CN109571982A - A kind of preparation method of the ageing-resistant antenna cover of uvioresistant - Google Patents
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant Download PDFInfo
- Publication number
- CN109571982A CN109571982A CN201811372461.6A CN201811372461A CN109571982A CN 109571982 A CN109571982 A CN 109571982A CN 201811372461 A CN201811372461 A CN 201811372461A CN 109571982 A CN109571982 A CN 109571982A
- Authority
- CN
- China
- Prior art keywords
- parts
- antenna cover
- ageing
- preparation
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of the ageing-resistant antenna cover of uvioresistant.Preparation method is the following steps are included: (1) makes mold;(2) plastics sucking moulding;(3) it binds.Then preparation method of the invention binds the method for forming antenna cover entirety using processing respectively, on the one hand reduce the difficulty of processing, and on the other hand, the antenna cover intensity processed is big, has the function of that uvioresistant is ageing-resistant.
Description
Technical field
The present invention relates to a kind of preparation methods of the ageing-resistant antenna cover of uvioresistant, belong to plastic uptake technical field.
Background technique
Communication base station antenna is typically mounted at high-altitude, such as is mounted on the positions such as steel tower or roof.After installation
Antenna for base station is chronically at harsh outdoor environment, and therefore, antenna cover material needs to have high-low temperature resistant impact and anti-UV
Characteristics or the performances such as (ultraviolet, ultraviolet light) radiation, to meet its long-term and reliable application outdoors.PVC
(polyvinyl chloride, polyvinyl chloride) material has low dielectric, corrosion-resistant, cold resistance, anti-UV and from fire-retardant etc.
Characteristic, compared with traditional antenna outer cover material glass reinforced plastic also have light specific gravity, at low cost, molding processibility is good, can be recycled etc. it is excellent
Point, thus PVC antenna cover is developed rapidly.
Nevertheless, larger change will occur after high/low-temperature impact for the PVC antenna cover of mainstream currently on the market
Shape, and because antenna cover differs larger with the linear expansion coefficient of reflecting plate, it will lead to antenna cover end cap and antenna cover
The problems such as being detached from and causing waterproof bad.Also, existing PVC antenna cover can be only applied to temperature at -40 DEG C ~ 70 DEG C
Scene, be unable to satisfy round-the-clock application requirement.Existing PVC antenna cover manufacturing cost is also higher, in order to improve day
The heat resistance of line outer cover and joined a large amount of heat resistance modified resin/ABS, it is high to lead to manufacturing cost, and the addition of ABS is also
It will lead to the reduction of the anti-UV ability of antenna cover.In addition, the prior art is not also old to the hot oxygen for influencing PVC antenna cover
Change effect proposes the method solved.
Summary of the invention
For overcome the deficiencies in the prior art, the present invention provides a kind of preparation sides of the ageing-resistant antenna cover of uvioresistant
Method.
The present invention is achieved through the following technical solutions:
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, comprising the following steps:
(1) it making mold: mold is made according to the shape of antenna cover, the mold includes that at least one divides mold, and described point
The shape of mold constitutes the mold altogether;
(2) plastics sucking moulding: by base sheet and divide mold be placed in Packing Machine carry out plastics sucking moulding, Packing Machine after processing is completed
It is cut out, the branch of at least one antenna cover is obtained after cutting out, there are fraction of sides in the two sides of branch when cutting out
Edge;
(3) it binds: the edge of branch being coated with adhesive, the branch is linked together by adhesive, is obtained most
Antenna cover afterwards.
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, the base sheet include following parts by weight
Several raw material: polyvinyl chloride resin, silicone oil, glass fibre, nano-titanium dioxide, nano silica and aluminium oxide.
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, the parts by weight of each raw material of base sheet
Number is respectively as follows: 100-120 parts of polyvinyl chloride resin, 30-40 parts of silicone oil, 10-15 parts of glass fibre, 2-6 parts of nano-titanium dioxide, nanometer
2-6 parts and aluminium oxide 10-15 parts of silica.
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, further includes surface treatment step, the table
Surface treatment step includes being placed in the antenna cover after bonding in surface protection liquid to take out after immersion.
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, the surface protection liquid include following weight
The raw material of number: epoxy resin, pentaerythrite, carbon black, vinyl acetate, zinc stearate and antioxidant.
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, the weight of each raw material of surface protection liquid
Number is respectively as follows: 100-120 parts of epoxy resin, 30-40 parts of pentaerythrite, 1-2 parts of carbon black, 3-6 parts of vinyl acetate, zinc stearate
3-6 parts and antioxidant 1-2 parts.
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, described adhesive is methylene chloride.
