CN109702842A - A kind of processing method of anticollision panda dado - Google Patents
A kind of processing method of anticollision panda dado Download PDFInfo
- Publication number
- CN109702842A CN109702842A CN201910082222.5A CN201910082222A CN109702842A CN 109702842 A CN109702842 A CN 109702842A CN 201910082222 A CN201910082222 A CN 201910082222A CN 109702842 A CN109702842 A CN 109702842A
- Authority
- CN
- China
- Prior art keywords
- dado
- panda
- anticollision
- bark
- cork oak
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention relates particularly to a kind of processing methods of anticollision panda dado.Cork oak bark is poured into hot-tub and impregnates and dries, wood shavings are made, is stirred after dry with urea-formaldehyde resin adhesive, mats formation into cork oak bark slab, it is hot-forming to be sawn into blank；Take it is partially dried after bark wood shavings, bark powder is made and is mixed well respectively with pigment, takes out prefabricated panda design drawing mold, it is placed on the center position of blank, white glue with vinyl brushing is dipped in die location, bark powder is sprinkling upon in the gluing sash of mold, repeatedly reaches scheduled thickness；After reaching certain intensity, bark powder glue-line is struck off with scraper plate, after cured, removes mold frame, is filled and led up the frame line of rabbet joint that mold leaves with black bark powder putty；After being fully cured, sanding, finished product is made in repairing, paint.The invention is simple and feasible, using cheap cork oak bark processing fent, have the characteristics that it is light-weight, rich in snubber elastomeric, and environment-protecting and non-poisonous evil, wide market.
Description
Technical field
The invention belongs to wood processing technique fields, and in particular to a kind of processing method of anticollision panda dado.
Background technique
Because autocontrol force is poor, Yi Fasheng is fallen down to be hit wall and causes unexpected injury child of tender age, is caused not to family and society
Necessary loss.Common corresponding method is to increase nursing staff, but still cannot prevent the event hair that accidental falls hit wall completely
It is raw.
Summary of the invention
To solve the above-mentioned problems, the present invention provides a kind of processing methods of anticollision panda dado.This method exploitation value
The cheap cork oak bark processing fent of lattice, is handled through special process, manufactures anticollision panda wall skirt plate.The anticollision panda dado
Plate have the characteristics that it is light-weight, rich in snubber elastomeric, and environment-protecting and non-poisonous evil can protect child, prevent it is unexpected tumble hit wall after
Caused by grievous injury, loss is minimized.Due to being added to lovely panda cartoon character, the happiness of children is firmly got
Love and welcome, wide market.
For achieving the above object, the present invention adopts the following technical scheme:
The present invention provides a kind of processing methods of anticollision panda dado, and this method comprises the following steps:
Step 1: collecting cork oak bark processing fent, pour into hot-tub and impregnate 48~60 hours, on the place of ventilation
Sunning is sent into flaking machining, wood shavings is made after the moisture content of cork oak bark processing fent is lower than 20%；
Step 2: manufactured wood shavings are sent into roller drier is dry, it is dry after moisture control 8~10%, it is spare；
Step 3: cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer, it is spare；
Step 4: sizing wood shavings being mated formation into the cork oak bark slab of gauge thickness in spreading machine, hot press is sent into and is hot pressed into
Type is sawn into the specification of anticollision dado blank after room temperature is 48 hours cooling；
Step 5: manufactured anticollision dado blank being sent into four side moulder processing dado and is longitudinally begun to speak after slot, both-end Milling Machining is recycled
The transverse direction of dado is begun to speak slot, and anticollision dado blank is made after polishing；
Step 6: take it is partially dried after cork oak bark wood shavings, be sent into pulverizer crush, cross 20 mesh sieve, it is spare；
Step 7: according to the design colours of design drawing 1, manufactured cork oak bark powder is mixed well respectively with a variety of different pigment, it is standby
With；
Step 8: taking out the plastic mould of prefabricated panda design drawing 1, be placed on the center position of anticollision dado blank, use clip
After fixation, dip white glue with vinyl with hairbrush, equably brush in the position that panda plastic mould limits, pinch taken with hand be mixed with it is various
The cork oak bark powder of pigment is equably sprinkling upon in the gluing sash of plastic mould by the requirement of Fig. 1 color；
Step 9: when the bark powder presentation overlap joint state under subsequent spread, showing that occurring starved in the gluing sash of plastic mould shows
As, it is necessary to white glue with vinyl is dipped with hairbrush and continues bark powder glue-line in brushing plastic mould sash, repeats this process, until tree
Until skin powder bondline thickness reaches scheduled thickness；
Step 10: after the intensity that bark powder glue-line hardness reaches certain (glue-line is not fully cured), striking off bark powder with scraper plate
Glue-line carefully removes plastic mould frame after bark powder glue-line is fully cured, the frame for being left mold with black bark powder putty
The line of rabbet joint is filled and led up；
Step 11: after the panda pattern of panda dado steel slab surface is fully cured, panda dado slab being sent into sander sand
Light, then repaired, painted, anticollision panda dado finished product is made.
