CN109575840A - 一种无缝墙/壁布胶及其制备方法 - Google Patents
一种无缝墙/壁布胶及其制备方法 Download PDFInfo
- Publication number
- CN109575840A CN109575840A CN201811356682.4A CN201811356682A CN109575840A CN 109575840 A CN109575840 A CN 109575840A CN 201811356682 A CN201811356682 A CN 201811356682A CN 109575840 A CN109575840 A CN 109575840A
- Authority
- CN
- China
- Prior art keywords
- wall
- cloth glue
- obtains
- seamless
- wall cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种无缝墙/壁布胶及其制备方法，所述无缝墙/壁布胶包括以下重量份的组分：羧甲基变性淀粉80‑120份、甘油1‑3份、水300‑500份、增粘树脂20‑50份、碱性糊化剂1‑6份、防腐防霉剂1‑2份、EVA乳液2‑5份和酸液调节剂1‑2份。利用羧甲基变性淀粉和甘油复配，提高墙/壁布胶的保水性，使其具有干透速度慢、不易“透胶”、调稠后易于涂刷的特点，改善了墙/壁布胶的特性，解决了现有墙/壁布胶施工难的问题。本发明还公开了所述无缝墙/壁布胶的制备方法，该方法具有工艺简单、易于操作的优点，易于实现工业化。
Description
技术领域
本发明属于胶粘剂领域，具体涉及一种无缝墙/壁布胶及其制备方法。
背景技术
无缝墙/壁布是整面墙一块布，无法做到布上涂胶，必需先在墙上涂刷胶液，再贴墙/壁布，因此，涂刷整面墙的时间较长，而且传统的胶液干透速度快，会出现一面墙胶液还没涂刷完，前面涂刷的胶已表干不能进行墙/壁布粘贴，给墙/壁布粘贴带来很大的不便。
传统墙/壁纸轻薄，对胶液的稀稠、粘力、剥离强度都要求不高，而且墙/壁纸密度较高，涂刷和施工时胶液不会从里面渗透到表面(即“透胶”现象)。现无缝墙/壁布是属于纺织产品，孔洞较大，当胶液较稀或涂刷到布上会出现“透胶”，一旦“透胶”后无法擦洗，表面会出现色差，只能用稠胶薄涂的方法来进行施工，而传统的胶液，调稠后不易于涂刷。
而且，现有的墙/壁纸胶中大多包含纤维素，纤维素的加入虽然会使胶液具有较高的保水性，但因纤维素本身的水溶解度不佳，会使在胶液开胶的过程中产生许多的颗粒，会造成工人在施工涂刷胶液时，出现涂刷不均匀的现象，甚至无法进行墙/壁布粘贴。
因此，有必要研究一种适用于无缝墙/壁布粘贴的高性能无缝墙/壁布胶，解决现有墙纸胶中存在的干透速度过快、易于“透胶”、调稠后不易涂刷的问题。
发明内容
针对现有技术的不足，本发明的目的之一是提供一种无缝墙/壁布胶，利用羧甲基变性淀粉和甘油复配，提高墙/壁布胶的保水性，使其具有干透速度慢、不易“透胶”、调稠后易于涂刷的特点，改善了墙/壁布胶的特性，解决了现有墙/壁布胶施工难的问题。本发明还提供了所述无缝墙/壁布胶的制备方法，该方法具有工艺简单、易于操作的优点，易于实现工业化。
本发明采用的技术方案是：一种无缝墙/壁布胶，包括以下重量份的组分：
优选的，羧甲基变性淀粉与甘油的质量比为40-60:1。
