CN109674581A - 一种透明柔性水膜疗伤贴和其制备方法 - Google Patents
一种透明柔性水膜疗伤贴和其制备方法 Download PDFInfo
- Publication number
- CN109674581A CN109674581A CN201811077152.6A CN201811077152A CN109674581A CN 109674581 A CN109674581 A CN 109674581A CN 201811077152 A CN201811077152 A CN 201811077152A CN 109674581 A CN109674581 A CN 109674581A
- Authority
- CN
- China
- Prior art keywords
- layer
- film
- wound
- gel
- patch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种透明柔性水膜疗伤贴和其制备方法，通过该制备方法制备的透明柔性水膜疗伤贴包括：剥离背衬层、凝胶薄膜外层、网状纱布层、凝胶薄膜内层以及外覆膜层，所述凝胶薄膜外层和凝胶薄膜内层相互胶连使得所述网状纱布层均匀地分布所述凝胶薄膜外层和所述凝胶薄膜内层之间，所述水剥离背衬层紧贴所述凝胶薄膜内层的外表面，所述外覆膜层设置在所述凝胶薄膜外层的外表面；其中，所述凝胶薄膜外层和凝胶薄膜内层由至少一种具有粘结力的成膜剂高分子聚合物制成。本发明中透明柔性水膜疗伤贴的凝胶薄膜内、外层之间具有粘结力，且内外层之间设置有网状纱布，这种多层结构有效提升了透明柔性水膜疗伤贴的机械强度，有利于剪裁成型。
Description
技术领域
本发明涉及一种医疗技术领域，具体涉及一种透明柔性水膜疗伤贴和其制备方法。
背景技术
日常生活中，战争期间，自然灾害发生，人们遭遇创伤、烧伤、枪伤、烫伤、灼伤是难免的，尤其是战争期间或自然灾害发生时，还有一些情况是外科手术所带来的伤口。传统的伤口治疗办法是伤口经清洗杀菌处理后，用纱布包覆，属干态治疗，需经常更换，更换过程中因敷料与伤口粘连，损伤肉芽组织，会给患者带来痛苦。
近年来，发展起来的水凝胶伤口被覆膜(简称：水膜)，因其具有高吸水性、保水性、生物相容性，用来处理伤口，可以吸收伤口分泌的体液，保持伤口清洁湿润的状态。临床应用表明，这种湿态治疗法相对于传统的纱布包覆的干态治疗法，可加速伤口的愈合。
目前，这种水膜疗伤贴的制备方法包括化学交联法、反复冻融法和辐射法等。其中，辐射法因其制备的水膜产品纯净，反应温和，且无需后续的灭菌处理等特点，是工业上常用的方法。但该方法制备的水膜机械强度差，导致水膜使用过程中存在裁剪造型困难、容易破损等技术不足。
现有技术中，是通过模具将水膜加工成特定的形状和制备较厚的水膜，来克服水膜使用过程中需要特定形状和极易破损的技术不足。模具成型，加大了工业生产水膜的难度，多种形状的水膜需要多套特定的模具。较厚的水膜虽然能提高机械强度，但导致水膜透光率低，影响美观，且较厚的水膜因其自重，在重力作用下容易脱落受伤部位。
综上，本领域缺少一种薄而透明且容易造型的水膜疗伤。
发明内容
本发明的目的在于提供一种透明柔性水膜疗伤贴和其制备方法，在保持水膜疗伤贴薄而透明情况下，提升水膜疗伤贴机械强度。
本发明实施例第一方面提供一种透明柔性水膜疗伤贴，该透明柔性水膜疗伤贴包括：外覆膜层、凝胶薄膜外层、网状纱布层、凝胶薄膜内层以及剥离背衬层；
