CN109181394A - A kind of water-based industrial paint multifunctional assistant - Google Patents
A kind of water-based industrial paint multifunctional assistant Download PDFInfo
- Publication number
- CN109181394A CN109181394A CN201810769341.3A CN201810769341A CN109181394A CN 109181394 A CN109181394 A CN 109181394A CN 201810769341 A CN201810769341 A CN 201810769341A CN 109181394 A CN109181394 A CN 109181394A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- water
- weight
- industrial paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of water-based industrial paint multifunctional assistant, is related to industrial paint production technical field.It is made of the raw material of following parts by weight: 390-410 parts of deionized water, 3-7 parts of thickener, 45-55 parts of propylene glycol, 25-35 parts of aqueous acrylic emulsion, 45-55 parts of defoaming agent, 90-110 parts of dispersing agent, 90-110 parts of wetting agent, 8-12 parts of regulator of ph value, anti-90-110 parts of flash rusting agent, 35-45 parts of film forming agent, 5-11 parts of anti-corrosive aids.Wherein ph value regulator is made of the raw material of following parts by weight: 65-80 parts of sodium carbonate, 10-15 parts of sodium tripolyphosphate, 7-13 parts of calgon, 1-5 parts of sodium sulfite, 3-5 parts of magnesium sulfate, 10-15 parts of ammonium sulfate.Water-based industrial paint of the invention can simplify the production technology of water paint and water-based industrial paint with multifunctional assistant, increase substantially production efficiency, reduce production cost.
Description
Technical field
The present invention relates to a kind of water-based industrial paint multifunctional assistants, are related to coating material production processing technique field.
Background technique
During producing water paint and water-based industrial paint, the function of adding numerous kinds into product is needed to help
Agent, such as thickener, dispersing agent, wetting agent, ph value regulator, film forming agent, anticorrosion and bactericidal agent, thus lead to existing aqueous painting
Material and water-based industrial paint production technology it is extremely complex, production efficiency is low, and equipment investment is big, the product cost produced compared with
Height, product quality are also not sufficiently stable.
Summary of the invention
In order to overcome the above-mentioned technical problem in the presence of the prior art, the purpose of the present invention is to provide a kind of aqueous works
Industry paint multifunctional assistant increases substantially production efficiency to simplify the production technology of water paint and water-based industrial paint, reduces
Production cost.
To achieve the above object, the invention adopts the following technical scheme:
A kind of water-based industrial paint multifunctional assistant, is made of the raw material of following parts by weight:
390-410 parts of deionized water,
3-7 parts of thickener,
45-55 parts of propylene glycol,
25-35 parts of aqueous acrylic emulsion,
45-55 parts of defoaming agent,
90-110 parts of dispersing agent,
90-110 parts of wetting agent,
8-12 parts of regulator of ph value,
Anti- 90-110 parts of flash rusting agent,
35-45 parts of film forming agent,
5-11 parts of anti-corrosive aids.
Preferably, a kind of water-based industrial paint multifunctional assistant of the invention, is made of the raw material of following parts by weight:
400 parts of deionized water,
5 parts of thickener,
50 parts of propylene glycol,
30 parts of aqueous acrylic emulsion,
50 parts of defoaming agent,
100 parts of dispersing agent,
100 parts of wetting agent,
10 parts of ph value regulator,
110 parts of anti-flash rusting agent,
40 parts of film forming agent,
10 parts of anti-corrosive aids.
Preferably, ph value regulator described in a kind of water-based industrial paint multifunctional assistant of the invention is by following parts by weight
Raw material is made:
65-80 parts by weight of sodium carbonate,
10-15 parts by weight of sodium tripolyphosphate,
7-13 parts by weight of calgon,
1-5 parts by weight of sodium sulfite
3-5 parts of magnesium sulfate
10-15 parts of ammonium sulfate.
The preparation step of water-based industrial paint multifunctional assistant of the invention is as follows:
1) deionized water of proportion parts by weight, thickener, propylene glycol, water, are sequentially added into dosing apparatus such as tempering tank
Then property acrylic emulsion, defoaming agent, dispersing agent, warming while stirring are stirred 0.5 hour to 75 DEG C;
2), keeping temperature is 75 DEG C, sequentially adds wetting agent, ph value regulator, anti-flash rusting agent, film forming agent, anti-corrosive aids,
It is stirred 2 hours.
Wherein the ph value regulator is only needed according to composition of raw materials feeding mixed configuration.
Beneficial effects of the present invention are mainly manifested in:
Due to the technique processing proportion for not needing individually to carry out various auxiliary agents during coating material production, but directly add
Enter the mode of multifunctional assistant of the invention, a kind of water-based industrial paint of the invention can simplify water paint with multifunctional assistant
And the production technology of water-based industrial paint, production efficiency is increased substantially, production cost is reduced.
Specific embodiment
Below with reference to embodiment, the present invention is described in detail.But embodiment content is only to this hair
Bright example and explanation, affiliated those skilled in the art do various repair to described specific embodiment
Change or supplement or be substituted in a similar manner, as long as it does not deviate from the concept of invention or surmounts defined in the claims
Range is within the scope of protection of the invention.
Embodiment 1
A kind of water-based industrial paint multifunctional assistant, is made of the raw material of following parts by weight:
400 parts of deionized water,
5 parts of thickener,
50 parts of propylene glycol,
30 parts of aqueous acrylic emulsion,
50 parts of defoaming agent,
100 parts of dispersing agent,
100 parts of wetting agent,
10 parts of ph value regulator,
110 parts of anti-flash rusting agent,
40 parts of film forming agent,
10 parts of anti-corrosive aids.