胶液易“透胶”是由于其保水性差导致的。在本发明中，采用羧甲基变性淀粉代替传统淀粉，这是因为羧甲基变性淀粉具有羧酸根阴离子，使其呈现较强的极性因子，亲水性极佳，易溶于水，从而使无缝墙/壁布胶呈现出高保水性的特点，减缓胶液干透速度，改善“透胶”现象。而且，由于羧甲基变性淀粉的高保水性，不再需要添加纤维素，避免了胶液开胶的过程中产生颗粒导致涂刷不均匀的问题的发生。
同时，加入具有高保湿性能的甘油与羧甲基变性淀粉复配使用，以羧甲基变性淀粉为主，甘油为辅，进一步提高无缝墙/壁布胶的保水性，减缓干透速度，减少“透胶”现象的发生。优选的，羧甲基变性淀粉和甘油的质量比在40-60:1下保水性能最佳。
EVA乳液在胶液的外观增白方面有着不可替代作用，其也能起到增粘作用。
优选的，增粘树脂为水溶性增粘树脂，选自PVA-1788、PVA-2488、PVA-1799和PVA-1792中的一种或几种。
增粘树脂起着增加粘贴力作用，使墙/壁布可以粘贴得更加牢固。
优选的，碱性糊化剂选自氢氧化钠、氢氧化钾、碳酸氢钠、碳酸钠、碳酸钾和碳酸氢钾中的一种或几种。
糊化剂起着淀粉更加糊化、更加熟化的作用，使淀粉糊化更加充分。
优选的，碱性糊化剂的用量与其浓度相关，根据碱性糊化剂的浓度不一样，其用量也就不同。
具体地，浓度为30％的碱性糊化剂添加1-2份，浓度为20％的碱性糊化剂添加2-4份，浓度为10％的碱性糊化剂添加5-6份。
优选的，防腐防霉剂选自2-甲基-4-异噻唑啉-3-酮、2-甲基-5-氯-4-异噻唑啉-3-酮、苯甲酸、苯甲酸钠、山梨酸、山梨酸钾和丙酸钙中的一种或几种。
优选的，酸液调节剂选自草酸、稀硝酸、稀盐酸、磷酸和乙酸中的一种或几种。
所述的无缝墙/壁布胶的制备方法，包括以下步骤：
1)将水、羧甲基变性淀粉和增粘树脂混合，得到混合物A；
2)往步骤1)得到的混合物A中加入碱性糊化剂，进行糊化反应，得到混合物B；
3)往步骤2)得到的混合物B中加入酸液调节剂，使pH值为5-7，得到混合物C；
4)往步骤3)得到的混合物C中加入甘油、EVA乳液和防腐防霉剂，进行消泡处理，得到无缝墙/壁布胶。
优选的，羧甲基变性淀粉与甘油的质量比为40-60:1。
优选的，步骤1)中，先加入水，开启搅拌，后缓慢加入羧甲基变性淀粉和增粘树脂。
优选的，步骤2)中，糊化反应的温度为30-40℃。
使用普通淀粉制备墙纸胶，一般需要在75-85℃进行糊化反应，而本发明使用羧甲基变性淀粉，糊化反应不再需要高温进行，只需30-40℃即可，节约资源和成本。
所述的无缝墙/壁布胶可应用于无缝墙/壁布的粘贴，粘贴性能好，不出现“透胶”现象，墙/壁布光滑平整，美观度高。
本发明与现有技术相比，具有如下有益效果：
1.本发明的无缝墙/壁布胶，采用羧甲基变性淀粉和甘油复配，利用羧甲基变性淀粉的高保水性和水溶性，以及甘油的高保湿性，进一步提高无缝墙/壁布胶的保水性，减缓干透速度，减少“透胶”现象的发生。
2.由于羧甲基变性淀粉的高保水性，不再需要添加纤维素，避免了胶液开胶的过程中产生颗粒导致涂刷不均匀的问题的发生。
3.本发明所述无缝墙/壁布胶的制备方法，具有工艺简单、易于操作的优点，而且，由于羧甲基变性淀粉的使用，使得糊化反应不再需要在高温下进行，节约资源和成本，更易于实现工业化。
4.所述的无缝墙/壁布胶可应用于无缝墙/壁布的粘贴，粘贴性能好，不出现“透胶”现象，墙/壁布光滑平整，美观度高。
具体实施方式
