CN109440297A - A kind of upright continuous material and preparation method thereof that the continuous net that tiles is combined with vertical type silk floss net - Google Patents
A kind of upright continuous material and preparation method thereof that the continuous net that tiles is combined with vertical type silk floss net Download PDFInfo
- Publication number
- CN109440297A CN109440297A CN201811635693.6A CN201811635693A CN109440297A CN 109440297 A CN109440297 A CN 109440297A CN 201811635693 A CN201811635693 A CN 201811635693A CN 109440297 A CN109440297 A CN 109440297A
- Authority
- CN
- China
- Prior art keywords
- net
- continuous
- silk floss
- vertical type
- type silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of upright continuous materials that the continuous net that tiles is combined with vertical type silk floss net, it is characterized in that, the following steps are included: first producing the tiling silk floss net being formed, regenerate the also unshaped vertical type silk floss net of output, the continuous net that tiles of being formed is entered into heat-shaping in heating equipment together with the also unshaped vertical type silk floss net when the vertical type silk floss net carries out heat-shaping, obtains the upright silk floss material that the continuous net that tiles is combined with vertical type silk floss net.The upright continuous material that the continuous net provided by the invention that tiles is combined with vertical type silk floss net, by the way that vertical type silk floss net is combined with the continuous net that tiles, under the premise of ensure that the performances such as upright continuous elastic properties of materials, the tear resistance of continuous sample, especially longitudinal tear resistance are further improved.
Description
Technical field
The present invention relates to non-woven material technical field, especially a kind of continuous net of tiling combines upright with vertical type silk floss net
The upright silk floss that the preparation method of continuous material and the continuous net of the tiling being prepared using the preparation method are combined with vertical type silk floss net
Material.
Background technique
Upright silk floss material is many excellent with high resiliency, resistance to compression, ventilative and environmental protection etc. as a kind of novel non-woven material
Point, has been widely applied in daily life.
Due to the particularity of production technology, for upright silk floss material in the case where identical grammes per square metre, elasticity ratio is current on the market
Other nonwovens process materials be intended to it is superior.Existing market application surface is also more and more extensive, is particularly subject to Japan and European & American Market
Have deep love for.
But when producing some frivolous clothes or quilt packing material, due to upright continuous molding structure problem, hold very much
It easily leads to longitudinal direction and easily stretches length.On the one hand inconvenient production in process of production easily leads to cut-parts and stretches length during spreading sanction,
Easily shorten again after sanction；On the other hand during taking, it is necessary to quilting flower pattern special designs, otherwise be easy washing stretching and become
Shape limits to product design.
Summary of the invention
In view of this, in order to overcome the drawbacks of the prior art, the object of the present invention is to provide a kind of continuous net of tiling and vertical types
The preparation method for the upright continuous material that continuous net combines, and the tiling silk floss net and vertical type silk floss that are prepared using the preparation method
The upright continuous material that net combines.
In order to achieve the above first purpose, the invention adopts the following technical scheme:
A kind of upright silk floss material that the continuous net that tiles is combined with vertical type silk floss net, comprising the following steps: first produce and be formed
Tile continuous net, regenerates the also unshaped vertical type silk floss net of output, will be described flat when the vertical type silk floss net carries out heat-shaping
It spreads continuous net and enters heat-shaping in heating equipment together with the vertical type silk floss net, obtain the continuous net of the tiling and mutually tied with vertical type silk floss net
The upright continuous material closed.
Preferably, the parameter of the heat-shaping is 130-200 DEG C of oven temperature, rotation speed of fan 300-400r/min, net
Tape speed 0.5-10m/min.
Preferably, the preparation tiling silk floss net being formed is the following steps are included: fibrous raw material is beaten with opener
It is added in proportion in mixed continuous storehouse afterwards and carries out mixed silk floss, and be machined to continuous net through combing, is heated for the first time by baking oven later
The continuous net of the tiling is made in sizing.