所述凝胶薄膜外层和凝胶薄膜内层相互胶连使得所述网状纱布层均匀地分布在所述凝胶薄膜外层和所述凝胶薄膜内层之间，所述剥离背衬层紧贴所述凝胶薄膜内层的外表面，所述外覆膜层设置在所述凝胶薄膜外层的外表面；其中，所述凝胶薄膜外层和凝胶薄膜内层由至少一种具有粘结力的成膜剂高分子聚合物制成。
本发明实施例第二方面提供一种透明柔性水膜疗伤贴的制备方法，该制备方法包括：
将所凝胶薄膜外层和凝胶薄膜内层的制备材料按照配方比例混合，以预设加热温度加热所述制备材料形成凝胶；
将网状纱布设置于所述凝胶中，形成网状纱布层和位于所述网状纱布层两侧的凝胶薄膜外层和凝胶薄膜内层；
将预制的剥离背衬设置于所述凝胶薄膜内层的外表面形成所述剥离背衬层，将预设的外覆膜设置于所述凝胶薄膜外层的外表面形成所述外覆膜层，得到预制水膜疗伤贴；
对所述预制水膜疗伤贴通过辐射进行交联固化；
对固化后的所述预制水膜疗伤贴进行滚压模切，得到所述透明柔性水膜疗伤贴。
本发明实施例提供了一种透明柔性水膜疗伤贴和其制备方法，通过该透明柔性水膜疗伤贴制备方法制备的透明柔性水膜疗伤贴包括：剥离背衬层、凝胶薄膜外层、网状纱布层、凝胶薄膜内层以及外覆膜层，所述凝胶薄膜外层和凝胶薄膜内层相互胶连使得所述网状纱布层均匀地分布所述凝胶薄膜外层和所述凝胶薄膜内层之间，所述水剥离背衬层紧贴所述凝胶薄膜内层的外表面，所述外覆膜层设置在所述凝胶薄膜外层的外表面；其中，所述凝胶薄膜外层和凝胶薄膜内层由至少一种具有粘结力的成膜剂高分子聚合物制成，本申请中透明柔性水膜疗伤贴的凝胶薄膜内、外层之间具有粘结力，且内外层之间设置有网状纱布，这种多层结构有效提升了水膜疗伤贴的机械强度，有利于剪裁成型。
附图说明：
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明对比例1中的水膜疗伤贴的结构示意图，图中，a凝胶薄膜，b剥离背衬层；
图2为本发明实施例一提供的一种透明柔性水膜疗伤贴的结构示意图，图中，(1)为凝胶薄膜外层，(2)为网状纱布层，(3)为凝胶薄膜内层，(4)为剥离背衬层(5)为外覆膜层；
图3为本发明实施例一中的透明柔性水膜疗伤贴的网状纱布层(2)的结构示意图；
图4为本发明实施例一中的透明柔性水膜疗伤贴的机械性能测试示意图；
图5为本发明实施例一提供的一种透明柔性水膜疗伤贴的制备方法的流程示意图。
具体实施方式：
为使得本发明的发明目的、特征、优点能够更加的明显和易懂，下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而非全部实施例。基于本发明中的实施例，本领域技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
对比例1：
参见图1，该水膜疗伤贴，由凝胶薄膜a和剥离背衬层b两层构成，其中凝胶薄膜厚度为3mm，凝胶薄膜其配方为聚乙烯吡咯烷酮12％，琼脂(Agar)3％，聚乙二醇0.8％，水含量81.2％，其他为根据特定功能需要添加的水溶性物质，占整个重量3％。按照上述配方与水混合加热，并搅拌均匀形成胶凝状，选择需要的模具，然后采用该模具制成对应形状的水膜，采用Co-60γ的射线辐照0.5小时，交联固化形成水膜疗伤贴。
该水膜疗伤贴的机械强度为0.2kg，不能裁剪成特定的形状。
实施例一：
本实施例提供一种透明柔性水膜疗伤贴，如图2所示，该透明柔性水膜疗伤贴包括：外覆膜层(5)、凝胶薄膜外层(1)、网状纱布层(2)、凝胶薄膜内层(3)以及剥离背衬层(4)；
