CN109868046A - A kind of automobile tire decorations and preparation method thereof - Google Patents

A kind of automobile tire decorations and preparation method thereof Download PDF

Info

Publication number
CN109868046A
CN109868046A CN201910095684.0A CN201910095684A CN109868046A CN 109868046 A CN109868046 A CN 109868046A CN 201910095684 A CN201910095684 A CN 201910095684A CN 109868046 A CN109868046 A CN 109868046A
Authority
CN
China
Prior art keywords
pigment
decorations
automobile tire
deionized water
resin
Prior art date
Application number
CN201910095684.0A
Other languages
Chinese (zh)
Inventor
李勇波
张建国
杨高产
陈柔好
Original Assignee
中山市大田汽车护理用品有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 中山市大田汽车护理用品有限公司 filed Critical 中山市大田汽车护理用品有限公司
Priority to CN201910095684.0A priority Critical patent/CN109868046A/en
Publication of CN109868046A publication Critical patent/CN109868046A/en

Abstract

The invention discloses a kind of automobile tire decorations, which is characterized in that including the following raw material: resin, solvent, pigment, dispersing agent, deionized water.Color film of the present invention is dry, and adhesive force is strong, and the comprehensive performances such as water resistance are excellent rapidly, has rich in color gorgeous, alternative strong, the excellent characteristic of decorative effect.

