CN109554820A - A kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric - Google Patents
A kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric Download PDFInfo
- Publication number
- CN109554820A CN109554820A CN201811477520.6A CN201811477520A CN109554820A CN 109554820 A CN109554820 A CN 109554820A CN 201811477520 A CN201811477520 A CN 201811477520A CN 109554820 A CN109554820 A CN 109554820A
- Authority
- CN
- China
- Prior art keywords
- cool
- nice
- preparation
- fiber
- bamboo fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of nice and cool ultraviolet ray-resistance type bamboo fibre fabric, are related to textile technology field, preparation method is following steps: S1, mixed yarn preparation, and S2, nice and cool veil preparation, S4, S3, weaving pad, S5, bake and bank up with earth, cool down.The present invention using mixed yarn and nice and cool veil by being woven, it is blended in nice and cool veil to have silk fiber, cool fiber, environment-protection fiber, the nice and cool property of bamboo fibre fabric can be further enhanced, the feature of environmental protection and lubricity, and pass through the anti-ultraviolet finishing liquid configured, can make the fabric of preparation has effects that uvioresistant, and ultraviolet transmittance is less than 5%, also there is stable nerve simultaneously, improve sleep and other effects, the present invention can not only process the bamboo fibre fabric of ultraviolet ray-resistance type, and high production efficiency, it is at low cost, the bamboo fibre fabric produced simultaneously has uviolresistance, and fabric is comfortable, it is nice and cool, good permeability, and the feature of environmental protection is high.
Description
Technical field
The present invention relates to textile technology field, the preparation method of specifically a kind of nice and cool ultraviolet ray-resistance type bamboo fibre fabric.
Background technique
Bamboo fibre, a kind of fiber that natural environmental-protective type is degradable, it is to be handled using bamboo as raw material, through special process
's.Bamboo fibre manufactures overall process and uses high-tech means, is the fifth-largest day after cotton, fiber crops, hair and the big natural fiber of silk four
So weaving element is a kind of real " ecological fiber ", and with good gas permeability, instant water absorption, natural antibacterial is antibacterial, anti-
The effects of mite deodorization.
The research and development of bamboo fibre is commonplace in the world, and traction is also relatively high, but is used in house
Spinning core is also fewer by product line, and traditional bamboo fibre there is also some problems on blanket, fabric, if washing shrinkage is high,
It is easy pilling, while uviolresistance in textile fabric of being in is poor, property of feeling nice and cool and smoothness difference.Therefore, those skilled in the art
Member provides a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric, to solve mentioned above in the background art ask
Topic.
Summary of the invention
It is above-mentioned to solve the purpose of the present invention is to provide a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric
The problem of being proposed in background technique.
To achieve the above object, the invention provides the following technical scheme: a kind of nice and cool ultraviolet ray-resistance type bamboo fibre fabric
Preparation method, preparation method are following steps:
S1, mixed yarn preparation: by wood-fibred, bamboo fibre, spandex fibre, cotton fiber, soybean fiber by blended, obtained mixed
Spinning;
S2, nice and cool veil preparation: again by silver fiber, silk fiber, cool fiber, environment-protection fiber by blended, obtained nice and cool face
Yarn;
S3, weaving: being woven the nice and cool veil in the mixed yarn and S2 in S1 using braider, forms bamboo fibre fabric;
S4, it pads: the bamboo fibre fabric being prepared in S3 being subjected to an immersing and rolling, a leaching one in anti-ultraviolet finishing liquid again
The pick-up rolled is 50-80%;
S5, it bakes and banks up with earth, cool down: after S4, then being baked, baking temperature is 130-180 DEG C, time 1-4min, finally
Cooling gets product fabric.
As a further solution of the present invention: mixed yarn component by weight is made in the S1: 5-15 parts of wood-fibred, bamboo
Fiber part 35-50,10-30 parts of spandex fibre, 30-60 parts of cotton fiber, 10-15 parts of soybean fiber.
As further scheme of the invention: the nice and cool veil component by weight in the S2 is made: silver fiber 1-5
Part, 5-10 parts of silk fiber, 5-15 parts of cool fiber, 2-10 parts of environment-protection fiber.
As the present invention further scheme: the anti-ultraviolet finishing liquid in the S4 be by zinc oxide, titanium dioxide,
Polyester master particle mixes, and is 30-50:4-10:5-20 according to mass ratio.