Advantageous effects of the invention:
Then preparation method of the invention binds the method for forming antenna cover entirety using processing respectively, on the one hand reduce and add
The difficulty of work, on the other hand, the antenna cover intensity processed is big, has the function of that uvioresistant is ageing-resistant.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of branch in embodiment 1.
Fig. 2 is the structural schematic diagram of antenna cover in embodiment 1.
Fig. 3 is the structural schematic diagram of 2 Zhong Liangge branch of embodiment.
Fig. 4 is the structural schematic diagram of antenna cover in embodiment 2.
In figure: 1, antenna cover, 11, branch, 12, edge.
Specific embodiment
The invention will be further described below in conjunction with the accompanying drawings.Following embodiment is only used for clearly illustrating the present invention
Technical solution, and not intended to limit the protection scope of the present invention.
Embodiment 1
As illustrated in fig. 1 and 2, for processing cylindric antenna cover.
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, comprising the following steps:
(1) it makes mold: mold being made according to the shape of antenna cover 1, the mold includes a point of mold;
(2) plastics sucking moulding: by base sheet and mold is divided to be placed in Packing Machine progress plastics sucking moulding, is completed the process in Packing Machine 4
After be cut out, the branch 11 of an antenna cover is obtained after cutting out, there are fraction of sides in the two sides of branch when cutting out
Along 12;Obtained branch 11 is the rectangle of a tiling, can be coiled into a cylindrical shape;
(3) it binds: the edge 12 of branch 11 being coated into methylene chloride, the branch 11 is linked together by methylene chloride,
Obtain antenna cover 1 to the end;
(4) it is surface-treated: the antenna cover 1 after bonding being placed in surface protection liquid after impregnating and taken out.
The base sheet includes the raw material of following parts by weight: polyvinyl chloride resin, silicone oil, glass fibre, nanometer titanium dioxide
Titanium, nano silica and aluminium oxide.The parts by weight of each raw material of base sheet are respectively as follows: 100 parts of polyvinyl chloride resin, silicone oil
30 parts, 10 parts of glass fibre, 6 parts of nano-titanium dioxide, 6 parts of nano silica and 10 parts of aluminium oxide.
The surface protection liquid includes the raw material of following parts by weight: epoxy resin, pentaerythrite, carbon black, vinyl acetate,
Zinc stearate and antioxidant.The parts by weight of each raw material of surface protection liquid are respectively as follows: 100 parts of epoxy resin, pentaerythrite
30 parts, 2 parts of carbon black, 3 parts of vinyl acetate, 3 parts of zinc stearate and 2 parts of antioxidant.
Embodiment 2
As shown in Figures 3 and 4, for processing square tube shape antenna cover
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, comprising the following steps:
(1) it makes mold: mold being made according to the shape of antenna cover 1, the mold includes two points of molds, described to divide mold
Shape constitute the mold altogether;
(2) plastics sucking moulding: by base sheet and mold is divided to be placed in Packing Machine progress plastics sucking moulding, is completed the process in Packing Machine 4
After be cut out, the branch 11 of two antenna covers is obtained after cutting out, there are fraction of in the two sides of branch 11 when cutting out
Edge 12;Obtained Liang Ge branch 11 may be combined to form a square tube shape;
(3) it binds: the edge 12 of branch 11 being coated with adhesive, the branch is linked together by adhesive, is obtained
Antenna cover to the end;
(4) it is surface-treated: the antenna cover after bonding being placed in surface protection liquid after impregnating and taken out.
The base sheet includes the raw material of following parts by weight: polyvinyl chloride resin, silicone oil, glass fibre, nanometer titanium dioxide
Titanium, nano silica and aluminium oxide.The parts by weight of each raw material of base sheet are respectively as follows: 120 parts of polyvinyl chloride resin, silicone oil
40 parts, 15 parts of glass fibre, 2 parts of nano-titanium dioxide, 2 parts of nano silica and 15 parts of aluminium oxide.
The surface protection liquid includes the raw material of following parts by weight: epoxy resin, pentaerythrite, carbon black, vinyl acetate,
Zinc stearate and antioxidant.The parts by weight of each raw material of surface protection liquid are respectively as follows: 120 parts of epoxy resin, pentaerythrite
40 parts, 1 part of carbon black, 6 parts of vinyl acetate, 6 parts of zinc stearate and 1 part of antioxidant.
