CN108914372B - A kind of manufacturing method and non-woven fabrics of jacquard weave pure cotton spunlace non-woven cloth - Google Patents

A kind of manufacturing method and non-woven fabrics of jacquard weave pure cotton spunlace non-woven cloth Download PDF

Info

Publication number
CN108914372B
CN108914372B CN201810754278.6A CN201810754278A CN108914372B CN 108914372 B CN108914372 B CN 108914372B CN 201810754278 A CN201810754278 A CN 201810754278A CN 108914372 B CN108914372 B CN 108914372B
Authority
CN
China
Prior art keywords
pure cotton
jacquard weave
woven cloth
woven fabrics
spunlace non
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201810754278.6A
Other languages
Chinese (zh)
Other versions
CN108914372A (en
Inventor
代五茜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Jian Wei Medical Supplies Co Ltd
Original Assignee
Fujian Jian Wei Medical Supplies Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujian Jian Wei Medical Supplies Co Ltd filed Critical Fujian Jian Wei Medical Supplies Co Ltd
Priority to CN201810754278.6A priority Critical patent/CN108914372B/en
Publication of CN108914372A publication Critical patent/CN108914372A/en
Application granted granted Critical
Publication of CN108914372B publication Critical patent/CN108914372B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention provides the manufacturing method and non-woven fabrics of a kind of jacquard weave pure cotton spunlace non-woven cloth, method is the following steps are included: by cotton after blowing, combing, lapping processing, pre- pure cotton spunlace non-woven cloth is formed through spun lacing, the spun lacing pressure used pierces the 85%~90% of pressure for normal water;Pre- pure cotton spunlace non-woven cloth obtained above is carried out boiling drift using single bath process;The pure cotton non-woven fabrics after floating will be boiled and require the 110%~115% of spun lacing pressure to carry out jacquard weave processing using same grammes per square metre;By above-mentioned jacquard weave, treated that pure cotton non-woven fabrics dry to get to jacquard weave pure cotton spunlace non-woven cloth.A kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth provided by the invention, solve the problems, such as that pure cotton non-woven fabrics, which are made, using raw cotton in the prior art can not carry out jacquard weave, a kind of hydro-entangled master technique for being easy to industrial application is provided, the cost of pure cotton non-woven fabrics jacquard weave and time in the prior art are greatly reduced.

Description

A kind of manufacturing method and non-woven fabrics of jacquard weave pure cotton spunlace non-woven cloth
Technical field
The present invention relates to textile manufacturing techniques field, in particular to the manufacturing method of a kind of jacquard weave pure cotton spunlace non-woven cloth and Non-woven fabrics.
Background technique
Pure cotton non-woven fabrics are prepared in sanitary goods industry at present generally there are two types of method, one is absorbent cotton is first made, then Non-woven fabrics is formed by spun lacing step;Another kind is non-woven fabrics first to be made in raw cotton, then carry out degreasing bleaching.Pure cotton non-woven fabrics system For product for beauty, surface usually requires to carry out jacquard weave or embossing, i.e., textile fabric with warp, weft staggered ridge design or Pattern.
If directlying adopt absorbent cotton is made non-woven fabrics, need to carry out defatting step, the cost to be spent, time are compared to making Manufacturing non-woven fabrics with raw cotton will spend more, and dry, frangible, the more puckery hardly possible of the absorbent cotton used combs, cloth cover is uneven, system It is low at rate;It and is usually all jacquard weave to be carried out on the non-woven fabrics of absorbent cotton manufacture, and raw cotton system can not used in the prior art Jacquard weave is carried out on the non-woven fabrics made, this is because non-woven fabrics made of raw cotton also needs to carry out degreasing whitening procedure, in this mistake The pattern of jacquard weave can be destroyed during boiling drift in journey.Therefore, how to manufacture jacquard weave on pure cotton non-woven fabrics in raw cotton is ability Domain unsolved problem always.
Summary of the invention
To solve problems of the prior art mentioned above, the present invention provides a kind of jacquard weave pure cotton spunlace non-woven cloth Manufacturing method, comprising the following steps:
S010, by cotton through blowing, combing, lapping processing after, form pre- pure cotton spunlace non-woven cloth through spun lacing;Wherein, it adopts Spun lacing pressure is the 85%~90% of normal water thorn pressure;
S020, pre- pure cotton spunlace non-woven cloth obtained above is carried out boiling drift using single bath process;
S030, the pure cotton non-woven fabrics after drift will be boiled 110%~115% mentioning for spun lacing pressure is required using same grammes per square metre Flower processing;
S040, by above-mentioned jacquard weave, treated that pure cotton non-woven fabrics dry to get to jacquard weave pure cotton spunlace non-woven cloth.