The cork oak bark processing fent after immersion hot water is spread out in the step 1 and is dried on the place of ventilation,
After the moisture content of bark leftover bits and pieces is lower than 20%, flaking and dry processing can be carried out.Moisture content is too low to easily cause wood shavings mistake
It is broken, influence the intensity of dado finished product plate；The energy consumption of the excessively high then drying process of moisture content is bigger than normal.
Cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer in the step 3, ureaformaldehyde tree
The additive amount of rouge adhesive is the 12~15% of cork oak bark wood shavings quality.
Hot-forming cork oak bark particieboard is sawn into anticollision dado blank, the specification of the blank in the step 4
It is thick having a size of the wide X of 1200~1500mm X 500mm X 18mm(long X).
Dry cork oak bark wood shavings grinding and sieving is chosen in the step 6, passes through the side mixed with selected pigment
Formula prepares panda pattern filler, can prevent the difference because of material to the maximum extent, causes panda pattern because of the cracking that expands with heat and contract with cold, takes off
The problem of falling.
Manufactured cork oak bark powder is mixed well respectively with a variety of different pigment in the step 7, the product of all pigment
Kind and quantity selection must be according to design drawings 1.
In the step 8 during shedding the cork oak bark powder for being mixed with various pigment, anticollision wall skirt plate base is necessary
The case where laying flat, preventing sagging and shed boundary generation.
It, need to be by adsorbing anticollision dado because pigment bark powder itself is without glue in the step 9 during shedding bark powder
As binder, such as starved during repeating to shed easily causes empty inside panda pattern the white glue with vinyl of steel slab surface brushing
The defects of heart, hole, bridging, influence the quality of finished product anticollision panda dado.
In the step 10 after the intensity that bark powder glue-line hardness reaches certain (glue-line is not fully cured), scraped with scraper plate
The defects of flat bark powder glue-line is compacted bark powder glue-line, prevents glue layer from generating hole.
In the step 10 after bark powder glue-line is fully cured, plastic mould frame is removed, it will with black bark powder putty
The frame line of rabbet joint that mold leaves is filled and led up, and the black bark powder putty is by cork oak bark: carbon black: edible vegetable oil=70%:10%:20%
(mass ratio) is formulated.
The present invention has the advantages that providing a kind of processing method of anticollision panda dado.This method utilizes cheap
Cork oak bark processing fent, handled through special process, manufacture anticollision panda wall skirt plate.The anticollision panda wall skirt plate has
The characteristics of light-weight, rich in snubber elastomeric, and environment-protecting and non-poisonous evil, it can protect child, caused by preventing unexpected wrestling from hitting after wall
Grievous injury minimizes loss.Due to being added to lovely panda cartoon character, liking and vigorously for children is firmly got
It meets, wide market.
Detailed description of the invention
Fig. 1 is panda pattern schematic diagram on anticollision of embodiment of the present invention panda wall skirt plate.