As the present invention further scheme: the anti-ultraviolet finishing liquid in the S4 be by zinc oxide, titanium dioxide,
Polyester master particle mixes, and is 40:8:12 according to mass ratio.
As the present invention further scheme: the anti-ultraviolet finishing liquid in the S4 be by zinc oxide, titanium dioxide,
Polyester master particle mixes, and is 30:5:7 according to mass ratio.
As the present invention further scheme: anti-ultraviolet finishing liquid in the S4 the preparation method comprises the following steps: will oxidation
Zinc, titanium dioxide, polyester master particle, which are added to the water according to mass ratio for 30-50:4-10:5-20 ratio, is configured to anti-ultraviolet finishing
Liquid, and adequately stirred, mixing time is 0.5-4 hours.
As further scheme of the invention: the cool fiber in the S2 is using addition nanoscale complex ore material
Polyamide fibre.
As further scheme of the invention: the environment-protection fiber in the S2 uses corn-based environment-protection fiber.
Compared with prior art, the beneficial effects of the present invention are: a kind of nice and cool ultraviolet ray-resistance type bamboo fibre that the present invention designs
The preparation method of fabric is tieed up, in actual use, by being woven using mixed yarn and nice and cool veil, bamboo fibre fabric is made to relax
Adaptive is good, and it is blended in nice and cool veil have silk fiber, cool fiber, environment-protection fiber, bamboo fibre face can be further enhanced
Nice and cool property, the feature of environmental protection and the lubricity of material, and the anti-ultraviolet finishing liquid by configuring can be such that the fabric of preparation has anti-
The effect of ultraviolet light, while also having stable nerve, improving sleep and other effects, compared with prior art, the present invention, not only can be with
Process the bamboo fibre fabric of ultraviolet ray-resistance type, and high production efficiency, at low cost, the wasting of resources is few, while the bamboo produced is fine
Tieing up fabric has uviolresistance, and ultraviolet transmittance is less than 5%, and fabric is comfortable, nice and cool, good permeability and the feature of environmental protection
Height is hardly damaged.
Detailed description of the invention
Fig. 1 is a kind of flow diagram of the preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric;
Fig. 2 is the component figure of anti-ultraviolet finishing liquid in a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Please refer to Fig. 1~2, in the embodiment of the present invention,
Embodiment 1
A kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric, preparation method is following steps:
S1, mixed yarn preparation: by wood-fibred, bamboo fibre, spandex fibre, cotton fiber, soybean fiber by blended, obtained mixed
Spinning;
S2, nice and cool veil preparation: again by silver fiber, silk fiber, cool fiber, environment-protection fiber by blended, obtained nice and cool face
Yarn;
S3, weaving: being woven the nice and cool veil in the mixed yarn and S2 in S1 using braider, forms bamboo fibre fabric;
S4, it pads: the bamboo fibre fabric being prepared in S3 being subjected to an immersing and rolling, a leaching one in anti-ultraviolet finishing liquid again
The pick-up rolled is 50-80%;
S5, it bakes and banks up with earth, cool down: after S4, then being baked, baking temperature is 130-180 DEG C, time 1-4min, finally
Cooling gets product fabric.
Further, mixed yarn component by weight is made in S1: 5-15 parts of wood-fibred, 35-50 parts of bamboo fibre, spandex are fine
Tie up 10-30 parts, 30-60 parts of cotton fiber, 10-15 parts of soybean fiber.
Further, the nice and cool veil component by weight in S2 is made: 1-5 parts of silver fiber, 5-10 parts of silk fiber,
5-15 parts of cool fiber, 2-10 parts of environment-protection fiber.
Further, the anti-ultraviolet finishing liquid in S4 is mixed by zinc oxide, titanium dioxide, polyester master particle,
It is 30-50:4-10:5-20 according to mass ratio.
Further, the anti-ultraviolet finishing liquid in S4 the preparation method comprises the following steps: zinc oxide, titanium dioxide, polyester is female
Grain, which is added to the water according to mass ratio for 30-50:4-10:5-20 ratio, is configured to anti-ultraviolet finishing liquid, and is adequately stirred
It mixes, mixing time is 0.5-4 hours.
Further, the cool fiber in S2 is using the polyamide fibre that nanoscale complex ore material is added.
