CN109208354A - A kind of sub- colouring method of environment-friendly type paper mulberry of dacron - Google Patents
A kind of sub- colouring method of environment-friendly type paper mulberry of dacron Download PDFInfo
- Publication number
- CN109208354A CN109208354A CN201811237964.2A CN201811237964A CN109208354A CN 109208354 A CN109208354 A CN 109208354A CN 201811237964 A CN201811237964 A CN 201811237964A CN 109208354 A CN109208354 A CN 109208354A
- Authority
- CN
- China
- Prior art keywords
- paper mulberry
- sub
- dacron
- environment
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of sub- colouring method of environment-friendly type paper mulberry of dacron, is handled polyester fiber using paper mulberry, and entire dyeing course is added without the chemical addition agent being harmful to the human body, and belongs to the novel dyeing terylene technique of environmental protection;Simultaneously do not use high temperature, strong acid-base carries out dyeing processing to terylene, can be effectively protected paper mulberry son in antibacterial, antiviral ingredients, reach better antibacterial, fungistatic effect.
Description
Technical field
The present invention relates to textile dyestuff technical field more particularly to a kind of environment-friendly type paper mulberry dyeing sides of dacron
Method.
Background technique
Terylene is an important species in synthetic fibers, is the product name of China's polyester fiber.It is with essence to benzene
Dioctyl phthalate (PTA) or dimethyl terephthalate (DMT) (DMT) and ethylene glycol (EG) are raw material through esterification or transesterification and polycondensation reaction
Prepared by fiber-forming polymer --- polyethylene terephthalate (PET), through spinning and post-process made of fiber.Using
The morphosis that terylene made from melt spinning process is observed in microscope has circular section and without special vertical structure.
Polyester fiber has the advantages that
1. intensity is high.Staple fiber intensity is 2.6~5.7cN/dtex, and high-tenacity fiber is 5.6~8.0cN/dtex.Due to
Hygroscopicity is lower, its wet strength and dry strength is essentially identical.Impact resistant strength is 4 times higher than polyamide fibre, higher than viscose rayon
20 times.
2. elasticity is good.Elasticity can almost be restored close to wool when extending 5%~6% completely.Crease resistance is more than it
His fiber, i.e. fabric not wrinkle, good stability of the dimension.Modulus of elasticity is 22~141cN/dtex, 2~3 times higher than polyamide fibre.It washs
Synthetic fibre fabric intensity with higher and elastic recovery capability, therefore, strong durable, wash and wear.
3. heat resistance terylene be made of fiber by melt spinning process, after forming can heated fusing again again, belong to thermoplasticity
Fiber.The fusing point of terylene is relatively high, and specific heat capacity and thermal conductivity are all smaller, thus the heat resistance of polyester fiber and thermal insulation want high
A bit.It is best in synthetic fibers.
4. thermoplasticity is good, melt resistance is poor.Since terylene surface is smooth, interior molecules arrangement is close, therefore terylene is to close
At the best fabric of heat resistance in fine fabric, there is thermoplasticity, accordion-pleated skirt can be manufactured, and rivel is lasting.Meanwhile dacron
Melt resistance is poor, meets cigarette ash, Mars etc. and easily forms hole.Therefore, it should avoid contacting with cigarette butt, spark etc. as far as possible when wearing.
5. wearability is good.Wearability is only second to the best polyamide fibre of wearability, all better than other natural fibers and synthetic fibers.
6. light resistance is good.Light resistance is only second to acrylic fibers.The light resistance of dacron is preferable, sun-proof in addition to poorer than acrylic fibers
Ability surpasses natural fabric.It is especially fine in the subsequent sun-proof ability of glass, it is almost equally matched with acrylic fibers.
7. corrosion-resistant.It can bleach tolerant, oxidant, hydro carbons, ketone, oil product and inorganic acid.Resistance to diluted alkaline, be not afraid of it is mould,
But thermokalite can make its decomposition.There are also stronger anti acid alkali performance, anti-ultraviolet abilities
But because without specific dye radical on terylene strand, and polarity is smaller, so dyeing is more difficult, easily contaminates
Property is poor, and dye molecule is not easily accessible fiber.
Summary of the invention
In order to develop the dacron for being conducive to human body, the present invention provides a kind of environment-friendly type paper mulberry dye of dacron
Color method.
