CN108923358A - A kind of high intensity bus duct easy to disassemble and its casting technique - Google Patents
A kind of high intensity bus duct easy to disassemble and its casting technique Download PDFInfo
- Publication number
- CN108923358A CN108923358A CN201810939172.3A CN201810939172A CN108923358A CN 108923358 A CN108923358 A CN 108923358A CN 201810939172 A CN201810939172 A CN 201810939172A CN 108923358 A CN108923358 A CN 108923358A
- Authority
- CN
- China
- Prior art keywords
- bus duct
- cover board
- high intensity
- closed bottom
- side plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high intensity bus ducts easy to disassemble, including bus duct shell, bus duct shell is made of left and right sides closing side plate, cover board and closed bottom, the inner surface that side plate, cover board and closed bottom are closed in the left and right sides is corrugated type flute constructions, left and right sides closing side plate, cover board and closed bottom are all made of the thin steel once cold rolling of cold rolling and are made, and weight percent composition is:Bi:0.15-0.36%, C:0.03-0.19%, Si:1.89-2.13%, Mn:2.22-2.56%, Mo:1.78-2.15%, Ga:2.66-2.78%, Zr:1.34-2.56%, Sc:1.36-2.45%, Ba:2.03-2.98%, rare earth:11-18%, remaining is Fe and trace impurity;It by weight percentage include following components in rare earth:La:1.56-2.13%, Ce:3.35-3.78%, Pm:2.56-3.56%, Nd:1.12-1.78%, Pb:2.25-2.89%, Mn:3.34-3.78%, surplus Gd.
Description
Technical field
The present invention relates to electrical equipment technical field, particularly relate to a kind of high intensity bus duct easy to disassemble and its
Casting technique.
Background technique
As modernization project facility is emerged in large numbers with what is equipped, the fast increasing of the electricity consumption of all trades and professions, especially numerous high levels
The appearance with large-sized workshop workshop is built, is had been unable to meet in the present high current transportation system of traditional cable as transmission pressure
It is required that the used in parallel of multiway cable brings inconvenience to in-site installation construction connection.Bus duct is used as one kind is novel to match
Electric lead comes into being, and bus duct in the prior art is easily damaged, be easy to cause unnecessary since groove body is hollow structure
Danger reduces damage frequency, staff is facilitated to operate to reinforce the hardness and intensity of bus duct, save the cost, this hair
It is bright to propose a kind of high intensity bus duct easy to disassemble and its casting technique.
Summary of the invention
The technical problem to be solved by the present invention is to propose a kind of high intensity side for the above disadvantage of the existing technology
Just bus duct and its casting technique are dismantled, the durability of product is not only increased, and reduce scrappage, has saved and be produced into
This, structure is simple, easy to maintain.
The technical solution that the present invention solves the above technical problem is:
A kind of high intensity bus duct easy to disassemble, including bus duct shell, bus duct shell close side plate, cover board by the left and right sides
And closed bottom composition, the inner surface that side plate, cover board and closed bottom are closed in the left and right sides is corrugated type wave groove knot
Structure, left and right sides sealing plate are made up of at least two pieces of splice plates metal buckle connection, and the inner sidewall of every piece of splice plate is all provided with
There are upper groove and lower groove, cover board and closed bottom are arranged in respectively in upper groove and lower groove, left and right sides closing
Side plate, cover board and closed bottom constitute bus duct enclosure space, and conductive mother is vertically built-in in the bus duct enclosure space
Row;Left and right sides closing side plate, cover board and closed bottom are all made of the thin steel once cold rolling of cold rolling and are made, weight percent at
Divide and is:Bi:0.15-0.36%, C:0.03-0.19%, Si:1.89-2.13%, Mn:2.22-2.56%, Mo:1.78-2.15%,
Ga:2.66-2.78%, Zr:1.34-2.56%, Sc:1.36-2.45%, Ba:2.03-2.98%, rare earth:11-18%, remaining is Fe
And trace impurity;
It by weight percentage include following components in rare earth:La:1.56-2.13%, Ce:3.35-3.78%, Pm:2.56-
3.56%, Nd:1.12-1.78%, Pb:2.25-2.89%, Mn:3.34-3.78%, surplus Gd.
