CN108930093A - A kind of composite fibre nonwoven cloth operation pad towel and preparation method thereof - Google Patents
A kind of composite fibre nonwoven cloth operation pad towel and preparation method thereof Download PDFInfo
- Publication number
- CN108930093A CN108930093A CN201810846439.4A CN201810846439A CN108930093A CN 108930093 A CN108930093 A CN 108930093A CN 201810846439 A CN201810846439 A CN 201810846439A CN 108930093 A CN108930093 A CN 108930093A
- Authority
- CN
- China
- Prior art keywords
- collagen
- preparation
- modified polypropylene
- polypropylene fibre
- operation pad
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of composite fibre nonwoven cloth operation pad towel and preparation method thereof, are related to field of nonwoven fabric technology, are made of the fiber of following weight percent: wood pulp cellulose 40-60%, collagen-modified polypropylene fibre 40-60%;Preparation method includes the preparation of collagen-modified polypropylene fibre, thick shredding, mixing, smart shredding, combing, networking, spun lacing reinforcing, drying, processing.Networking is uniform between wood pulp cellulose of the present invention and collagen-modified polypropylene fibre, it will be remixed after wood pulp cellulose and collagen-modified polypropylene fibre respectively thick shredding, smart shredding, combing, networking, networking is combed again, improve the uniformity of the two mixing, it is reinforced using spun lacing, the good hygroscopicity of wood pulp cellulose and modified polypropylene fiber, it is good that twining between the two connects effect, the non-woven fabrics prepared has good water imbibition, antistatic, and it is soft, ventilative, thickness is big, light soft, dry and comfortable moisture-inhibiting, improves its service performance.
Description
Technical field
The present invention relates to field of nonwoven fabric technology more particularly to a kind of composite fibre nonwoven cloth operation pad towel and its preparation sides
Method.
Background technique
Non-woven fabrics is also known as non-woven cloth, is a kind of fabric for not needing spinning and weaving and being formed, only by textile staple
Or long filament is oriented or randomizing, forms fibre net structure, then using the methods of mechanical, hot sticky or chemical reinforcing and
At.Non-woven fabrics is widely used in the industries such as medical treatment, health, including operating coat, protective garment, disinfection infantees, mask, diaper, sanitary napkin
Deng being mostly using made of non-woven fabrics.
Currently, the three big fibers for nonwoven production include polypropylene, polyester and viscose rayon.Wherein polypropylene is it
In with fastest developing speed, proportion highest, the advantage is that: Young's modulus is high, elastic recovery is good, easy to wash easily dry, dimensionally stable
Property is good, intensity is high, heat-resist, wearability is good.But the disadvantage of polypropylene non-woven fabric is that hydrophily is too poor, moisture pick-up properties
It is bad, and skin-friendly is not very comfortably, to be used for medical and hygiene article, absorbency is poor, and comfort is insufficient, is easy to produce electrostatic
Phenomenon and by stain.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of composite fibre nonwoven cloth operation pad towel and its
Preparation method is that wood pulp cellulose and collagen-modified polypropylene fibre compounding are prepared non-woven fabrics using spun lacing reinforcing, this two
Between kind of fiber networking uniformly, twine and connect that effect is good, the non-woven fabrics prepared has good water imbibition, antistatic and soft, thoroughly
Gas, thickness is big, light soft, dry and comfortable moisture-inhibiting.
A kind of composite fibre nonwoven cloth operation pad towel proposed by the present invention, is made of the fiber of following weight percent: wood
Pulp fibres 40-60%, collagen-modified polypropylene fibre 40-60%.