Further, in S010, the blowing is to be cleaned out cotton using textile technology, removes impurity, short flannel;Institute Combing is stated as raw cotton is combed into single fiber state;The lapping is netted for the single fiber cotton combed to be paved into.
Further, in S010, the fibre matting elasticity of the pre- pure cotton spunlace non-woven cloth requires institute for corresponding grammes per square metre The 85%~90% of elasticity need to be reached.
Further, in S040, the pure cotton non-woven fabrics water content after drying is less than 8%.
Further, in S010, the combing is 15 DEG C~25 DEG C in temperature, and relative humidity is 15 °~70 °;The paving The temperature of net is 20 DEG C~30 DEG C, and relative humidity is 50 °~60 °.
Further, in S020, the single bath process step includes:
S021: the water through 5 μm of membrane filtrations and ultraviolet sterilization processing, airtight heating to 55 DEG C~60 are added in a reservoir DEG C and keep the temperature 70min~90min, add the fatty alcohol polyoxyethylene ether bleeding agent obtained solution of 0.8g/L~1.2g/L;
S022, the pure cotton non-woven fabrics for obtaining S020 are put into the solution that S021 is obtained;
S023, the Standard entertion sodium hydroxide that 1.88g/L~2.2g/L is pressed in the solution of S022, material 4min~ 8min, then the Standard entertion hydrogen peroxide of 7.6g/L~8.2g/L is pressed, and material 4min~8min;
S024, the water softener that 0.8g/L~1.2g/L is added in the solution of S023, and material 4min~8min;
S025, the solution of S024 is warming up between 95 DEG C~100 DEG C with 1 DEG C/min~2 DEG C/min rate, and kept the temperature 60min~70min;The solution after heat preservation is cooled to 75 DEG C~85 DEG C again, completes to boil drift after solution is discharged.
Further, water softener used in the S024 step is sodium phosphate water softener.
Further, in S030, the pure cotton non-woven fabrics after floating will be boiled, passes sequentially through rotary drum, water is required using same grammes per square metre Pierce pressure 110%~115% carries out hydro-entangled master;Wherein, convex-concave flower pattern drum set is provided on the rotary drum.
The present invention also provides a kind of using jacquard weave pure cotton spunlace non-woven cloth prepared by as above any manufacturing method.
A kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth provided by the invention, by using above-mentioned processing step, First by raw cotton after combing, cross lapping and drawing-off handle to obtain neat and well spaced thick fibre web, using degreasing, bleaching and place is cleaned Pretreated pure cotton spunlace non-woven cloth is made in reason, then by spun lacing rotary drum jacquard process, on pretreatment pure cotton spunlace non-woven cloth Carry out jacquard weave, while by the effect of high pressure cascade to pre-process pure cotton spunlace non-woven cloth reinforce, the pure cotton made without The intensity of woven fabric reaches requirement.The water-washing process being related to need to only be completed during " single bath process " boils drift, reduce additional water Journey is washed, the dosage of water is greatly reduced, has saved resource and cost, while being also disposably to have adjusted pH in water-washing process Value (makes pH between 5-6), meets the requirement standard of actual use.
During the preparation process, the spun lacing step of S010 can form entanglement point between cotton fiber net, obtain nothing to reinforce Woven fabric, specifically used spun lacing pressure are the 85%~90% of the normal spun lacing pressure of the pure cotton non-woven fabrics of the grammes per square metre, are being weaved Field, grammes per square metre are weaving silk product evaluation conventional unit, are the weight of every square metre of fabric, unit is " gram/m " (g/ m2), and in the conventional technology, after grammes per square metre determines, used spun lacing pressure is also accordingly determined, heretofore described is normal Corresponding spun lacing pressure under spun lacing pressure, that is, corresponding grammes per square metre;Similarly, the fibre for the non-woven fabrics to be formed is made by lower spun lacing pressure Entanglement elasticity between dimension is the 85%~90% of the elasticity of the pure cotton non-woven fabrics of the grammes per square metre, i.e. the non-woven fabrics present invention uses Elasticity correspond under grammes per square metre the 85%~90% of the normal non-woven fabrics elasticity of tradition, enable the fibre through spun lacing treated non-woven fabrics Securely tangling in slightly loose state, to facilitate the hydro-entangled master of next step between dimension.In the hydro-entangled master of S030 In step, cotton fiber further tangle using higher spun lacing pressure and is reinforced, while carrying out jacquard weave operation, is specifically made Spun lacing pressure is the 110%~115% of the normal spun lacing pressure of the pure cotton non-woven fabrics of the grammes per square metre.Pass through the work of high pressure cascade Used in entanglement reinforcing is carried out to cotton fiber while carrying out jacquard weave by rotary drum, make jacquard weave shape securely, clearly.If first time water Thorn uses normal pressure during forming non-woven fabrics, then cotton fiber tangles securely, can not then be formed in hydro-entangled master step Pattern flower pattern, therefore, by using the difference of pressure during spun lacing twice, solve flower pattern boil occur after drift it is unintelligible, Unstable problem.
A kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth provided by the invention solves and uses raw cotton in the prior art The problem of pure cotton non-woven fabrics can not carry out jacquard weave is made, provides a kind of hydro-entangled master technique for being easy to industrial application, drops significantly The low cost of pure cotton non-woven fabrics jacquard weave and time in the prior art.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention Technical solution be clearly and completely described, it is clear that described embodiments are some of the embodiments of the present invention, rather than Whole embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making creative work premise Under every other embodiment obtained, shall fall within the protection scope of the present invention.
A kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth provided by the invention, steps are as follows:
One, it combs: under the conditions of 15 DEG C~25 DEG C of temperature, 15 ° of relative humidity~70 °, dustfree environment, removing raw material cotton In impurity and short flannel, and using carding equipment to after cleaning raw cotton carry out single fiber operation, to the cotton fiber after single fiber Mixing combing is carried out, first allows cotton fiber longitudinally to mix along cotton flow, then allow cotton fiber along cotton flow empir-ical formulation, is finally combed into fiber Net;
Two, cross lapping: under the conditions of 20 DEG C~30 DEG C of temperature, 50 ° of relative humidity~60 °, dustfree environment, by web It moves reciprocatingly perpendicular to lapping machine, laying enables cotton fiber in thick fibre web in laterally row at thick fibre web in a manner of reciprocating cross Column;
Three, preferred, drawing-off is carried out to thick fibre web: at 20 DEG C~30 DEG C of temperature, 50 °~60 ° of relative humidity, dustfree environment Under the conditions of, multistage small multiple drawing-off is carried out to thick fibre web using mixed and disorderly drafting machine, is made in thick fibre web into transversely arranged part cotton Fiber elongates thick fibre web, neat and well spaced operation towards longitudinal movement;
Four, spun lacing: in the case where temperature is 20 DEG C~30 DEG C of environmental condition, first pass through filtered soft water to elongate, it is neat and well spaced Rear thick fibre web carries out pre- wet blasting, and with the air for being compacted thick fibre web and being discharged in thick fibre web, the pressure of soft water will be with can will be thick fine Subject to air total number discharge in net, then the high pressure soft water water needle jet stream of filter is proceeded through, after water needle jet stream penetrates thick fibre web, Rebound effect using support lace curtaining or rotary drum makes the cotton fiber in thick fibre web with different backscattering to the reverse side of thick fibre web It is subjected to displacement, interts, tangling, obvolvent, forming a plurality of flexible entanglement points, thick fibre web is enabled to be reinforced;After spun lacing is processed Pure cotton non-woven fabrics winding is stand-by;The high pressure water needle jet stream used at this time uses 5 water jets, and fibre matting elasticity is the pure cotton The 85%~90% of the elasticity reached is required under non-woven fabrics grammes per square metre, the pressure of high pressure water needle jet stream is the pure cotton non-woven fabrics grammes per square metre The 85%~90% of the lower pressure for requiring to reach;
Five, pre- pure cotton spunlace non-woven cloth obtained above is carried out boiling drift using single bath process, comprising the following steps:
1) water through 5 μm of membrane filtrations and ultraviolet sterilization processing, is added in a reservoir, airtight heating is to 55 DEG C~60 DEG C And 70min~90min is kept the temperature, then according to the Standard entertion fatty alcohol polyoxyethylene ether bleeding agent of 0.8g/L~1.2g/L, be made Solution;Wherein, 1g/L refers to addition 1g bleeding agent in 1L water, and following g/L units, which equally refer to, is added corresponding weight in every liter of solution Chemicals;
2), obtained pure cotton non-woven fabrics are put into solution obtained above;