The technical solution that the present invention further limits is:
High intensity bus duct easy to disassemble above-mentioned, it is thin that left and right sides closing side plate, cover board and closed bottom are all made of cold rolling
Steel once cold rolling is made, and weight percent composition is:Bi:0.15%, C:0.03%, Si:1.89%, Mn:2.22%, Mo:
1.78%, Ga:2.66%, Zr:1.34%, Sc:1.36%, Ba:2.03%, rare earth:11%, remaining is Fe and trace impurity;
It by weight percentage include following components in rare earth:La:1.56%, Ce:3.35%, Pm:2.56%, Nd:1.12%, Pb:
2.25%, Mn:3.34%, surplus Gd.
High intensity bus duct easy to disassemble above-mentioned, left and right sides closing side plate, cover board and closed bottom are all made of cold
It rolls thin steel once cold rolling to be made, weight percent composition is:Bi:0.36%, C:0.19%, Si:2.13%, Mn:2.56%,
Mo:2.15%, Ga:2.78%, Zr:2.56%, Sc:2.45%, Ba:2.98%, rare earth:18%, remaining is Fe and trace impurity;
It by weight percentage include following components in rare earth:La:2.13%, Ce:3.78%, Pm:3.56%, Nd:1.78%, Pb:
2.89%, Mn:3.78%, surplus Gd.
High intensity bus duct easy to disassemble above-mentioned, left and right sides closing side plate, cover board and closed bottom are all made of cold
It rolls thin steel once cold rolling to be made, weight percent composition is:Bi:0.25%, C:0.12%, Si:1.98%, Mn:2.32%,
Mo:1.98%, Ga:2.72%, Zr:2.13%, Sc:2.11%, Ba:2.56%, rare earth:15%, remaining is Fe and trace impurity;
It by weight percentage include following components in rare earth:La:1.73%, Ce:3.45%, Pm:3.12%, Nd:1.56%, Pb:
2.78%, Mn:3.56%, surplus Gd.
High intensity bus duct easy to disassemble above-mentioned, after conductive bus bar wraps up dielectric and the package dielectric outside
Conductive bus bar and closed bottom and the contact surface of cover board between using U-shaped rubber pad as buffer protection layer.
The dielectric of high intensity bus duct easy to disassemble above-mentioned, package conductive bus bar is polyester film or poly- four
Fluorine ethylene orientation film.
The casting technique of high intensity bus duct easy to disassemble above-mentioned, including following steps:
(One)Coremaking:Sand core is produced according to plate face shape using resin sand;Then it is applied in sand core surface brush special-purpose fire-resistant obtained
Expect and lights processing;Sand core is finally sent into drying box, 350-450 DEG C of solidification temperature;
(Two)Molding:It will mold and be placed on pedestal before and after a pair of of metal outer mold first, so that the sprue in metal outer mold
Bottom is corresponding with cast gate on pedestal, and sprue, cross gate and Inner cast gate are provided in the metal outer mold;Then sand core is placed on
In metal outer mold, the sand core and metal outer mold cooperatively form four casting mold type chambers being axially sequentially distributed along sand core lateral wall, most
After close die cap;
(Three)Casting:By step(Two)Mold after middle molding, which is placed on cast-iron pot smelting furnace, carries out low-pressure casting, casting temperature
Degree:Between 700-750 DEG C, filling velocity:10-15cm/s, filling time:60-70s ;Boost pressure:1-1.2 kPa, pressure maintaining
Pressure:0.6-0.9kPa, dwell time:900-950s ;It must slowly be carried out when release, be sure not to be unable to fast pressure relief;
(Four)It unpacks and clears up:It unpacks after natural cooling 2 hours, successively opens die cap, metal outer mold when unpacking, then smash sand
Core takes out plate face blank and clears up the edge grinding at molding;
(Five)Cut off cast gate:Rack work cuts off the waste material at the cast gate of plate face blank.
