CN109530429A - A kind of rolling mill practice of steady production martensite air-valve steel rolling base - Google Patents

A kind of rolling mill practice of steady production martensite air-valve steel rolling base Download PDF

Info

Publication number
CN109530429A
CN109530429A CN201811350695.0A CN201811350695A CN109530429A CN 109530429 A CN109530429 A CN 109530429A CN 201811350695 A CN201811350695 A CN 201811350695A CN 109530429 A CN109530429 A CN 109530429A
Authority
CN
China
Prior art keywords
rolling
cooling water
steel
roll
martensite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201811350695.0A
Other languages
Chinese (zh)
Other versions
CN109530429B (en
Inventor
邱雄文
周小兵
蒋国强
潘泽林
冯富友
李学保
孙应军
张宝华
蒋志华
杨洁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Baowu JFE Special Steel Co Ltd
Original Assignee
Baosteel Special Steel Shaoguan Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baosteel Special Steel Shaoguan Co Ltd filed Critical Baosteel Special Steel Shaoguan Co Ltd
Priority to CN201811350695.0A priority Critical patent/CN109530429B/en
Publication of CN109530429A publication Critical patent/CN109530429A/en
Application granted granted Critical
Publication of CN109530429B publication Critical patent/CN109530429B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of rolling mill practice of steady production martensite air-valve steel rolling base, processing step is that the side's 320*425/280*280 continuous casting billet → stepped heating stove heating → blooming mill → 1# hydraulic shear is cut off, back-end crop → 160F Continuous mill train → 2# hydraulic shear is cut off, is segmented → trolley furnace annealing;Martensite air-valve steel rolling base face checking and production efficiency can be solved the problems, such as very well.

Description

A kind of rolling mill practice of steady production martensite air-valve steel rolling base
Technical field
The invention belongs to steel rolling Controlled Rolling And Controlled Cooling fields, are related to a kind of rolling for steady production martensite air-valve steel rolling base Technique processed.
Background technique
Martensite Valve Steel is the one kind that can not ignore in current special steel kind, is Diesel Engine's Air Valve common used material, 900 DEG C Following non-scale, 600 DEG C ~ 700 DEG C have good anti-oxidant and elevated temperature strength, in middle-size and small-size diesel engine, truck It is used widely in exhaust valve part, it plays vital effect in the manufacture and development of automobile.Martensite gas Valve steel category high-alloy steel, the operation of rolling are to ensure product quality, cooling water should be avoided to contact with steel surface as far as possible.Rolling is horse A required link in family name's body Valve Steel production process, rolling quality directly influence the comprehensive performance of finished steel.Currently Martensite air-valve steel rolling base rolling mill practice mainly using traditional rolled blank rolling mill practice production, traditional rolling mill practice is more Extensive, in the operation of rolling, high-pressure water descaling, roll are cooling etc. can all cause steel to contact with water and the naturally cold side of rolled blank Formula etc. causes product surface to crack, and therefore, current tradition rolling mill practice is unable to satisfy the demand of Valve Steel fining rolling, The cooling controlling and rolling controlling process for seeking a kind of suitable martensite Valve Steel is imperative.
Conventional process flow:
The side's 320*425/280*280 continuous casting billet → stepped heating stove heating → high-pressure water descaling → blooming mill (pair rolling work Skill, roll cooling water are in normally open) (roll cooling water is in normally opened to → 1# hydraulic shear (cutting head, back-end crop) → Continuous mill train State) → 2# hydraulic shear (cutting head, segmentation) → cold bed (natural cooling).
Summary of the invention
In order to overcome the disadvantages mentioned above of the prior art, the present invention provides a kind of steady production martensite air-valve steel rolling base Rolling mill practice can solve the problems, such as martensite air-valve steel rolling base face checking and production efficiency very well.
The technical solution adopted by the present invention to solve the technical problems is: a kind of steady production martensite air-valve steel rolling base Rolling mill practice, processing step is the side's 320*425/280*280 continuous casting billet → stepped heating stove heating → blooming mill → 1# Hydraulic shear is cut off, back-end crop → 160F Continuous mill train → 2# hydraulic shear is cut off, is segmented → trolley furnace annealing;Specific steps It is:
Step 1: stock bank checks the side's 320*425/280*280 continuous casting billet, it is ensured that blank surface quality meets presentation quality and wants It asks;
Step 2: steel billet is put into heating stove heating, heating temperature, time reach tapping when technique requires;
Step 3: closing high pressure water dephosphorization, martensite Valve Steel steel billet not dephosphorization;
Step 4: first being slotted using other steel billets before blooming mill rolling;When rolling, using slighter compress rolling mill practice, roll is closed And roller-way cooling water;After every steel rolls, air-cooled roll 2 minutes or so, then open roll cooling water 2 minutes or so (cooling water flows Amount is controlled by 35%, and about 62 cubes ms/h), it is then shut off roll cooling water and crosses steel;
Step 5: the cutting head of 1# hydraulic shear and back-end crop, tandem rolling preincubation cover are closed;
Step 6: milling train cooling water carries out adjustment in advance, under the premise of guaranteeing that roll is cooling, roll cooling water is adjusted as far as possible It is small, cooling water is closed after mixing up, before rolled piece does not bite milling train, which is in close state, and is bitten to rolled piece After milling train, program automatically turns on the roll cooling water of the rack;After the completion of rolling, roll cooling water is closed;
Step 7: hot saw is using the cutting head of 2# hydraulic shear, segmentation and sampling, not back-end crop;
Step 8: rolled blank is quickly entered furnace stress relief annealing after finishing receives rolled blank.
The positive effect of the present invention is: slotting and can effectively be preheated to roll before rolling Valve Steel, when cogging closes Roll cooling water, high pressure dephosphorization water and control tandem rolling cooling water can utmostly avoid steel contacts, will quickly roll after rolling Base enters furnace stress relief annealing, can effectively eliminate rolled blank internal residual stress, is ensureing that martensite Valve Steel is every physical and chemical Under the premise of performance, technique very good solution martensite air-valve steel rolling base face checking problem.
Specific embodiment
Below with reference to embodiment, the present invention is further described.
The embodiment of the present invention specifically comprises the following steps: so that 9 martensite Valve Steels roll rear surface quality as an example
Step 1: selecting 9 martensite air valve steel continuous casting billets, 3 45 steel continuous casting billets, section 320mm × 425mm, it is ensured that blank Surface meets appearance requirement;
It is sequentially loaded into heating furnace before 9 Valve Steels step 2: 3 45 steel are come, by heating process standard normal heating;
Step 3: first rolling 3 45 steel by traditional rolling mill practice after the completion of heating, martensite air valve is rolled as blooming mill Fluting before steel prepares;
Step 4: stokehold dephosphorization apparatus is closed, martensite Valve Steel not dephosphorization;
Step 5: blooming mill changes slighter compress rolling mill practice, roll cooling water is closed when rolling Valve Steel, rolls latter air-cooled 2 points Clock goes out next again;
Step 6: the cutting head of 1# hydraulic shear and back-end crop, tandem rolling preincubation cover are closed;
Step 7: steel billet bites K4(tandem rolling First milling train) afterwards program automatic water similarly bite K3, K2, K1(tandem rolling most Latter milling train) program automatic water afterwards, while roll cooling water is turned down as far as possible.The program when steel billet is detached from K4, K3, K2, K1 Cooling water is automatically closed;
Step 8: the segmentation of 2# hydraulic shear enters rapidly car type furnace stress relief annealing by cold bed after the completion of rolled blank rolling.It presses 9 martensite Valve Steels are rolled according to the step;
Step 9: taking rolled blank sample to make physical and chemical performance analysis after rolled blank stress relief annealing;
After annealing is come out of the stove, the surface quality of this 9 martensite Valve Steels is intact, and cracking phenomena, every physicochemical property report is not present It is qualified to accuse.The rolling mill practice can be effectively applied to the production of martensite air-valve steel rolling base, make the surface matter of martensite Valve Steel Amount meets product quality requirement, realizes the Precise control to martensite air-valve steel rolling technique, reaches and effectively solves martensite The problem of air-valve steel rolling base face checking, improves the rolling quality and production efficiency of martensite Valve Steel to greatest extent.It adopts With this rolling mill practice, martensite air-valve steel rolling base surface did not occurred the phenomenon that cracking, and the present invention has good practicability, It has successfully ensured the steady production of martensite air-valve steel rolling base, there is biggish economic benefit, it can be in similar producing line Expanded application.
The foregoing is merely a prefered embodiment of the invention, is not intended to limit the invention, all within principle of the invention, institute It changes, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.