The invention also provides the preparation methods of above-mentioned composite fibre nonwoven cloth operation pad towel, comprising the following steps:
The preparation of S1, collagen-modified polypropylene fibre: polypropylene, maleic anhydride and cumyl peroxide are mixed
It closes, it is dry, it is added in double screw extruder, melt blending, extruding pelletization, obtains modified polypropene pellet;By modified polypropene
Pellet, which is added in melt spinning machine, carries out melting extrusion, then drawn machine carries out spinning drawing, obtains polypropylene fibre;By polypropylene
Fiber is placed in tea polyphenols aqueous solution, is stirred to react, and is taken out, dry, obtains tea polyphenols modified polypropylene fiber;Tea polyphenols are modified
Polypropylene fibre is placed in collagen aqueous solution, is stirred to react, and is taken out, dry, obtains collagen-modified polypropylene fibre;
S2, thick shredding: wood pulp cellulose and collagen-modified polypropylene fibre are put into respectively in opener and slightly opened
Pine;
S3, mixing, smart shredding: the wood pulp cellulose handled through thick shredding and collagen-modified polypropylene fibre are added to
It is mixed in cotton blender machine, is then transferred in opener and carries out smart shredding;
S4, combing, networking: it carries out the composite fibre feeding carding machine after smart shredding to be combed into web, by web
It is combed again, networking;
S5, spun lacing are reinforced: being carried out spun lacing to web and reinforced to form non-woven fabrics base fabric;
S6, drying, processing: by non-woven fabrics base fabric drying, winding, be processed into operation pad towel to get.
Preferably, in S1, the weight ratio of polypropylene, maleic anhydride and cumyl peroxide is 100:3-6:0.5-1.5.
Preferably, in S1, the draw ratio of spinning traction is 4-7 times, spinning speed 800-1200m/min.
Preferably, in S1, polypropylene fibre is placed in 7-15% tea polyphenols aqueous solution, is stirred to react at 40-50 DEG C
2-4h。
Preferably, in S1, polypropylene fibre is placed in tea polyphenols aqueous solution, sodium hypophosphite is additionally added, is stirred to react;
Preferably, the additional amount of sodium hypophosphite is the 3-5% of tea polyphenols aqueous solution total weight.
Preferably, in S1, tea polyphenols modified polypropylene fiber is placed in 5-10% collagen aqueous solution, in 40-45
DEG C it is stirred to react 2-4h.
Preferably, in S5, spun lacing reinforcing is carried out to web using 6 type high pressure jet heads, spun lacing pressure is respectively set as
30-50bar、80-100bar、140-150bar、110-130bar、90-110bar、20-40bar。
The utility model has the advantages that a kind of composite fibre nonwoven cloth operation pad towel disclosed by the invention, is using wood pulp cellulose and collagen
What protein modified polypropylene fibre was mixed with, wherein containing hydroxyl, a small amount of carboxyl and aldehyde radical in wood pulp cellulose, have only
Special absorbability and imbibition ability and superior soft, antistatic performance, in collagen-modified polypropylene fibre due to
Contain on collagen there are many polar group carboxyl, amino, hydroxyl etc., it is affine with water height, it is easy to which that adsorbed water molecule has
Preferable hydrophily, and wearability, elasticity and obdurability are good, networking is uniform between this two kinds of fibers, by wood pulp cellulose and collagen
Protein modified polypropylene fibre remixes after thick shredding respectively, smart shredding, combing, networking, then combs networking, both improves mixing
Uniformity, reinforced using spun lacing, the good hygroscopicity of wood pulp cellulose and modified polypropylene fiber, twining between the two connects effect
Good, the non-woven fabrics prepared has good water imbibition, antistatic and soft, ventilative, and thickness is big, light soft, dry and comfortable
It is wet, improve its service performance.
In collagen-modified polypropylene fibre preparation, polypropylene and maleic anhydride are first subjected to melt blending, in peroxide
Under the action of changing diisopropylbenzene (DIPB), maleic anhydride is grafted on polypropylene, is obtained surface through melt spinning and is contained the poly- of anhydride group
Tacryl places it in tea polyphenols solution, and acid anhydrides can occur hydrolysis and react with the phenolic hydroxyl group on tea polyphenols, and secondary phosphorous
The presence of sour sodium can speed up the progress of reaction, and the introducing of tea polyphenols can assign the good convergence of polypropylene fibre, hemostasis, suppression
Bacterium, anti-inflammatory performance, then be dipped in collagen aqueous solution, tea polyphenols can pass through hydrophobic bond and multiple spot hydrogen bond and collagen
Association reaction occurs for albumen, to be grafted on polypropylene fibre, significantly improve the hydrophilic of polypropylene fibre, hygroscopicity and
Skin-friendly can absorb rapidly the liquid flowed out in operation, avoid cross contamination.
