CN109694676A - A kind of reflector plate protection glue, adhesive tape and preparation method thereof - Google Patents
A kind of reflector plate protection glue, adhesive tape and preparation method thereof Download PDFInfo
- Publication number
- CN109694676A CN109694676A CN201811625568.7A CN201811625568A CN109694676A CN 109694676 A CN109694676 A CN 109694676A CN 201811625568 A CN201811625568 A CN 201811625568A CN 109694676 A CN109694676 A CN 109694676A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- reflector plate
- glue
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of reflector plate protection glue, adhesive tape and preparation method thereof; belong to adhesive tape processing technique field; a kind of reflector plate protection glue is formulated by following components according to following weight proportion: acrylic acid 2-5 parts by weight; Isooctyl acrylate monomer 17-20 parts by weight; butyl acrylate 7-10 parts by weight; vinyl acetate 5-8 parts by weight, ethyl acetate 57-60 parts by weight, BPO0.2-0.3 parts by weight.The reflector plate protects glue initial cohesiveness with higher and retention property, while having preferable stripping performance.
Description
Technical field
The invention belongs to adhesive tape processing technique fields, and in particular to a kind of reflector plate protection glue, adhesive tape and its preparation side
Method.
Background technique
Reflector plate can be made up of a kind of the slide that its back side generates reflection, slide have one partly
Or the front being all made of multiple composite surfaces, each composite surface are from only to the inclined cylindrical surface in a direction and Xiang Fanfang
It is formed to inclined curved surface or plane, above-mentioned composite surface continuously or is therebetween inserted with plane, and its structure is
Cylindrical surface accounts for most of area of composite surface, and above-mentioned slide also has the back being made of multiple adjacent right-angle prisms
Face.
In order to improve the utilization efficiency of light commonly using light reflecting material.For example, being arranged light reflecting material in liquid crystal display
The most back side of curtain, so that the light that the light sources such as LED or cold-cathode fluorescence lamp (CCFL) issue is reflected into front with preferable efficiency.
In addition, also light reflecting material is mounted on fluorescent lamp or LED type lighting device to good efficiency reflected light.
In the production process of LCD screen, in the transportational process especially before reflector plate assembling, reflector plate in order to prevent
It is destroyed, usually uses reflector plate protective glue band, cut into small strip, glued on the protection sheet on one side, another side is sticked to
On reflector plate；Reflector plate protective glue band is torn when assembling；Realize that the transportational process of the reflector plate of mould group below LCD screen is protected
Shield.
Existing reflector plate protective glue band or not easy to attach, easily falls；When tearing, the more difficult removing from reflector plate
It falls off, and destruction can be generated to reflector plate, there are residue glues for meeting.
Summary of the invention
In order to solve the above technical problems, the present invention provides a kind of reflector plate protection glue, initial cohesiveness with higher
And retention property, while there is preferable stripping performance.
Another object of the present invention is to provide a kind of preparation method of reflector plate protective glue band.
The technical scheme is that:
Scheme one:
A kind of reflector plate protection glue, is formulated by following components according to following weight proportion:
Scheme two:
A kind of preparation method of reflector plate protection glue, comprising the following steps:
Step 1: by the acrylic acid of 2-5 parts by weight, the Isooctyl acrylate monomer of 17-20 parts by weight, 7-10 parts by weight propylene
Acid butyl ester, 5-8 parts by weight vinyl acetate mixed with the ethyl acetate of 49-52 parts by weight；
Step 2: opening blender, and revolving speed is controlled in 25 turns/min, is warming up to 80 DEG C, starts to titrate 0.2-0.3 parts by weight
The titrating solution that BPO and the ethyl acetate of 8 parts by weight are formulated titrates 20 minutes, and temperature rises to 85-86 DEG C, stops titration；
Step 3: starting to cool down, and temperature continues to titrate when being down to 80 DEG C, and the used time 100 minutes, heat preservation 4 hours after having titrated
It crosses cooling and unloads glue；Obtain finished product reflector plate protection glue.
Scheme three:
A kind of preparation method of reflector plate protective glue band, the reflector plate protective glue prepared using preparation method described in scheme two
Water, the preparation method comprises the following steps:
Step 1: it comes unglued: the modified terpene phenol resin of 5 parts by weight and 9 resin of carbon of 5 parts by weight is put into 100 parts by weight
Reflector plate protection glue in stirring to dissolve, add 0.5-0.9 parts by weight polyurethane curing agent stir 30 minutes；
Step 2: coating: head release paper gluing, tail are made into single side with 12uPET is compound, and head uses release paper again
Gluing, tail is compound with ready-made single side, pulls out one layer of release paper, is made into the two-sided of 50u, temperature setting: 60,80,90,95,
100,105,100,90；Interval time 3 minutes；Speed: 13-15 ms/min；Obtain reflector plate protective glue band finished product.
