CN109207083B - 一种热弯膜及其制备方法 - Google Patents
一种热弯膜及其制备方法 Download PDFInfo
- Publication number
- CN109207083B CN109207083B CN201810996494.1A CN201810996494A CN109207083B CN 109207083 B CN109207083 B CN 109207083B CN 201810996494 A CN201810996494 A CN 201810996494A CN 109207083 B CN109207083 B CN 109207083B
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- glue
- film
- pet resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种热弯膜，其中该热弯膜从下到上包括剥离层、PET树脂膜层和硬化膜层，硬化层由UV胶水固化而成，UV胶水包括如下重量份的原料：金属离子交联聚合物、纳米蛭石和低密度聚乙烯，其中金属离子交联聚合物和纳米蛭石的重量和与低密度聚乙烯重量之比为3‑5:1。本发明通过将改进热弯膜的硬化层的组成，金属离子交联聚合物、低密度聚乙烯和纳米蛭石巧妙结合，能够获得硬度和拉伸性能均能兼顾的热弯膜。
Description
技术领域
本发明涉及膜技术领域，具体涉及一种热弯膜及其制备方法。
背景技术
现有的保护膜被广泛应用于具有显示屏的电子产品上，如电脑显示屏、PAD显示屏和手机屏幕等等。热弯膜是一种立体产品膜，能够对立体显示屏进行保护。
热弯膜需要满足耐磨性和抗划性，即需要满足较高的表面硬度，同时还需要满足具有很好的柔韧性，即能够易于拉伸成型，如此才能应用在各种2.5D、3D、4D等产品的立体造型上。而表面硬度和拉伸性能二者本身是矛盾的，即表面硬度大则拉伸性能小，反之亦反。因此需要一种表面硬度和拉伸性能兼顾的热弯膜以满足实际需求。
发明内容
本发明目的在于提供一种热弯膜及其制备方法，解决现有热弯膜无法兼顾表面硬度和拉伸性能的问题。
本发明通过下述技术方案实现：
一种热弯膜，其中该热弯膜从下到上包括剥离层、PET树脂膜层和硬化膜层，硬化层由UV胶水固化而成，UV胶水包括如下重量份的原料：金属离子交联聚合物、纳米蛭石和低密度聚乙烯，其中金属离子交联聚合物和纳米蛭石的重量和与低密度聚乙烯重量之比为3-5:1。
UV胶水包括如下重量份的原料：50-60份金属离子交联聚合物、12-30份低密度聚乙烯、5-10份纳米蛭石。
金属离子交联聚合物以甲基丙烯酸酯型聚合物或者丙烯酸酯型聚合物为骨架链。
金属离子为碱金属离子、锌离子、镁离子、钙离子、铝离子中的一种或多种。
剥离层为氟塑离型膜层。
纳米蛭石的粒径为1-20nm。
UV胶水还包括1-5份光引发剂、1-5份UV吸收剂。
如前所述的热弯膜的制备方法，包括以下步骤：
(1)、将UV胶水在紫外光条件下固化在PET树脂膜层上得到固化有硬化层的PET树脂膜层；
(2)、将固化有硬化层的PET树脂膜层和剥离层叠放在一起并放置在具有弧度的模具上进行加热处理。
UV胶水涂覆在PET树脂膜层上的厚度为0.2-0.3mm。
紫外光辐照距离为10-20cm，辐照时间为10-20s。
本发明通过特定配比的金属离子交联聚合物、低密度聚乙烯和纳米蛭石之间的协同作用，能够使得硬化层既具有硬度又能够具有一定的拉伸性能：金属离子交联聚合物为硬化层提供适当的硬度，而纳米蛭石能够和金属离子交联聚合物的金属离子之间发生协同作用提高硬化层的硬度，即纳米蛭石和金属离子之间发生络合而使得纳米蛭石和金属离子交联聚合物结合在一起，提高了硬化层表面的硬度，即耐磨性和抗划性，低密度聚乙烯能够提供适当的韧性赋予硬化层适当的拉伸性能。
本发明中纳米蛭石的粒径为1-20nm。当纳米蛭石的粒径在1-20mm范围内时，对热弯膜的透明度影响不大，且能够和金属离子交联聚合物具有更好的结合作用。
本发明中光引发剂为紫外光固化领域常用的引发剂，如烷基苯酮类引发剂等。UV吸收剂为紫外光固化领域常用的吸收剂，如2-羟基-4-正辛氧基二苯甲酮等。
另外，本发明中金属离子交联聚合物的制备方法为现有技术，如金属离子交联型丙烯酸酯乳液聚合物等。
本发明与现有技术相比，具有如下的优点和有益效果：
本发明通过将改进热弯膜的硬化层的组成，金属离子交联聚合物、低密度聚乙烯和纳米蛭石巧妙结合，能够获得硬度和拉伸性能均能兼顾的热弯膜。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明白，下面结合实施例，对本发明作进一步的详细说明，本发明的示意性实施方式及其说明仅用于解释本发明，并不作为对本发明的限定。
