CN109518346A - A kind of peppermint cotton blended knitted fabric and preparation method thereof - Google Patents

A kind of peppermint cotton blended knitted fabric and preparation method thereof Download PDF

Info

Publication number
CN109518346A
CN109518346A CN201710841597.6A CN201710841597A CN109518346A CN 109518346 A CN109518346 A CN 109518346A CN 201710841597 A CN201710841597 A CN 201710841597A CN 109518346 A CN109518346 A CN 109518346A
Authority
CN
China
Prior art keywords
cotton
peppermint
knitted fabric
fiber
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710841597.6A
Other languages
Chinese (zh)
Inventor
钟俊杰
周建
王峰
王鸿博
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Xiangfei Fashion Co Ltd
Original Assignee
Jiangyin Xiangfei Fashion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Xiangfei Fashion Co Ltd filed Critical Jiangyin Xiangfei Fashion Co Ltd
Priority to CN201710841597.6A priority Critical patent/CN109518346A/en
Publication of CN109518346A publication Critical patent/CN109518346A/en
Pending legal-status Critical Current

Abstract

The present invention relates to textile technology field, specifically a kind of peppermint cotton blended knitted fabric and preparation method thereof, the peppermint cotton blended knitted fabric uses cotton fiber and mint fibers for spinning material, blended mass ratio are as follows: 80%/mint fibers of cotton fiber 20%;It is spinned using close SEILE textile technology, front roller speed is 165 r/min, and spindle revolving speed is 12000r/min;Fabric uses single side plain stitch, and horizontal close 65.8 stringers/10cm indulges close 40.3 rows/10cm.The invention has the advantages that: the present invention is combined with mint fibers with cotton fiber, it is blended go out 32SSingle thread, then through bifilar doubling, weave to obtain knitting fabric using Computerized flat knitting machine, with the good characteristic of soft touch, washability, be provided simultaneously with good refrigerant and good skin-friendly, be particularly suitable for makeing underwear and summer high-grade fabric.