Specific embodiment
In the following, technical solution of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of composite fibre nonwoven cloth operation pad towel proposed by the present invention, is made of the fiber of following weight percent: wood
Pulp fibres 40%, collagen-modified polypropylene fibre 60%.
The invention also provides the preparation methods of above-mentioned composite fibre nonwoven cloth operation pad towel, comprising the following steps:
The preparation of S1, collagen-modified polypropylene fibre: by polypropylene, maleic anhydride and cumyl peroxide according to
The weight ratio of 100:3:0.5 mixes, dry, is added in double screw extruder, melt blending, extruding pelletization, must be modified poly- third
Alkene pellet;Modified polypropene pellet is added in melt spinning machine and carries out melting extrusion, then drawn machine carries out spinning drawing, leads
It stretches than being 4 times, spinning speed 800m/min obtains polypropylene fibre;Polypropylene fibre is placed in 7% tea polyphenols aqueous solution,
It is stirred to react 2h at 40 DEG C, takes out, it is dry, obtain tea polyphenols modified polypropylene fiber;Tea polyphenols modified polypropylene fiber is set
In 10% collagen aqueous solution, it is stirred to react 4h at 45 DEG C, is taken out, it is dry, obtain collagen-modified polypropylene fibre;
S2, thick shredding: wood pulp cellulose and collagen-modified polypropylene fibre are put into respectively in opener and slightly opened
Pine;
S3, mixing, smart shredding: the wood pulp cellulose handled through thick shredding and collagen-modified polypropylene fibre are added to
It is mixed in cotton blender machine, is then transferred in opener and carries out smart shredding;
S4, combing, networking: it carries out the composite fibre feeding carding machine after smart shredding to be combed into web, by web
It is combed again, networking;
S5, spun lacing are reinforced: being carried out spun lacing to web using 6 type high pressure jet heads and reinforced to form non-woven fabrics base fabric, spun lacing
Pressure is respectively set as 30bar, 80bar, 140bar, 110bar, 90bar, 20bar;
S6, drying, processing: by non-woven fabrics base fabric drying, winding, be processed into operation pad towel to get.
Embodiment 2
A kind of composite fibre nonwoven cloth operation pad towel proposed by the present invention, is made of the fiber of following weight percent: wood
Pulp fibres 60%, collagen-modified polypropylene fibre 40%.
The invention also provides the preparation methods of above-mentioned composite fibre nonwoven cloth operation pad towel, comprising the following steps:
The preparation of S1, collagen-modified polypropylene fibre: by polypropylene, maleic anhydride and cumyl peroxide according to
The weight ratio of 100:6:1.5 mixes, dry, is added in double screw extruder, melt blending, extruding pelletization, must be modified poly- third
Alkene pellet;Modified polypropene pellet is added in melt spinning machine and carries out melting extrusion, then drawn machine carries out spinning drawing, leads
It stretches than being 7 times, spinning speed 1200m/min obtains polypropylene fibre;Polypropylene fibre is placed in 15% tea polyphenols aqueous solution
In, the sodium hypophosphite for accounting for total solution weight 5% is added, 4h is stirred to react at 50 DEG C, takes out, it is dry, it is modified to obtain tea polyphenols
Polypropylene fibre;Tea polyphenols modified polypropylene fiber is placed in 5% collagen aqueous solution, 4h is stirred to react at 45 DEG C, takes
Out, dry, obtain collagen-modified polypropylene fibre;
S2, thick shredding: wood pulp cellulose and collagen-modified polypropylene fibre are put into respectively in opener and slightly opened
Pine;
S3, mixing, smart shredding: the wood pulp cellulose handled through thick shredding and collagen-modified polypropylene fibre are added to
It is mixed in cotton blender machine, is then transferred in opener and carries out smart shredding;
S4, combing, networking: it carries out the composite fibre feeding carding machine after smart shredding to be combed into web, by web
It is combed again, networking;
S5, spun lacing are reinforced: being carried out spun lacing to web using 6 type high pressure jet heads and reinforced to form non-woven fabrics base fabric, spun lacing
Pressure is respectively set as 50bar, 100bar, 150bar, 130bar, 110bar, 40bar;
S6, drying, processing: by non-woven fabrics base fabric drying, winding, be processed into operation pad towel to get.
