CN109370048A - The preparation method of wear-resisting landscape sprinkler - Google Patents
The preparation method of wear-resisting landscape sprinkler Download PDFInfo
- Publication number
- CN109370048A CN109370048A CN201811196455.XA CN201811196455A CN109370048A CN 109370048 A CN109370048 A CN 109370048A CN 201811196455 A CN201811196455 A CN 201811196455A CN 109370048 A CN109370048 A CN 109370048A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastics
- sprinkler
- weight
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of wear-resisting landscape sprinkler, the landscape sprinkler includes plastics sprinkler head, and the plastics sprinkler head includes 30-40 parts PP, 20-30 parts ABS, 10-20 parts HDPE, 10-20 parts equal styrene, 1-2 parts of antioxidants, 1-5 parts of abrasion resistant particles, 2-3 parts of toughener, 2-3 parts of pigment and 5-10 parts of glass fibres by weight.The preparation method for the wear-resisting landscape sprinkler that the present invention obtains, it uses polystyrene and ABS to be mixed as flocculating agent with PP and HDPE, it is set to improve the flexibility of plastics in coacervation process, make plastics that there is certain crushing resistance, in addition antioxidant and abrasion resistant particles are added, so that plastics sprinkler head can be satisfied with the feature of environmental protection, safety and wearability simultaneously.
Description
Technical field
The present invention relates to a kind of preparation method of hydraulic giant, the preparation method of especially wear-resisting landscape sprinkler.
Background technique
Landscape sprinkler is that people usually require that different types of garden instrument is used alternatingly in horticulture-working.The garden
Woods sprinkler includes plastics sprinkler head, and plastics sprinkler head needs to guarantee the feature of environmental protection of its material, safety and resistance to when in use
Mill property, however existing plastics sprinkler head is tended not to due to the unicity of material so that being satisfied with the feature of environmental protection, peace simultaneously at present
Full property and wearability, this also causes its service life shorter, and product replacement rate is high.
Summary of the invention
The wear-resisting landscape sprinkler of one kind is provided the purpose of the present invention is to solve above-mentioned the deficiencies in the prior art
Preparation method.
To achieve the goals above, the preparation method of a kind of wear-resisting landscape sprinkler designed by the present invention, the garden
Woods sprinkler includes plastics sprinkler head, and the plastics sprinkler head includes 30-40 parts PP, 20-30 parts ABS, 10-20 parts by weight
HDPE, 10-20 parts of equal styrene, 1-2 parts of antioxidants, 1-5 parts of abrasion resistant particles, 2-3 parts of toughener, 2-3 parts of pigment and 5-
10 parts of glass fibres,
The antioxidant includes 30-40 parts of sodium tripolyphosphates, 10-15 parts of hexamethylenetetramines, 20-30 parts of tertiary fourths by weight
Base hydroquinone, 5-10 part polybutadiene polyurethane, 5-10 parts of potassium fluoborates and 2-5 parts of benzotriazole,
The abrasion resistant particles include 50-60 parts of aluminium oxide, 5-15 parts of silicon carbide, 8-15 parts of quartz sands, 5-10 part four by weight
Silicon fluoride and 1-5 parts of graphenes,
The toughener include by weight 70-80 parts of ethylene octane copolymers, 10-15 parts of polyether sulfones, 3-5 parts of maleic anhydrides with
And 3-5 parts of hexamethylene diamines,
The pigment includes titanium dioxide, iron oxide red, iron oxide yellow, iron oxide black, carbon black, cadmium red, cadmium yellow, lead chromate yellow, oxidation
One or more of chrome green, barba hispanica, zinc oxide, zinc yellow, cobalt blue.
The preparation method of the plastics sprinkler head the following steps are included:
Step 1: antioxidant is prepared, by weight by 30-40 parts of sodium tripolyphosphates, 10-15 parts of hexamethylenetetramines, 20-30
Part tert-butyl hydroquinone, 5-10 parts of polybutadiene polyurethanes, 5-10 parts of potassium fluoborates and 2-5 parts of benzotriazole are uniformly mixed,
It is melted, is then pulverized after cooling up to antioxidant in high temperature furnace；
Step 2: preparation abrasion resistant particles, by weight by 50-60 parts of aluminium oxide, 5-15 parts of silicon carbide, 8-15 parts of quartz sands, 5-
10 parts of ocratations and 1-5 parts of graphenes after mixing, are dissolved in ethanol solution, and then ball grinds are up to abrasion resistant particles,
Step 3: plastics sprinkler head is prepared, by weight by 30-40 parts PP, 20-30 parts ABS, 10-20 parts HDPE, 10-20 parts
Equal styrene, 1-2 parts of antioxidants, 1-5 parts of abrasion resistant particles, 2-3 parts of toughener, 2-3 parts of pigment and 5-10 parts of glass fibres
Mixing, melt blending is then carried out by way of heating, is finally injected in injection molding machine and is molded, after cooling
To the plastics sprinkler head, wherein injection pressure is 60Mpa, and dwell pressure 50Mpa, the dwell time is 3-4 seconds, cooling
Time is 10 seconds, and mold temperature is maintained between 40-50 DEG C.
