Lanthanum Stearate
Modified powdered carbon.
Further, the tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber the preparation method comprises the following steps:
88 parts of nitrile rubber, 3 parts of tetrahydrofurfuryl amine, 1.2 parts of 2- vinyl naphthalene, 8 parts of sericite in powder are added to mixing by weight
In machine, temperature is increased to 135 DEG C, insulation reaction 40min, is then further continued for being heated to 168 DEG C, then add maleimide 2.8
Part with 0.2 part of benzoyl peroxide, insulation reaction 2 hours, then discharge, cooling, washing, drying to constant weight to get four
Hydrogen chaff amine modified butadiene acrylonitrile rubber.
Further, the sericite in powder granularity is 800 mesh.
Further, the anti-aging agent is antioxidant MB.
Further, the surfactant is neopelex.
Further, ethyl alcohol, alkali, water mixing mass ratio are 20:10:50 in the ethyl alcohol alkali mixed solution.
Further, the alkali is sodium hydroxide.
Further, the ultra micro pine Powder Particle Size is 1300 mesh.
Embodiment 3
A kind of self-priming chemical pump rubber seal, is made of following component by weight: tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber
113, Lanthanum Stearate modified powdered carbon 23, white carbon black 6.5, chlorinated paraffin 4.6, anti-aging agent 1.3, sulphur 1.2, surfactant 0.8;
The preparation method of the modified powdered carbon of the Lanthanum Stearate the following steps are included:
(1) pine is crushed to 500 mesh, obtains pine point, then impregnated 55-60min with ethyl alcohol alkali mixed solution, then carry out
Filtering, cleaning, drying to constant weight, obtains pretreatment pine powder;
(2) pretreatment pine powder obtained above is placed in twin-screw extruder and carries out expanding treatment, then by gained
Puffing material pulverizes, and obtains ultra micro pine powder;
(3) ultra micro pine powder obtained above and fatty acid loss water sorbit ester, petroleum ether are added by 10:1:50 mass ratio
Into reaction kettle, 80 DEG C are heated to, with 1500r/min revolving speed stirring 2 hours, is then filtered, it is dry to constant weight, changed
Property ultra micro pine powder;
(4) Lanthanum Stearate of its quality 1.5% will be added in modified ultra micro pine powder obtained above, after mixing, then in nitrogen
Charing process is carried out under gas atmosphere, until after modified ultra micro pine powder carbonizes completely, then grinding is carried out 1 hour to get Lanthanum Stearate
Modified powdered carbon.
Further, the tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber the preparation method comprises the following steps:
88 parts of nitrile rubber, 3 parts of tetrahydrofurfuryl amine, 1.2 parts of 2- vinyl naphthalene, 8 parts of sericite in powder are added to mixing by weight
In machine, temperature is increased to 135 DEG C, insulation reaction 40min, is then further continued for being heated to 168 DEG C, then add maleimide 2.8
Part with 0.2 part of benzoyl peroxide, insulation reaction 2 hours, then discharge, cooling, washing, drying to constant weight to get four
Hydrogen chaff amine modified butadiene acrylonitrile rubber.
Further, the sericite in powder granularity is 800 mesh.
Further, the anti-aging agent is antioxidant MB.
Further, the surfactant is neopelex.
Further, ethyl alcohol, alkali, water mixing mass ratio are 20:10:50 in the ethyl alcohol alkali mixed solution.
Further, the alkali is sodium hydroxide.
Further, the ultra micro pine Powder Particle Size is 1300 mesh.
Comparative example 1: it is distinguished with embodiment 1 and is only that the fourth that tetrahydrofurfuryl amine modified butadiene acrylonitrile rubber is replaced with to unmodified processing
Nitrile rubber.
The modified acrylonitrile butadiene packing material of comparative example 2:CN101134889 preparation.
Comparative example 3: it is only that with the difference of embodiment 1 and the modified powdered carbon of Lanthanum Stearate is replaced with into unmodified powdered carbon.
Performance comparison will be carried out using embodiment made of same process and comparative example rubber seal;
Processing performance: hardness, tensile strength are tested using method disclosed in GB528;
Cryogenic property test:
Brittleness temperature is tested using method disclosed in GB/T1682-94;
Table 1
Chemical pump prepared by the present invention has excellent tensile strength, hardness and crisp with rubber seal as can be seen from Table 1
Warm-natured degree, can adapt to the working environment of Various Complex, and service life is greatly ensured.
Claims (8)
1. a kind of self-priming chemical pump rubber seal, which is characterized in that be made by weight of following component: tetrahydrofurfuryl amine
Modified butadiene acrylonitrile rubber 112-115, Lanthanum Stearate modified powdered carbon 22-26, white carbon black 6-7, chlorinated paraffin 4.5-4.9, anti-aging agent
1.2-1.5, sulphur 1-2, surfactant 0.5-1.5;
The preparation method of the modified powdered carbon of the Lanthanum Stearate the following steps are included:
(1) pine is crushed to 500 mesh, obtains pine point, then impregnated 55-60min with ethyl alcohol alkali mixed solution, then carry out
Filtering, cleaning, drying to constant weight, obtains pretreatment pine powder;
(2) pretreatment pine powder obtained above is placed in twin-screw extruder and carries out expanding treatment, then by gained
Puffing material pulverizes, and obtains ultra micro pine powder;
(3) ultra micro pine powder obtained above and fatty acid loss water sorbit ester, petroleum ether are added by 10:1:50 mass ratio
Into reaction kettle, 80 DEG C are heated to, with 1500r/min revolving speed stirring 2 hours, is then filtered, it is dry to constant weight, changed
Property ultra micro pine powder;
(4) Lanthanum Stearate of its quality 1.5% will be added in modified ultra micro pine powder obtained above, after mixing, then in nitrogen
Charing process is carried out under gas atmosphere, until after modified ultra micro pine powder carbonizes completely, then grinding is carried out 1 hour to get Lanthanum Stearate
Modified powdered carbon.
2. a kind of self-priming chemical pump rubber seal as described in claim 1, which is characterized in that the tetrahydrofurfuryl amine
Modified butadiene acrylonitrile rubber the preparation method comprises the following steps:
88 parts of nitrile rubber, 3 parts of tetrahydrofurfuryl amine, 1.2 parts of 2- vinyl naphthalene, 8 parts of sericite in powder are added to mixing by weight
In machine, temperature is increased to 135 DEG C, insulation reaction 40min, is then further continued for being heated to 168 DEG C, then add maleimide 2.8
Part with 0.2 part of benzoyl peroxide, insulation reaction 2 hours, then discharge, cooling, washing, drying to constant weight to get four
Hydrogen chaff amine modified butadiene acrylonitrile rubber.
3. a kind of self-priming chemical pump rubber seal as claimed in claim 2, which is characterized in that the sericite powder
Degree is 800 mesh.
4. a kind of self-priming chemical pump rubber seal as described in claim 1, which is characterized in that the anti-aging agent is anti-old
Agent MB.
5. a kind of self-priming chemical pump rubber seal as described in claim 1, which is characterized in that the surfactant is
Neopelex.
6. a kind of self-priming chemical pump rubber seal as described in claim 1, which is characterized in that the ethyl alcohol alkali mixing is molten
Ethyl alcohol, alkali, water mixing mass ratio are 20:10:50 in liquid.
7. a kind of self-priming chemical pump rubber seal as claimed in claim 6, which is characterized in that the alkali is hydroxide
Sodium.
8. a kind of self-priming chemical pump rubber seal as described in claim 1, which is characterized in that the ultra micro pine powder
Degree is 1300 mesh.