凝胶薄膜外层(1)和凝胶薄膜内层(3)相互胶连使得网状纱布层(2)均匀地分布在凝胶薄膜外层(1)和凝胶薄膜内层(3)之间，剥离背衬层(4)紧贴凝胶薄膜内层(3)的外表面，外覆膜层(5)设置在凝胶薄膜外层(1)的外表面；其中，凝胶薄膜外层(1)和凝胶薄膜内层(3)由至少一种具有粘结力的成膜剂高分子聚合物制成。
本实施例中，网状纱布层(2)的设置使得柔性透明水膜疗伤帖的强度得到提升，网状纱布层的材料选择有很多种，可选的，网状纱布层(2)选择与凝胶薄膜外层和内层具有较好浸润性的材料，例如网状纱布的材料为蚕丝网、天然纤维网、化学纤维网和塑料网，或由蚕丝网、天然纤维网、化学纤维网和塑料网中的至少两种合成的聚合物网。可选的，化学纤维网的制备材料包括但不限于由锦纶、涤纶、腈纶等。可选的，网状纱布层的厚度范围为10微米-200微米，网状纱布层的网格的大小范围为10目-50目，网状纱布层的网格边的粗细范围在3微米-20微米，网状纱布层的网格形状包括六边形(如图3所示)，网状纱布层(2)为透明柔性水膜疗伤贴提供良好的机械性能，如韧性及弹性，使得透明柔性水膜疗伤贴不易撕裂和易于裁剪成特定的形状。
剥离背衬层(4)的材料可以为PET/PE或复合材质的塑料薄片、箔或纸，可选的，剥离背衬层(4)的厚度为20微米-300微米，其作用是提供透明柔性水膜疗伤贴未使用时的托底保护，其易于与凝胶薄膜内层剥离，方便用户的使用。
外覆膜层(5)的材料可以为PE/PET或复合材料，可选的，外覆膜层(5)的厚度为0.03mm-0.07mm，主要用途为外层对透明柔性水膜疗伤贴进行保护，在使用时用户可揭掉该外覆膜层，便于使用。
其中，可以理解的是，上述对于网状纱布层(2)、剥离背衬层(4)和外覆膜层(5)的材料的说明并不作为本实施例对这些层结构的材料选择的限定。
可选的，本实施例中凝胶薄膜外层(1)和凝胶薄膜内层(3)由能形成一定粘结力的成膜剂高分子聚合物或它们的混合物制成，凝胶薄膜外层(1)和凝胶薄膜内层(3)的配方为：
聚乙烯吡咯烷酮 5-12％，
琼脂 0.5-3％，
聚乙二醇 0.5-3％，
胶原蛋白粉 1-3％，
维生素 0.5-3％，
玻尿酸原液 2-5％，
纯水 87-90％。
其中，上述配方中各成分的比例是重量百分比。可选的，上述的维生素包括维生素A、维生素B1、维生素B2、维生素C、维生素D中的一种或多种。
可以理解的是，根据不同的需要，可以对上述的配方中的成分的种类和重量百分比进行调整，例如为了使得透明柔性水膜疗伤贴具有更强的美容功能，可以在透明柔性水膜疗伤贴中添加其他的美容成分。
本实施例中，上述的聚乙烯基吡咯烷酮是一种非离子型高分子化合物，极易溶于水及含卤代烃类溶剂、醇类、胺类、硝基烷烃及低分子脂肪酸等。且在水性环境下形成的单体无毒性，可以通过辐射诱发交联形成水凝胶。而传统高分子材料聚合物在形成单体时有毒，如果交联不足，有残留的单体存在会导致水膜产生毒性，对人体有害。
在上述的成分比例下，本发明的透明柔性水膜疗伤贴中的凝胶薄膜外层和凝胶薄膜内层具有透明可视的特点，具有“平衡”人体皮肤水分的特殊功能(与人体皮肤正常含水水平近似，贴合部位缺水时水膜自动给予适当补水，人体渗出液或其他多余的水分可被水膜吸收，吸收能力可达30％-70％)，以及保持湿润凉爽的特点。
