CN109763233A - The method for weaving of the fabric tissue of imitative knitted structure - Google Patents

Abstract

The invention discloses a weaving method of a fabric structure imitating a knitted structure. The weaving method is as follows: from the front, 16 pieces of healds, 16 pieces/cycle: 1-2-3-4-5-6-7-8 ‑9‑10‑11‑12‑13‑14‑15‑16, one-pass threading method; weaving heddle method: front up, 16 picks/cycle: 1) 1‑5‑9‑13 A, 2) 1‑9B, 3) 2‑6‑10‑14A, 4) 6‑14B, 5) 4‑8‑12‑16A, 6) 8‑16B, 7) 3‑7‑11‑15 A, 8) 3-11 B, 9) 1-5-9-13 A, 10) 5-13 B, 11) 2-6-10-14 A, 12) 2-10 B, 13) 4-8 ‑12‑16A, 14) 4‑12B, 15) 3‑7‑11‑15A, 16) 7‑15B. The products woven by this method have original appearance, not only the appearance and performance of knitted fabrics, but also the style of woven fabrics. The products and garments have good application prospects and broad prospects for industrialization.

Description

Weaving method of fabric weave with knitted structure

technical field

The invention belongs to the field of textiles, and in particular relates to a weaving method of a fabric structure imitating a knitted structure.

Background technique

Knitted fabric is a fabric produced by a knitting machine, which has the advantages of multi-directional deformation, comfortable wearing and good plasticity. The appearance of the organizational structure shows the staggered patterns of the silk threads in the upper and lower, front and rear, and left and right. Coupled with the pattern, it has a good vision and is a unique style of knitted fabrics. The shuttleless loom uses a set of warp threads and a set of weft threads to interweave, and the threads show a horizontal or vertical shape on the fabric. It is a good research and development direction to weave the texture style of knitted fabric with a shuttleless loom, and the market prospect is broad.

SUMMARY OF THE INVENTION

The purpose of the present invention is to provide a weaving method of a knitted fabric weave.

In order to solve the above-mentioned technical problems, the present invention adopts the following technical solutions: a weaving method of a fabric weave imitating a knitted structure,

Produced by water jet loom;

The warp direction raw materials are made of polyester low elastic yarn and spandex covered yarn. The weft direction raw materials are divided into two groups: A weft and B weft. A weft is: 750D/T400, and B weft is: 150DDTY;

The weaving method is: from the front, 16 healds, 16/cycle: 1-2-3-4-5-6-7-8-9-10-11-12-13-14-15-16 , a shunting method;

The weaving method is: front, 16 picks/cycle: 1) 1-5-9-13A, 2) 1-9B, 3) 2-6-10-14A, 4) 6-14B , 5) 4-8-12-16A, 6) 8-16B, 7) 3-7-11-15A, 8) 3-11B, 9) 1-5-9-13A, 10) 5-13B, 11) 2-6-10-14A, 12) 2-10B, 13) 4-8-12-16A, 14) 4-12B, 15) 3-7-11-15 A, 16) 7-15B.

Optimized, the warp direction raw material adopts 75D polyester low elastic yarn and 40D spandex covered yarn.

Optimized, the organization structure is 16*16 weft weight organization.

The beneficial effects of the invention are: the products woven by the method have original appearance, not only the appearance and performance of knitted cloth, but also the style of woven cloth, the production process is simple, novel and unique, and the innovation is strong, which can guide and satisfy consumption. This product has good prospects for clothing application and broad prospects for industrialization.

Description of drawings

Accompanying drawing 1 is the structure diagram of imitation knitted cloth;

Accompanying drawing 2 is the back single-layer organizational structure diagram;

Accompanying drawing 3 is the front single-layer organizational structure diagram;

Accompanying drawing 4 is the effect diagram of the single-layer object on the reverse side.