Specific embodiment
Embodiment 1
A kind of specific steps of the processing method of anticollision panda dado are as follows:
Step 1: cork oak bark processing fent is collected, pours into hot-tub and impregnates 48 hours, dried on the place of ventilation,
After the moisture content of cork oak bark processing fent is lower than 20%, it is sent into flaking machining, wood shavings are made；
Step 2: manufactured wood shavings are sent into roller drier is dry, it is dry after moisture control 8~10%, it is spare；
Step 3: cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer, it is spare；
Step 4: sizing wood shavings being mated formation into the cork oak bark slab of gauge thickness in spreading machine, hot press is sent into and is hot pressed into
Type is sawn into the specification of anticollision dado blank after room temperature is 48 hours cooling；
Step 5: manufactured anticollision dado blank being sent into four side moulder processing dado and is longitudinally begun to speak after slot, both-end Milling Machining is recycled
The transverse direction of dado is begun to speak slot, and anticollision dado blank is made after polishing；
Step 6: take it is partially dried after cork oak bark wood shavings, be sent into pulverizer crush, cross 20 mesh sieve, it is spare；
Step 7: according to the design colours of design drawing 1, manufactured cork oak bark powder is mixed well respectively with a variety of different pigment, it is standby
With；
Step 8: taking out the plastic mould of prefabricated panda design drawing 1, be placed on the center position of anticollision dado blank, use clip
After fixation, dip white glue with vinyl with hairbrush, equably brush in the position that panda plastic mould limits, pinch taken with hand be mixed with it is various
The cork oak bark powder of pigment is equably sprinkling upon in the gluing sash of plastic mould by the requirement of Fig. 1 color；
Step 9: when the bark powder presentation overlap joint state under subsequent spread, showing that occurring starved in the gluing sash of plastic mould shows
As, it is necessary to white glue with vinyl is dipped with hairbrush and continues bark powder glue-line in brushing plastic mould sash, repeats this process, until tree
Until skin powder bondline thickness reaches scheduled thickness；
Step 10: after the intensity that bark powder glue-line hardness reaches certain (glue-line is not fully cured), striking off bark powder with scraper plate
Glue-line carefully removes plastic mould frame after bark powder glue-line is fully cured, the frame for being left mold with black bark powder putty
The line of rabbet joint is filled and led up；
Step 11: after the panda pattern of panda dado steel slab surface is fully cured, panda dado slab being sent into sander sand
Light, then repaired, painted, anticollision panda dado finished product is made.
Cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer in the step 3, ureaformaldehyde tree
The additive amount of rouge adhesive is the 12% of cork oak bark wood shavings quality.
Hot-forming cork oak bark particieboard is sawn into anticollision dado blank, the specification of the blank in the step 4
It is thick having a size of the wide X of 1200~1500mm X 500mm X 18mm(long X).
Dry cork oak bark wood shavings grinding and sieving is chosen in the step 6, passes through the side mixed with selected pigment
Formula prepares panda pattern filler, can prevent the difference because of material to the maximum extent, causes panda pattern because of the cracking that expands with heat and contract with cold, takes off
The problem of falling.
It, need to be by adsorbing anticollision dado because pigment bark powder itself is without glue in the step 9 during shedding bark powder
As binder, such as starved during repeating to shed easily causes empty inside panda pattern the white glue with vinyl of steel slab surface brushing
The defects of heart, hole, bridging, influence the quality of finished product anticollision panda dado.
In the step 10 after bark powder glue-line is fully cured, plastic mould frame is removed, it will with black bark powder putty
The frame line of rabbet joint that mold leaves is filled and led up, and the black bark powder putty is by cork oak bark: carbon black: edible vegetable oil=70%:10%:20%
(mass ratio) is formulated.