Compared with prior art, the beneficial effects of the present invention are:
1, the present invention can be improved the initial cohesiveness and retention property of glue, control stripping performance.
2, the present invention can be such that adhesive tape is attached on reflector plate, can not only be easier to be bonded, be not easy to fall, be easy when removing from
It falls off on reflector plate, and destruction will not be generated to reflector plate, it will not residue glue.
3, reflector plate protective glue band of the invention will not occur tacky film and be partially stripped when adhesive layer is removed from adherend
The case where, while can get stable physical property.
Specific embodiment
The following examples are used to illustrate the present invention, but are not intended to limit the scope of the present invention..
Embodiment 1:
A kind of preparation method of reflector plate protective glue band, comprising the following steps:
Step 1: by the acrylic acid of 2 parts by weight, the Isooctyl acrylate monomer of 17 parts by weight, the butyl acrylate of 7 parts by weight, 5
The vinyl acetate of parts by weight is mixed with the ethyl acetate of 49 parts by weight；
Step 2: opening blender, and revolving speed is controlled in 25 turns/min, is warming up to 80 DEG C, starts to titrate 0.2 parts by weight BPO
The titrating solution being formulated with the ethyl acetate of 8 parts by weight titrates 20 minutes, and temperature rises to 85 DEG C, stops titration；
Step 3: starting to cool down, and temperature continues to titrate when being down to 80 DEG C, and the used time 100 minutes, heat preservation 4 hours after having titrated
It crosses cooling and unloads glue；Obtain finished product reflector plate protection glue；
Step 4: it comes unglued: the modified terpene phenol resin of 5 parts by weight and 9 resin of carbon of 5 parts by weight is put into 100 parts by weight
Reflector plate protection glue in stirring to dissolve, add 0.5 parts by weight polyurethane curing agent stir 30 minutes；
Step 5: coating: head release paper gluing, tail are made into single side with 12uPET is compound, and head uses release paper again
Gluing, tail is compound with ready-made single side, pulls out one layer of release paper, is made into the two-sided of 50u, temperature setting: 60,80,90,95,
100,105,100,90；Interval time 3 minutes；Speed: 13 ms/min；Obtain reflector plate protective glue band finished product.
Embodiment 2:
A kind of preparation method of reflector plate protective glue band, comprising the following steps:
Step 1: by the acrylic acid of 5 parts by weight, the Isooctyl acrylate monomer of 20 parts by weight, 10 parts by weight butyl acrylate,
The vinyl acetate of 8 parts by weight is mixed with the ethyl acetate of 52 parts by weight；
Step 2: opening blender, and revolving speed is controlled in 25 turns/min, is warming up to 80 DEG C, starts to titrate 0.3 parts by weight BPO
The titrating solution being formulated with the ethyl acetate of 8 parts by weight titrates 20 minutes, and temperature rises to 86 DEG C, stops titration；
Step 3: starting to cool down, and temperature continues to titrate when being down to 80 DEG C, and the used time 100 minutes, heat preservation 4 hours after having titrated
It crosses cooling and unloads glue；Obtain finished product reflector plate protection glue；
Step 4: it comes unglued: the modified terpene phenol resin of 5 parts by weight and 9 resin of carbon of 5 parts by weight is put into 100 parts by weight
Reflector plate protection glue in stirring to dissolve, add 0.6 parts by weight polyurethane curing agent stir 30 minutes；
Step 5: coating: head release paper gluing, tail are made into single side with 12uPET is compound, and head uses release paper again
Gluing, tail is compound with ready-made single side, pulls out one layer of release paper, is made into the two-sided of 50u, temperature setting: 60,80,90,95,
100,105,100,90；Interval time 3 minutes；Speed: 15 ms/min；Obtain reflector plate protective glue band finished product.