Description

A kind of peppermint cotton blended knitted fabric and preparation method thereof
Technical field
The present invention relates to textile technology fields, specifically, being a kind of for mint fibers are blended with cotton fiber, and knit Cause the production technology of fabric.
Background technique
Occur in the market in today that science and technology continues to develop with the application that plant fiber is loaded onto textile product kimonos Various clothing and textile product containing " certain plant ".Peppermint is one of common Chinese herbal medicine in China earliest, in " this of Li Shizhen (1518-1593 A.D.) Careless detailed outline " in its character and effect be documented in detail.Peppermint has many uses, and can be used for medicine, food, cosmetics, perfume (or spice) Material and tobacco industry etc..It can be said that peppermint is to integrate medicine, health care, beauty, food and ornamental natural green plant. The effective component of peppermint can be divided into volatile menthol and nine kinds of chemical components.Menthol can distribute the special side of peppermint To smell, and (rheum emodin, Chrysophanol, Physcion, ortho-aminobenzoic acid, sitosterol, aloe are big for nine kinds of main chemical compositions Flavine, ursolic acid, daucosterol, trans isomer cinnamic acid) assign peppermint basic effect: antibacterial, anti-inflammatory is refrigerant, refreshes oneself.Peppermint is fine Dimension is using natural plants peppermint as raw material, in conjunction with nanometer pulverization technology and microcapsules technology, by peppermint extract with microcapsules packet The form covered is spun to fibre in conjunction with cellulose blending.Its extract does not add any chemical substance in extraction process, both protects The good skin-friendly of cellulose fibre, spinnability have been demonstrate,proved, and has highlighted its natural, green, the concept of health.
Mint fibers have the effects that antibacterial bacteriostatic, refrigerant eye-catching, prevention typhoid fever.In wearing process, with human skin With the continuous CONTACT WITH FRICTION of fiber, effect ingredient in peppermint is constantly discharged from fiber, and is absorbed by the human body, and is met various The demand of Green Textile Base product.The spinnability of mint fibers is relatively good, is easy dyeing, absorbs good air permeability, antibacterial functions are held Long, the market vacancy has been filled up.The feel that its fabric not only maintains viscose rayon is smooth, dangles, takes as comfortable, ventilative and silk The features such as with performance, the effect of being provided simultaneously with natural cool feeling and antibacterial, and also mint fibers fabric is vulnerable to bacterium in soil and water Decomposition, natural environment will not be destroyed, when burning will not generate toxic gas, and the peppermint of " from naturally, back to nature " is fine Dimension fabric is the green fiber fabric for meeting current environmentally protective trend.
Cotton fiber is time-honored traditional fibre, and main component is cellulose, is contained on macromolecular chain segment very much Hydrophilic radical, so that cotton fiber has good moisture pick-up properties.Cotton fabric product is approved that feel is moistened by the majority of consumers It is good and snugness of fit is good with, skin affinity.The advantages of mint fibers are blended with cotton fiber, two kinds of fibers is sufficiently sent out It waves, has not only remained the excellent wearability such as the good pro-skin of cellulose fibre, ventilative, but also given full play to natural peppermint and extracted Object skin-friendly, refrigerant eye-catching and prevention typhoid fever and other effects, improve performance when fiber individually spins, meet people to weaving Natural, the green and healthy pursuit of product.It can be applied to infant's dress ornament, home textile product, underwear socks, home wear series, filling Object, medical care articles, high-grade fabric etc..
On the one hand peppermint cotton blended knitted fabric meets reply dress-goods comfortableization, health care, superior, fashion-orientation The market demand, while improving product specification, enhance enterprise core competence.
At this stage, with the development of textile industry, the pure spinning textile of Single Fiber spinning is no longer satisfied market Demand.Mint fibers and cotton fiber it is blended, can make full use of both advantages of different fibers respectively, improve yam linear Can, the new textile with natural environmental-protective and unique taking is developed on its basis, and it is multifarious to meet properties of product Feature, being capable of the World Textile Market demand that increasingly changes of further satisfaction.
Chinese patent literature CN105525406A discloses a kind of mint fibers and cotton fiber blended yarn and its spinner Skill, wherein the content of mint fibers is 1% ~ 99%, and surplus is cotton fiber, is spinned using close SEILE textile technology, front roller speed For 146r/min, 11000 r/min of ingot speed.But it uses long-staple cotton to carry out blended, higher cost with peppermint, and can not solve two The uniformly mixed problem of kind fiber.
Summary of the invention
The purpose of the present invention is to provide a kind of peppermint cotton blended knitted fabric and preparation method thereof, solve fine with common cotton Tie up blended resultant yarn;By by the mixed carded sliver return again griping cotton machine mix primary mode solve two kinds of fibers be uniformly mixed ask Topic;By realizing that fabric smoothly produces to guide tension optimization when fabric weaves;The horizontal at material of final fabric is improved, is met real Border application demand.