In some embodiments, specifically includes the following steps:
1) fibrous raw material shredding: fibrous raw material is beaten with opener；
2) the mixed silk floss in big storehouse: fiber after adding shredding in proportion and through the mixed silk floss in big storehouse, to improve uniformity；
3) smart shredding: mixing continuous material to big storehouse and carry out fine shredding again, carries out fine shredding to fiber；
4) it vibrates continuous storehouse and blends silk floss: the fiber after smart shredding being used and is mixed again in vibrating continuous storehouse, improve uniform
Property；
5) continuous net is combed by one of carding machine: mixed fiber is prepared into continuous net through carding machine；
6) cross lapping: the continuous net after one of carding machine combs is intersected；
7) continuous net is combed by second carding machine: the fiber after cross lapping is combed into continuous net again, improve continuous net
Uniformity；
8) entering to dry case heat-shaping；By baking oven and hot air shaping, low-melting fiber material shaping is melted；
9) molding winding, obtains the tiling silk floss net of solidifying and setting.
It is further preferred that the parameter of the heat-shaping for the first time is 130-200 DEG C of oven temperature, rotation speed of fan 300-
400r/min, mesh belt speed 10-40m/min.
Preferably, after preparing the unshaped vertical type silk floss net the following steps are included: fibrous raw material is beaten with opener
It is added in mixed continuous storehouse in proportion and carries out mixed silk floss, and be machined to continuous net through combing, is then carried out silk floss net using Zhe Mian mechanism
It folds, obtains the unshaped vertical type silk floss net.
In some embodiments, specifically includes the following steps:
1) fibrous raw material shredding: fibrous raw material is beaten with opener；
2) the mixed silk floss in big storehouse: fiber after adding shredding in proportion and through the mixed silk floss in big storehouse, to improve uniformity；
3) smart shredding: mixing continuous material to big storehouse and carry out fine shredding again, carries out fine shredding to fiber；
4) it vibrates continuous storehouse and blends silk floss: the fiber after smart shredding being used and is mixed again in vibrating continuous storehouse, improve uniform
Property；
5) continuous net is combed by one of carding machine: mixed fiber is prepared into continuous net through carding machine；
6) cross lapping: the continuous net after one of carding machine combs is intersected；
7) continuous net is combed by second carding machine: the fiber after cross lapping is combed into continuous net again, improve continuous net
Uniformity；
8) it folds continuous net: being folded with the continuous net that bis- carding machine of Zhe Mian mechanism Jiang Jing is combed into, at perpendicular to the big face of continuous sample
Long-pending direction；Unshaped vertical type silk floss net is obtained at this time；
In the present invention, it needs the above-mentioned continuous net of tiling being formed that is prepared together with the vertical type silk floss net of non-hot briquetting
Into carrying out heat-shaping in baking oven, the upright silk floss material that the continuous net that tiles is combined with vertical type silk floss net is made, thus further include with
Lower step:
9) entering to dry case heat-shaping: by continuous net also unshaped after folding and the tiling silk floss net being formed by baking oven and heat
Wind sizing, melts low-melting fiber, and the upright continuous material that the continuous net that tiles is combined with vertical type silk floss net is made in material shaping；It is described
The parameter of heat-shaping is 130-200 DEG C of oven temperature, rotation speed of fan 300-400r/min, mesh belt speed 0.5-10m/min；
10) molding winding, the upright continuous material cutting and winding that the continuous net that tiles is combined with vertical type silk floss net by latter equipment.
The grammes per square metre of the finally obtained upright continuous material is 30-500g/m2。
It is further preferred that according to parts by weight, the fibrous raw material includes 10-40 parts of low-melting fiber, 60-90 parts
Two dimension or three-dimensional short fibre.
It is further preferred that the fusing point that the low-melting fiber is is 100-180 DEG C, fiber number 0.55-22.2dtex is put down
Equal length is 32-88mm.In some embodiments, the low-melting fiber can be specially the PET fiber of 2-7dtex.
It is further preferred that the two dimension or the fiber number of three-dimensional short fibre are 2.2-22dtex, average length 32-88mm.