3), by the Standard entertion sodium hydroxide of 1.88g/L~2.2g/L, material 4min~8min, then by 7.6g/L~ The Standard entertion hydrogen peroxide of 8.2g/L, and material 4min~8min;
4) cotton, is added with brightening agent (VBL) by 0.5g/L~0.7g/L again, and the soft water of 0.8g/L~1.2g/L is added Agent, and material 4min~8min;
5) it, after material, is warming up between 95 DEG C~100 DEG C with 1 DEG C/min~2 DEG C/min rate by above-mentioned, and keep the temperature 60min~70min;The solution after heat preservation is cooled to 75 DEG C~85 DEG C again, can be obtained after degreasing, bleaching after solution is discharged Pure cotton non-woven fabrics;It is washed to non-woven fabrics is obtained, washes away the chemical residue on surface;
Six, hydro-entangled master: obtained pure cotton non-woven fabrics are passed through into high pressure cascade by rotary drum, are equipped in the drum surface It is carved with the drum set of the relief pattern for nonwoven surface jacquard weave;The pressure of the high pressure cascade is that the pure cotton non-woven fabrics grammes per square metre is wanted The 110%~115% of pressure is sought, high pressure cascade is incident upon pure cotton non-woven fabrics surface, enables cotton fiber therein tangle again, the height Press cascade is soft water after filtering with water.
Seven, by the pure cotton non-woven fabrics drying after jacquard weave, winding, the jacquard weave pure cotton spunlace non-woven cloth can be obtained.
It according to above-mentioned preparation step, is required with normal grammes per square metre as 50 grammes per square metres, normal spun lacing pressure is 50MPa, corresponding pine Tightness is MD=55N;The CD=48N present invention provides following preparation embodiment, as shown in table 1:
Table 1
Embodiment 1 Embodiment 2 Embodiment 3
Pre- pure cotton spun lacing pressure 43MPa 44MPa 45MPa
Jacquard weave handles spun lacing pressure after boiling drift 55MPa 55MPa 57MPa
Elasticity MD=55N;CD=50N MD=56N;CD=50N MD=54N;CD=48N
Raw cotton is carried out at jacquard weave by jacquard weave pure cotton non-woven fabrics product prepared in the above embodiments and using traditional technology Reason is made, and carries out boiling drift in treatment process, is comparative example 1 (grammes per square metre requires to be 50 grammes per square metres);Degreasing is directlyed adopt using the prior art Jacquard non-woven fabrics 2 (grammes per square metre requires to be 50 grammes per square metres) as a comparison case is made in cotton;Using FZ/T 64012 " spunlacing method " Standard carries out performance measurement, and observes jacquard non-woven fabrics pattern obtained, and test result is as shown in table 2:
Table 2
By above performance data it can be concluded that, the spun lacing pure cotton non-woven fabrics of the technique that provides through the invention production it is white Degree is high, and appearance is beautiful, and water absorption is outstanding, and mass area ratio CV value is very excellent, and ultimate strength is high, and using it is extremely short when Between, it is formed without boiling drift, just can obtain clear obvious, the clearly demarcated figured pattern of longitude and latitude, and in the prior art, to obtain jacquard weave figure Case needs to carry out to boil drift sizing for a long time, therefore scheme provided by the invention has significant progress and high practical application Value.
In addition, the manufacturing method and public patent application " spun lacing nonwoven of jacquard weave pure cotton spunlace non-woven cloth provided by the invention The jacquard process of cloth ", it application No. is 201710798706.0, compares, has the following characteristics that
1), process is few: compared with the jacquard process of the comparison patent, without carrying out additional water-washing process;
2), solve the time: compared with the technique of comparison comparison patent, preparation procedure is shortened 3-4 seconds;
3), industrial chemicals uses few: manufacturing method provided by the invention is not only not necessarily to additional washing process, and with comparison Patent is compared, and the industrial chemicals used is less, and reducing influences caused by pollution environmental and human health impacts;
4) it, is pullled without carrying out tension to cloth cover, consolidates the flower pattern being prepared more intact.