Embodiment 2
A kind of specific steps of the processing method of anticollision panda dado are as follows:
Step 1: cork oak bark processing fent is collected, pours into hot-tub and impregnates 55 hours, dried on the place of ventilation,
After the moisture content of cork oak bark processing fent is lower than 20%, it is sent into flaking machining, wood shavings are made；
Step 2: manufactured wood shavings are sent into roller drier is dry, it is dry after moisture control 8~10%, it is spare；
Step 3: cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer, it is spare；
Step 4: sizing wood shavings being mated formation into the cork oak bark slab of gauge thickness in spreading machine, hot press is sent into and is hot pressed into
Type is sawn into the specification of anticollision dado blank after room temperature is 48 hours cooling；
Step 5: manufactured anticollision dado blank being sent into four side moulder processing dado and is longitudinally begun to speak after slot, both-end Milling Machining is recycled
The transverse direction of dado is begun to speak slot, and anticollision dado blank is made after polishing；
Step 6: take it is partially dried after cork oak bark wood shavings, be sent into pulverizer crush, cross 20 mesh sieve, it is spare；
Step 7: according to the design colours of design drawing 1, manufactured cork oak bark powder is mixed well respectively with a variety of different pigment, it is standby
With；
Step 8: taking out the plastic mould of prefabricated panda design drawing 1, be placed on the center position of anticollision dado blank, use clip
After fixation, dip white glue with vinyl with hairbrush, equably brush in the position that panda plastic mould limits, pinch taken with hand be mixed with it is various
The cork oak bark powder of pigment is equably sprinkling upon in the gluing sash of plastic mould by the requirement of Fig. 1 color；
Step 9: when the bark powder presentation overlap joint state under subsequent spread, showing that occurring starved in the gluing sash of plastic mould shows
As, it is necessary to white glue with vinyl is dipped with hairbrush and continues bark powder glue-line in brushing plastic mould sash, repeats this process, until tree
Until skin powder bondline thickness reaches scheduled thickness；
Step 10: after the intensity that bark powder glue-line hardness reaches certain (glue-line is not fully cured), striking off bark powder with scraper plate
Glue-line carefully removes plastic mould frame after bark powder glue-line is fully cured, the frame for being left mold with black bark powder putty
The line of rabbet joint is filled and led up；
Step 11: after the panda pattern of panda dado steel slab surface is fully cured, panda dado slab being sent into sander sand
Light, then repaired, painted, anticollision panda dado finished product is made.
Cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer in the step 3, ureaformaldehyde tree
The additive amount of rouge adhesive is the 13% of cork oak bark wood shavings quality.
Hot-forming cork oak bark particieboard is sawn into anticollision dado blank, the specification of the blank in the step 4
It is thick having a size of the wide X of 1200~1500mm X 500mm X 18mm(long X).
Dry cork oak bark wood shavings grinding and sieving is chosen in the step 6, passes through the side mixed with selected pigment
Formula prepares panda pattern filler, can prevent the difference because of material to the maximum extent, causes panda pattern because of the cracking that expands with heat and contract with cold, takes off
The problem of falling.
It, need to be by adsorbing anticollision dado because pigment bark powder itself is without glue in the step 9 during shedding bark powder
As binder, such as starved during repeating to shed easily causes empty inside panda pattern the white glue with vinyl of steel slab surface brushing
The defects of heart, hole, bridging, influence the quality of finished product anticollision panda dado.
In the step 10 after bark powder glue-line is fully cured, plastic mould frame is removed, it will with black bark powder putty
The frame line of rabbet joint that mold leaves is filled and led up, and the black bark powder putty is by cork oak bark: carbon black: edible vegetable oil=70%:10%:20%
(mass ratio) is formulated.
