CN109403017A - A kind of tension Quality Pure Cotton Yarn Production preparation method - Google Patents
A kind of tension Quality Pure Cotton Yarn Production preparation method Download PDFInfo
- Publication number
- CN109403017A CN109403017A CN201811205349.3A CN201811205349A CN109403017A CN 109403017 A CN109403017 A CN 109403017A CN 201811205349 A CN201811205349 A CN 201811205349A CN 109403017 A CN109403017 A CN 109403017A
- Authority
- CN
- China
- Prior art keywords
- parts
- yarn
- adhesive
- fire retardant
- pure cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to cotton yarn textile technology field, especially a kind of tension Quality Pure Cotton Yarn Production preparation method, including Blowing carding process, combing process, mixing in doubling step, Roving Frames, spinning process, winding procedure, packaging process, the spinning process include: S1, match network；It is S2, close；S3, drawing-off；S4, twisting；S5, reinforcing: by the spun yarn after twisting by spray gun even application fire retardant and adhesive, fire retardant sprays after being mixed with adhesive according to weight ratio 1:2-3, and yarn is sent into drying box after the completion of spraying and is dried, and 80-95 DEG C of drying temperature；S6, winding；S7, molding.The present invention sprays on yarn and has cured fire retardant and adhesive, and fire retardant can be improved the anti-flammability of yarn, improves safe effect, and adhesive increases the intensity of yarn, improves tension effect.
Description
Technical field
The present invention relates to cotton yarn textile technology field more particularly to a kind of tension Quality Pure Cotton Yarn Production preparation methods.
Background technique
Purified cotton yarns are obtained by frame production, including general comb yarn and combed yarn using cotton as raw material, main to use
In production pure cotton product, pure cotton product has the advantage that 1. good hygroscopicity；2. having good moisture retention；3. heat-resisting
It is functional；4. the resistivity to alkali is larger；5. being contacted with skin without any stimulation, no negative interaction is worn beneficial to human body long
Harmless, sanitation performance is good.Therefore pure cotton product is very popular, widely used, so as to cause the demand of purified cotton yarns
It is more vigorous.The cotton yarn of traditional technique weaving, intensity is poor, is easy to happen the case where breaking, and do not have flame retardant effect.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of tension Quality Pure Cotton Yarn Production preparation proposed
Method.
To achieve the goals above, present invention employs following technical solutions:
Design a kind of tension Quality Pure Cotton Yarn Production preparation method, including Blowing carding process, combing process, mixing in doubling step, Roving Frames,
Spinning process, winding procedure, packaging process, the spinning process include:
S1, match network: double roving feeding makes the brighter and cleaner softness of spun yarn；
It is S2, close: to increase negative pressure device, reduce filoplume, improve strength；
S3, drawing-off: rove is drawn to required fineness, keeps straightening of fibers parallel；
S4, twisting: being subject to turn for yarn, becomes the spun yarn compact siro spinning device with certain twist, certain strength；
S5, reinforcing: by the spun yarn after twisting by spray gun even application fire retardant and adhesive, fire retardant is hydroxide
The mixture of magnesium, aluminium hydroxide and water, and in percentage by weight, the content of each component is magnesium hydroxide 25-40%, hydrogen-oxygen
Change aluminium 15-20%, surplus is water；
Adhesive is the mixture of formaldehyde, urea, ammonium chloride, NaOH, ethyl alcohol and NH40H, and each component is in parts by weight
It is calculated as 30-50 parts of formaldehyde, 10-15 parts of urea, 2-5 parts of ammonium chloride, 0.2-3 parts of NaOH, 20-40 parts of ethyl alcohol, NH40H 0.5-4
Part；
Fire retardant sprays after being mixed with adhesive according to weight ratio 1:2-3, is sent into yarn after the completion of spraying and dries
It is dried in dry case, 80-95 DEG C of drying temperature；
S6, winding: by the spun yarn-winding after sizing on bobbin；
S7, molding: the coil of a certain size and shape, easy to carry and rear process processing is made.
Preferably, adhesive is the mixture of formaldehyde, urea, ammonium chloride, NaOH, ethyl alcohol and NH40H, and each component is by weight
Amount number is calculated as 35 parts of formaldehyde, 12 parts of urea, 3 parts of ammonium chloride, 1 part of NaOH, 25 parts of ethyl alcohol, 1 part of NH40H.