In some embodiments, the two dimension or the three-dimensional short fine specially PET fiber of 0.5-22dtex.
The present invention also provides a kind of tiling silk floss nets that preparation method as described above is prepared and vertical type silk floss net mutually to tie
The upright continuous material closed, including being located in the middle vertical type silk floss net and positioned at the flat of the above and or below of the vertical type silk floss net
Spread continuous net.
Preferably, the ratio of the thickness of the thickness and vertical type silk floss net of the continuous net of single layer tiling is 1:5-20；It is described flat
The continuous net of paving with a thickness of 0.5-20mm, the vertical type silk floss net with a thickness of 5-120mm.In some embodiments preferably, described flat
The continuous net of paving with a thickness of 0.5-5mm, the vertical type silk floss net with a thickness of 5-20mm.
Due to the technical solution more than using, the present invention compared with prior art have the beneficial effect that the present invention mentions
The upright continuous material that the continuous net of the tiling of confession is combined with vertical type silk floss net, by the way that vertical type silk floss net is combined with the continuous net that tiles,
Under the premise of ensure that the performances such as upright continuous elastic properties of materials, the tear resistance of continuous sample is further improved, it is especially longitudinal anti-
Tear resistance.
Detailed description of the invention
To describe the technical solutions in the embodiments of the present invention more clearly, make required in being described below to embodiment
Attached drawing is briefly described, it should be apparent that, drawings in the following description are only some embodiments of the invention, for
For those of ordinary skill in the art, without creative efforts, it can also be obtained according to these attached drawings other
Attached drawing.
Fig. 1 is the schematic diagram one for the upright continuous material that the continuous net of tiling is combined with vertical type silk floss net in embodiment 1；
Fig. 2 is the schematic diagram two for the upright continuous material that the continuous net of tiling is combined with vertical type silk floss net in embodiment 1.
Wherein: the continuous continuous net -2 of net -1, the second tiling of the first tiling founds type silk floss net -3.
Specific embodiment
Detailed description of the preferred embodiments with reference to the accompanying drawing.
Embodiment 1 tiles the upright continuous material that continuous net combines with vertical type silk floss net
Referring to Fig. 1, the upright continuous material that a kind of tiling silk floss net of the present embodiment is combined with vertical type silk floss net, including it is located at centre
Vertical type silk floss net and tiling silk floss net positioned at the above and or below of vertical type silk floss net.As shown in Figure 1, vertical type silk floss net and tiling
Continuous net is respectively one layer, and the continuous net that tiles is located above or below vertical type silk floss net, that is, includes the first tiling silk floss net 1 and be located at first
The vertical type silk floss net 3 to tile on continuous net 1, or as shown in Fig. 2, vertical type silk floss net is located at centre, the continuous net that tiles is located at vertical type silk floss net
Above and below, that is, include be located in the middle vertical type silk floss net 3 and above vertical type silk floss net 3 first tile continuous net 1 and
The continuous net 2 of the second tiling positioned at vertical 3 lower section of type silk floss net.
According to parts by weight, the continuous net of tiling or vertical type silk floss net include 10-40 parts of low-melting fiber, 60-90 parts of two dimension
Or three-dimensional short fibre.The fusing point that low-melting fiber is is 100-180 DEG C, fiber number 0.55-22.2dtex, average length 32-
88mm, preferably low-melting fiber are the PET fiber of 2-7dtex.Two dimension or the fiber number of three-dimensional short fibre are 2.2-22dtex, average long
Degree is 32-88mm.It is preferred that two dimension or the three-dimensional short fine PET fiber for being 0.5-22dtex.
Specifically, the continuous net that tiles in the present embodiment includes the low-melting fiber and 75 parts of 2D*51mm of 25 parts of 2D*51mm
Two-dimentional solid fibre.Low-melting fiber, the two dimension of 35 parts of 1.7D*44mm for founding the 2D*51mm that type silk floss net includes 25 parts are hollow
The two-dimentional doughnut of fiber and 50 parts of 1.5D*51mm.Low-melting fiber, 2D*51mm, 1.7D*44mm two dimension doughnut
It is PET fiber with 1.5D*51mm two dimension doughnut.