根据本实施例的透明柔性水膜疗伤贴的上述特点，本实施例的透明柔性水膜疗伤贴除了用于医疗还可以用于美容。可选的，透明柔性水膜疗伤贴的厚度范围为0.5mm-5mm，透明柔性水膜疗伤贴中还含有预设美容成分物质，其中，预设美容成分物质包括但不限于：透明质酸钠、胶原蛋白粉、熊果苷、辅酶Q10、蛋清素钠、酒石酸、芦荟提取物、维生素、肝素钠和VC多糖体，透明柔性水膜疗伤贴中加入的预设美容成分物质的剂量占水膜重量百分比的1％-5％，且根据功能不同，可以采取加入上述美容成分物质中的一种或多种物质。可选的，用于美容时，透明柔性水膜疗伤贴被剪裁成与人体的面部形状匹配的形状。
可选的，本实施例的凝胶薄膜外层和凝胶薄膜内层的总厚度为0.3mm-1.5mm。可选的，透明柔性水膜疗伤贴的厚度的范围为1mm-3mm。
本实施例中的透明柔性水膜疗伤贴具有良好的机械性能，可以被剪切成任意的形状，以满足不同患处的需求。
对本实施例的透明柔性水膜疗伤贴机械性能评估：
对透明柔性水膜疗伤贴的机械强度通过如附图4所示的方式，通过在水膜上加载砝码。当随砝码质量的增加，观察水膜破损时能加载的最大砝码质量来评判透明柔性水膜疗伤贴的机械性能。
本发明实施例还提供一种透明柔性水膜疗伤贴的制备方法，用于制备如上的透明柔性水膜疗伤贴，参见图5，该透明柔性水膜疗伤贴的制备方法包括：
步骤501、将凝胶薄膜外层和凝胶薄膜内层的制备材料按照配方比例混合，以预设加热温度加热制备材料形成凝胶；其中，配方比例指的是凝胶薄膜内、外层的制备材料的配方比例。
步骤502、将网状纱布设置于凝胶中，形成网状纱布层和位于网状纱布层两侧的凝胶薄膜外层和凝胶薄膜内层；
步骤503、将预制的剥离背衬设置于凝胶薄膜内层的外表面形成剥离背衬层，将预设的外覆膜设置于凝胶薄膜外层的外表面形成外覆膜层，得到预制水膜疗伤贴；
步骤504、对预制水膜疗伤贴通过辐射进行交联固化；
步骤505、对固化后的预制水膜疗伤贴进行滚压模切，得到透明柔性水膜疗伤贴。
可选的，将凝胶薄膜外层和凝胶薄膜内层的制备材料按照配方比例混合，以预设加热温度加热制备材料形成凝胶包括：
将凝胶薄膜外层和凝胶薄膜内层的配方中的各种成分按各自的重量百分比混合，并以预设加热温度加热混合各成分形成凝胶，其中，预设加热温度在70摄氏度到95摄氏度的范围内。
可选的，将网状纱布设置于凝胶中，形成网状纱布层和位于网状纱布层两侧的凝胶薄膜外层和凝胶薄膜内层包括：
将凝胶涂布于网状纱布的外表面，形成网状纱布层和位于网状纱布层两侧的凝胶薄膜外层和凝胶薄膜内层；
或者，将网状纱布压入凝胶中，形成外沿周边连体的凝胶薄膜外层和凝胶薄膜内层以及在凝胶薄膜外层和凝胶薄膜内层中间的网状纱布层。
可选的，本实施例可采用Co-60γ的射线对预制水膜疗伤贴进行辐射，射线的强度为10kGy-30kGy。但是应当理解的是，本实施例中用于对预制水膜疗伤帖进行辐射的射线并不局限于Co-60γ，还可以是其它类型。而前述列举的射线强度的取值范围也仅作为示例，并不对实际的射线强度范围造成限定，在生产水膜疗伤贴时，可以根据实际需要设置射线辐照强度。其中，对预制水膜疗伤贴的辐照时间可以根据对预制水膜疗伤贴中凝胶薄膜内层和外层的材料和总厚度，以及预制水膜疗伤贴的面积大小和使用性能来设置，本实施例中对此没有限定。
本实施例的透明柔性水膜疗伤贴具有高强度，便于裁剪成特定的形状，美观性强，厚度范围可调。超薄水膜(1mm)具有透明度高、贴时附力强/揭时不粘皮的优点；厚水膜(1mm-5mm)具有锁水时间长、耐用的特点。本实施例通过加入纱网替代了原有的模具化成型技术，大大提高了生产效率(提高3-5倍)。
进一步的，涂布式生产减少了托盘的使用并缩小了外包装，从而大大降低了生产成本(降低成本50％以上)。