Claims (1)

1. a kind of rolling mill practice of steady production martensite air-valve steel rolling base, processing step is the side 320*425/280*280 Continuous casting billet → stepped heating stove heating → blooming mill → 1# hydraulic shear is cut off, back-end crop → 160F Continuous mill train → 2# is hydraulic It cuts and is cut off, is segmented → trolley furnace annealing;It is characterized by: comprising the concrete steps that:
Step 1: stock bank checks the side's 320*425/280*280 continuous casting billet, it is ensured that blank surface quality meets presentation quality and wants It asks;
Step 2: steel billet is put into heating stove heating, heating temperature, time reach tapping when technique requires;
Step 3: closing high pressure water dephosphorization, martensite Valve Steel steel billet not dephosphorization;
Step 4: first being slotted using other steel billets before blooming mill rolling;When rolling, using slighter compress rolling mill practice, roll is closed And roller-way cooling water;After every steel rolls, air-cooled roll 2 minutes or so, then open roll cooling water 2 minutes or so (cooling water flows Amount is controlled by 35%, and about 62 cubes ms/h), it is then shut off roll cooling water and crosses steel;
Step 5: the cutting head of 1# hydraulic shear and back-end crop, tandem rolling preincubation cover are closed;
Step 6: milling train cooling water carries out adjustment in advance, under the premise of guaranteeing that roll is cooling, roll cooling water is adjusted as far as possible It is small, cooling water is closed after mixing up, before rolled piece does not bite milling train, which is in close state, and is bitten to rolled piece After milling train, program automatically turns on the roll cooling water of the rack;After the completion of rolling, roll cooling water is closed;
Step 7: hot saw is using the cutting head of 2# hydraulic shear, segmentation and sampling, not back-end crop;
Step 8: rolled blank is quickly entered furnace stress relief annealing after finishing receives rolled blank.
CN201811350695.0A 2018-11-14 2018-11-14 Rolling process for stably producing martensite air valve steel rolled blank Active CN109530429B (en)