The casting technique of high intensity bus duct easy to disassemble above-mentioned, the granularity of resin sand are 3-4 sieve, two in resin sand
Silica content >=96%, clay content < 1%, moisture < 3%.
The casting technique of high intensity bus duct easy to disassemble above-mentioned, in step(Three)Metallic solution be poured before to mould
It is sequentially added in tool after the pretreating agent and the static 30-35min of nodulizer based on barium, supplemented by lanthanum on the surface of metallic solution again
Perlite slag making is dispensed to purify metallic solution and skim at once.
It is using technical solution of the present invention beneficial effect:The bus duct cover plate plays the role of floor in heat dissipation,
Increase heat dissipation area, every busbar is all made of U-shaped rubber pad as buffer protection layer, is conducive to directly distributing and respectively for heat
Alternate Homogeneouslly-radiating, heat dissipation performance is superior, current-carrying capacity is big;It is empty that bus duct closing is placed in after conductive bus bar package dielectric
Between in corresponding corrugated type flute constructions, form high-strength tubular structure after overall package, bus duct can be greatly enhanced
The intensity of system, in the technical scheme, maximum break through pass through metal card by two pieces of splice plates for the left and right sides sealing plate
Button connection composition, the inner sidewall of every piece of splice plate are equipped with upper groove and lower groove, and cover board and closed bottom block respectively to be set
In upper groove and lower groove, metal buckle is movable, and splice plate can be passed through during transportation to the side of superposition
Formula is put into transport vehicle, when installation splice plate need to be only combined into one block of complete side plate and by metal buckle it is stuck after, by cover board
And closed bottom is inserted respectively into upper groove and lower groove, is greatly facilitated the transport of operator, is worked as bus duct
It is time saving and energy saving conducive to the maintenance and disassembly of staff when damaging, it is energy-efficient, and the technical solution structure letter
It is single, it is easy to make;And left and right sides closing side plate, cover board and closed bottom are all made of the thin steel once cold rolling of cold rolling and are made,
And it is high-strength metal material, significantly increases the intensity and hardness of bus duct, reduce scrappage, improve reality
The property used.
Detailed description of the invention
Fig. 1, Fig. 2 are structural schematic diagram of the invention;
Wherein:Side plate, 2- cover board, 3- closed bottom, 4- splice plate, 5- metal buckle, 6- upper groove, 7- are closed at left and right sides of 1-
Lower groove, 8- conductive bus bar.
Specific embodiment
Embodiment 1
The present embodiment provides a kind of high intensity bus ducts easy to disassemble, including bus duct shell, and bus duct shell is by the left and right sides
It closes side plate 1, cover board 2 and closed bottom 3 to form, the inner surface of side plate 1, cover board 2 and closed bottom 3 is closed in the left and right sides
It is corrugated type flute constructions, left and right sides sealing plate 1 is made up of two pieces of splice plates 4 connection of metal buckle 5, every piece of spelling
The inner sidewall of fishplate bar 4 is equipped with upper groove 6 and lower groove 7, cover board 2 and closed bottom 3 be arranged in respectively upper groove 6 and
In lower groove 7, left and right sides closing side plate 1, cover board 2 and closed bottom 3 constitute bus duct enclosure space, bus duct envelope
It closes and is vertically built-in with conductive bus bar 8 in space;Dielectric is wrapped up outside conductive bus bar 8 and wraps up the conductive bus bar after dielectric
The exhausted of conductive bus bar 8 is wrapped up as buffer protection layer using U-shaped rubber pad between closed bottom and the contact surface of cover board