The ratio of the thickness of the thickness and vertical type silk floss net of the continuous net of single layer tiling is 1:5-20, the continuous net that tiles with a thickness of 0.5-
20mm, stand type silk floss net with a thickness of 5-120mm.In the present embodiment the continuous net of preferred tiling with a thickness of 0.5-5mm, found type silk floss net
With a thickness of 5-20mm.More specifically, in the present embodiment, the ratio of the thickness and the thickness of vertical type silk floss net of the continuous net of single layer tiling is
1:5, the continuous net that tiles with a thickness of 4mm, stand type silk floss net with a thickness of 20mm.
Embodiment 2 tiles the preparation method of upright continuous material that continuous net combines with vertical type silk floss net
A kind of upright silk floss material that the continuous net that tiles is combined with vertical type silk floss net, comprising the following steps: first produce and be formed
Tile continuous net, regenerates the also unshaped vertical type silk floss net of output, will tile when vertical type silk floss net carries out heat-shaping continuous net and
Vertical type silk floss net enters heat-shaping in heating equipment together, the upright silk floss material that the continuous net that obtains tiling is combined with vertical type silk floss net.
The parameter of heat-shaping is 200 DEG C of oven temperature, rotation speed of fan 400r/min, mesh belt speed 3.5m/min.Implement in others
In example, the parameter of heat-shaping is 130-200 DEG C of oven temperature, rotation speed of fan 300-400r/min, mesh belt speed 0.5-10m/
min。
A. the tiling silk floss net being formed
The tiling silk floss net being formed is prepared the following steps are included: being added in proportion after fibrous raw material is beaten with opener mixed
Mixed silk floss is carried out in continuous storehouse, and is machined to continuous net through combing, is carried out heat-shaping for the first time by baking oven later, is made and has been formed
Tiling silk floss net.
Specifically, the tiling silk floss net be formed of preparation the following steps are included:
1) fibrous raw material shredding: fibrous raw material is beaten with opener.Fibrous raw material includes 25 parts of 2D*51mm low-melting fiber
With 75 parts of 2D*51mm two dimension solid fibres.The fusing point that low-melting fiber is is 100-180 DEG C, fiber number 0.55-22.2dtex,
Average length is 32-88mm, preferably low-melting fiber be 2-7dtex PET fiber.Two dimension or the fiber number of three-dimensional short fibre are 2.2-
22dtex, average length 32-88mm.It is preferred that two dimension or the three-dimensional short fine PET fiber for being 0.5-22dtex.
2) the mixed silk floss in big storehouse: fiber after adding shredding in proportion and through the mixed silk floss in big storehouse, to improve uniformity.
3) smart shredding: mixing continuous material to big storehouse and carry out fine shredding again, carries out fine shredding to fiber.
4) it vibrates continuous storehouse and blends silk floss: the fiber after smart shredding being used and is mixed again in vibrating continuous storehouse, is improved
Uniformity.
5) continuous net is combed by one of carding machine: mixed fiber is prepared into continuous net through carding machine.
6) cross lapping: the continuous net after one of carding machine combs is intersected.
7) continuous net is combed by second carding machine: the fiber after cross lapping is combed into continuous net again, improve
The uniformity of silk floss net.
8) entering to dry case heat-shaping；By baking oven and hot air shaping, low-melting fiber material shaping is melted.Heating is fixed for the first time
The parameter of type is 150 DEG C of oven temperature, rotation speed of fan 300-400r/min, mesh belt speed 25m/min.In other embodiments
In, the parameter of heat-shaping is 130-200 DEG C of oven temperature, rotation speed of fan 300-400r/min for the first time, mesh belt speed 10-40m/
min。
9) molding winding, obtains the tiling silk floss net of solidifying and setting.