Further, the environment-protection fiber in S2 uses corn-based environment-protection fiber.
By according to standard GB/T/T18830-2009 " evaluation of ultraviolet resistance of fabric ", to 1 institute of embodiment
The nice and cool ultraviolet ray-resistance type bamboo fibre fabric of the invention obtained carries out anti-ultraviolet property test, with wavelength 290nm -400nm's
UV ray is irradiated on bamboo fibre fabric, and test show that ultraviolet transmittance is less than 3-5%.
Embodiment 2
A kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric, preparation method is following steps:
S1, mixed yarn preparation: by wood-fibred, bamboo fibre, spandex fibre, cotton fiber, soybean fiber by blended, obtained mixed
Spinning;
S2, nice and cool veil preparation: again by silver fiber, silk fiber, cool fiber, environment-protection fiber by blended, obtained nice and cool face
Yarn;
S3, weaving: being woven the nice and cool veil in the mixed yarn and S2 in S1 using braider, forms bamboo fibre fabric;
S4, it pads: the bamboo fibre fabric being prepared in S3 being subjected to an immersing and rolling, a leaching one in anti-ultraviolet finishing liquid again
The pick-up rolled is 65%;
S5, it bakes and banks up with earth, cool down: after S4, then being baked, baking temperature is 160 DEG C, and time 1.5min is finally cooled down
Get product fabric.
Further, mixed yarn component by weight is made in S1: 12 parts of wood-fibred, 40 parts of bamboo fibre, spandex fibre 20
Part, 50 parts of cotton fiber, 12 parts of soybean fiber.
Further, the nice and cool veil component by weight in S2 is made: 4 parts of silver fiber, is felt nice and cool at 7 parts of silk fiber
8 parts of fiber, 7 parts of environment-protection fiber.
Further, the anti-ultraviolet finishing liquid in S4 is mixed by zinc oxide, titanium dioxide, polyester master particle,
It is 40:8:12 according to mass ratio.
Further, the anti-ultraviolet finishing liquid in S4 the preparation method comprises the following steps: zinc oxide, titanium dioxide, polyester is female
Grain is added to the water the anti-ultraviolet finishing liquid for being configured to 1L according to mass ratio for 40:8:12 ratio, and is adequately stirred, and stirs
Mixing the time is 3 hours.
Further, the cool fiber in S2 is using the polyamide fibre that nanoscale complex ore material is added.
Further, the environment-protection fiber in S2 uses corn-based environment-protection fiber.
By according to standard GB/T/T18830-2009 " evaluation of ultraviolet resistance of fabric ", to 2 institute of embodiment
The nice and cool ultraviolet ray-resistance type bamboo fibre fabric of the invention obtained carries out anti-ultraviolet property test, with wavelength 290nm -400nm's
UV ray is irradiated on bamboo fibre fabric, and test obtains ultraviolet transmittance less than 3%.
Embodiment 3
A kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric, preparation method is following steps:
S1, mixed yarn preparation: by wood-fibred, bamboo fibre, spandex fibre, cotton fiber, soybean fiber by blended, obtained mixed
Spinning;
S2, nice and cool veil preparation: again by silver fiber, silk fiber, cool fiber, environment-protection fiber by blended, obtained nice and cool face
Yarn;
S3, weaving: being woven the nice and cool veil in the mixed yarn and S2 in S1 using braider, forms bamboo fibre fabric;
S4, it pads: the bamboo fibre fabric being prepared in S3 being subjected to an immersing and rolling, a leaching one in anti-ultraviolet finishing liquid again
The pick-up rolled is 70%;
S5, it bakes and banks up with earth, cool down: after S4, then being baked, baking temperature is 160 DEG C, time 2min, and finally cooling is
Obtain finished fabric.
Further, mixed yarn component by weight is made in S1: 10 parts of wood-fibred, 35 parts of bamboo fibre, spandex fibre 18
Part, 45 parts of cotton fiber, 10 parts of soybean fiber.
Further, the nice and cool veil component by weight in S2 is made: 3 parts of silver fiber, is felt nice and cool at 5 parts of silk fiber
6 parts of fiber, 5 parts of environment-protection fiber.
Further, the anti-ultraviolet finishing liquid in S4 is mixed by zinc oxide, titanium dioxide, polyester master particle,
It is 30:5:7 according to mass ratio.