实施例二
本实施例提供一种透明柔性水膜疗伤贴，该透明柔性水膜疗伤贴的结构示意图参见图2，其具体结构的描述参见实施例一的相关记载，本实施例在此不再赘述。
可选的，本实施例中的网状纱布层(2)由蚕丝制成，具体为蚕丝薄网格层(2)。
可选的，本实施例中凝胶薄膜外层和凝胶薄膜内层采用的配方的具体比例可以是：
聚乙烯吡咯烷酮 8％，
琼脂 3％，
聚乙二醇 0.5％，
胶原蛋白粉 2％，
维生素 0.5％，
玻尿酸原液 2％，
纯水 84％。
本实施例中，按照上述配方中的各种成分的重量百分比混合上述各成分，对混合的物质加热到85℃，并混合搅拌均匀后形成凝胶状物质，将该凝胶状物质涂布于蚕丝薄网格层(2)上(其中网格层厚度为10微米，网格大小为10目)，形成平整的厚度为1.5mm的凝胶薄膜外层(1)和厚度为1.5mm的凝胶薄膜内层(3)，将剥离背衬层(4)和外覆膜层(5)的材料分别紧贴于凝胶薄膜内层(3)和凝胶薄膜外层(1)的表面形成预制水膜疗伤贴。然后利用Co-60γ的射线辐射预制水膜疗伤贴2h(Co-60γ的射线能量为15kGy)进行交联固化，最后再对交联固化后的预制水膜疗伤贴经过滚压模切制成需要的透明柔性水膜疗伤贴。
本实施例中该透明柔性水膜疗伤贴的机械强度为1.5kg，透光率为80％，保湿锁水能达到或5小时，能裁剪成特定的形状，如裁剪成面膜的形状，通过在该透明柔性水膜疗伤贴的基础上加入透明质酸钠1.5％、胶原蛋白粉2％和芦荟提取物1％，维生素0.5％形成具有美容作用的面膜。
本实施例中，剥离背衬层是透明或不透明的塑料片，表面上涂布有保持凝胶弹性的稳定剂。
实施例三：
本实施例提供一种透明柔性水膜疗伤贴，该透明柔性水膜疗伤贴的结构示意图参见图2，其具体结构的描述参见实施例一的相关记载，本实施例在此不再赘述。
可选的，本实施例中的网状纱布层(2)由蚕丝制成，具体为蚕丝薄网格层(2)。
可选的，本实施例中凝胶薄膜外层和凝胶薄膜内层采用的配方的具体比例可以是：
聚乙烯吡咯烷酮 6％
琼脂 1％
聚乙二醇 2％，
维生素 1％
玻尿酸原液 2.5％
纯水 87.5％；
本实施例中，按照配方中的各种成分的重量百分比混合，对混合的物质加热到85℃混合搅拌均匀后，涂布于蚕丝薄网格层(2)上(其中网格层厚度为30微米，网格大小为30目)，形成平整的凝胶薄膜，凝胶薄膜外层(1)厚度为0,5mm和凝胶薄膜内层(3)厚度为1.5mm，将剥离背衬层(4)和外覆膜层(5)分别紧贴于凝胶薄膜内层(3)和凝胶薄膜外层(1)的表面制成预制水膜疗伤贴，然后对预制水膜疗伤贴经过Co-60γ的射线辐射2h(Co-60γ的射线的能量为25kGy)，进行交联固化，最后对交联固化后的预制水膜疗伤贴进行滚压模切制成需要的透明柔性水膜疗伤贴。
该透明柔性水膜疗伤贴的机械强度为2kg，透光率为85％，保湿锁水能达到或12小时，能裁剪成特定的形状，如裁剪成面膜的形状，通过在该透明柔性水膜疗伤贴的基础上加入透明质酸钠1.5％、胶原蛋白粉2％和芦荟提取物1％，维生素0.5％可形成具有美容作用的面膜。
实施例四：
本实施例提供一种透明柔性水膜疗伤贴，该透明柔性水膜疗伤贴的结构示意图参见图2，其具体结构的描述参见实施例一的相关记载，本实施例在此不再赘述。
可选的，本实施例中的网状纱布层(2)由蚕丝制成，具体为蚕丝薄网格层(2)。
可选的，本实施例中凝胶薄膜外层和凝胶薄膜内层采用的配方的具体比例可以是：
聚乙烯吡咯烷酮 10％
琼脂 1％
聚乙二醇 2.5％，
胶原蛋白粉 2％，
