CN109231918B - 一种高韧性高抗渗高耐久性混凝土及其制备方法 - Google Patents
一种高韧性高抗渗高耐久性混凝土及其制备方法 Download PDFInfo
- Publication number
- CN109231918B CN109231918B CN201811198116.5A CN201811198116A CN109231918B CN 109231918 B CN109231918 B CN 109231918B CN 201811198116 A CN201811198116 A CN 201811198116A CN 109231918 B CN109231918 B CN 109231918B
- Authority
- CN
- China
- Prior art keywords
- parts
- graphene oxide
- powder
- mass
- concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (8)