B. unshaped vertical type silk floss net
Unshaped vertical type silk floss net is prepared the following steps are included: being added to mixed silk floss after fibrous raw material is beaten with opener in proportion
Mixed silk floss is carried out in storehouse, and is machined to continuous net through combing, and then continuous net is folded using Zhe Mian mechanism, is obtained unshaped
Vertical type silk floss net.
Specifically, prepare unshaped vertical type silk floss net specifically includes the following steps:
1) fibrous raw material shredding: fibrous raw material is beaten with opener.Fibrous raw material includes that the low melting point of 25 parts of 2D*51mm is fine
The two-dimentional doughnut of dimension, the two-dimentional doughnut of 35 parts of 1.7D*44mm and 50 parts of 1.5D*51mm.Low-melting fiber
It is 2-7dtex that fusing point, which is 100-180 DEG C, fiber number 0.55-22.2dtex, average length 32-88mm, preferably low-melting fiber,
PET fiber.Two dimension or the fiber number of three-dimensional short fibre are 2.2-22dtex, average length 32-88mm.It is preferred that two dimension or three-dimensional short
Fibre is the PET fiber of 0.5-22dtex.
2) the mixed silk floss in big storehouse: fiber after adding shredding in proportion and through the mixed silk floss in big storehouse, to improve uniformity.
3) smart shredding: mixing continuous material to big storehouse and carry out fine shredding again, carries out fine shredding to fiber.
4) it vibrates continuous storehouse and blends silk floss: the fiber after smart shredding being used and is mixed again in vibrating continuous storehouse, is improved
Uniformity.
5) continuous net is combed by one of carding machine: mixed fiber is prepared into continuous net through carding machine.
6) cross lapping: the continuous net after one of carding machine combs is intersected.
7) continuous net is combed by second carding machine: the fiber after cross lapping is combed into continuous net again, improve
The uniformity of silk floss net.
8) it folds continuous net: being folded with the continuous net that bis- carding machine of Zhe Mian mechanism Jiang Jing is combed into, at perpendicular to continuous sample
The direction of large area；Unshaped vertical type silk floss net is obtained at this time.
C. the upright continuous material that the continuous net that tiles is combined with vertical type silk floss net
In the present invention, it needs the vertical type that non-hot briquetting in the continuous net of tiling and B being formed is prepared in above-mentioned A is continuous
Net enters together carries out heat-shaping in baking oven, the upright continuous material that the continuous net that tiles is combined with vertical type silk floss net is made, so also
The following steps are included:
1) entering to dry case heat-shaping: simultaneously by baking oven by vertical type silk floss net unshaped after folding and the tiling silk floss net being formed
Hot air shaping, melts low-melting fiber, and the upright continuous material that the continuous net that tiles is combined with vertical type silk floss net is made in material shaping；Add
The parameter of thermal finalization is 160 DEG C of oven temperature, rotation speed of fan 300-400r/min, mesh belt speed 3.5m/min.Some other
In embodiment, the parameter of heat-shaping is 130-200 DEG C of oven temperature, rotation speed of fan 300-400r/min, mesh belt speed 0.5-
10m/min；
2) molding winding, the upright continuous material cutting and winding that the continuous net that tiles is combined with vertical type silk floss net by latter equipment.
The grammes per square metre of finally obtained upright continuous material is 30-500g/m2。
I.e. in the present embodiment, first production has already passed through the tiling silk floss net of heat-shaping, then prepares unshaped vertical type silk floss net,
To tile continuous net heat-shaping again together with unshaped vertical type silk floss net when vertical type silk floss net heat-shaping, and tiling is continuous
Net is fabricated into together with vertical type silk floss net, forms the upright continuous material that the continuous net that tiles is combined with vertical type silk floss net.
Comparative example 1
Upright continuous material is prepared using conventional method, does not include the continuous net that tiles in the upright continuous material.
3 Comparative result of embodiment
The upright continuous product conventional without the continuous net of tiling that upright continuous product in embodiment 1 is prepared with comparative example 1
It is tested, performance comparison is as follows:
Tearing toughness: the upright continuous material of embodiment 1 improves 100% than traditional continuous sample for not adding tiling silk floss net.