Embodiment 3
A kind of composite fibre nonwoven cloth operation pad towel proposed by the present invention, is made of the fiber of following weight percent: wood
Pulp fibres 50%, collagen-modified polypropylene fibre 50%.
The invention also provides the preparation methods of above-mentioned composite fibre nonwoven cloth operation pad towel, comprising the following steps:
The preparation of S1, collagen-modified polypropylene fibre: by polypropylene, maleic anhydride and cumyl peroxide according to
The weight ratio of 100:4:0.7 mixes, dry, is added in double screw extruder, melt blending, extruding pelletization, must be modified poly- third
Alkene pellet;Modified polypropene pellet is added in melt spinning machine and carries out melting extrusion, then drawn machine carries out spinning drawing, leads
It stretches than being 5 times, spinning speed 900m/min obtains polypropylene fibre;Polypropylene fibre is placed in 10% tea polyphenols aqueous solution,
The sodium hypophosphite for accounting for total solution weight 3.5% is added, 2.5h is stirred to react at 40 DEG C, takes out, it is dry, it is modified to obtain tea polyphenols
Polypropylene fibre;Tea polyphenols modified polypropylene fiber is placed in 7% collagen aqueous solution, 3h is stirred to react at 40 DEG C, takes
Out, dry, obtain collagen-modified polypropylene fibre;
S2, thick shredding: wood pulp cellulose and collagen-modified polypropylene fibre are put into respectively in opener and slightly opened
Pine;
S3, mixing, smart shredding: the wood pulp cellulose handled through thick shredding and collagen-modified polypropylene fibre are added to
It is mixed in cotton blender machine, is then transferred in opener and carries out smart shredding;
S4, combing, networking: it carries out the composite fibre feeding carding machine after smart shredding to be combed into web, by web
It is combed again, networking;
S5, spun lacing are reinforced: being carried out spun lacing to web using 6 type high pressure jet heads and reinforced to form non-woven fabrics base fabric, spun lacing
Pressure is respectively set as 40bar, 90bar, 140bar, 120bar, 95bar, 30bar;
S6, drying, processing: by non-woven fabrics base fabric drying, winding, be processed into operation pad towel to get.
Embodiment 4
A kind of composite fibre nonwoven cloth operation pad towel proposed by the present invention, is made of the fiber of following weight percent: wood
Pulp fibres 45%, collagen-modified polypropylene fibre 55%.
The invention also provides the preparation methods of above-mentioned composite fibre nonwoven cloth operation pad towel, comprising the following steps:
The preparation of S1, collagen-modified polypropylene fibre: by polypropylene, maleic anhydride and cumyl peroxide according to
The weight ratio of 100:5:1.3 mixes, dry, is added in double screw extruder, melt blending, extruding pelletization, must be modified poly- third
Alkene pellet;Modified polypropene pellet is added in melt spinning machine and carries out melting extrusion, then drawn machine carries out spinning drawing, leads
It stretches than being 6 times, spinning speed 1000m/min obtains polypropylene fibre;Polypropylene fibre is placed in 12% tea polyphenols aqueous solution
In, the sodium hypophosphite for accounting for total solution weight 4% is added, 3h is stirred to react at 45 DEG C, takes out, it is dry, it is modified to obtain tea polyphenols
Polypropylene fibre;Tea polyphenols modified polypropylene fiber is placed in 8% collagen aqueous solution, 3h is stirred to react at 45 DEG C, takes
Out, dry, obtain collagen-modified polypropylene fibre;
S2, thick shredding: wood pulp cellulose and collagen-modified polypropylene fibre are put into respectively in opener and slightly opened
Pine;
S3, mixing, smart shredding: the wood pulp cellulose handled through thick shredding and collagen-modified polypropylene fibre are added to
It is mixed in cotton blender machine, is then transferred in opener and carries out smart shredding;
S4, combing, networking: it carries out the composite fibre feeding carding machine after smart shredding to be combed into web, by web
It is combed again, networking;
S5, spun lacing are reinforced: being carried out spun lacing to web using 6 type high pressure jet heads and reinforced to form non-woven fabrics base fabric, spun lacing
Pressure is respectively set as 35bar, 85bar, 145bar, 115bar, 100bar, 25bar;
S6, drying, processing: by non-woven fabrics base fabric drying, winding, be processed into operation pad towel to get.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of composite fibre nonwoven cloth operation pad towel, which is characterized in that be made of the fiber of following weight percent: wood pulp is fine
Tie up 40-60%, collagen-modified polypropylene fibre 40-60%.