Embodiment 3
A kind of preparation method of the ageing-resistant antenna cover of uvioresistant, comprising the following steps:
(1) it making mold: mold is made according to the shape of antenna cover, the mold includes that at least one divides mold, and described point
The shape of mold constitutes the mold altogether;
(2) plastics sucking moulding: by base sheet and divide mold be placed in Packing Machine carry out plastics sucking moulding, Packing Machine after processing is completed
It is cut out, the branch of at least one antenna cover is obtained after cutting out, there are fraction of sides in the two sides of branch when cutting out
Edge;
(3) it binds: the edge of branch being coated with methylene chloride, the branch is linked together by methylene chloride, is obtained
Antenna cover to the end;
(4) it is surface-treated: the antenna cover after bonding being placed in surface protection liquid after impregnating and taken out.
The base sheet includes the raw material of following parts by weight: polyvinyl chloride resin, silicone oil, glass fibre, nanometer titanium dioxide
Titanium, nano silica and aluminium oxide.The parts by weight of each raw material of base sheet are respectively as follows: 110 parts of polyvinyl chloride resin, silicone oil
36 parts, 12 parts of glass fibre, 5 parts of nano-titanium dioxide, 5 parts of nano silica and 12 parts of aluminium oxide.
Use polyvinyl chloride resin for major ingredient, glass fibre, nano-titanium dioxide and nano silica improve polyvinyl chloride resin
Intensity increases certain ageing resistance, meanwhile, aluminium oxide improves the anti-uv-ray of polyvinyl chloride resin, is prepared
Base sheet is suitable for making antenna outer cover.
The surface protection liquid includes the raw material of following parts by weight: epoxy resin, pentaerythrite, carbon black, vinyl acetate,
Zinc stearate and antioxidant.The parts by weight of each raw material of surface protection liquid are respectively as follows: 110 parts of epoxy resin, pentaerythrite
35 parts, 1 part of carbon black, 4 parts of vinyl acetate, 4 parts of zinc stearate and 1 part of antioxidant.
Liquid is protected in antenna cover surface sprayed surface, the ageing-resistant function of antenna cover uvioresistant is improved, extends
The service life of antenna cover, passes through the group of epoxy resin, pentaerythrite, carbon black, vinyl acetate, zinc stearate and antioxidant
It closes, surface protection liquid ageing-resistant ability is strong, and uvioresistant effect is good.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvement and deformations can also be made, these improvement and deformations
Also it should be regarded as protection scope of the present invention.
Claims (7)
1. a kind of preparation method of the ageing-resistant antenna cover of uvioresistant, characterized in that the following steps are included:
(1) it making mold: mold is made according to the shape of antenna cover, the mold includes that at least one divides mold, and described point
The shape of mold constitutes the mold altogether;
(2) plastics sucking moulding: by base sheet and divide mold be placed in Packing Machine carry out plastics sucking moulding, Packing Machine after processing is completed
It is cut out, the branch of at least one antenna cover is obtained after cutting out, there are fraction of sides in the two sides of branch when cutting out
Edge;
(3) it binds: the edge of branch being coated with adhesive, the branch is linked together by adhesive, is obtained most
Antenna cover afterwards.
2. a kind of preparation method of the ageing-resistant antenna cover of uvioresistant according to claim 1, characterized in that the base
Plinth sheet material includes the raw material of following parts by weight: polyvinyl chloride resin, silicone oil, glass fibre, nano-titanium dioxide, nano silica
And aluminium oxide.
3. a kind of preparation method of the ageing-resistant antenna cover of uvioresistant according to claim 2, characterized in that the base
The parts by weight of each raw material of plinth sheet material are respectively as follows: 100-120 parts of polyvinyl chloride resin, 30-40 parts of silicone oil, 10-15 parts of glass fibre, receive
2-6 parts of titanium dioxide of rice, 2-6 parts of nano silica and 10-15 parts of aluminium oxide.
4. a kind of preparation method of the ageing-resistant antenna cover of uvioresistant according to claim 1, characterized in that further include
Surface treatment step, the surface treatment step include being placed in the antenna cover after bonding in surface protection liquid to take after immersion
Out.
5. a kind of preparation method of the ageing-resistant antenna cover of uvioresistant according to claim 4, characterized in that the table
Face protection liquid includes the raw material of following parts by weight: epoxy resin, pentaerythrite, carbon black, vinyl acetate, zinc stearate and antioxygen
Agent.
6. a kind of preparation method of the ageing-resistant antenna cover of uvioresistant according to claim 4 or 5, characterized in that institute
The parts by weight for stating each raw material of surface protection liquid are respectively as follows: 100-120 parts of epoxy resin, 30-40 parts of pentaerythrite, carbon black 1-2
Part, 3-6 parts of vinyl acetate, 3-6 parts of zinc stearate and 1-2 parts of antioxidant.
7. a kind of preparation method of the ageing-resistant antenna cover of uvioresistant according to claim 1, characterized in that described viscous
Mixture is methylene chloride.