Raw cotton is first formed nothing through a water jet process by the manufacturing method of jacquard weave pure cotton spunlace non-woven cloth provided by the invention Woven fabric, then degreasing, bleaching and clean process are carried out, the high-pressure water-jet after recycling acidification carries out jacquard weave, since raw cotton is passing through Non-woven fabrics is formd after spun lacing, moldable surface is stronger, and the pattern fastness of jacquard weave is good, and passes through spun lacing process twice, The intensity of non-woven fabrics is significantly enhanced, it is stronger using comfort to make it, while being mentioned after degreasing, bleaching and clean process Worker employed in a plant nursery's sequence avoids destruction of the de- drift process to jacquard structure, protects the complete beauty of figured pattern.
The present invention also provides nothings prepared by the manufacturing method using jacquard weave pure cotton spunlace non-woven cloth provided by the present invention Woven fabric.
Finally, it should be noted that the above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations;To the greatest extent Pipe present invention has been described in detail with reference to the aforementioned embodiments, those skilled in the art should understand that: its according to So be possible to modify the technical solutions described in the foregoing embodiments, or to some or all of the technical features into Row equivalent replacement;And these are modified or replaceed, various embodiments of the present invention technology that it does not separate the essence of the corresponding technical solution The range of scheme.

Claims (8)

1. a kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth, which comprises the following steps:
S010, by cotton through blowing, combing, lapping processing after, form pre- pure cotton spunlace non-woven cloth through spun lacing;Wherein, use Spun lacing pressure is that normal water pierces the 85%~90% of pressure 50MPa;
S020, pre- pure cotton spunlace non-woven cloth obtained above is carried out boiling drift using single bath process;
S030, will boil drift after pure cotton non-woven fabrics using same grammes per square metre require spun lacing pressure 110%~115% carry out jacquard weave at Reason;
S040, by above-mentioned jacquard weave, treated that pure cotton non-woven fabrics dry to get to jacquard weave pure cotton spunlace non-woven cloth;
In S020, the single bath process step includes:
S021: be added in a reservoir through 5 μm of membrane filtrations and ultraviolet sterilization processing water, airtight heating to 55 DEG C~60 DEG C simultaneously 70min~90min is kept the temperature, the fatty alcohol polyoxyethylene ether bleeding agent obtained solution of 0.8g/L~1.2g/L is added;
S022, the pure cotton non-woven fabrics for obtaining S020 are put into the solution that S021 is obtained;
S023, the Standard entertion sodium hydroxide that 1.88g/L~2.2g/L is pressed in the solution of S022, material 4min~8min, then By the Standard entertion hydrogen peroxide of 7.6g/L~8.2g/L, and material 4min~8min;
S024, the water softener that 0.8g/L~1.2g/L is added in the solution of S023, and material 4min~8min;
S025, the solution of S024 is warming up between 95 DEG C~100 DEG C with 1 DEG C/min~2 DEG C/min rate, and kept the temperature 60min~70min;The solution after heat preservation is cooled to 75 DEG C~85 DEG C again, completes to boil drift after solution is discharged.
2. a kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth according to claim 1, it is characterised in that: in S010, The blowing is to be cleaned out cotton using textile technology, removes impurity, short flannel;The combing is that raw cotton is combed into single fiber Dimension state;The lapping is netted for the single fiber cotton combed to be paved into.
3. a kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth according to claim 1, it is characterised in that: in S010, The fibre matting elasticity of the pre- pure cotton spunlace non-woven cloth is to reach the 85%~90% of elasticity needed for corresponding grammes per square metre requires.
4. according to a kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth described in claim 1, it is characterised in that: in S040, dry Pure cotton non-woven fabrics water content after dry is less than 8%.
5. a kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth according to claim 1, it is characterised in that: in S010, The combing is 15 DEG C~25 DEG C in temperature, and relative humidity is 15 °~70 °;The temperature of the lapping is 20 DEG C~30 DEG C, relatively Humidity is 50 °~60 °.
6. a kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth according to claim 1, it is characterised in that: the S024 Water softener used in step is sodium phosphate water softener.
7. a kind of manufacturing method of jacquard weave pure cotton spunlace non-woven cloth according to claim 1, it is characterised in that: in S030, The pure cotton non-woven fabrics after floating will be boiled, pass sequentially through rotary drum, require spun lacing pressure using same grammes per square metre 110%~115% carries out Hydro-entangled master;Wherein, convex-concave flower pattern drum set is provided on the rotary drum.
8. a kind of using jacquard weave pure cotton spunlace non-woven cloth prepared by the manufacturing method as described in claim any one of 1-7.
CN201810754278.6A 2018-07-11 2018-07-11 A kind of manufacturing method and non-woven fabrics of jacquard weave pure cotton spunlace non-woven cloth Active CN108914372B (en)