Preferably, adhesive is the mixture of formaldehyde, urea, ammonium chloride, NaOH, ethyl alcohol and NH40H, and each component is by weight
Amount number is calculated as 40 parts of formaldehyde, 14 parts of urea, 4 parts of ammonium chloride, 2 parts of NaOH, 35 parts of ethyl alcohol, 3 parts of NH40H.
Preferably, the mixing in doubling step includes:
A1 is simultaneously closed: more combing slivers being carried out autoleveller and are closed, it is more uniform to reach thickness；
A2, drawing-off: it by more yarn drawn downs, reduces hook raising fibers parallel and stretches.
Preferably, the winding procedure includes:
B1, winding and forming: by incidental looping big, forming and with the bobbin of certain density at capacity；
B2, removal of impurities: part fault and impurity on yarn are removed, to improve the quality of yarn.
Preferably, the packaging process includes: to be packed into packaging bag or packaging by cylinder yarn mantle and by predetermined weight, number of elements
Case is carried convenient for storage.
A kind of tension Quality Pure Cotton Yarn Production preparation method proposed by the present invention, beneficial effect are: the present invention sprays simultaneously on yarn
Fire retardant and adhesive are had cured, fire retardant can be improved the anti-flammability of yarn, improve safe effect, and adhesive increases yarn
Intensity improves tension effect.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.
Embodiment 1
A kind of tension Quality Pure Cotton Yarn Production preparation method, including Blowing carding process, combing process, mixing in doubling step, Roving Frames, spun yarn
Process, winding procedure, packaging process, spinning process include:
S1, match network: double roving feeding makes the brighter and cleaner softness of spun yarn；
It is S2, close: to increase negative pressure device, reduce filoplume, improve strength；
S3, drawing-off: rove is drawn to required fineness, keeps straightening of fibers parallel；
S4, twisting: being subject to turn for yarn, becomes the spun yarn compact siro spinning device with certain twist, certain strength；
S5, reinforcing: by the spun yarn after twisting by spray gun even application fire retardant and adhesive, fire retardant is hydroxide
The mixture of magnesium, aluminium hydroxide and water, and in percentage by weight, the content of each component is magnesium hydroxide 25%, hydroxide
Aluminium 15%, surplus are water；
Adhesive is the mixture of formaldehyde, urea, ammonium chloride, NaOH, ethyl alcohol and NH40H, and each component is in parts by weight
It is calculated as 30 parts of formaldehyde, 10 parts of urea, 2 parts of ammonium chloride, NaOH0.2 parts, 20 parts of ethyl alcohol, 0.5 part of NH40H；
Fire retardant sprays after being mixed with adhesive according to weight ratio 1:2, is sent into yarn after the completion of spraying and dries
It is dried in case, 80 DEG C of drying temperature；
S6, winding: by the spun yarn-winding after sizing on bobbin；
S7, molding: the coil of a certain size and shape, easy to carry and rear process processing is made.
Mixing in doubling step includes:
A1 is simultaneously closed: more combing slivers being carried out autoleveller and are closed, it is more uniform to reach thickness；
A2, drawing-off: it by more yarn drawn downs, reduces hook raising fibers parallel and stretches.
Winding procedure includes:
B1, winding and forming: by incidental looping big, forming and with the bobbin of certain density at capacity；
B2, removal of impurities: part fault and impurity on yarn are removed, to improve the quality of yarn.
Packaging process includes: to be packed into packaging bag or packing case by cylinder yarn mantle and by predetermined weight, number of elements, is removed convenient for storage
Fortune.
Embodiment 2
A kind of tension Quality Pure Cotton Yarn Production preparation method, including Blowing carding process, combing process, mixing in doubling step, Roving Frames, spun yarn
Process, winding procedure, packaging process, spinning process include:
S1, match network: double roving feeding makes the brighter and cleaner softness of spun yarn；
It is S2, close: to increase negative pressure device, reduce filoplume, improve strength；
S3, drawing-off: rove is drawn to required fineness, keeps straightening of fibers parallel；
S4, twisting: being subject to turn for yarn, becomes the spun yarn compact siro spinning device with certain twist, certain strength；
S5, reinforcing: by the spun yarn after twisting by spray gun even application fire retardant and adhesive, fire retardant is hydroxide
The mixture of magnesium, aluminium hydroxide and water, and in percentage by weight, the content of each component is magnesium hydroxide 28%, hydroxide
Aluminium 18%, surplus are water；
Adhesive is the mixture of formaldehyde, urea, ammonium chloride, NaOH, ethyl alcohol and NH40H, and each component is in parts by weight
It is calculated as 35 parts of formaldehyde, 12 parts of urea, 3 parts of ammonium chloride, NaOH1 parts, 25 parts of ethyl alcohol, 1 part of NH40H；
Fire retardant sprays after being mixed with adhesive according to weight ratio 1:2, is sent into yarn after the completion of spraying and dries
It is dried in case, 85 DEG C of drying temperature；
S6, winding: by the spun yarn-winding after sizing on bobbin；
S7, molding: the coil of a certain size and shape, easy to carry and rear process processing is made.