Upright recovery: the two is identical.
Clo value: comparative example 1 is 2.5, and embodiment 1 is 2.4, substantially close to.
Wash washing shrinkage: comparative example 1 is -5%, and embodiment 1 is -2%.
So the upright continuous material that the continuous net of tiling in embodiment 1 is combined with vertical type silk floss net ensure that other performances
Under the premise of such as elasticity, upright recovery, tearing toughness is greatly improved.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art
Scholar cans understand the content of the present invention and implement it accordingly, and it is not intended to limit the scope of the present invention, it is all according to the present invention
Equivalent change or modification made by Spirit Essence, should be covered by the protection scope of the present invention.
Claims (10)
1. a kind of upright continuous material that the continuous net that tiles is combined with vertical type silk floss net, which comprises the following steps: first produce
The tiling silk floss net being formed out regenerates the also unshaped vertical type silk floss net of output, carries out heat-shaping in the vertical type silk floss net
When the continuous net of the tiling entered into heat-shaping in heating equipment together with the also unshaped vertical type silk floss net, obtain described in
The upright continuous material that the continuous net that tiles is combined with vertical type silk floss net.
2. the upright continuous material that the continuous net according to claim 1 that tiles is combined with vertical type silk floss net, which is characterized in that described
The parameter of heat-shaping is 130-200 DEG C of oven temperature, rotation speed of fan 300-400r/min, mesh belt speed 0.5-10m/min.
3. the upright continuous material that the continuous net according to claim 1 that tiles is combined with vertical type silk floss net, which is characterized in that preparation
The tiling silk floss net being formed the following steps are included: be added to mixed continuous storehouse in proportion after fibrous raw material is beaten with opener
In carry out mixed silk floss, and be machined to continuous net through combing, carry out heat-shaping for the first time by baking oven later, be made described and be formed
Tiling silk floss net.
4. the upright continuous material that the continuous net according to claim 3 that tiles is combined with vertical type silk floss net, which is characterized in that described
The parameter of heat-shaping is 130-200 DEG C of oven temperature, rotation speed of fan 300-400r/min for the first time, mesh belt speed 10-40m/
min。
5. the upright continuous material that the continuous net according to claim 1 that tiles is combined with vertical type silk floss net, which is characterized in that preparation
The unshaped vertical type silk floss net the following steps are included: be added to mixed continuous storehouse in proportion after fibrous raw material is beaten with opener
In carry out mixed silk floss, and be machined to continuous net through combing, then continuous net folded using Zhe Mian mechanism, obtains the prepattern
Vertical type silk floss net.
6. the upright continuous material that the continuous net of the tiling according to claim 3 or 5 is combined with vertical type silk floss net, which is characterized in that
According to parts by weight, the fibrous raw material includes 10-40 parts of low-melting fiber, 60-90 parts of two dimension or three-dimensional short fibre.
7. the upright continuous material that the continuous net according to claim 6 that tiles is combined with vertical type silk floss net, which is characterized in that described
The fusing point that low-melting fiber is is 100-180 DEG C, fiber number 0.55-22.2dtex, average length 32-88mm.
8. the upright continuous material that the continuous net according to claim 6 that tiles is combined with vertical type silk floss net, which is characterized in that described
Two dimension or the fiber number of three-dimensional short fibre are 2.2-22dtex, average length 32-88mm.
9. a kind of continuous net of the tiling that preparation method according to claims 1-8 is prepared combines upright with vertical type silk floss net
Continuous material, the tiling silk floss net including being located in the middle vertical type silk floss net and positioned at the above and or below of the vertical type silk floss net.
10. the upright continuous material that the continuous net according to claim 9 that tiles is combined with vertical type silk floss net, which is characterized in that institute
State the continuous net of tiling with a thickness of 0.5-20mm, the vertical type silk floss net with a thickness of 5-120mm.