Embodiment 3
A kind of specific steps of the processing method of anticollision panda dado are as follows:
Step 1: cork oak bark processing fent is collected, pours into hot-tub and impregnates 60 hours, dried on the place of ventilation,
After the moisture content of cork oak bark processing fent is lower than 20%, it is sent into flaking machining, wood shavings are made；
Step 2: manufactured wood shavings are sent into roller drier is dry, it is dry after moisture control 8~10%, it is spare；
Step 3: cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer, it is spare；
Step 4: sizing wood shavings being mated formation into the cork oak bark slab of gauge thickness in spreading machine, hot press is sent into and is hot pressed into
Type is sawn into the specification of anticollision dado blank after room temperature is 48 hours cooling；
Step 5: manufactured anticollision dado blank being sent into four side moulder processing dado and is longitudinally begun to speak after slot, both-end Milling Machining is recycled
The transverse direction of dado is begun to speak slot, and anticollision dado blank is made after polishing；
Step 6: take it is partially dried after cork oak bark wood shavings, be sent into pulverizer crush, cross 20 mesh sieve, it is spare；
Step 7: according to the design colours of design drawing 1, manufactured cork oak bark powder is mixed well respectively with a variety of different pigment, it is standby
With；
Step 8: taking out the plastic mould of prefabricated panda design drawing 1, be placed on the center position of anticollision dado blank, use clip
After fixation, dip white glue with vinyl with hairbrush, equably brush in the position that panda plastic mould limits, pinch taken with hand be mixed with it is various
The cork oak bark powder of pigment is equably sprinkling upon in the gluing sash of plastic mould by the requirement of Fig. 1 color；
Step 9: when the bark powder presentation overlap joint state under subsequent spread, showing that occurring starved in the gluing sash of plastic mould shows
As, it is necessary to white glue with vinyl is dipped with hairbrush and continues bark powder glue-line in brushing plastic mould sash, repeats this process, until tree
Until skin powder bondline thickness reaches scheduled thickness；
Step 10: after the intensity that bark powder glue-line hardness reaches certain (glue-line is not fully cured), striking off bark powder with scraper plate
Glue-line carefully removes plastic mould frame after bark powder glue-line is fully cured, the frame for being left mold with black bark powder putty
The line of rabbet joint is filled and led up；
Step 11: after the panda pattern of panda dado steel slab surface is fully cured, panda dado slab being sent into sander sand
Light, then repaired, painted, anticollision panda dado finished product is made.
Cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer in the step 3, ureaformaldehyde tree
The additive amount of rouge adhesive is the 15% of cork oak bark wood shavings quality.
Hot-forming cork oak bark particieboard is sawn into anticollision dado blank, the specification of the blank in the step 4
It is thick having a size of the wide X of 1200~1500mm X 500mm X 18mm(long X).
Dry cork oak bark wood shavings grinding and sieving is chosen in the step 6, passes through the side mixed with selected pigment
Formula prepares panda pattern filler, can prevent the difference because of material to the maximum extent, causes panda pattern because of the cracking that expands with heat and contract with cold, takes off
The problem of falling.
It, need to be by adsorbing anticollision dado because pigment bark powder itself is without glue in the step 9 during shedding bark powder
As binder, such as starved during repeating to shed easily causes empty inside panda pattern the white glue with vinyl of steel slab surface brushing
The defects of heart, hole, bridging, influence the quality of finished product anticollision panda dado.
In the step 10 after bark powder glue-line is fully cured, plastic mould frame is removed, it will with black bark powder putty
The frame line of rabbet joint that mold leaves is filled and led up, and the black bark powder putty is by cork oak bark: carbon black: edible vegetable oil=70%:10%:20%
(mass ratio) is formulated.
The present invention provides a kind of processing method of anticollision panda dado, and this method is added using cheap cork oak bark
Work leftover bits and pieces, is handled through special process, manufactures anticollision panda wall skirt plate.The anticollision panda wall skirt plate has light-weight, rich slow
Rush the feature of elasticity, and environment-protecting and non-poisonous evil can protect child, prevent it is unexpected tumble hit wall after caused by grievous injury, will damage
Mistake minimizes.Due to being added to lovely panda cartoon character, liking and welcoming for children is firmly got, market prospects are wide
It is wealthy.
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with
Modification, is all covered by the present invention.