The preparation method for the wear-resisting landscape sprinkler that the present invention obtains, uses polystyrene and ABS as flocculating agent
It is mixed with PP and HDPE, it is made to improve the flexibility of plastics in coacervation process, make plastics that there is certain crushing resistance, separately
Outer addition antioxidant and abrasion resistant particles, so that plastics sprinkler head can be satisfied with the feature of environmental protection, safety and resistance to simultaneously
Mill property.
Specific embodiment
Below with reference to embodiment, the present invention is further described.
Embodiment 1:
The preparation method of the wear-resisting landscape sprinkler of one kind provided in this embodiment, the landscape sprinkler include plastics sprinkling
Head, the plastics sprinkler head include by weight 30 parts of PP, 20 parts of ABS, 10 parts of HDPE, 10 parts of equal styrene, 1 part it is anti-oxidant
Agent, 1 part of abrasion resistant particles, 2 parts of toughener, 2 parts of pigment and 5 parts of glass fibres,
The antioxidant includes 30 parts of sodium tripolyphosphates, 10 parts of hexamethylenetetramines, 20 parts of tert-butyls to benzene two by weight
Phenol, 5 parts of polybutadiene polyurethanes, 5 parts of potassium fluoborates and 2 parts of benzotriazole,
The abrasion resistant particles include 50 parts of aluminium oxide, 5 parts of silicon carbide, 8 parts of quartz sands, 5 parts of ocratations and 1 part by weight
Graphene,
The toughener include by weight 70 parts of ethylene octane copolymers, 10 parts of polyether sulfones, 3 parts of maleic anhydrides and 3 parts oneself
Diamines,
The pigment includes titanium dioxide, iron oxide red, iron oxide yellow, iron oxide black, carbon black, cadmium red, cadmium yellow, lead chromate yellow, oxidation
One or more of chrome green, barba hispanica, zinc oxide, zinc yellow, cobalt blue.
The preparation method of the plastics sprinkler head the following steps are included:
Step 1: antioxidant is prepared, by weight by 30 parts of sodium tripolyphosphates, 10 parts of hexamethylenetetramines, 20 parts of tert-butyls
Hydroquinone, 5 parts of polybutadiene polyurethanes, 5 parts of potassium fluoborates and 2 parts of benzotriazole are uniformly mixed, and are melted in high temperature furnace
Melt, then pulverizes after cooling up to antioxidant；
Step 2: preparation abrasion resistant particles, by weight by 50 parts of aluminium oxide, 5 parts of silicon carbide, 8 parts of quartz sands, 5 parts of ocratations
And 1 part of graphene is after mixing, is dissolved in ethanol solution, then ball grinds are up to abrasion resistant particles,
Step 3: plastics sprinkler head is prepared, by weight by 30 parts of PP, 20 parts of ABS, 10 parts of HDPE, 10 parts of equal styrene, 1 part
Antioxidant, 1 part of abrasion resistant particles, 2 parts of toughener, 2 parts of pigment and 5 parts of glass fibre mixing, then by way of heating
Melt blending is carried out, is finally injected in injection molding machine and is molded, obtains the plastics sprinkler head after cooling, wherein
Injection pressure is 60Mpa, and dwell pressure 50Mpa, the dwell time is 3-4 seconds, and cooling time is 10 seconds, and mold temperature is protected
It holds between 40-50 DEG C.
Embodiment 2:
The preparation method of the wear-resisting landscape sprinkler of one kind provided in this embodiment, substantially production method and embodiment 1 are consistent,
Its difference is that the plastics sprinkler head includes 40 parts of PP, 30 parts of ABS, 20 parts of HDPE, 20 parts of equal styrene, 2 parts by weight
Antioxidant, 5 parts of abrasion resistant particles, 3 parts of toughener, 3 parts of pigment and 10 parts of glass fibres.