A kind of sub- colouring method of environment-friendly type paper mulberry of dacron, which comprises the following steps:
Step 1: the sub- raw material of paper mulberry is rinsed well with clear water, is mechanically pulverized repeatedly after drying with weight method;
Step 2: the paper mulberry crushed being added to the water, dispersing agent and dyeing auxiliaries is added, is heated to 45-50 DEG C, into
Row ultrasonic disperse, ultrasonic power 200-300W, time are 10-15 minutes;
Step 3: being added polyester fabric, carries out microwave treatment, and initial power 2500w is gradually dropped with the speed of 500w/h
Down to 500w, this power 1.5-2h is kept;
Step 4: it after polyester fabric is taken out, is rinsed with clear water and carries out 150-170 DEG C of high-temperature shaping.
Paper mulberry also known as Paper mulberry Fruit, the draw a bow to the full wooden son, tissue paper tree, paper mulberry etc., are a kind of moraceae plants.Its lead be longer than Henan,
The areas such as Hubei, Hunan, Gansu.The plant is cold in nature, sweet in flavor, has the function of kidney tonifying clearing liver, improving eyesight, diuresis, is usually used in waist and knee
The illnesss such as aching and limp, consumptive disease hectic fever due to yin, raw screen film of mesh, edema swelling.
This product is the fresh mature fruits of moraceae plants paper mulberry Broussoneria papyrifera (L.) Vent..It is dry
For fruit in oval to width egg shape, top is tapering, 2~2.5 millimeters, 1.5~2 millimeters of diameter long.Outer surface yellowish red color is to yellowish-brown
Color, it is coarse, have fine wrinkle.Side has concave rill, and the other side is significantly swelled, and is in ridge shape, and base portion has remaining carpopodium, stripping
Visible white is full of the idiosome of grease after shedding skin.Gas is weak, lightly seasoned and have greasy feeling, and old, free from admixture person red with color, sub is preferred.
Fruit is containing saponin (0.51%), vitamin B and grease.Seed oil-containing 31.7%, oil in contain unsaponifiable matter 2.67%,
Saturated fatty acid 9.0%, oleic acid 15.0%, linoleic acid 76.0%.
Preferably, in the step two, the partial size for paper mulberry being added to the water is 100-500 microns.
The sub- particle of paper mulberry is added in the present invention in the solution, and with microwave to polyester fiber processing, it is therefore an objective in strength microwave
Under concussion effect, paper mulberry is rubbed with PET fiber surface, PET fiber surface will form little groove or defect, thus
Polyester fiber is set to be easier to paint.
It is larger to the injury of polyester fiber intensity that the partial size of paper mulberry is higher than 500 microns, or even will affect polyester fiber
Textile performance;And the partial size of paper mulberry is not easy to form little groove less than 100 microns smaller to the rubbing action of PET fiber surface
Or defect.
Meanwhile rheum emodin, Chrysophanol etc. can be had the ingredient of antibacterial action under microwave action by the sub- particle of paper mulberry,
It is gradually dissolved into water, and over time, partial penetration is into polyester fiber, so that it is certain to have polyester fiber
Antibacterial, bacteriostasis property.
The power of microwave gradually decreases from big to small, and polyester fiber can be made more violent when starting friction.It is easy to form
Little groove lacks, and stage prevents the intensity of polyester fiber by too big influence based on permeating, supplemented by friction.
Preferably, the dispersing agent is ammonium lauryl sulfate.
Ammonium lauryl sulfate category mild acidulous anion surfactant.Its foaming abundancy, irritation is small, viscosity
Greatly, it easily rinses, is the primary raw material of medium-to-high grade shampoo, bath foam.
It is the peptizaiton for reinforcing paper mulberry that ammonium lauryl sulfate is added in the present invention on the one hand, on the other hand can be had
Help the dissolution of the beneficiating ingredients such as rheum emodin, Chrysophanol.
Preferably, the weight percent of the dispersing agent and dyeing auxiliaries in water is 3-8% and 0.8-1.2%.
Preferably, the exhaust process parameter are as follows: the sub- dosage of paper mulberry is 3-5%o.w.f., temperature: 55-60 DEG C, is dyed
Time: 10-15min, bath raio: 1:10-30.