Edge medium is polyester film or polytetrafluoroethylene orientation film;It is equal that side plate 1, cover board 2 and closed bottom 3 are closed in the left and right sides
It is made of the thin steel once cold rolling of cold rolling, weight percent composition is:Bi:0.15%, C:0.03%, Si:1.89%, Mn:
2.22%, Mo:1.78%, Ga:2.66%, Zr:1.34%, Sc:1.36%, Ba:2.03%, rare earth:11%, remaining is Fe and micro miscellaneous
Matter;
It by weight percentage include following components in rare earth:La:1.56%, Ce:3.35%, Pm:2.56%, Nd:1.12%, Pb:
2.25%, Mn:3.34%, surplus Gd;
The casting technique of high intensity bus duct easy to disassemble above-mentioned, including following steps:
(One)Coremaking:Sand core is produced according to plate face shape using resin sand;Then it is applied in sand core surface brush special-purpose fire-resistant obtained
Expect and lights processing;Sand core is finally sent into drying box, 350 DEG C of solidification temperature;
(Two)Molding:It will mold and be placed on pedestal before and after a pair of of metal outer mold first, so that the sprue in metal outer mold
Bottom is corresponding with cast gate on pedestal, and sprue, cross gate and Inner cast gate are provided in the metal outer mold;Then sand core is placed on
In metal outer mold, the sand core and metal outer mold cooperatively form four casting mold type chambers being axially sequentially distributed along sand core lateral wall, most
After close die cap;
(Three)Casting:By step(Two)Mold after middle molding, which is placed on cast-iron pot smelting furnace, carries out low-pressure casting, casting temperature
Degree:Between 700 DEG C, filling velocity:10cm/s, filling time:60s ;Boost pressure:1 kPa, dwell pressure:0.6kPa,
Dwell time:900s ;It must slowly be carried out when release, be sure not to be unable to fast pressure relief;
(Four)It unpacks and clears up:It unpacks after natural cooling 2 hours, successively opens die cap, metal outer mold when unpacking, then smash sand
Core takes out plate face blank and clears up the edge grinding at molding;
(Five)Cut off cast gate:Rack work cuts off the waste material at the cast gate of plate face blank;
The granularity of resin sand is 3 sieves, dioxide-containing silica >=96% in resin sand, clay content < 1%, moisture < 3%;In step
(Three)Metallic solution sequentially adds pretreating agent based on barium, supplemented by lanthanum into mold before being poured and nodulizer is static
Perlite slag making is dispensed on the surface of metallic solution to purify metallic solution and skim at once again after 30min.
Embodiment 2
The present embodiment provides a kind of high intensity bus ducts easy to disassemble, including bus duct shell, and bus duct shell is by the left and right sides
It closes side plate 1, cover board 2 and closed bottom 3 to form, the inner surface of side plate 1, cover board 2 and closed bottom 3 is closed in the left and right sides
It is corrugated type flute constructions, left and right sides sealing plate 1 is made up of two pieces of splice plates 4 connection of metal buckle 5, every piece of spelling
The inner sidewall of fishplate bar 4 is equipped with upper groove 6 and lower groove 7, cover board 2 and closed bottom 3 be arranged in respectively upper groove 6 and
In lower groove 7, left and right sides closing side plate 1, cover board 2 and closed bottom 3 constitute bus duct enclosure space, bus duct envelope
It closes and is vertically built-in with conductive bus bar 8 in space;Dielectric is wrapped up outside conductive bus bar 8 and wraps up the conductive bus bar after dielectric
The exhausted of conductive bus bar 8 is wrapped up as buffer protection layer using U-shaped rubber pad between closed bottom and the contact surface of cover board
Edge medium is polyester film or polytetrafluoroethylene orientation film;It is equal that side plate 1, cover board 2 and closed bottom 3 are closed in the left and right sides
It is made of the thin steel once cold rolling of cold rolling, weight percent composition is:Bi:0.36%, C:0.19%, Si:2.13%, Mn:
2.56%, Mo:2.15%, Ga:2.78%, Zr:2.56%, Sc:2.45%, Ba:2.98%, rare earth:18%, remaining is Fe and micro miscellaneous