2. a kind of preparation method based on composite fibre nonwoven cloth operation pad towel described in claim 1, which is characterized in that including
Following steps:
The preparation of S1, collagen-modified polypropylene fibre: polypropylene, maleic anhydride and cumyl peroxide are mixed, and are done
It is dry, it is added in double screw extruder, melt blending, extruding pelletization, obtains modified polypropene pellet;Modified polypropene pellet is added
Enter and carry out melting extrusion in melt spinning machine, then drawn machine carries out spinning drawing, obtains polypropylene fibre;Polypropylene fibre is set
It in tea polyphenols aqueous solution, is stirred to react, takes out, it is dry, obtain tea polyphenols modified polypropylene fiber;By tea polyphenols modified polypropene
Fiber is placed in collagen aqueous solution, is stirred to react, and is taken out, dry, obtains collagen-modified polypropylene fibre;
S2, thick shredding: wood pulp cellulose and collagen-modified polypropylene fibre are put into respectively and carry out thick shredding in opener;
S3, mixing, smart shredding: the wood pulp cellulose handled through thick shredding and collagen-modified polypropylene fibre are added to mixed cotton
It is mixed in machine, is then transferred in opener and carries out smart shredding;
S4, combing, networking: it carries out the composite fibre feeding carding machine after smart shredding to be combed into web, web is carried out
It combs again, networking;
S5, spun lacing are reinforced: being carried out spun lacing to web and reinforced to form non-woven fabrics base fabric;
S6, drying, processing: by non-woven fabrics base fabric drying, winding, be processed into operation pad towel to get.
3. the preparation method of composite fibre nonwoven cloth operation pad towel according to claim 2, which is characterized in that in S1, gather
The weight ratio of propylene, maleic anhydride and cumyl peroxide is 100:3-6:0.5-1.5.
4. the preparation method of composite fibre nonwoven cloth operation pad towel according to claim 2 or 3, which is characterized in that in S1,
The draw ratio of spinning traction is 4-7 times, spinning speed 800-1200m/min.
5. according to the preparation method of any composite fibre nonwoven cloth operation pad towel of claim 2-4, which is characterized in that S1
In, polypropylene fibre is placed in 7-15% tea polyphenols aqueous solution, is stirred to react 2-4h at 40-50 DEG C.
6. according to the preparation method of any composite fibre nonwoven cloth operation pad towel of claim 2-5, which is characterized in that S1
In, polypropylene fibre is placed in tea polyphenols aqueous solution, sodium hypophosphite is additionally added, is stirred to react;Preferably, sodium hypophosphite
Additional amount be tea polyphenols aqueous solution total weight 3-5%.
7. according to the preparation method of any composite fibre nonwoven cloth operation pad towel of claim 2-6, which is characterized in that S1
In, tea polyphenols modified polypropylene fiber is placed in 5-10% collagen aqueous solution, is stirred to react 2-4h at 40-45 DEG C.
8. according to the preparation method of any composite fibre nonwoven cloth operation pad towel of claim 2-7, which is characterized in that S5
In, spun lacing reinforcing is carried out to web using 6 type high pressure jet heads, spun lacing pressure is respectively set as 30-50bar, 80-
100bar、140-150bar、110-130bar、90-110bar、20-40bar。