Preferably, the dyeing auxiliaries is the mixture of ethylene glycol monobutyl ether and odium stearate.
It is further preferred that the weight ratio of ethylene glycol monobutyl ether and odium stearate is (5-8): 1 in the dyeing auxiliaries.
The sub- colouring method of environment-friendly type paper mulberry of dacron of the present invention, using paper mulberry to polyester fiber at
Reason, entire dyeing course are added without the chemical addition agent being harmful to the human body, and belong to the novel dyeing terylene technique of environmental protection, dyeing
Afterwards, the good color fastness, antibacterial bacteriostatic effect of polyester fiber are good;High temperature is not used, strong acid-base carries out dyeing processing to terylene, can be with
Be effectively protected paper mulberry son in antibacterial, antiviral ingredients, reach better antibacterial, fungistatic effect.
Specific embodiment
Embodiment 1
A kind of sub- colouring method of environment-friendly type paper mulberry of dacron, which comprises the following steps:
Step 1: the sub- raw material of paper mulberry is rinsed well with clear water, is mechanically pulverized repeatedly after drying with weight method;
Step 2: the paper mulberry crushed is added to the water, dispersing agent and dyeing auxiliaries is added, is heated to 48 DEG C, is surpassed
Sound dispersion, ultrasonic power 250W, time are 12 minutes;
Step 3: being added polyester fabric, carries out microwave treatment, and initial power 2500w is gradually dropped with the speed of 500w/h
Down to 500w, this power 2h is kept;
Step 4: it after polyester fabric is taken out, is rinsed with clear water and carries out 155 DEG C of high-temperature shapings.
In the step two, the partial size for paper mulberry being added to the water is 100-500 microns.
The dispersing agent is ammonium lauryl sulfate.
The weight percent of the dispersing agent and dyeing auxiliaries in water is 6% and 1.1%.
The exhaust process parameter are as follows: the sub- dosage of paper mulberry be 4%o.w.f., temperature: 58 DEG C, dyeing time: 15min,
Bath raio: 1:20.
The dyeing auxiliaries is the mixture of ethylene glycol monobutyl ether and odium stearate.
In the dyeing auxiliaries, the weight ratio of ethylene glycol monobutyl ether and odium stearate is 6:1.
Embodiment 2
A kind of sub- colouring method of environment-friendly type paper mulberry of dacron, which comprises the following steps:
Step 1: the sub- raw material of paper mulberry is rinsed well with clear water, is mechanically pulverized repeatedly after drying with weight method;
Step 2: the paper mulberry crushed is added to the water, dispersing agent and dyeing auxiliaries is added, is heated to 50 DEG C, is surpassed
Sound dispersion, ultrasonic power 300W, time are 10 minutes;
Step 3: being added polyester fabric, carries out microwave treatment, and initial power 2500w is gradually dropped with the speed of 500w/h
Down to 500w, this power 1.5h is kept;
Step 4: it after polyester fabric is taken out, is rinsed with clear water and carries out 170 DEG C of high-temperature shapings.
In the step two, the partial size for paper mulberry being added to the water is 100-500 microns.
The dispersing agent is ammonium lauryl sulfate.
The weight percent of the dispersing agent and dyeing auxiliaries in water is 8% and 0.8%.
The exhaust process parameter are as follows: the sub- dosage of paper mulberry be 3%o.w.f., temperature: 60 DEG C, dyeing time: 10min,
Bath raio: 1:10.
The dyeing auxiliaries is the mixture of ethylene glycol monobutyl ether and odium stearate.
In the dyeing auxiliaries, the weight ratio of ethylene glycol monobutyl ether and odium stearate is 5:1.
Embodiment 3
A kind of sub- colouring method of environment-friendly type paper mulberry of dacron, which comprises the following steps:
Step 1: the sub- raw material of paper mulberry is rinsed well with clear water, is mechanically pulverized repeatedly after drying with weight method;
Step 2: the paper mulberry crushed is added to the water, dispersing agent and dyeing auxiliaries is added, is heated to 45 DEG C, is surpassed
Sound dispersion, ultrasonic power 300W, time are 10 minutes;
Step 3: being added polyester fabric, carries out microwave treatment, and initial power 2500w is gradually dropped with the speed of 500w/h
Down to 500w, this power 1.8h is kept;
Step 4: it after polyester fabric is taken out, is rinsed with clear water and carries out 150 DEG C of high-temperature shapings.