The first aspect of the present invention, provides a kind of preparation method of peppermint cotton blended knitted fabric, and the peppermint cotton is mixed Spinning knitting fabric uses cotton fiber and mint fibers for spinning material, blended mass ratio are as follows: 80%/mint fibers of cotton fiber 20%, Preparation method includes the following steps:
A) cotton carding: cotton fiber and mint fibers are passed through into carding step respectively, the fiber carded sliver is made;
A1) cotton fiber: opening picking → cotton carding → carded sliver;
A2) mint fibers: opening picking → cotton carding → carded sliver;
B) the cotton carded sliver mixes in rolls with the peppermint carded sliver;
C) fiber mixing volume carries out drafting, and ripe bar is made;
D) ripe bar spin, be first spun into rove, after be spun into spun yarn;
E) through winder doubling twisting, strand is made;
F) finished fabric is made through rewinding, upper horizontal woven sheet in strand.
Preferably, in the step A, cotton carding takes " low velocity, small tension receiving coil, fast transfer, damages fiber at middle gauge less " Technological principle, to be avoided in carding process fiber in carding process be damaged, prevent fiber rubs repeatedly transfer form cotton knot.
Wherein, the specific processing parameter of cotton carding are as follows: carded sliver Dry Weight per Unit 20.5g/5m, cylinder revolving speed 330r/min, thorn Roller revolving speed 820r/min, 19 r/min of doffing speed, cylinder and Flat Gauge 0.23mm, 0.20 mm, 0.20 mm, 0.20mm, 0.23mm, 1.25 times of tension draft, cylinder and licker-in differential surface speed 2.15 or so, feed plate and licker-in gauge 0.30mm, licker-in with 0.18 mm of cylinder gauge, cylinder and doffer's gauge 0.13mm.
Preferably, in the step B, two kinds of fibers are mixed twice: first two kinds of fibers are mixed it is coiled, after again It is primary to return griping cotton machine mixing.Solve the problems, such as that blended deviation rate is high.
Preferably, in the step B, overstriking sliver when coiled, and antistatic process is done, plastic film is used after lower machine Package.Phenomena such as preventing examination paper excessively fluffy and glutinous volume, broken volume occurs.
Preferably, it in the step C, using three and closes, ripe bar is made.It is flat to stretching for fiber to give full play to drawing-off Row effect improves the bar evenness of sliver;An irregularity is reduced into, guarantee is mixed evenly and blending ratio is accurate.Specifically simultaneously Technological parameter is as shown in table 2 below.
Preferably, it in the step D, selects close SEILE textile technology to spin, to control yarn quality, mentions High yarn strength.Stringent control is carried out to spinning matching device, selects rubber roller before high-elastic soft, it is ensured that roller and apron have good Good control ability.
Preferably, in the step D, front roller speed is 165 r/min, and spindle revolving speed is about 12000r/min;Together When properly increase yarn twist factor, about 370 ~ 390, to reduce the thickness section in resultant yarn, reduce hairiness number.
Preferably, in the step D, compact spinning device is installed additional in equipment spinning twist triangle zone, utilizes negative pressure gas flow Increase by two kinds of fibre migrations, uniformly Cheng Buhou made to be not easy pilling to guarantee that yarn is bright and clean, filoplume, item are dry less,
Preferably, in the step D, yarn strength and weavability are increased using doubling.
Preferably, it in the step F, is woven, yarn is lubricated first and upper Lasaxing Oilfield using Computerized flat knitting machine, kept away Exempt from broken yarn phenomenon caused by knotting in weaving process because of yarn.
Preferably, it in the step F, is woven using doublet cord, yarn weavability enhancing, fabric surface presents plentiful Fabric Style effect.
Preferably, in the step F, fabric uses single side plain stitch, and horizontal close 65.8 stringers/10cm indulges close 40.3 Row/10cm.The technological parameter of specific fabric braiding is as shown in table 3 below.
It is furthermore preferred that after the step F, it is further comprising the steps of:
Running-on → flatcar → hand seam → washing → drying → whole boiling hot → packaging → storage.
It is furthermore preferred that the concrete technology flow process of the preparation method of the peppermint cotton blended knitted fabric includes:
A, cotton fiber: opening picking → cotton carding → carded sliver
Mint fibers: opening picking → cotton carding → carded sliver
B, the cotton carded sliver+peppermint carded sliver → mixed simultaneously (three) → rove → spun yarn → winder → doubling twisting
C, strand → rewinding → knits piece → running-on → flatcar → hand seam → washing → drying → whole boiling hot → packaging → storage.
The second aspect of the present invention provides a kind of peppermint cotton blended knitted fabric, the peppermint cotton blended knitted fabric Use cotton fiber and mint fibers for spinning material, blended mass ratio are as follows: 80%/mint fibers of cotton fiber 20%;Using close match The spinning of network spinning process technology, front roller speed are 165 r/min, and spindle revolving speed is 12000r/min;Fabric uses single side plain Tissue, horizontal close 65.8 stringers/10cm, indulges close 40.3 rows/10cm.
Preferably, the peppermint cotton blended knitted fabric is prepared using any of the above-described preparation method.
The invention has the advantages that:
1, the present invention combined with mint fibers with cotton fiber, it is blended out 32SSingle thread, then through bifilar doubling, using Computerized flat knitting machine Braiding obtains knitting fabric, with the good characteristic of soft touch, washability, is provided simultaneously with good refrigerant and good skin-friendly, It is particularly suitable for makeing underwear and summer high-grade fabric.
2, blended using mint fibers and cotton fiber, by the way that it is respective excellent to give full play to fiber to the preferred of blending rate Gesture feature makes product fabric with functional while having a good wearability again, meets the weaving market demand.