Description

A kind of automobile tire decorations and preparation method thereof
Technical field
The invention belongs to household chemicals technical fields, and in particular to a kind of automobile tire decorations and preparation method thereof.
Background technique
In recent years, with economic sustainable growth, people's lives level is improved rapidly.Automobile is by simple traffic Tool gradually assigns it now and function is more used to form it as a luxury goods, enters common people house surgingly, Just constantly influence and change everybody life.As the important component of automobile, the appearance of automobile tire is seriously affected The appearance of one automobile.Automobile tire service life under normal use is started probably in 3-5 using 1 year rear tyre Change colour, gloomy equal the problem of influencing appearance.In addition present automobile tire only has the selection of black, do not influence it is safe and resistance to With the decoration that can also carry out color under the premise of property.
In conclusion develop it is a kind of it is convenient to use, to automobile tire, environmentally friendly automobile tire retreading and decorations Urgent need as market.
Summary of the invention
The purpose of the present invention is to provide a kind of automobile tire decorations and preparation method thereof.
The technical solution used in the present invention is:
A kind of automobile tire decorations, which is characterized in that the main product made of the following raw material: resin, solvent, face Material, dispersing agent, deionized water.
Including the following raw material preferably, according to the mass fraction: 10-15 parts of resin, 5-15 parts of solvent, 2-8 parts of pigment, point 3-8 parts of powder, 55-75 parts of deionized water.
Preferably, the resin be with one of moral resin 3AH0545, polyurethane resin, modified rubber lotion or Multiple combinations.
Preferably, the solvent is 95% ethyl alcohol, in dehydrated alcohol, propylene glycol, isopropanol, diethylene glycol monobutyl ether One or more combinations.
Preferably, the pigment be one of inorganic pigment, pearlescent pigment, fluorescent pigment, glitter powder, chameleon or Multiple combinations.
Preferably, the dispersing agent is white carbon black, talcum powder, bentonite, diatomite, zinc stearate, Bentone 38 One of or multiple combinations.
A kind of preparation method of automobile tire decorations, which comprises the steps of:
(1) resin is added in solvent and deionized water, stirring and dissolving;
(2) pigment or dispersible pigment color paste, dispersing agent is added, is uniformly mixed, obtains automobile tire decorations.
Preferably, the dispersible pigment color paste, prepares by the following method: pigment, dispersing agent and solvent are mixed pre- point It dissipates, then by this feed liquid grinding distribution, feed liquid obtains dispersible pigment color paste via sock filtration.
Preferably, the pigment is one of inorganic pigment, fluorescent pigment, chameleon or multiple combinations.
Specific preparation method of the invention:
(1) deionized water, solvent are added and are prepared in pot, start stirring, resin is added when stirring, mixed, sufficiently dissolution;
(2) ground pigment or dispersible pigment color paste are added again and are prepared in pot, continued high speed dispersion stirring, be uniformly dispersed Automobile tire decorations.
When pigment is one of inorganic pigment, fluorescent pigment, chameleon or multiple combinations, pigment can also be made in advance Standby is dispersible pigment color paste, dispersible pigment color paste specific the preparation method comprises the following steps:
(1) pre-dispersed: deionized water being put into pill tank, stirring is slowly started, the face of accurate measurement is put into when stirring Material, dispersing agent mix, and obtain heavy colour slurry, can be ready for use on subsequent grinding and use.
(2) grinding distribution: the mill base after will be pre-dispersed is dispersed by colloid mill equipment, and the feed liquid of dispersion is through filter bag mistake Filter, uses in this, as pigment underflow used in product.During colloid mill carries out homogenous disperse to underflow agent liquid, observation dispersion feelings Condition needs to adjust colloid mill spacing immediately or circulation time of the feed liquid in colloid mill is appropriately extended if dispersion is bad, with The dispersion effect ensured.
Inventive formulation design principle: automobile tire is made with natural rubber, to be repaired on his surface Material similar in selection and his property is had to decoration, the resin for being formulated selection can be combined with rubber surface well to be formed One layer of film for having a covering power, is added ground toner, adds the time that suitable solvent accelerates film forming, and deionized water tune is added Whole cost performance.
Same moral resin 3AH0545 in the present invention, index are as follows: solid content: 45%, viscosity: 300-2000cps/30 ℃;Feature: versatile, gloss is high, excellent water resistance, chemical-resistant);, modified rubber lotion be Dow day damTM 2012。
The beneficial effects of the present invention are:
The present invention can both meet automobile tire appearance repair and decoration demand, while it is pollution-free to people and vehicle, without wound Evil, safety and environmental protection realize following index, effect simultaneously in actual use:
1, color variety multiplicity, it is rich and varied, more selections are provided to user, colouring is easy, covering power is good, fixed The ability of color is good, not fugitive color;
2, adhesive force is good, realizes that nothing falls off;
3, rate of drying is very fast, and repetitive operation is facilitated to use;
4, water-resistance is good, can resistance of rainwater washing against;
Color film of the present invention is dry, and adhesive force is strong, and the comprehensive performances such as water resistance are excellent rapidly, have it is rich in color gorgeous, it is optional Selecting property is strong, the excellent characteristic of decorative effect.
Detailed description of the invention
Fig. 1 is comparison diagram before and after product of the present invention use.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated.
Embodiment 1
Black car tire decorations
Raw material: polyurethane resin 12kg, charcoal blacks 5kg, talcum powder 4kg, white carbon black 1kg, 95% ethyl alcohol 15kg, go from Sub- water 58kg.
The preparation method is as follows:
(1) pre-dispersed: deionized water 18kg to be put into pill tank, placing into power is 22-35KW, frequency conversion 0-3000 Turn/the stirring dispersion machine of min, slowly start stirring, charcoal blacks 5kg, the talcum powder 4kg of accurate measurement and white are put into when stirring Carbon black 1kg is mixed, and obtains heavy colour slurry, can be ready for use on subsequent grinding and be used.
(2) grinding distribution: the mill base after will be pre-dispersed is dispersed by colloid mill equipment, and the feed liquid of dispersion is through 100 mesh Sock filtration is used in this, as pigment underflow used in product.During colloid mill carries out homogenous disperse to underflow agent liquid, observation Dispersion needs to adjust colloid mill spacing immediately or circulation of the feed liquid in colloid mill is appropriately extended if dispersion is bad Time, with the dispersion effect ensured.
(3) agent liquid is prepared: remaining deionized water 40kg, 95% ethyl alcohol 15kg being added and prepared in pot, stirring, side are started It stirs side and 12kg polyurethane resin is added, mix, after completely dissolution, then ground pigment underflow is added and is prepared in pot, continue High speed dispersion stirs 20 minutes, is uniformly dispersed and obtains agent material.
(4) it fills tank finished product: by the production method of barreled paint product, after filling according to required weight dose of liquid, being packaged sealing Obtain automobile tire retreading and decorations.
Embodiment 2
Pearly-lustre red car tire decorations
Raw material: with moral resin 3AH054515kg, 95% ethyl alcohol 10kg, diethylene glycol monobutyl ether 5kg, pearly-lustre red powder 6kg, white carbon black 1kg, talcum powder 5kg, deionized water 55kg.
The preparation of car light reparation aerosol:
The preparation method is as follows:
(1) agent liquid is prepared: deionized water 55kg being added and is prepared in pot, starts stirring, slow that 15kg is added when stirring is same The cunning of moral resin 3AH0545,5kg diethylene glycol monobutyl ether, 95% ethyl alcohol 10kg, 6kg pearly-lustre red powder, 1kg white carbon black, 5kg The materials such as mountain flour, after elementary mixing, high speed dispersion is stirred 20 minutes, is uniformly dispersed and is obtained agent material.
(2) tank finished product is filled: with embodiment 1.
Embodiment 3
Blue cars tire decorations
Raw material: modified rubber lotion 15kg, 95% ethyl alcohol 5kg, diethylene glycol monobutyl ether 5kg, blue powder 6kg, bentonite 3kg, zinc stearate 0.5kg, deionized water 55.5kg.
The preparation method is as follows:
(1) pre-dispersed: deionized water 15kg to be put into pill tank, placing into power is 22-35KW, frequency conversion 0-3000 Turn/the stirring dispersion machine of min, slowly starts stirring, blue powder 6kg, the bentonite 3kg, tristearin of accurate measurement are put into when stirring Sour zinc 0.5kg is mixed, and obtains heavy colour slurry, can be ready for use on subsequent grinding and be used.
(2) grinding distribution: the mill base after will be pre-dispersed is dispersed by colloid mill equipment, and the feed liquid of dispersion is through 100 mesh Sock filtration is used in this, as pigment underflow used in product.During colloid mill carries out homogenous disperse to underflow agent liquid, observation Dispersion needs to adjust colloid mill spacing immediately or circulation of the feed liquid in colloid mill is appropriately extended if dispersion is bad Time, with the dispersion effect ensured.
(3) agent liquid is prepared: by remaining deionized water 40.5kg, 95% ethyl alcohol 5kg, diethylene glycol monobutyl ether 5kg is added It prepares in pot, starts stirring, be added modified rubber lotion 15kg when stirring, mixing, after completely dissolution, then by ground pigment Underflow, which is added, to be prepared in pot, is continued high speed dispersion and is stirred 20 minutes, is uniformly dispersed and obtains agent material.
(4) it fills tank finished product: by the production method of barreled paint product, after filling according to required weight dose of liquid, being packaged sealing Obtain automobile tire retreading and decorations.
Embodiment 4
Blue cars tire decorations
Raw material: modified rubber lotion 10kg, isopropanol 5kg, chameleon 2kg, diatomite 3kg, deionized water 59kg.
The preparation method is as follows:
(1) pre-dispersed: deionized water 18kg to be put into pill tank, placing into power is 22-35KW, frequency conversion 0-3000 Turn/the stirring dispersion machine of min, slowly starts stirring, the chameleon 2kg of accurate measurement, diatomite 3kg are put into when stirring, mixing, Heavy colour slurry is obtained, subsequent grinding can be ready for use on and used.
(2) grinding distribution: the mill base after will be pre-dispersed is dispersed by colloid mill equipment, and the feed liquid of dispersion is through 100 mesh Sock filtration is used in this, as pigment underflow used in product.During colloid mill carries out homogenous disperse to underflow agent liquid, observation Dispersion needs to adjust colloid mill spacing immediately or circulation of the feed liquid in colloid mill is appropriately extended if dispersion is bad Time, with the dispersion effect ensured.
(3) agent liquid is prepared: remaining deionized water 41kg, isopropanol 5kg being added and prepared in pot, stirring is started, while stirring Modified rubber lotion 10kg is added in side, mixes, after completely dissolution, then ground pigment underflow is added and is prepared in pot, continues High speed dispersion stirs 20 minutes, is uniformly dispersed and obtains agent material.
(4) it fills tank finished product: by the production method of barreled paint product, after filling according to required weight dose of liquid, being packaged sealing Obtain automobile tire retreading and decorations.
Embodiment 5
Blue cars tire decorations
Raw material: modified rubber lotion 15kg, propylene glycol 5kg, 38 8kg of blue-fluorescence pigment 8kg, Bentone, deionization Water 75kg.
The preparation method is as follows:
(1) pre-dispersed: deionized water 15kg to be put into pill tank, placing into power is 22-35KW, frequency conversion 0-3000 Turn/the stirring dispersion machine of min, slowly starts stirring, blue-fluorescence pigment 8kg, Bentone of accurate measurement are put into when stirring 388kg is mixed, and obtains heavy colour slurry, can be ready for use on subsequent grinding and be used.
(2) grinding distribution: the mill base after will be pre-dispersed is dispersed by colloid mill equipment, and the feed liquid of dispersion is through 100 mesh Sock filtration is used in this, as pigment underflow used in product.During colloid mill carries out homogenous disperse to underflow agent liquid, observation Dispersion needs to adjust colloid mill spacing immediately or circulation of the feed liquid in colloid mill is appropriately extended if dispersion is bad Time, with the dispersion effect ensured.
(3) agent liquid is prepared: remaining deionized water 60kg, propylene glycol 5kg being added and prepared in pot, stirring is started, while stirring Modified rubber lotion 15kg is added in side, mixes, after completely dissolution, then ground pigment underflow is added and is prepared in pot, continues High speed dispersion stirs 20 minutes, is uniformly dispersed and obtains agent material.
(4) it fills tank finished product: by the production method of barreled paint product, after filling according to required weight dose of liquid, being packaged sealing Obtain automobile tire retreading and decorations.
Embodiment 6
Pearly-lustre red car tire decorations
Raw material: with moral resin 3AH054515kg, dehydrated alcohol 15kg, glitter powder 6kg, white carbon black 1kg, talcum powder 5kg, Deionized water 55kg.
The preparation of car light reparation aerosol:
The preparation method is as follows:
(1) agent liquid is prepared: deionized water 55kg being added and is prepared in pot, starts stirring, slow that 15kg is added when stirring is same The materials such as moral resin 3AH0545, dehydrated alcohol 15kg, glitter powder 6kg, white carbon black 1kg, talcum powder 5kg are high after elementary mixing It speed dispersion stirring 20 minutes, is uniformly dispersed and obtains agent material.
(2) tank finished product is filled: with embodiment 1.
Performance test
Every physical and chemical, functional attributes method of inspection:
1. smell: product are heard.
2. adhesive force: by application method, correctly product is uniformly sprayed on a tinplate small iron plate by spray pattern, 30 points Clock touches film surface after color film is completely dried, with finger, to be that adhesive force is good without decoloration.
3. surface drying time (25 DEG C, min): referring to " dry tack free in GB1728-79 paint film putty membrane drying time measuring method The fingers-touch method of chronometry " touches color film surface with finger, such as feels that some are tacky, but stick to the finger without toner, that is, recognize For dry tack free.
4. water-resistance: method one: will be sprayed with the small test piece (such as adhesion test iron plate) of colorant, impregnate into the water, see Examine whether color film dissolves.Method two: opening tap, small test piece be placed under water flow and is rinsed, and whether observation color film dissolves.
The quality index for the product that embodiment 1-3 is prepared is as shown in table 1.
Table 1
Index parameter Embodiment 1 Embodiment 2 Embodiment 3
Smell Free from extraneous odour Free from extraneous odour Free from extraneous odour
Adhesive force It is good Preferably Generally
Surface drying time (25 DEG C, min) < 5 < 4 < 6
Water-resistance It is good It is good It is good
From the data and attached drawing 1 of table 1: doughnut decorations tool Coloured film of the invention is dry rapidly, adhesive force is strong, The advantages that water-fast, and its is rich in color gorgeous, alternative strong, decorative effect is excellent, can meet consumer and arbitrarily express displaying The demand of individual character wish.
Above-described embodiment is merely illustrative of the technical solution of the present invention and is not intended to limit it, all without departing from the present invention Any modification of spirit and scope or equivalent replacement should all cover the range in technical solution of the present invention.

