CN109836038A - A kind of bottle body processing technology of gas absorption bottle - Google Patents
A kind of bottle body processing technology of gas absorption bottle Download PDFInfo
- Publication number
- CN109836038A CN109836038A CN201711199365.1A CN201711199365A CN109836038A CN 109836038 A CN109836038 A CN 109836038A CN 201711199365 A CN201711199365 A CN 201711199365A CN 109836038 A CN109836038 A CN 109836038A
- Authority
- CN
- China
- Prior art keywords
- bottle body
- bottle
- hours
- gas absorption
- processing technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of bottle body processing technology of gas absorption bottle, it includes (1) by soft soda chemical glass material, quartz sand, boric acid, that magnesium fluoride is put into stirrer for mixing is uniform；(2) above-mentioned mixture is put into high temperature kiln, is heated to 1280 DEG C, fired 3-5 hours, be then cooled to 680 DEG C with 6 DEG C/min, heat preservation；(3) chrome green is added, 1580 DEG C is warming up to 15 DEG C/min, keeps the temperature 2-4 hours；(4) material in step (3) is sent into molding machine, bottle body, natural cooling is made according to specification；(5) bottle body is sprayed.High heat-resisting, the long service life thoroughly of finished product of the present invention.
Description
Technical field
The present invention relates to a kind of bottle bodies, and in particular to a kind of bottle body processing technology.
Background technique
The bottle body material of existing gas absorption bottle, generally existing raw material ratio is complicated, and end properties are general, are processed into
The problems such as this is high does not meet actual production requirement.
Summary of the invention
Goal of the invention: purpose of the invention is to overcome the shortcomings in the prior art, and it is high thoroughly heat-resisting to provide a kind of finished product,
The bottle body processing technology of gas absorption bottle with long service life.
Technical solution: in order to solve the above-mentioned technical problem, a kind of bottle body processing work of gas absorption bottle of the present invention
Skill, it includes the following steps,
(1) by soft soda chemical glass material, quartz sand, boric acid, that magnesium fluoride is put into stirrer for mixing is uniform；
(2) above-mentioned mixture is put into high temperature kiln, is heated to 1280 DEG C, fired 3-5 hours, then with 6 DEG C/min cooling
To 680 DEG C, heat preservation；
(3) chrome green is added, 1580 DEG C is warming up to 15 DEG C/min, keeps the temperature 2-4 hours；
(4) material in step (3) is sent into molding machine, bottle body, natural cooling is made according to specification；
(5) bottle body is sprayed.
The utility model has the advantages that compared with prior art, the present invention its remarkable advantage is: the present invention by rigorous procedure of processing,
It is had excellent performance finished-product material, it is whole high thoroughly heat-resisting, coloured glass material is sprayed on bottle body, guarantees that product is beautiful, this technique
It runs smoothly, is suitble to large-scale production, meets actual operation requirements.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated.
A kind of bottle body processing technology of gas absorption bottle of the present invention, it includes the following steps,
(1) by soft soda chemical glass material, quartz sand, boric acid, that magnesium fluoride is put into stirrer for mixing is uniform；
(2) above-mentioned mixture is put into high temperature kiln, is heated to 1280 DEG C, fired 4 hours, be then cooled to 6 DEG C/min
680 DEG C, heat preservation；
(3) chrome green is added, 1580 DEG C is warming up to 15 DEG C/min, keeps the temperature 3 hours；
(4) material in step (3) is sent into molding machine, bottle body, natural cooling is made according to specification；
(5) bottle body is sprayed.
The present invention has excellent performance finished-product material by rigorous procedure of processing, whole high thoroughly heat-resisting, by coloured glass material
It is sprayed on bottle body, guarantees that product is beautiful, this process operation is steady, is suitble to large-scale production, meets actual operation requirements.
The present invention provides a kind of thinking and methods, and there are many method and the approach for implementing the technical solution, the above institute
Stating is only the preferred embodiment of the present invention, it is noted that for those skilled in the art, is not being departed from
Under the premise of the principle of the invention, several improvements and modifications can also be made, these improvements and modifications also should be regarded as guarantor of the invention
Range is protected, all undefined components in this embodiment can be implemented in the prior art.
Claims (1)
1. a kind of bottle body processing technology of gas absorption bottle, it is characterised in that: it includes the following steps,
(1) by soft soda chemical glass material, quartz sand, boric acid, that magnesium fluoride is put into stirrer for mixing is uniform；
(2) above-mentioned mixture is put into high temperature kiln, is heated to 1280 DEG C, fired 3-5 hours, then with 6 DEG C/min cooling
To 680 DEG C, heat preservation；
(3) chrome green is added, 1580 DEG C is warming up to 15 DEG C/min, keeps the temperature 2-4 hours；
(4) material in step (3) is sent into molding machine, bottle body, natural cooling is made according to specification；
(5) bottle body is sprayed.