Further, the anti-ultraviolet finishing liquid in S4 the preparation method comprises the following steps: zinc oxide, titanium dioxide, polyester is female
Grain is added to the water the anti-ultraviolet finishing liquid for being configured to 1L according to mass ratio for 30:5:7 ratio, and is adequately stirred, and stirs
Mixing the time is 2 hours.
Further, the cool fiber in S2 is using the polyamide fibre that nanoscale complex ore material is added.
Further, the environment-protection fiber in S2 uses corn-based environment-protection fiber.
By according to standard GB/T/T18830-2009 " evaluation of ultraviolet resistance of fabric ", to 3 institute of embodiment
The nice and cool ultraviolet ray-resistance type bamboo fibre fabric of the invention obtained carries out anti-ultraviolet property test, with wavelength 290nm -400nm's
UV ray is irradiated on bamboo fibre fabric, and test obtains ultraviolet transmittance less than 4%.
In conclusion a kind of preparation method for nice and cool ultraviolet ray-resistance type bamboo fibre fabric that the present invention designs, with existing skill
Art is compared, and the present invention can not only process the bamboo fibre fabric of ultraviolet ray-resistance type, but also high production efficiency, and the wasting of resources is few,
The bamboo fibre fabric produced has imparted simultaneously, and fabric is comfortable, nice and cool, the good permeability and feature of environmental protection is high, is not easy
Damage, while also there is stable nerve, improve sleep and other effects, and ultraviolet transmittance is less than 5%.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (9)
1. a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric, which is characterized in that preparation method is following steps:
S1, mixed yarn preparation: by wood-fibred, bamboo fibre, spandex fibre, cotton fiber, soybean fiber by blended, obtained mixed
Spinning;
S2, nice and cool veil preparation: again by silver fiber, silk fiber, cool fiber, environment-protection fiber by blended, obtained nice and cool face
Yarn;
S3, weaving: being woven the nice and cool veil in the mixed yarn and S2 in S1 using braider, forms bamboo fibre fabric;
S4, it pads: the bamboo fibre fabric being prepared in S3 being subjected to an immersing and rolling, a leaching one in anti-ultraviolet finishing liquid again
The pick-up rolled is 50-80%;
S5, it bakes and banks up with earth, cool down: after S4, then being baked, baking temperature is 130-180 DEG C, time 1-4min, finally
Cooling gets product fabric.
2. a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric according to claim 1, which is characterized in that institute
State mixed yarn component by weight in S1 to be made: 5-15 parts of wood-fibred, bamboo fibre part 35-50,10-30 parts of spandex fibre, cotton are fine
30-60 parts, 10-15 parts of soybean fiber of dimension.
3. a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric according to claim 1, which is characterized in that institute
The nice and cool veil component by weight stated in S2 is made: 1-5 parts of silver fiber, 5-10 parts of silk fiber, 5-15 parts of cool fiber, ring
Protect fiber 2-10 parts.
4. a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric according to claim 1, which is characterized in that institute
Stating the anti-ultraviolet finishing liquid in S4 is mixed by zinc oxide, titanium dioxide, polyester master particle, is 30-50 according to mass ratio:
4-10:5-20。
5. a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric according to claim 1, which is characterized in that institute
Stating the anti-ultraviolet finishing liquid in S4 is mixed by zinc oxide, titanium dioxide, polyester master particle, is 40:8 according to mass ratio:
12。
6. a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric according to claim 1, which is characterized in that institute
Stating the anti-ultraviolet finishing liquid in S4 is mixed by zinc oxide, titanium dioxide, polyester master particle, is 30:5 according to mass ratio:
7。
7. a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric according to claim 1, which is characterized in that institute
State the anti-ultraviolet finishing liquid in S4 the preparation method comprises the following steps: according to mass ratio be 30- by zinc oxide, titanium dioxide, polyester master particle
50:4-10:5-20 ratio, which is added to the water, is configured to anti-ultraviolet finishing liquid, and is adequately stirred, mixing time 0.5-4
Hour.
8. a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric according to claim 1, which is characterized in that institute
The cool fiber in S2 is stated using the polyamide fibre that nanoscale complex ore material is added.
9. a kind of preparation method of nice and cool ultraviolet ray-resistance type bamboo fibre fabric according to claim 1, which is characterized in that institute
The environment-protection fiber in S2 is stated using corn-based environment-protection fiber.