Claims (9)

1. a kind of automobile tire decorations, which is characterized in that the main product made of the following raw material: resin, solvent, pigment, Dispersing agent, deionized water.
2. a kind of automobile tire decorations according to claim 1, which is characterized in that according to the mass fraction, including it is as follows Raw material: 10-15 parts of resin, 5-15 parts of solvent, 2-8 parts of pigment, 3-8 parts of dispersing agent, 55-75 parts of deionized water.
3. a kind of automobile tire decorations according to claim 1 or 2, which is characterized in that the resin is with moral tree One of rouge 3AH0545, polyurethane resin, modified rubber lotion or multiple combinations.
4. a kind of automobile tire decorations according to claim 1 or 2, which is characterized in that the solvent is 95% second One of alcohol, dehydrated alcohol, propylene glycol, isopropanol, diethylene glycol monobutyl ether or multiple combinations.
5. a kind of automobile tire decorations according to claim 1 or 2, which is characterized in that the pigment is inorganic face One of material, pearlescent pigment, fluorescent pigment, glitter powder, chameleon or multiple combinations.
6. a kind of automobile tire decorations according to claim 1 or 2, which is characterized in that the dispersing agent is hard charcoal One of black, talcum powder, bentonite, diatomite, zinc stearate, Bentone 38 or multiple combinations.
7. a kind of preparation method of automobile tire decorations, which comprises the steps of:
(1) resin is added in solvent and deionized water, stirring and dissolving;
(2) pigment or dispersible pigment color paste, dispersing agent is added, is uniformly mixed, obtains automobile tire decorations.
8. a kind of preparation method of automobile tire decorations according to claim 7, which is characterized in that the pigment colour Slurry, prepares by the following method: the mixing of pigment, dispersing agent, solvent and deionized water is pre-dispersed, then this feed liquid is ground Dispersion, feed liquid obtain dispersible pigment color paste via sock filtration.
9. a kind of preparation method of automobile tire decorations according to claim 8, which is characterized in that the pigment is nothing One of machine pigment, fluorescent pigment, chameleon or multiple combinations.
CN201910095684.0A 2019-01-31 2019-01-31 A kind of automobile tire decorations and preparation method thereof CN109868046A (en)