Wherein, ph value regulator is made of the raw material of following parts by weight:
70 parts of sodium carbonate,
10 parts of sodium tripolyphosphate,
7 parts of calgon,
1 part of sodium sulfite
3 parts of magnesium sulfate
10 parts of ammonium sulfate.
The preparation step of water-based industrial paint multifunctional assistant of the invention is as follows:
1) deionized water of proportion parts by weight, thickener, propylene glycol, water, are sequentially added into dosing apparatus such as tempering tank
Then property acrylic emulsion, defoaming agent, dispersing agent, warming while stirring are stirred 0.5 hour to 75 DEG C;
2), keeping temperature is 75 DEG C, sequentially adds wetting agent, ph value regulator, anti-flash rusting agent, film forming agent, anti-corrosive aids,
It is stirred 2 hours.
Wherein the ph value regulator is only needed according to composition of raw materials feeding mixed configuration.
Embodiment 2
A kind of water-based industrial paint multifunctional assistant, is made of the raw material of following parts by weight:
410 parts of deionized water,
7 parts of thickener,
45 parts of propylene glycol,
35 parts of aqueous acrylic emulsion,
55 parts of defoaming agent,
110 parts of dispersing agent,
110 parts of wetting agent,
12 parts of ph value regulator,
110 parts of anti-flash rusting agent,
45 parts of film forming agent,
8 parts of anti-corrosive aids.
Wherein, ph value regulator is made of the raw material of following parts by weight:
65 parts by weight of sodium carbonate,
13 parts by weight of sodium tripolyphosphate,
10 parts by weight of calgon,
3 parts by weight of sodium sulfite
4 parts of magnesium sulfate
15 parts of ammonium sulfate.
The preparation step of above-mentioned water-based industrial paint multifunctional assistant is as follows:
1) deionized water of proportion parts by weight, thickener, propylene glycol, water, are sequentially added into dosing apparatus such as tempering tank
Then property acrylic emulsion, defoaming agent, dispersing agent, warming while stirring are stirred 0.5 hour to 75 DEG C;
2), keeping temperature is 75 DEG C, sequentially adds wetting agent, ph value regulator, anti-flash rusting agent, film forming agent, anti-corrosive aids,
It is stirred 2 hours.
Wherein the ph value regulator is only needed according to composition of raw materials feeding mixed configuration.
Embodiment 3
A kind of water-based industrial paint multifunctional assistant, is made of the raw material of following parts by weight:
400 parts of deionized water,
6 parts of thickener,
45 parts of propylene glycol,
35 parts of aqueous acrylic emulsion,
45 parts of defoaming agent,
100 parts of dispersing agent,
100 parts of wetting agent,
10 parts of ph value regulator,
100 parts of anti-flash rusting agent,
45 parts of film forming agent,
10 parts of anti-corrosive aids.
Wherein, ph value regulator is made of the raw material of following parts by weight:
80 parts by weight of sodium carbonate,
13 parts by weight of sodium tripolyphosphate,
10 parts by weight of calgon,
3 parts by weight of sodium sulfite
4 parts of magnesium sulfate
15 parts of ammonium sulfate.
The preparation step of above-mentioned water-based industrial paint multifunctional assistant is as follows:
1) deionized water of proportion parts by weight, thickener, propylene glycol, water, are sequentially added into dosing apparatus such as tempering tank
Then property acrylic emulsion, defoaming agent, dispersing agent, warming while stirring are stirred 0.5 hour to 75 DEG C;
2), keeping temperature is 75 DEG C, sequentially adds wetting agent, ph value regulator, anti-flash rusting agent, film forming agent, anti-corrosive aids,
It is stirred 2 hours.
Wherein the ph value regulator is only needed according to composition of raw materials feeding mixed configuration.
Claims (3)
1. a kind of water-based industrial paint multifunctional assistant, it is characterised in that: be made of the raw material of following parts by weight:
390-410 parts of deionized water,
3-7 parts of thickener,
45-55 parts of propylene glycol,
25-35 parts of aqueous acrylic emulsion,
45-55 parts of defoaming agent,
90-110 parts of dispersing agent,
90-110 parts of wetting agent,
8-12 parts of regulator of ph value,
Anti- 90-110 parts of flash rusting agent,
35-45 parts of film forming agent,
5-11 parts of anti-corrosive aids.
2. a kind of water-based industrial paint multifunctional assistant as described in claim 1, which is characterized in that by the original of following parts by weight
Material is made:
400 parts of deionized water,
5 parts of thickener,
50 parts of propylene glycol,
30 parts of aqueous acrylic emulsion,
50 parts of defoaming agent,
100 parts of dispersing agent,
100 parts of wetting agent,
10 parts of ph value regulator,
110 parts of anti-flash rusting agent,
40 parts of film forming agent,
10 parts of anti-corrosive aids.
3. a kind of water-based industrial paint multifunctional assistant as described in claim 1, which is characterized in that the ph value regulator by
The raw material of following parts by weight is made: 65-80 parts by weight of sodium carbonate, 10-15 parts by weight of sodium tripolyphosphate, calgon 7-
13 parts by weight, 1-5 parts by weight of sodium sulfite, 3-5 parts of magnesium sulfate, 10-15 parts of ammonium sulfate.