Mixing in doubling step includes:
A1 is simultaneously closed: more combing slivers being carried out autoleveller and are closed, it is more uniform to reach thickness；
A2, drawing-off: it by more yarn drawn downs, reduces hook raising fibers parallel and stretches.
Winding procedure includes:
B1, winding and forming: by incidental looping big, forming and with the bobbin of certain density at capacity；
B2, removal of impurities: part fault and impurity on yarn are removed, to improve the quality of yarn.
Packaging process includes: to be packed into packaging bag or packing case by cylinder yarn mantle and by predetermined weight, number of elements, is removed convenient for storage
Fortune.
Embodiment 3
A kind of tension Quality Pure Cotton Yarn Production preparation method, including Blowing carding process, combing process, mixing in doubling step, Roving Frames, spun yarn
Process, winding procedure, packaging process, spinning process include:
S1, match network: double roving feeding makes the brighter and cleaner softness of spun yarn；
It is S2, close: to increase negative pressure device, reduce filoplume, improve strength；
S3, drawing-off: rove is drawn to required fineness, keeps straightening of fibers parallel；
S4, twisting: being subject to turn for yarn, becomes the spun yarn compact siro spinning device with certain twist, certain strength；
S5, reinforcing: by the spun yarn after twisting by spray gun even application fire retardant and adhesive, fire retardant is hydroxide
The mixture of magnesium, aluminium hydroxide and water, and in percentage by weight, the content of each component is magnesium hydroxide 35%, hydroxide
Aluminium 18%, surplus are water；
Adhesive is the mixture of formaldehyde, urea, ammonium chloride, NaOH, ethyl alcohol and NH40H, and each component is in parts by weight
It is calculated as 40 parts of formaldehyde, 14 parts of urea, 4 parts of ammonium chloride, NaOH2 parts, 35 parts of ethyl alcohol, 3 parts of NH40H；
Fire retardant sprays after being mixed with adhesive according to weight ratio 1:3, is sent into yarn after the completion of spraying and dries
It is dried in case, 88 DEG C of drying temperature；
S6, winding: by the spun yarn-winding after sizing on bobbin；
S7, molding: the coil of a certain size and shape, easy to carry and rear process processing is made.
Mixing in doubling step includes:
A1 is simultaneously closed: more combing slivers being carried out autoleveller and are closed, it is more uniform to reach thickness；
A2, drawing-off: it by more yarn drawn downs, reduces hook raising fibers parallel and stretches.
Winding procedure includes:
B1, winding and forming: by incidental looping big, forming and with the bobbin of certain density at capacity；
B2, removal of impurities: part fault and impurity on yarn are removed, to improve the quality of yarn.
Packaging process includes: to be packed into packaging bag or packing case by cylinder yarn mantle and by predetermined weight, number of elements, is removed convenient for storage
Fortune.
Embodiment 4
A kind of tension Quality Pure Cotton Yarn Production preparation method, including Blowing carding process, combing process, mixing in doubling step, Roving Frames, spun yarn
Process, winding procedure, packaging process, spinning process include:
S1, match network: double roving feeding makes the brighter and cleaner softness of spun yarn；
It is S2, close: to increase negative pressure device, reduce filoplume, improve strength；
S3, drawing-off: rove is drawn to required fineness, keeps straightening of fibers parallel；
S4, twisting: being subject to turn for yarn, becomes the spun yarn compact siro spinning device with certain twist, certain strength；
S5, reinforcing: by the spun yarn after twisting by spray gun even application fire retardant and adhesive, fire retardant is hydroxide
The mixture of magnesium, aluminium hydroxide and water, and in percentage by weight, the content of each component is magnesium hydroxide 40%, hydroxide
Aluminium 20%, surplus are water；
Adhesive is the mixture of formaldehyde, urea, ammonium chloride, NaOH, ethyl alcohol and NH40H, and each component is in parts by weight
It is calculated as 50 parts of formaldehyde, 15 parts of urea, 5 parts of ammonium chloride, NaOH3 parts, 40 parts of ethyl alcohol, 4 parts of NH40H；
Fire retardant sprays after being mixed with adhesive according to weight ratio 1:3, is sent into yarn after the completion of spraying and dries
It is dried in case, 95 DEG C of drying temperature；
S6, winding: by the spun yarn-winding after sizing on bobbin；
S7, molding: the coil of a certain size and shape, easy to carry and rear process processing is made.