Embodiment 3:
A kind of preparation method of reflector plate protective glue band, comprising the following steps:
Step 1: by the acrylic acid of 3.5 parts by weight, the Isooctyl acrylate monomer of 18.5 parts by weight, 8.5 parts by weight acrylic acid
Butyl ester, 6.5 parts by weight vinyl acetate mixed with the ethyl acetate of 50.5 parts by weight；
Step 2: opening blender, and revolving speed is controlled in 25 turns/min, is warming up to 80 DEG C, starts to titrate 0.25 parts by weight BPO
The titrating solution being formulated with the ethyl acetate of 8 parts by weight titrates 20 minutes, and temperature rises to 85.5 DEG C, stops titration；
Step 3: starting to cool down, and temperature continues to titrate when being down to 80 DEG C, and the used time 100 minutes, heat preservation 4 hours after having titrated
It crosses cooling and unloads glue；Obtain finished product reflector plate protection glue；
Step 4: it comes unglued: the modified terpene phenol resin of 5 parts by weight and 9 resin of carbon of 5 parts by weight is put into 100 parts by weight
Reflector plate protection glue in stirring to dissolve, add 0.7 parts by weight polyurethane curing agent stir 30 minutes；
Step 5: coating: head release paper gluing, tail are made into single side with 12uPET is compound, and head uses release paper again
Gluing, tail is compound with ready-made single side, pulls out one layer of release paper, is made into the two-sided of 50u, temperature setting: 60,80,90,95,
100,105,100,90；Interval time 3 minutes；Speed: 14 ms/min；Obtain reflector plate protective glue band finished product.
Embodiment 4:
A kind of preparation method of reflector plate protective glue band, comprising the following steps:
Step 1: by the acrylic acid of 2 parts by weight, the Isooctyl acrylate monomer of 20 parts by weight, the butyl acrylate of 7 parts by weight, 8
The vinyl acetate of parts by weight is mixed with the ethyl acetate of 49 parts by weight；
Step 2: opening blender, and revolving speed is controlled in 25 turns/min, is warming up to 80 DEG C, starts to titrate 0.3 parts by weight BPO
The titrating solution being formulated with the ethyl acetate of 8 parts by weight titrates 20 minutes, and temperature rises to 85 DEG C, stops titration；
Step 3: starting to cool down, and temperature continues to titrate when being down to 80 DEG C, and the used time 100 minutes, heat preservation 4 hours after having titrated
It crosses cooling and unloads glue；Obtain finished product reflector plate protection glue；
Step 4: it comes unglued: the modified terpene phenol resin of 5 parts by weight and 9 resin of carbon of 5 parts by weight is put into 100 parts by weight
Reflector plate protection glue in stirring to dissolve, add 0.8 parts by weight polyurethane curing agent stir 30 minutes；
Step 5: coating: head release paper gluing, tail are made into single side with 12uPET is compound, and head uses release paper again
Gluing, tail is compound with ready-made single side, pulls out one layer of release paper, is made into the two-sided of 50u, temperature setting: 60,80,90,95,
100,105,100,90；Interval time 3 minutes；Speed: 15 ms/min；Obtain reflector plate protective glue band finished product.
Embodiment 5:
A kind of preparation method of reflector plate protective glue band, comprising the following steps:
Step 1: by the acrylic acid of 5 parts by weight, the Isooctyl acrylate monomer of 17 parts by weight, 10 parts by weight butyl acrylate,
The vinyl acetate of 5 parts by weight is mixed with the ethyl acetate of 52 parts by weight；
Step 2: opening blender, and revolving speed is controlled in 25 turns/min, is warming up to 80 DEG C, starts to titrate 0.2 parts by weight BPO
The titrating solution being formulated with the ethyl acetate of 8 parts by weight titrates 20 minutes, and temperature rises to 86 DEG C, stops titration；
Step 3: starting to cool down, and temperature continues to titrate when being down to 80 DEG C, and the used time 100 minutes, heat preservation 4 hours after having titrated
It crosses cooling and unloads glue；Obtain finished product reflector plate protection glue；
Step 4: it comes unglued: the modified terpene phenol resin of 5 parts by weight and 9 resin of carbon of 5 parts by weight is put into 100 parts by weight
Reflector plate protection glue in stirring to dissolve, add 0.9 parts by weight polyurethane curing agent stir 30 minutes；
Step 5: coating: head release paper gluing, tail are made into single side with 12uPET is compound, and head uses release paper again
Gluing, tail is compound with ready-made single side, pulls out one layer of release paper, is made into the two-sided of 50u, temperature setting: 60,80,90,95,
100,105,100,90；Interval time 3 minutes；Speed: 13 ms/min；Obtain reflector plate protective glue band finished product.