实施例1
一种热弯膜，其中该热弯膜从下到上包括剥离层、PET树脂膜层和硬化膜层，硬化层由UV胶水固化而成，UV胶水包括如下重量份的原料：50份铝离子交联型丙烯酸酯聚合物、20份低密度聚乙烯、10份纳米蛭石、2份光引发剂、5份UV吸收剂。
实施例2
一种热弯膜，其中该热弯膜从下到上包括剥离层、PET树脂膜层和硬化膜层，硬化层由UV胶水固化而成，UV胶水包括如下重量份的原料：50份钙离子交联型丙烯酸酯聚合物、20份低密度聚乙烯、10份纳米蛭石、2份光引发剂、5份UV吸收剂。
实施例3
一种热弯膜，其中该热弯膜从下到上包括剥离层、PET树脂膜层和硬化膜层，硬化层由UV胶水固化而成，UV胶水包括如下重量份的原料：50份镁离子交联型丙烯酸酯聚合物、20份低密度聚乙烯、10份纳米蛭石、2份光引发剂、5份UV吸收剂。
实施例4
一种热弯膜，其中该热弯膜从下到上包括剥离层、PET树脂膜层和硬化膜层，硬化层由UV胶水固化而成，UV胶水包括如下重量份的原料：55份钠离子交联型丙烯酸酯聚合物、12份低密度聚乙烯、5份纳米蛭石、2份光引发剂、5份UV吸收剂。
实施例5
一种热弯膜，其中该热弯膜从下到上包括剥离层、PET树脂膜层和硬化膜层，硬化层由UV胶水固化而成，UV胶水包括如下重量份的原料：60份钾离子交联型丙烯酸酯聚合物、20份低密度聚乙烯、10份纳米蛭石、2份光引发剂、5份UV吸收剂。
对比例1
和实施例1类似，区别在于：UV胶水包括如下重量份的原料：60份铝离子交联型丙烯酸酯聚合物、30份低密度聚乙烯、2份光引发剂、5份UV吸收剂。
对比例2：
和实施例1类似，区别在于：UV胶水包括如下重量份的原料：60份铝离子交联型丙烯酸酯聚合物、10份纳米蛭石、2份光引发剂、5份UV吸收剂。
对比例3：
和实施例1类似，区别在于：UV胶水包括如下重量份的原料：20份金属离子交联聚合物、60份低密度聚乙烯、40份纳米蛭石、1-5份光引发剂、1-5份UV吸收剂。
如前所述的热弯膜的制备方法，包括以下步骤：
(1)、将UV胶水在紫外光条件下固化在PET树脂膜层上得到固化有硬化层的PET树脂膜层；
(2)、将固化有硬化层的PET树脂膜层和剥离层叠放在一起并放置在具有弧度的模具上进行加热处理。
UV胶水涂覆在PET树脂膜层上的厚度为0.2-0.3mm。
紫外光辐照距离为10-20cm，辐照时间为10-20s。实施固化时可在1000W高压汞灯下进行。
对上述实施例1-5按照上述相同的制备方法制备得到热弯膜后进行硬度和拉伸性能测试，获得如下数据：
从上表可看出，本发明的制备的热弯膜能够兼顾硬度和拉伸性能。
以上所述的具体实施方式，对本发明的目的、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施方式而已，并不用于限定本发明的保护范围，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (9)
1.一种热弯膜，其中该热弯膜从下到上包括剥离层、PET树脂膜层和硬化层，其特征在于，硬化层由UV胶水固化而成，UV胶水包括如下重量份的原料：金属离子交联聚合物50-60份、纳米蛭石5-10份和低密度聚乙烯12-30份，其中金属离子交联聚合物和纳米蛭石的重量与低密度聚乙烯重量之比为3-5:1。
2.根据权利要求1所述的热弯膜，其特征在于，金属离子交联聚合物以甲基丙烯酸酯型聚合物或者丙烯酸酯型聚合物为骨架链。
3.根据权利要求1所述的热弯膜，其特征在于，金属离子为碱金属离子、锌离子、镁离子、钙离子、铝离子中的一种或多种。
4.根据权利要求1所述的热弯膜，其特征在于，剥离层为氟塑离型膜层。
5.根据权利要求1所述的热弯膜，其特征在于，纳米蛭石的粒径为1-20nm。
6.根据权利要求1所述的热弯膜，其特征在于，以重量份计，UV胶水还包括1-5份光引发剂、1-5份UV吸收剂。
7.如权利要求1-5任一项所述的热弯膜的制备方法，其特征在于，包括以下步骤：
（1）、将UV胶水在紫外光条件下固化在PET树脂膜层上得到固化有硬化层的PET树脂膜层；
（2）、将固化有硬化层的PET树脂膜层和剥离层叠放在一起并放置在具有弧度的模具上进行加热处理。
8.根据权利要求7所述的制备方法，其特征在于，UV胶水涂覆在PET树脂膜层上的厚度为0.2-0.3mm。
9.根据权利要求7所述的制备方法，其特征在于，紫外光辐照距离为10-20cm，辐照时间为10-20s。