下面结合实施例对本发明做进一步说明。
实施例1
一种无缝墙/壁布胶，包括以下重量份的组分：
所述的无缝墙/壁布胶的制备方法，包括以下步骤：
1)先加入水，开启搅拌，后缓慢加入羧甲基变性淀粉和PVA-1788，得到混合物A；
2)往步骤1)得到的混合物A中加入氢氧化钠，在35℃温度下进行糊化反应，得到混合物B；
3)往步骤2)得到的混合物B中加入稀盐酸，使pH值为6，得到混合物C；
4)往步骤3)得到的混合物C中加入甘油、EVA乳液、2-甲基-4-异噻唑啉-3-酮和2-甲基-5-氯-4-异噻唑啉-3-酮，进行消泡处理，得到无缝墙/壁布胶。
实施例2
一种无缝墙/壁布胶，包括以下重量份的组分：
所述的无缝墙/壁布胶的制备方法，包括以下步骤：
1)先加入水，开启搅拌，后缓慢加入羧甲基变性淀粉和PVA-2488，得到混合物A；
2)往步骤1)得到的混合物A中加入碳酸钠，在30℃温度下进行糊化反应，得到混合物B；
3)往步骤2)得到的混合物B中加入稀硝酸，使pH值为5，得到混合物C；
4)往步骤3)得到的混合物C中加入甘油、EVA乳液和苯甲酸，进行消泡处理，得到无缝墙/壁布胶。
实施例3
一种无缝墙/壁布胶，包括以下重量份的组分：
所述的无缝墙/壁布胶的制备方法，包括以下步骤：
1)先加入水，开启搅拌，后缓慢加入羧甲基变性淀粉、PVA-1799和PVA-1792，得到混合物A；
2)往步骤1)得到的混合物A中加入碳酸氢钠，在40℃温度下进行糊化反应，得到混合物B；
3)往步骤2)得到的混合物B中加入磷酸，使pH值为7，得到混合物C；
4)往步骤3)得到的混合物C中加入甘油、EVA乳液和苯甲酸钠，进行消泡处理，得到无缝墙/壁布胶。
实施例4
一种无缝墙/壁布胶，包括以下重量份的组分：
所述的无缝墙/壁布胶的制备方法，包括以下步骤：
1)先加入水，开启搅拌，后缓慢加入羧甲基变性淀粉、PVA-1788和PVA-1799，得到混合物A；
2)往步骤1)得到的混合物A中加入氢氧化钾，在35℃温度下进行糊化反应，得到混合物B；
3)往步骤2)得到的混合物B中加入乙酸，使pH值为6，得到混合物C；
4)往步骤3)得到的混合物C中加入甘油、EVA乳液和山梨酸，进行消泡处理，得到无缝墙/壁布胶。
实施例5
一种无缝墙/壁布胶，包括以下重量份的组分：
所述的无缝墙/壁布胶的制备方法，包括以下步骤：
1)先加入水，开启搅拌，后缓慢加入羧甲基变性淀粉和PVA-1792，得到混合物A；
2)往步骤1)得到的混合物A中加入碳酸钾，在40℃温度下进行糊化反应，得到混合物B；
3)往步骤2)得到的混合物B中加入稀盐酸，使pH值为6，得到混合物C；
4)往步骤3)得到的混合物C中加入甘油、EVA乳液和丙酸钙，进行消泡处理，得到无缝墙/壁布胶。
实施例1-5的无缝墙/壁布胶均符合以下技术指标：
(1)粘度：70000-80000mpa.s；
(2)初粘：10～12#；
(3)pH值：5-7；
(4)游离甲醛：≤40mg/kg；
(5)VOC：≤40g/l。
对比例1
一种无缝墙/壁布胶，包括以下重量份的组分：
所述无缝墙/壁布胶的制备方法，包括以下步骤：
1)先加入水，开启搅拌，后缓慢加入羧甲基变性淀粉和PVA-1788，得到混合物A；
2)往步骤1)得到的混合物A中加入氢氧化钠，在35℃温度下进行糊化反应，得到混合物B；
3)往步骤2)得到的混合物B中加入稀盐酸，使pH值为6，得到混合物C；