Matter;
It by weight percentage include following components in rare earth:La:2.13%, Ce:3.78%, Pm:3.56%, Nd:1.78%, Pb:
2.89%, Mn:3.78%, surplus Gd;
The casting technique of above-mentioned high intensity bus duct easy to disassemble, including following steps:
(One)Coremaking:Sand core is produced according to plate face shape using resin sand;Then it is applied in sand core surface brush special-purpose fire-resistant obtained
Expect and lights processing;Sand core is finally sent into drying box, 450 DEG C of solidification temperature;
(Two)Molding:It will mold and be placed on pedestal before and after a pair of of metal outer mold first, so that the sprue in metal outer mold
Bottom is corresponding with cast gate on pedestal, and sprue, cross gate and Inner cast gate are provided in the metal outer mold;Then sand core is placed on
In metal outer mold, the sand core and metal outer mold cooperatively form four casting mold type chambers being axially sequentially distributed along sand core lateral wall, most
After close die cap;
(Three)Casting:By step(Two)Mold after middle molding, which is placed on cast-iron pot smelting furnace, carries out low-pressure casting, casting temperature
Degree:Between 750 DEG C, filling velocity:15cm/s, filling time:70s ;Boost pressure:1.2 kPa, dwell pressure:
0.9kPa, dwell time:950s ;It must slowly be carried out when release, be sure not to be unable to fast pressure relief;
(Four)It unpacks and clears up:It unpacks after natural cooling 2 hours, successively opens die cap, metal outer mold when unpacking, then smash sand
Core takes out plate face blank and clears up the edge grinding at molding;
(Five)Cut off cast gate:Rack work cuts off the waste material at the cast gate of plate face blank;
The granularity of resin sand is 4 sieves, dioxide-containing silica >=96% in resin sand, clay content < 1%, moisture < 3%;In step
(Three)Metallic solution sequentially adds pretreating agent based on barium, supplemented by lanthanum into mold before being poured and nodulizer is static
Perlite slag making is dispensed on the surface of metallic solution to purify metallic solution and skim at once again after 35min.
Embodiment 3
The present embodiment provides a kind of high intensity bus ducts easy to disassemble, including bus duct shell, and bus duct shell is by the left and right sides
It closes side plate 1, cover board 2 and closed bottom 3 to form, the inner surface of side plate 1, cover board 2 and closed bottom 3 is closed in the left and right sides
It is corrugated type flute constructions, left and right sides sealing plate 1 is made up of two pieces of splice plates 4 connection of metal buckle 5, every piece of spelling
The inner sidewall of fishplate bar 4 is equipped with upper groove 6 and lower groove 7, cover board 2 and closed bottom 3 be arranged in respectively upper groove 6 and
In lower groove 7, left and right sides closing side plate 1, cover board 2 and closed bottom 3 constitute bus duct enclosure space, bus duct envelope
It closes and is vertically built-in with conductive bus bar 8 in space;Dielectric is wrapped up outside conductive bus bar 8 and wraps up the conductive bus bar after dielectric
The exhausted of conductive bus bar 8 is wrapped up as buffer protection layer using U-shaped rubber pad between closed bottom and the contact surface of cover board
Edge medium is polyester film or polytetrafluoroethylene orientation film;It is equal that side plate 1, cover board 2 and closed bottom 3 are closed in the left and right sides
It is made of the thin steel once cold rolling of cold rolling, weight percent composition is:Bi:0.25%, C:0.12%, Si:1.98%, Mn:
2.32%, Mo:1.98%, Ga:2.72%, Zr:2.13%, Sc:2.11%, Ba:2.56%, rare earth:15%, remaining is Fe and micro miscellaneous
Matter;
It by weight percentage include following components in rare earth:La:1.73%, Ce:3.45%, Pm:3.12%, Nd:1.56%, Pb:
2.78%, Mn:3.56%, surplus Gd;
The casting technique of above-mentioned high intensity bus duct easy to disassemble, including following steps:
(One)Coremaking:Sand core is produced according to plate face shape using resin sand;Then it is applied in sand core surface brush special-purpose fire-resistant obtained
Expect and lights processing;Sand core is finally sent into drying box, 400 DEG C of solidification temperature;
(Two)Molding:It will mold and be placed on pedestal before and after a pair of of metal outer mold first, so that the sprue in metal outer mold
Bottom is corresponding with cast gate on pedestal, and sprue, cross gate and Inner cast gate are provided in the metal outer mold;Then sand core is placed on
In metal outer mold, the sand core and metal outer mold cooperatively form four casting mold type chambers being axially sequentially distributed along sand core lateral wall, most
After close die cap;
(Three)Casting:By step(Two)Mold after middle molding, which is placed on cast-iron pot smelting furnace, carries out low-pressure casting, casting temperature
Degree:Between 720 DEG C, filling velocity:13cm/s, filling time:65s ;Boost pressure:1.1kPa, dwell pressure:0.7kPa,
Dwell time:930s ;It must slowly be carried out when release, be sure not to be unable to fast pressure relief;
(Four)It unpacks and clears up:It unpacks after natural cooling 2 hours, successively opens die cap, metal outer mold when unpacking, then smash sand
Core takes out plate face blank and clears up the edge grinding at molding;
(Five)Cut off cast gate:Rack work cuts off the waste material at the cast gate of plate face blank;
The granularity of resin sand is 3 sieves, dioxide-containing silica >=96% in resin sand, clay content < 1%, moisture < 3%;In step
(Three)Metallic solution sequentially adds pretreating agent based on barium, supplemented by lanthanum into mold before being poured and nodulizer is static
Perlite slag making is dispensed on the surface of metallic solution to purify metallic solution and skim at once again after 32min.
In addition to the implementation, the present invention can also have other embodiments.It is all to use equivalent substitution or equivalent transformation shape
At technical solution, fall within the scope of protection required by the present invention.
Claims (9)
1. a kind of high intensity bus duct easy to disassemble, including bus duct shell, it is characterised in that:The bus duct shell is by left and right
Close side plate in two sides(1), cover board(2)And closed bottom(3)Side plate is closed in composition, the left and right sides(1), cover board(2)With
And closed bottom(3)Inner surface be corrugated type flute constructions, the left and right sides sealing plate(1)Spliced by least two pieces
Plate(4)Pass through metal buckle(5)Connection composition, every piece of splice plate(4)Inner sidewall be equipped with upper groove(6)And it is recessed
Slot(7), the cover board(2)And closed bottom(3)It is arranged in upper groove respectively(6)And lower groove(7)In, the left and right two
Side seal closes side plate(1), cover board(2)And closed bottom(3)Constitute bus duct enclosure space, the described bus duct enclosure space
In be vertically built-in with conductive bus bar(8);Close side plate in the left and right sides(1), cover board(2)And closed bottom(3)It is all made of
The thin steel once cold rolling of cold rolling is made, and weight percent composition is:Bi:0.15-0.36%, C:0.03-0.19%, Si:1.89-
2.13%, Mn:2.22-2.56%, Mo:1.78-2.15%, Ga:2.66-2.78%, Zr:1.34-2.56%, Sc:1.36-2.45%,
Ba:2.03-2.98%, rare earth:11-18%, remaining is Fe and trace impurity;
It by weight percentage include following components in the rare earth:La:1.56-2.13%, Ce:3.35-3.78%, Pm:2.56-
3.56%, Nd:1.12-1.78%, Pb:2.25-2.89%, Mn:3.34-3.78%, surplus Gd.
2. high intensity bus duct easy to disassemble according to claim 1, it is characterised in that:The left and right sides closed side
Plate, cover board and closed bottom are all made of the thin steel once cold rolling of cold rolling and are made, and weight percent composition is:Bi:0.15%,
C:0.03%, Si:1.89%, Mn:2.22%, Mo:1.78%, Ga:2.66%, Zr:1.34%, Sc:1.36%, Ba:2.03%, rare earth:
11%, remaining is Fe and trace impurity;
It by weight percentage include following components in the rare earth:La:1.56%, Ce:3.35%, Pm:2.56%, Nd:1.12%,
Pb:2.25%, Mn:3.34%, surplus Gd.