In the step two, the partial size for paper mulberry being added to the water is 100-500 microns.
The dispersing agent is ammonium lauryl sulfate.
The weight percent of the dispersing agent and dyeing auxiliaries in water is 3% and 1.2%.
The exhaust process parameter are as follows: the sub- dosage of paper mulberry be 3%o.w.f., temperature: 55 DEG C, dyeing time: 12min,
Bath raio: 1:30.
The dyeing auxiliaries is the mixture of ethylene glycol monobutyl ether and odium stearate.
In the dyeing auxiliaries, the weight ratio of ethylene glycol monobutyl ether and odium stearate is 8:1.
Comparative example 1
By the dyeing auxiliaries removal in embodiment 1, remaining proportion and colouring method are constant.
Comparative example 2
By the ethylene glycol monobutyl ether removal in the dyeing auxiliaries in embodiment 1, remaining proportion and colouring method are constant.
Comparative example 3
By the odium stearate removal in the dyeing auxiliaries in embodiment 1, remaining proportion and colouring method are constant.
Color fastness detection, specific testing number are carried out to the terylene sample of the dyeing of embodiment 1-3 and comparative example 1-3 below
According to being shown in Table 1.
Table 1: the color fastness testing result of terylene sample;
Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 | Comparative example 3 | |
WASHING COLOR FASTNESS | 4 grades | 4 grades | 4 grades | 2-2.5 grade | 3 grades | 2-2.5 grade |
Dry fastness | 4 grades | 4 grades | 4 grades | 2.5-3 grade | 3 grades | 2.5-3 grade |
Fastness to wet rubbing | 4 grades | 4 grades | 4 grades | 2.5-3 grade | 3 grades | 2.5-3 grade |
Through detecting, the terylene sample of embodiment 1-3 and comparative example 1-3 in the present invention, to Candida albicans, Escherichia coli
Reach 90% or more with the bacteriostasis rate of staphylococcus aureus.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of sub- colouring method of environment-friendly type paper mulberry of dacron, which comprises the following steps:
Step 1: the sub- raw material of paper mulberry is rinsed well with clear water, is mechanically pulverized repeatedly after drying with weight method;
Step 2: the paper mulberry crushed is added to the water, dispersing agent and dyeing auxiliaries is added, is heated to 45-50 DEG C, is surpassed
Sound dispersion, ultrasonic power 200-300W, time are 10-15 minutes;
Step 3: being added polyester fabric, carries out microwave treatment, and initial power 2500w is gradually decrease to the speed of 500w/h
500w keeps this power 1.5-2h;
Step 4: it after polyester fabric is taken out, is rinsed with clear water and carries out 150-170 DEG C of high-temperature shaping.
2. the sub- colouring method of environment-friendly type paper mulberry of dacron as described in claim 1, which is characterized in that the step two
In, the partial size for paper mulberry being added to the water is 100-500 microns.
3. the sub- colouring method of environment-friendly type paper mulberry of dacron as described in claim 1, which is characterized in that the step two
In, the weight percent of the dispersing agent and dyeing auxiliaries in water is 3-8% and 0.8-1.2%.
4. the sub- colouring method of environment-friendly type paper mulberry of dacron as described in claim 1, which is characterized in that the dispersing agent
For ammonium lauryl sulfate.
5. the sub- colouring method of environment-friendly type paper mulberry of dacron as described in claim 1, which is characterized in that the dipper
Skill parameter are as follows: the sub- dosage of paper mulberry be 3-5%o.w.f., temperature: 55-60 DEG C, dyeing time: 10-15min, bath raio: 1:10-30.
6. the sub- colouring method of environment-friendly type paper mulberry of dacron as described in claim 1, which is characterized in that the dyeing auxiliaries
For the mixture of ethylene glycol monobutyl ether and odium stearate.
7. the sub- colouring method of environment-friendly type paper mulberry of dacron as claimed in claim 6, which is characterized in that the dyeing auxiliaries
In, the weight ratio of ethylene glycol monobutyl ether and odium stearate is (5-8): 1.