Experimental data
The present invention surveys reflector plate protective glue band finished product prepared in specific embodiment according to following experimental method
Examination:
1, peeling force is measured
The release film of tacky film on reflector plate is removed, 1 inch × 1 inch of tablet is then cut into.Use matter
Amount is that the roller reciprocating rolling of 2Kg is primary, and tacky film is attached to one block of non-alkali glass plate, with autoclave at 50 DEG C and
It handles under conditions of 0.5MPa 30 minutes, places two hours at room temperature.Then, using Instron (Instron) measuring device
With 180 ° of peeling forces of tachometric survey of 300mm/min.
2, initial bonding strength and retention time are measured
Initial bonding strength performance test methods: the one side that test agent double faced adhesive tape is not tested with 25 μm of PET films it is laminating after, cut
At 20mm × 150mm, one face stripping film is torn when testing one side, in PC, GLASS, containing being bonded on APCF layers of polaroid, then is used
The pressing device of 2Kg pressurizes three and is placed in 23 DEG C × 65%RH environment back and forth, after keeping r, 48hr, 72hr for 24 hours, is placed in
The test of 180 ° of pulling plates is carried out with 300mm/min in fixture, records data, a kind of sample will be measured in parallel two samples, be averaged
Value, and record the retention time.
Reflector plate protective glue band of the invention is viscous relative to 10 average surface roughness Rz coated steel plate for being 8.0 μm
Relay is 0.05N/20mm or more.Here, " coated steel plate that 10 average surface roughness Rz are 8.0 μm " refers to defined
Adherend in the evaluation of the bonding force of reflector plate protective glue band of the invention as benchmark." 10 average surface roughness
Rz " be as indicate surface roughness index and well known index.
The experimental data of reflector plate protection glue, tape performance in specific embodiments of the present invention
| Initial bonding strength (#) | Peel strength (N/25mm) | Retention time (h) | |
| Embodiment 1 | 13/14 | 8.5/8.9 | 24/ ﹥ 24 of ﹥ |
| Embodiment 2 | 12/13 | 8.6/8.7 | 24/ ﹥ 24 of ﹥ |
| Embodiment 3 | 13/12 | 8.0/8.3 | 24/ ﹥ 24 of ﹥ |
| Embodiment 4 | 12/12 | 8.1/7.8 | 24/ ﹥ 24 of ﹥ |
| Embodiment 5 | 12/12 | 7.5/7.6 | 24/ ﹥ 24 of ﹥ |
Protect glue, adhesive tape with higher from can be seen that reflector plate in specific embodiments of the present invention in above data
Initial cohesiveness and retention property, while there is preferable stripping performance.
Claims (3)
1. a kind of reflector plate protects glue, it is characterised in that:
It is formulated by following components according to following weight proportion:
2. the preparation method of reflector plate protection glue according to claim 1, it is characterised in that: the following steps are included:
Step 1: by the acrylic acid of 2-5 parts by weight, the Isooctyl acrylate monomer of 17-20 parts by weight, 7-10 parts by weight acrylic acid fourth
Ester, 5-8 parts by weight vinyl acetate mixed with the ethyl acetate of 49-52 parts by weight；
Step 2: opening blender, and revolving speed is controlled in 25 turns/min, is warming up to 80 DEG C, starts to titrate 0.2-0.3 parts by weight BPO
The titrating solution being formulated with the ethyl acetate of 8 parts by weight titrates 20 minutes, and temperature rises to 85-86 DEG C, stops titration；
Step 3: starting to cool down, and temperature continues to titrate when being down to 80 DEG C, the used time 100 minutes, kept the temperature 4 hours i.e. after having titrated
Glue is unloaded in cooling；Obtain finished product reflector plate protection glue.
3. a kind of preparation method of reflector plate protective glue band, it is characterised in that: protected using the reflector plate of claim 1 vegetation
Glue, the preparation method comprises the following steps:
Step 1: it comes unglued: the modified terpene phenol resin of 5 parts by weight and 9 resin of carbon of 5 parts by weight is put into the anti-of 100 parts by weight
Penetrating stirring in piece protection glue, to dissolving, the polyurethane curing agent for adding 0.5-0.9 parts by weight stirs 30 minutes；
Step 2: coating: head release paper gluing, tail are made into single side with 12uPET is compound, and head uses release paper gluing again,
Tail is compound with ready-made single side, pulls out one layer of release paper, is made into the two-sided of 50u, temperature setting: 60,80,90,95,100,
105,100,90；Interval time 3 minutes；Speed: 13-15 ms/min；Obtain reflector plate protective glue band finished product.