3. high intensity bus duct easy to disassemble according to claim 1, it is characterised in that:The left and right sides closed side
Plate, cover board and closed bottom are all made of the thin steel once cold rolling of cold rolling and are made, and weight percent composition is:Bi:0.36%,
C:0.19%, Si:2.13%, Mn:2.56%, Mo:2.15%, Ga:2.78%, Zr:2.56%, Sc:2.45%, Ba:2.98%, rare earth:
18%, remaining is Fe and trace impurity;
It by weight percentage include following components in the rare earth:La:2.13%, Ce:3.78%, Pm:3.56%, Nd:1.78%,
Pb:2.89%, Mn:3.78%, surplus Gd.
4. high intensity bus duct easy to disassemble according to claim 1, it is characterised in that:The left and right sides closed side
Plate, cover board and closed bottom are all made of the thin steel once cold rolling of cold rolling and are made, and weight percent composition is:Bi:0.25%,
C:0.12%, Si:1.98%, Mn:2.32%, Mo:1.98%, Ga:2.72%, Zr:2.13%, Sc:2.11%, Ba:2.56%, rare earth:
15%, remaining is Fe and trace impurity;
It by weight percentage include following components in the rare earth:La:1.73%, Ce:3.45%, Pm:3.12%, Nd:1.56%,
Pb:2.78%, Mn:3.56%, surplus Gd.
5. high intensity bus duct easy to disassemble according to claim 1, it is characterised in that:The conductive bus bar(8)Outsourcing
Using U-shaped between conductive bus bar and closed bottom and the contact surface of cover board after wrapping up in dielectric and the package dielectric
Rubber pad is as buffer protection layer.
6. high intensity bus duct easy to disassemble according to claim 5, it is characterised in that:The package conductive bus bar(8)
Dielectric is polyester film or polytetrafluoroethylene orientation film.
7. a kind of casting technique of high intensity bus duct easy to disassemble, which is equipped with any claim in claim 1-6
The high intensity bus duct easy to disassemble, which is characterized in that the technique includes following steps:
(One)Coremaking:Sand core is produced according to plate face shape using resin sand;Then it is applied in sand core surface brush special-purpose fire-resistant obtained
Expect and lights processing;Sand core is finally sent into drying box, 350-450 DEG C of solidification temperature;
(Two)Molding:It will mold and be placed on pedestal before and after a pair of of metal outer mold first, so that the sprue in metal outer mold
Bottom is corresponding with cast gate on pedestal, and sprue, cross gate and Inner cast gate are provided in the metal outer mold;Then sand core is placed on
In metal outer mold, the sand core and metal outer mold cooperatively form four casting mold type chambers being axially sequentially distributed along sand core lateral wall, most
After close die cap;
(Three)Casting:By step(Two)Mold after middle molding, which is placed on cast-iron pot smelting furnace, carries out low-pressure casting, casting temperature
Degree:Between 700-750 DEG C, filling velocity:10-15cm/s, filling time:60-70s ;Boost pressure:1-1.2 kPa, pressure maintaining
Pressure:0.6-0.9kPa, dwell time:900-950s ;It must slowly be carried out when release, be sure not to be unable to fast pressure relief;
(Four)It unpacks and clears up:It unpacks after natural cooling 2 hours, successively opens die cap, metal outer mold when unpacking, then smash sand
Core takes out plate face blank and clears up the edge grinding at molding;
(Five)Cut off cast gate:Rack work cuts off the waste material at the cast gate of plate face blank.
8. the casting technique of high intensity bus duct easy to disassemble according to claim 7, it is characterised in that:The resin sand
Granularity be 3-4 sieve, dioxide-containing silica >=96% in resin sand, clay content < 1%, moisture < 3%.
9. the casting technique of high intensity bus duct easy to disassemble according to claim 7, it is characterised in that:In step(Three)
Metallic solution sequentially adds pretreating agent and the static 30- of nodulizer based on barium, supplemented by lanthanum into mold before being poured
Perlite slag making is dispensed on the surface of metallic solution to purify metallic solution and skim at once again after 35min.