Mixing in doubling step includes:
A1 is simultaneously closed: more combing slivers being carried out autoleveller and are closed, it is more uniform to reach thickness；
A2, drawing-off: it by more yarn drawn downs, reduces hook raising fibers parallel and stretches.
Winding procedure includes:
B1, winding and forming: by incidental looping big, forming and with the bobbin of certain density at capacity；
B2, removal of impurities: part fault and impurity on yarn are removed, to improve the quality of yarn.
Packaging process includes: to be packed into packaging bag or packing case by cylinder yarn mantle and by predetermined weight, number of elements, is removed convenient for storage
Fortune.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of tension Quality Pure Cotton Yarn Production preparation method, including Blowing carding process, combing process, mixing in doubling step, Roving Frames, spun yarn work
Sequence, winding procedure, packaging process, which is characterized in that the spinning process includes:
S1, match network: double roving feeding makes the brighter and cleaner softness of spun yarn；
It is S2, close: to increase negative pressure device, reduce filoplume, improve strength；
S3, drawing-off: rove is drawn to required fineness, keeps straightening of fibers parallel；
S4, twisting: being subject to turn for yarn, becomes the spun yarn compact siro spinning device with certain twist, certain strength；
S5, reinforcing: by the spun yarn after twisting by spray gun even application fire retardant and adhesive, fire retardant is magnesium hydroxide, hydrogen
The mixture of aluminium oxide and water, and in percentage by weight, the content of each component is magnesium hydroxide 25-40%, aluminium hydroxide
15-20%, surplus are water；
Adhesive is the mixture of formaldehyde, urea, ammonium chloride, NaOH, ethyl alcohol and NH40H, and each component is calculated by weight as
30-50 parts of formaldehyde, 10-15 parts of urea, 2-5 parts of ammonium chloride, 0.2-3 parts of NaOH, 20-40 parts of ethyl alcohol, 0.5-4 parts of NH40H；
Fire retardant sprays after being mixed with adhesive according to weight ratio 1:2-3, and yarn is sent into drying box after the completion of spraying
Middle drying, 80-95 DEG C of drying temperature；
S6, winding: by the spun yarn-winding after sizing on bobbin；
S7, molding: the coil of a certain size and shape, easy to carry and rear process processing is made.
2. a kind of tension Quality Pure Cotton Yarn Production preparation method according to claim 1, which is characterized in that adhesive be formaldehyde, urea,
Ammonium chloride, NaOH, ethyl alcohol and NH40H mixture, and each component is calculated by weight as 35 parts of formaldehyde, 12 parts of urea, chlorination
3 parts of amine, NaOH1 parts, 25 parts of ethyl alcohol, 1 part of NH40H.
3. a kind of tension Quality Pure Cotton Yarn Production preparation method according to claim 1, it is characterised in that: adhesive be formaldehyde, urea,
Ammonium chloride, NaOH, ethyl alcohol and NH40H mixture, and each component is calculated by weight as 40 parts of formaldehyde, 14 parts of urea, chlorination
4 parts of amine, NaOH2 parts, 35 parts of ethyl alcohol, 3 parts of NH40H.
4. a kind of tension Quality Pure Cotton Yarn Production preparation method according to claim 1, it is characterised in that: the mixing in doubling step includes:
A1 is simultaneously closed: more combing slivers being carried out autoleveller and are closed, it is more uniform to reach thickness；
A2, drawing-off: it by more yarn drawn downs, reduces hook raising fibers parallel and stretches.
5. a kind of tension Quality Pure Cotton Yarn Production preparation method according to claim 1, which is characterized in that the winding procedure includes:
B1, winding and forming: by incidental looping big, forming and with the bobbin of certain density at capacity；
B2, removal of impurities: part fault and impurity on yarn are removed, to improve the quality of yarn.
6. a kind of tension Quality Pure Cotton Yarn Production preparation method according to claim 1, which is characterized in that the packaging process includes:
It is packed into packaging bag or packing case by cylinder yarn mantle and by predetermined weight, number of elements, is carried convenient for storage.