Detailed ways

The present invention is described in detail below in conjunction with the embodiments shown in the accompanying drawings:

The weaving method of the fabric weave with a knitted structure: it is produced by a water jet loom; considering the multi-directional stretchability and comfort of knitted products, the warp raw materials are 75D polyester low elastic yarn and 40D spandex covered yarn, and the weft raw materials are It is divided into two groups: A weft and B weft. A weft is: 750D/T400, and B weft is: 150DDTY. This combination of raw materials can make the fabric have a four-way elastic style, and has a certain skinny and comfortable; The comprehensive method is: from the front, 16 pieces of comprehensive, 16 pieces/cycle: 1-2-3-4-5-6-7-8-9-10-11-12-13-14-15-16, one order Threading method; weaving method is: front, 16 picks/cycle: 1) 1-5-9-13A, 2) 1-9B, 3) 2-6-10-14A, 4)6 -14B, 5) 4-8-12-16A, 6) 8-16B, 7) 3-7-11-15A, 8) 3-11B, 9) 1-5-9-13A , 10) 5-13 B, 11) 2-6-10-14 A, 12) 2-10 B, 13) 4-8-12-16 A, 14) 4-12 B, 15) 3-7- 11-15A, 16) 7-15B, A latitude and B latitude should correspond to designated positions.

The organization structure is 16*16 double-sided weft weight organization. Using the interweaving rules of warp and weft, and the length, position and shrinkage of different thread floats, the appearance and performance of knitted fabric can be woven.

Figure 1 is an organizational chart of the imitation knitted structure. The vertical is the warp and the horizontal is the weft. The first group consists of the 1st, 3rd, 5th, 7th, 9th, 11th, 13th, and 15th wefts, and the 2nd, 4th, 6th, 8th, 10th, The 12th, 14th, and 16th wefts form the second group.

Since the weft float lengths of the second group of weft threads are respectively longer than the weft float lengths of the first group of adjacent weft threads and have the same warp and float threads, the second group of weft threads can completely cover the first group of weft threads on the front, so that the The first group of wefts are all presented on the reverse side of the fabric, and the single-layer weft structure on the reverse side is shown in Figure 2, while the second group of weft threads are all presented on the front of the fabric, and the front single-layer structure is shown in Figure 3, with different shapes and styles on both sides. The first group of weft threads are high-shrinkage elastic threads, which are presented on the reverse side of the cloth and tighten the weft threads, and the second group of non-elastic threads is squeezed to bulge on the front of the fabric, enhancing the three-dimensional, bulky and comfortable feeling of the fabric. In the front single-layer weave, the weft threads are long and misaligned with each other, which increases the gap and space area of the fabric, and forms small and dislocated holes on the front and back at the same time. When the force is pulled left and right, an "S"-shaped twist is formed, and the twist range is strengthened, so as to achieve the effect of imitating the appearance and performance of knitted fabrics.

The above-mentioned embodiments are only intended to illustrate the technical concept and characteristics of the present invention, and the purpose thereof is to enable those who are familiar with the art to understand the content of the present invention and implement them accordingly, and cannot limit the protection scope of the present invention. All equivalent changes or modifications made according to the spirit of the present invention should be included within the protection scope of the present invention.

Claims (3)

1. a kind of method for weaving of the fabric tissue of imitative knitted structure, it is characterised in that:

It is produced using water-jet loom；

Through using low elastic polyester filament and polyurethane covered yarn to raw material, broadwise raw material is divided into two groups of first latitude, second latitude, first latitude are as follows: 750D/ T400, second latitude are as follows: 150DDTY；

Woven fabric is gaited method are as follows: and preceding, 16 are comprehensive, and 16/circulation: 1-2-3-4-5-6-7-8-9-10-11-12-13-14-15- 16, a straight arrangement；

Woven fabric shaft raising method are as follows: preceding, 16 latitudes/circulation: 1) 1-5-9-13 first, 2) 1-9 second, 3) 2-6-10-14 first, 4) 6-14 second, 5) 4-8-12-16 first, 6) 8-16 second, 7) 3-7-11-15 first, 8) 3-11 second, 9) 1-5-9-13 first, 10) 5-13 second, 11) 2-6- 10-14 first, 12) 2-10 second, 13) 4-8-12-16 first, 14) 4-12 second, 15) 3-7-11-15 first, 16) 7-15 second.

2. the method for weaving of the fabric tissue of imitative knitted structure according to claim 1, it is characterised in that: described through to original Material is using 75D low elastic polyester filament and 40D polyurethane covered yarn.

3. the method for weaving of the fabric tissue of imitative knitted structure according to claim 1, it is characterised in that: institutional framework is 16*16 latitude re-organized.