Embodiment 3:
The preparation method of the wear-resisting landscape sprinkler of one kind provided in this embodiment, substantially production method and embodiment 1 are consistent,
It includes 40 parts of sodium tripolyphosphates, 15 parts of hexamethylenetetramines, 30 parts of tert-butyls that its difference, which is the antioxidant by weight,
Hydroquinone, 10 parts of polybutadiene polyurethanes, 10 parts of potassium fluoborates and 5 parts of benzotriazole.
Embodiment 4:
The preparation method of the wear-resisting landscape sprinkler of one kind provided in this embodiment, substantially production method and embodiment 1 are consistent,
It includes 60 parts of aluminium oxide, 15 parts of silicon carbide, 15 parts of quartz sands, 10 parts of tetrafluorides that its difference, which is the abrasion resistant particles by weight,
Silicon and 5 parts of graphenes.
Embodiment 5:
The preparation method of the wear-resisting landscape sprinkler of one kind provided in this embodiment, substantially production method and embodiment 1 are consistent,
Its distinguish be the toughener by weight and include 80 parts of ethylene octane copolymers, 15 parts of polyether sulfones, 5 parts of maleic anhydrides and
5 parts of hexamethylene diamines.
Claims (3)
1. a kind of preparation method of wear-resisting landscape sprinkler, the landscape sprinkler includes plastics sprinkler head, it is characterised in that:
The plastics sprinkler head includes 30-40 parts PP, 20-30 parts ABS, 10-20 parts HDPE, 10-20 parts equal styrene, 1- by weight
2 parts of antioxidants, 1-5 parts of abrasion resistant particles, 2-3 parts of toughener, 2-3 parts of pigment and 5-10 parts of glass fibres,
The antioxidant includes 30-40 parts of sodium tripolyphosphates, 10-15 parts of hexamethylenetetramines, 20-30 parts of tertiary fourths by weight
Base hydroquinone, 5-10 part polybutadiene polyurethane, 5-10 parts of potassium fluoborates and 2-5 parts of benzotriazole,
The abrasion resistant particles include 50-60 parts of aluminium oxide, 5-15 parts of silicon carbide, 8-15 parts of quartz sands, 5-10 part four by weight
Silicon fluoride and 1-5 parts of graphenes,
The preparation method of the plastics sprinkler head the following steps are included:
Step 1: antioxidant is prepared, by weight by 30-40 parts of sodium tripolyphosphates, 10-15 parts of hexamethylenetetramines, 20-30
Part tert-butyl hydroquinone, 5-10 parts of polybutadiene polyurethanes, 5-10 parts of potassium fluoborates and 2-5 parts of benzotriazole are uniformly mixed,
It is melted, is then pulverized after cooling up to antioxidant in high temperature furnace；
Step 2: preparation abrasion resistant particles, by weight by 50-60 parts of aluminium oxide, 5-15 parts of silicon carbide, 8-15 parts of quartz sands, 5-
10 parts of ocratations and 1-5 parts of graphenes after mixing, are dissolved in ethanol solution, and then ball grinds are up to abrasion resistant particles,
Step 3: plastics sprinkler head is prepared, by weight by 30-40 parts PP, 20-30 parts ABS, 10-20 parts HDPE, 10-20 parts
Equal styrene, 1-2 parts of antioxidants, 1-5 parts of abrasion resistant particles, 2-3 parts of toughener, 2-3 parts of pigment and 5-10 parts of glass fibres
Mixing, melt blending is then carried out by way of heating, is finally injected in injection molding machine and is molded, after cooling
To the plastics sprinkler head, wherein injection pressure is 60Mpa, and dwell pressure 50Mpa, the dwell time is 3-4 seconds, cooling
Time is 10 seconds, and mold temperature is maintained between 40-50 DEG C.
2. the preparation method of wear-resisting landscape sprinkler according to claim 1, it is characterised in that: the toughener is by weight
Measuring part includes 70-80 parts of ethylene octane copolymers, 10-15 parts of polyether sulfones, 3-5 parts of maleic anhydrides and 3-5 parts of hexamethylene diamines.
3. the preparation method of wear-resisting landscape sprinkler according to claim 1, it is characterised in that: the pigment includes titanium
White powder, iron oxide red, iron oxide yellow, iron oxide black, carbon black, cadmium red, cadmium yellow, lead chromate yellow, chrome oxide green, barba hispanica, zinc oxide, zinc
One or more of yellow, cobalt blue.