3, it is woven using doublet cord, promotes knitted surfaces saturation degree and plentiful degree, assign fabric stereovision.
Specific embodiment
It elaborates below with reference to embodiment to specific embodiment provided by the invention.
(1) raw material is chosen
It uses cotton fiber and mint fibers for spinning material, and its blending ratio is carried out preferably, raw material parameter is as shown in table 1. In trial-manufacturing process, two kinds of fiber blend mass ratioes are chosen are as follows: 80%/peppermint of cotton 20%.
1 raw material parameter of table
Fiber Fineness/dtex Fibre length/mm Breaking strength/cNdtex-1 Elongation at break/%
Mint fibers 2.04 38.00 3.27 9.76
Cotton fiber 1.73 29.00 3.10 6.10
(2) spinning process
Strict control is carried out to cotton carding and mixing in doubling step technological parameter emphatically in spinning process, overall plan is as follows:
Carding step: carding step should consider the combing situation of fiber, consider the degree of impairment of fiber in carding process again. Cotton carding takes the technological principle of " low velocity, small tension receiving coil, fast transfer, damages fiber at middle gauge less ", to avoid in carding process Fiber is damaged in carding process, is prevented fiber from rubbing with the hands repeatedly then is formed cotton knot.Simultaneously in production engineering, to reinforce to equipment The maintenance of state.
Specific processing parameter are as follows: carded sliver Dry Weight per Unit 20.5g/5m, cylinder revolving speed 330r/min, licker-in revolving speed 820r/min, 19 r/min of doffing speed, cylinder and Flat Gauge 0.23mm, 0.20 mm, 0.20 mm, 0.20mm, 0.23mm, 1.25 times of tension draft, cylinder and licker-in differential surface speed 2.15 or so, feed plate and licker-in gauge 0.30mm, licker-in and cylinder gauge 0.18 mm, cylinder and doffer's gauge 0.13mm.
In order to solve the problems, such as that blended deviation rate is high, two kinds of fibers are mixed twice, two kinds of fibers mix coiled Return griping cotton machine amalgamation time again afterwards;Phenomena such as examination paper is excessively fluffy in order to prevent and glutinous volume, broken volume occurs, overstriking yarn when coiled Item, and antistatic process is done, it is wrapped up after lower machine with plastic film.
Mixing in doubling step: to reduce into an irregularity, guarantee is mixed evenly and blending ratio is accurate, using three and closes, is made Ripe bar gives full play to drawing-off and stretches paralleling effect to fiber, improves the bar evenness of sliver.Its drawing process parameter such as table Shown in 2.
2 drawing process parameter of table
Drawing frame channel number Quantitative/g (5m)-1 Front roller speed/mmin-1 Back zone drafting multiple Roller gauge/mm Strip dry CV value/%
One 21.0 195 1.72 13×19 3.65
Two 19.5 185 1.69 13×18 3.62
Three 18.5 175 1.33 13×15 2.89
In product development and production process, strict control is carried out to preceding spinning semi-manufactured goods quality.According to mint fibers and cotton fiber The characteristics of raw material, improves yarn strength, close SEILE textile technology is selected to spin to control yarn quality.To spinning Matching device carries out stringent control, selects rubber roller before high-elastic soft, it is ensured that roller and apron have good control ability.Preceding sieve Pulling rate degree is 165 r/min.The revolving speed of spindle, about 12000r/min are suitably reduced in production process, while being properly increased thin Yarn twist factor, about 370 ~ 390 reduce hairiness number to reduce the thickness section in resultant yarn;It spins and twists in equipment at the same time Trigonum installs compact spinning device additional, increases by two kinds of fibre migrations using negative pressure gas flow, to guarantee that yarn is bright and clean, filoplume, item are dry less Uniformly, so that Cheng Buhou is not easy pilling, yarn strength and weavability are increased using doubling.In addition, in process of production, strictly Monitor the temperature and humidity variation of workshop condition.
(3) straight-bar machines technique
Blended yarn weaved fabric using Computerized flat knitting machine weave when, related blend fibre there are aiming at the problem that, yarn is lubricated first And upper Lasaxing Oilfield, avoid broken yarn phenomenon caused by knotting in weaving process because of yarn.It is woven using doublet cord, yarn weavability increases By force, plentiful Fabric Style effect is presented in fabric surface.The technological parameter of fabric braiding is as shown in table 3.
3 fabric organizational parameter of table
Raw material 80%/peppermint of cotton 20%, 32S/ 2 doublet cords
Tissue Single side plain stitch
Equipment Computerized flat knitting machine, 12G
It is horizontal close 65.8 stringers/10cm
It indulges close 40.3 rows/10cm
Grammes per square metre 290g/m2
The present invention to raw material selection, yarn design, spinning technique parameter preferably and straight-bar machines process optimization, finally successfully have developed Peppermint cotton blended knitted fabric.Product processes are feasible, product quality and function reach advanced international level, and product has been manufactured experimently It completes, and has produced in batches, achieve preferable economic benefit and social benefit.
The preferred embodiment of the present invention has been described in detail above, but the invention be not limited to it is described Embodiment, those skilled in the art can also make various equivalent on the premise of not violating the inventive spirit of the present invention Variation or replacement, these equivalent variation or replacement are all included in the scope defined by the claims of the present application.