纯水 84.5％；
本实施例，对上述配方中的各种成分以各自的重量百分比混合，加热到75℃混合搅拌均匀后，涂布于蚕丝薄网格层(2)上(其中网格层厚度为15微米，网格大小为15目)，形成平整的厚度为1mm的凝胶薄膜外层(1)和厚度为1mm的凝胶薄膜内层(3)，将剥离背衬层(4)和外覆膜层(5)分别紧贴于凝胶薄膜内层(3)和凝胶薄膜外层(1)的表面制成预制水膜疗伤贴，然后对预制水膜疗伤贴经过Co-60γ的射线辐射1h(Co-60γ的射线的能量为18kGy)进行交联固化，最后再对固化后的预制水膜疗伤贴进行滚压模切制成需要的透明柔性水膜疗伤贴。
该透明柔性水膜疗伤贴的机械强度为1kg，透光率为85％，保湿锁水能达到或6小时，能裁剪成特定的形状，如裁剪成面膜的形状，通过在该透明柔性水膜疗伤贴的基础上加入透明质酸钠1.5％、胶原蛋白粉2％和芦荟提取物1％，维生素0.5％可形成具有美容作用的面膜。
实施例五：
本实施例提供一种透明柔性水膜疗伤贴，该透明柔性水膜疗伤贴的结构示意图参见图2，其具体结构的描述参见实施例一的相关记载，本实施例在此不再赘述。
可选的，本实施例中的网状纱布层(2)由腈纶制成，具体为腈纶薄网格层(2)。
可选的，本实施例中凝胶薄膜外层和凝胶薄膜内层采用的配方的具体比例可以是：
聚乙烯吡咯烷酮 7％，
琼脂 1.5％，
聚乙二醇 1.5％，
胶原蛋白粉 1％，
维生素 1％，
玻尿酸原液 1％，
纯水 87％。
本实施例中，按照上述配方中的各种成分的重量百分比混合上述各成分，加热混合的物质到85℃混合搅拌均匀后，涂布于腈纶薄网格层(2)上(其中网格层厚度为20微米，网格大小为30目)，形成平整的厚度为1.5mm的凝胶薄膜外层(1)和厚度为1mm的凝胶薄膜内层(3)，将剥离背衬层(4)和外覆膜层(5)分别紧贴于凝胶薄膜内层(3)和凝胶薄膜外层(1)的表面制成预制水膜疗伤贴，然后对预制水膜疗伤贴经过Co-60γ的射线辐射1h(Co-60γ的射线的能量为25kGy)进行交联固化，最后再对固化后的预制水膜疗伤贴进行滚压模切得到需要的透明柔性水膜疗伤贴。
该透明柔性水膜疗伤贴的机械强度为3kg，透光率为85％，保湿锁水能达到或15小时，能裁剪成特定的形状，如裁剪成面膜的形状，通过在该透明柔性水膜疗伤贴的基础上加入透明质酸钠1.5％、胶原蛋白粉2％和芦荟提取物1％，维生素0.5％可以形成具有美容作用的面膜。
实施例六：
本实施例提供一种透明柔性水膜疗伤贴，该透明柔性水膜疗伤贴的结构示意图参见图2，其具体结构的描述参见实施例一的相关记载，本实施例在此不再赘述。
可选的，本实施例中的网状纱布层(2)由腈纶制成，具体为腈纶薄网格层(2)。
可选的，本实施例中凝胶薄膜外层和凝胶薄膜内层采用的配方的具体比例可以是：
聚乙烯吡咯烷酮 5％
琼脂 2.5％
聚乙二醇 0.5％，
胶原蛋白粉 1％，
维生素 0.5％
玻尿酸原液 2％
纯水 90％；
本实施例中，将上述配方中的各种成分的重量百分比混合，加热混合的物质到90℃混合搅拌均匀后，涂布于腈纶薄网格层(2)上(其中网格层厚度为10微米，网格大小为50目)，形成平整的厚度为0.25mm的凝胶薄膜外层(1)和厚度为0.25mm的凝胶薄膜内层(3)，将剥离背衬层(4)和外覆膜层(5)分别紧贴于凝胶薄膜内层(3)和凝胶薄膜外层(1)的表面制成预制水膜疗伤贴。然后对预制水膜疗伤贴经过Co-60γ的射线辐射0.3h(Co-60γ的射线的能量为25kGy)进行交联固化，最后再对固化后的预制水膜疗伤贴进行滚压模切得到需要的透明柔性水膜疗伤贴。