4)往步骤3)得到的混合物C中加入EVA乳液、2-甲基-4-异噻唑啉-3-酮和2-甲基-5-氯-4-异噻唑啉-3-酮，进行消泡处理，得到无缝墙/壁布胶。
对比例2
一种无缝墙/壁布胶，包括以下重量份的组分：
所述的无缝墙/壁布胶的制备方法，包括以下步骤：
1)先加入水，开启搅拌，后缓慢加入淀粉和PVA-1788，得到混合物A；
2)往步骤1)得到的混合物A中加入氢氧化钠，在80℃温度下进行糊化反应，得到混合物B；
3)往步骤2)得到的混合物B中加入稀盐酸，使pH值为6，得到混合物C；
4)往步骤3)得到的混合物C中加入甘油、EVA乳液、2-甲基-4-异噻唑啉-3-酮和2-甲基-5-氯-4-异噻唑啉-3-酮，进行消泡处理，得到无缝墙/壁布胶。
对比例3
一种制备糊化淀粉墙纸胶浆的方法，包括以下步骤：
(1)将6kg玉米淀粉加入到装有50kg水的带夹套升、降温的不锈钢搅拌釜内，搅拌加热到80℃，保持搅拌15min，使浆液糊化均匀透明；
(2)将步骤(1)的浆液的pH值调到10，于78℃保持搅拌15min；
(3)将1.5kg羟乙基纤维素溶解于36kg水中，然后加进搅拌釜内，于55℃搅拌15min；
(4)加进1kg甘油，55℃搅拌10min；
(5)将0.1kg苯甲酸钠溶解于3kg水中，然后加进搅拌釜内，50℃搅拌10min；
(6)降温到45℃，加进1g香精，搅拌15min，继续搅拌、冷却到35℃，出料、包装、成品，得到糊化淀粉墙纸胶浆。
实施例1-5和对比例1-3的产品性能参数如表1所示。
表1无缝墙/壁布胶的性能参数
从表1可以看到，实施例1-5与对比例1和2相比，羧甲基变性淀粉和甘油的复配使用可以提高无缝墙/壁布胶的保水性，减缓干透速度，减少“透胶”现象的发生，调稠后仍易于涂刷。
实施例1-5与对比例3相比，由于不添加纤维素，避免了胶液开胶的过程中产生颗粒导致涂刷不均匀的问题的发生，降低了糊化反应的温度。
Claims (8)
1.一种无缝墙/壁布胶，其特征在于，包括以下重量份的组分：
2.根据权利要求1所述的无缝墙/壁布胶，其特征在于，增粘树脂为水溶性增粘树脂，选自PVA-1788、PVA-2488、PVA-1799和PVA-1792中的一种或几种。
3.根据权利要求1所述的无缝墙/壁布胶，其特征在于，碱性糊化剂选自氢氧化钠、氢氧化钾、碳酸氢钠、碳酸钠、碳酸钾和碳酸氢钾中的一种或几种。
4.根据权利要求1所述的无缝墙/壁布胶，其特征在于，防腐防霉剂选自2-甲基-4-异噻唑啉-3-酮、2-甲基-5-氯-4-异噻唑啉-3-酮、苯甲酸、苯甲酸钠、山梨酸、山梨酸钾和丙酸钙中的一种或几种。
5.根据权利要求1所述的无缝墙/壁布胶，其特征在于，酸液调节剂选自草酸、稀硝酸、稀盐酸、磷酸和乙酸中的一种或几种。
6.权利要求1-5中任一项所述的无缝墙/壁布胶的制备方法，其特征在于，包括以下步骤：
1)将水、羧甲基变性淀粉和增粘树脂混合，得到混合物A；
2)往步骤1)得到的混合物A中加入碱性糊化剂，进行糊化反应，得到混合物B；
3)往步骤2)得到的混合物B中加入酸液调节剂，使pH值为5-7，得到混合物C；
4)往步骤3)得到的混合物C中加入甘油、EVA乳液和防腐防霉剂，进行消泡处理，得到无缝墙/壁布胶。
7.根据权利要求6所述的制备方法，其特征在于，步骤1)中，先加入水，开启搅拌，后缓慢加入羧甲基变性淀粉和增粘树脂。
8.根据权利要求6所述的制备方法，其特征在于，步骤2)中，糊化反应的温度为30-40℃。