Claims (7)

1. a kind of preparation method of peppermint cotton blended knitted fabric, which is characterized in that the peppermint cotton blended knitted fabric is adopted It is spinning material with cotton fiber and mint fibers, blended mass ratio are as follows: 80%/mint fibers of cotton fiber 20%, preparation method packet Include following steps:
A) cotton carding: cotton fiber and mint fibers are passed through into carding step respectively, the fiber carded sliver is made;
B) the cotton carded sliver mixes in rolls with the peppermint carded sliver, and two kinds of fibers are mixed twice: first two kinds of fibers are mixed in rolls, after It is primary that griping cotton machine mixing is returned again;Overstriking sliver when coiled, and antistatic process is done, it is wrapped up after lower machine with plastic film;
C) fiber mixing volume carries out drafting, using three and closes, ripe bar is made;
D) ripe bar spin, be first spun into rove, after be spun into spun yarn;Close SEILE textile technology is selected to spin, front roller speed Degree is 165 r/min, and spindle revolving speed is 12000r/min;
E) through winder doubling twisting, strand is made;
F) finished fabric is made through rewinding, upper horizontal woven sheet in strand;Fabric uses single side plain stitch, and horizontal close 65.8 stringer/ 10cm indulges close 40.3 rows/10cm.
2. the preparation method of peppermint cotton blended knitted fabric according to claim 1, which is characterized in that the step A In, the processing parameter of cotton carding are as follows: carded sliver Dry Weight per Unit 20.5g/5m, cylinder revolving speed 330r/min, licker-in revolving speed 820r/min, 19 r/min of doffing speed, cylinder and Flat Gauge 0.23mm, 0.20 mm, 0.20 mm, 0.20mm, 0.23mm, tension draft 1.25 times, cylinder and licker-in differential surface speed 2.15 or so, feed plate and licker-in gauge 0.30mm, licker-in and 0.18 mm of cylinder gauge, Cylinder and doffer's gauge 0.13mm.
3. the preparation method of peppermint cotton blended knitted fabric according to claim 1, which is characterized in that the step D In, yarn twist factor is 370 ~ 390.
4. the preparation method of peppermint cotton blended knitted fabric according to claim 1, which is characterized in that the step D In, compact spinning device is installed additional in equipment spinning twist triangle zone;Yarn strength and weavability are increased using doubling.
5. the preparation method of peppermint cotton blended knitted fabric according to claim 1, which is characterized in that the step F In, it is woven, yarn is lubricated first and upper Lasaxing Oilfield using Computerized flat knitting machine;It is woven using doublet cord.
6. a kind of peppermint cotton blended knitted fabric, which is characterized in that the peppermint cotton blended knitted fabric using cotton fiber and Mint fibers are spinning material, blended mass ratio are as follows: 80%/mint fibers of cotton fiber 20%;Using close SEILE textile technology Spinning, front roller speed are 165 r/min, and spindle revolving speed is 12000r/min;Fabric uses single side plain stitch, cross close 65.8 Close 40.3 rows/10cm is indulged in stringer/10cm.
7. peppermint cotton blended knitted fabric according to claim 8, which is characterized in that the cotton blended knitted face of the peppermint Material is prepared using any preparation method of claim 1-5.
CN201710841597.6A 2017-09-18 2017-09-18 A kind of peppermint cotton blended knitted fabric and preparation method thereof Pending CN109518346A (en)