该透明柔性水膜疗伤贴的机械强度为1kg，透光率为95％，保湿锁水能达到或12小时，能裁剪成特定的形状，如裁剪成面膜的形状，通过在该透明柔性水膜疗伤贴的基础上加入透明质酸钠1.5％、胶原蛋白粉2％和芦荟提取物1％，维生素0.5％可形成具有美容作用的面膜。
Claims (10)
1.一种透明柔性水膜疗伤贴，其特征在于，所述透明柔性水膜疗伤贴包括：外覆膜层、凝胶薄膜外层、网状纱布层、凝胶薄膜内层以及剥离背衬层；
所述凝胶薄膜外层和凝胶薄膜内层相互胶连使得所述网状纱布层均匀地分布在所述凝胶薄膜外层和所述凝胶薄膜内层之间，所述剥离背衬层紧贴所述凝胶薄膜内层的外表面，所述外覆膜层设置在所述凝胶薄膜外层的外表面；其中，所述凝胶薄膜外层和凝胶薄膜内层由至少一种具有粘结力的成膜剂高分子聚合物制成。
2.如权利要求1所述的透明柔性水膜疗伤贴，其特征在于，所述凝胶薄膜外层和凝胶薄膜内层的配方是：
聚乙烯吡咯烷酮5％-12％，琼脂0.5％-3％，聚乙二醇0.5％-3％，胶原蛋白粉1％-3％，维生素0.5％-3％，玻尿酸原液2％-5％，纯水87％-90％，其中，所述配方的上述成分比例是重量百分比。
3.如权利要求1或2所述的透明柔性水膜疗伤贴，其特征在于，所述透明柔性水膜疗伤贴的厚度范围为0.5mm-5mm，所述透明柔性水膜疗伤贴中还含有预设美容成分物质。
4.如权利要求1或2所述的透明柔性水膜疗伤贴，其特征在于，所述网状纱布层的厚度范围为10微米-200微米，所述网状纱布层的网格的大小范围为10目-50目，所述网状纱布层的网格边的粗细范围在3微米-20微米，所述网状纱布层的网格形状包括六边形。
5.如权利要求1或2所述的透明柔性水膜疗伤贴，其特征在于，所述凝胶薄膜外层和凝胶薄膜内层的总厚度为0.3mm-1.5mm。
6.如权利要求1或2所述的透明柔性水膜疗伤贴，其特征在于，所述透明柔性水膜疗伤贴的厚度的范围为1mm-3mm。
7.如权利要求1或2所述的透明柔性水膜疗伤贴，其特征在于，所述维生素包括维生素A、维生素B1、维生素B2、维生素C和维生素D中的至少一种。
8.一种透明柔性水膜疗伤贴的制备方法，用于制备如权利要求1-7任一项所述的透明柔性水膜疗伤贴，其特征在于，所述透明柔性水膜疗伤贴的制备方法包括：
将所凝胶薄膜外层和凝胶薄膜内层的制备材料按照配方比例混合，以预设加热温度加热所述制备材料形成凝胶；
将网状纱布设置于所述凝胶中，形成网状纱布层和位于所述网状纱布层两侧的凝胶薄膜外层和凝胶薄膜内层；
将预制的剥离背衬设置于所述凝胶薄膜内层的外表面形成所述剥离背衬层，将预设的外覆膜设置于所述凝胶薄膜外层的外表面形成所述外覆膜层，得到预制水膜疗伤贴；
对所述预制水膜疗伤贴通过辐射进行交联固化；
对固化后的所述预制水膜疗伤贴进行滚压模切，得到所述透明柔性水膜疗伤贴。
9.如权利要求8所述的透明柔性水膜疗伤贴的制备方法，其特征在于，所述将网状纱布设置于所述凝胶中，形成网状纱布层和位于所述网状纱布层两侧的凝胶薄膜外层和凝胶薄膜内层包括：
将所述凝胶涂布于网状纱布的外表面，形成网状纱布层和位于所述网状纱布层两侧的凝胶薄膜外层和凝胶薄膜内层；
或者，将网状纱布压入所述凝胶中，形成外沿周边连体的凝胶薄膜外层和凝胶薄膜内层以及在所述凝胶薄膜外层和凝胶薄膜内层中间的所述网状纱布层。
10.如权利要求8或9所述的透明柔性水膜疗伤贴的制备方法，其特征在于，采用Co-60γ的射线对所述预制水膜疗伤贴进行辐射，所述射线的强度为10kGy-30kGy。