Claims (8)
1. a kind of processing method of anticollision panda dado, which comprises the steps of:
Step 1: collecting cork oak bark processing fent, pour into hot-tub and impregnate 48~60 hours, on the place of ventilation
Sunning is sent into flaking machining, wood shavings is made after the moisture content of cork oak bark processing fent is lower than 20%；
Step 2: manufactured wood shavings are sent into roller drier is dry, it is dry after moisture control 8~10%, it is spare；
Step 3: cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer, it is spare；
Step 4: sizing wood shavings being mated formation into the cork oak bark slab of gauge thickness in spreading machine, hot press is sent into and is hot pressed into
Type is sawn into the specification of anticollision dado blank after room temperature is 48 hours cooling；
Step 5: manufactured anticollision dado blank being sent into four side moulder processing dado and is longitudinally begun to speak after slot, both-end Milling Machining is recycled
The transverse direction of dado is begun to speak slot, and anticollision dado blank is made after polishing；
Step 6: take it is partially dried after cork oak bark wood shavings, be sent into pulverizer crush, cross 20 mesh sieve, be made cork robur
Pi Fen, it is spare；
Step 7: according to the design colours of the panda pattern of design, by manufactured cork oak bark powder and a variety of different pigment point
It does not mix well, it is spare；
Step 8: the plastic mould of prefabricated panda pattern is taken out, the center position of anticollision dado blank is placed on, it is solid with clip
After fixed, white glue with vinyl is dipped with hairbrush, is equably brushed in the position that panda plastic mould limits, is taken with hand pinch and is mixed with various face
The cork oak bark powder of material is equably sprinkling upon in the gluing sash of plastic mould by the requirement of pattern color；
Step 9: when the bark powder presentation overlap joint state under subsequent spread, showing that occurring starved in the gluing sash of plastic mould shows
As, it is necessary to white glue with vinyl is dipped with hairbrush and continues bark powder glue-line in brushing plastic mould sash, repeats this process, until tree
Until skin powder bondline thickness reaches scheduled thickness；
Step 10: after the intensity that bark powder glue-line hardness reaches certain, glue-line is not fully cured, strikes off bark arogel with scraper plate
Layer, after bark powder glue-line is fully cured, carefully removes plastic mould frame, the frame slot for being left mold with black bark powder putty
Line is filled and led up；
Step 11: after the panda pattern of panda dado steel slab surface is fully cured, panda dado slab being sent into sander sand
Light, then repaired, painted, anticollision panda dado finished product is made.
2. a kind of processing method of anticollision panda dado according to claim 1, it is characterised in that: it will described in step 1
Cork oak bark processing fent after impregnating hot water is spread out to be dried on the place of ventilation, when the moisture content of bark leftover bits and pieces is low
After 20%, flaking and dry processing can be carried out；Moisture content is too low to easily cause wood shavings excessively broken, influences the strong of dado finished product plate
Degree；The energy consumption of the excessively high then drying process of moisture content is bigger than normal.
3. a kind of processing method of anticollision panda dado according to claim 1, it is characterised in that: described in step 3
Cork oak bark wood shavings are stirred evenly with urea-formaldehyde resin adhesive in glue mixer, the additive amount of urea-formaldehyde resin adhesive is cork
The 12~15% of oak bark wood shavings quality.
4. a kind of processing method of anticollision panda dado according to claim 1, it is characterised in that: it will described in step 4
Hot-forming cork oak bark particieboard is sawn into anticollision dado blank, the specification of the blank be the wide X thickness of long X 1200~
1500mmⅹ500mmⅹ18mm。
5. a kind of processing method of anticollision panda dado according to claim 1, it is characterised in that: it is selected described in step 6
Dry cork oak bark wood shavings grinding and sieving is taken, panda pattern filler is prepared by way of mixing with selected pigment, it can
The difference because of material is prevented to the maximum extent, causes panda pattern because of the cracking that expands with heat and contract with cold, the problem of falling off.
6. a kind of processing method of anticollision panda dado according to claim 1, it is characterised in that: it will described in step 7
Manufactured cork oak bark powder is mixed well respectively with a variety of different pigment, and kind and the quantity selection of all pigment must be according to bears
Cat pattern.
7. a kind of processing method of anticollision panda dado according to claim 1, it is characterised in that: described in step 8
During shedding the cork oak bark powder for being mixed with various pigment, anticollision wall skirt plate base keeps flat, and prevents sagging and shed
The case where boundary, occurs.
8. a kind of processing method of anticollision panda dado according to claim 1, it is characterised in that: described in step 10
After bark powder glue-line is fully cured, plastic mould frame is removed, is filled and led up the frame line of rabbet joint that mold leaves with black bark powder putty,
The black bark powder putty is in mass ratio by cork oak bark: carbon black: edible vegetable oil=70%:10%:20% is formulated.