CN108914333A - A kind of high light sensation, silk like fabric velvet are knitted the preparation method of fabric - Google Patents
A kind of high light sensation, silk like fabric velvet are knitted the preparation method of fabric Download PDFInfo
- Publication number
- CN108914333A CN108914333A CN201810938474.9A CN201810938474A CN108914333A CN 108914333 A CN108914333 A CN 108914333A CN 201810938474 A CN201810938474 A CN 201810938474A CN 108914333 A CN108914333 A CN 108914333A
- Authority
- CN
- China
- Prior art keywords
- fabric
- base cloth
- material base
- carries out
- opposite material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of high light sensation, silk like fabric velvet are knitted the preparation method of fabric, step A：It chooses 75D/36F (DTY has greatly light) (S) and is used as looped pile, 100D/36F (DTY) * 40D spandex thread (Lycra 562B) opens cloth weaving into the fabric fabric of suede structure by stop mechanism for towel machine as wire gauze；Step B：Fabric fabric is subjected to pre-setting；Step C：Opposite material base cloth surface carries out repairing hair, the villus on fabric fabric surface is trimmed to by shearing machine consistent with natural velvet height of naps；Step D：Opposite material base cloth is dyed；Step E：Opposite material base cloth is dehydrated；Step F：Opposite material base cloth carries out ring baking；Step G：Opposite material base cloth carries out reverse side cropping；Step H：Opposite material base cloth carries out shaking grain；Step I：Opposite material base cloth carries out hot light；Step J：Opposite material base cloth carries out multiple sizing.Compared with prior art, smooth glossy by the woven web surface of this method, solve the problems, such as that previous imitation velvet fabric reflecting feel is universal bad and not smooth compact enough.
Description
Technical field
The present invention relates to a kind of preparation method for being knitted fabric, especially a kind of preparation methods of imitation velvet fabric.
Background technique
Velvet is to be constituted the silk weaving name of pile loop or villus in fabric surface with suede.Also known as Zhangzhou velvet, in originating from
Fujian Province of state Zhangzhou Area and gain the name.The Ming Dynasty has mass production, is one of Chinese tradition fabric.There are flower, plain two classes.Velvet
Making raw material using mulberry silk can also be passed through with mulberry silk, and cotton yarn makees the ground tissue of latitude intertexture, with mulberry silk or artificial silk raising
Circle.A raising bar is woven into after often knitting four knitting wools when weaving（Thin wire）, when knitting certain length（About 20 centimetres or so）, i.e.,
Dissected with cutter along iron wire on machine, iron wire is detached from fabric, then at lint.This lint can make grain pattern according to the design of grain pattern
It is most clearly shown on satin face, and glossy.The grain pattern of fabric is constituted there are two types of form, one is velvet flowers satin, i.e. Zhang satin；One
It kind is suede ground gold-and-silver flower, i.e. velvet.Be divided into it is monochromatic and double-colored, it is gorgeous luxurious, autumn and winter dress material or advanced slip cover, curtain can be done
Deng.Imitation velvet fabric on the market at present, reflecting feel is generally bad, even if the fabric of good luster is again not smooth compact enough, causes
The application of imitation velvet fabric is limited to.
Summary of the invention
The present invention aiming at the shortcomings in the prior art, provides a kind of high light sensation, and silk like fabric velvet is knitted the system of fabric
Preparation Method, it is smooth glossy by the woven web surface of this method, it is generally bad to solve previous imitation velvet fabric reflecting feel
Not smooth enough compact problem again.
In order to solve the above-mentioned technical problem, a kind of high light sensation, silk like fabric velvet are knitted the preparation method of fabric, feature
Being includes following steps, step A：It chooses 75D/36F (DTY has greatly light) (S) and is used as looped pile, 100D/36F (DTY) * 40D
Spandex thread (Lycra 562B) opens cloth weaving into the fabric fabric of suede structure by stop mechanism for towel machine as wire gauze；Step B：By fabric base
Cloth carries out pre-setting, and pre-setting temperature is between 170 DEG C -200 DEG C, and speed is between the m/min of 10m/min ~ 30, and overfeeding is than 10%
~40%.Step C：Opposite material base cloth surface carries out repairing hair, by the villus on fabric fabric surface by shearing machine be trimmed to naturally
Velvet height of naps is consistent；Step D：Opposite material base cloth is dyed；Step E：Opposite material base cloth is dehydrated；Step F：It is right
Fabric fabric carries out ring baking, and ring dries temperature between 70 DEG C -110 DEG C when ring dries, and ring dries the time between 10min-30min；Step
Rapid G：Opposite material base cloth carries out reverse side cropping；Step H：Opposite material base cloth carries out shaking grain；Step I：Opposite material base cloth carries out hot light,
The flannelette of temperature control at 150 DEG C -180 DEG C and only opposite material base cloth carries out hot light when hot light；Step J：Opposite material base cloth carries out
Multiple sizing, obtains a kind of high light sensation after the completion of multiple sizing, silk like fabric velvet is knitted fabric.
In above-mentioned technical proposal, it is preferred that in step D：When opposite material base cloth is dyed, fabric fabric needs are immersed in
In dyeing liquor, the bath raio 1 of fabric fabric and dyeing liquor:10, dyeing temperature is 90 DEG C ~ 100 DEG C, and the processing time is 50min ~ 70
Min further includes 0.1g/L ~ 1g/L glacial acetic acid, 0.1g/L ~ 1g/L sodium acetate, 1g/L ~ 2g/L chelating agent, 1g/L ~ 4g/L in dyeing
Anhydrous sodium sulphate, 1g/L ~ 3g/L Disperse Leveler, 1% (owf) ~ 5% (owf) softening agent and 1% (owf) ~ 7% (owf) KY cation
Dyestuff.
In above-mentioned technical proposal, it is preferred that when the rapid opposite J material base cloth carries out multiple sizing, fabric fabric is formed in open-width
Sizing in machine, 100 DEG C ~ 150 DEG C of setting temperature, speed 10m/min ~ 30m/min, overfeeding ratio 25%-35%, air quantity 100%, fixed
Softening agent is added while type.
In above-mentioned technical proposal, it is preferred that by fabric fabric carry out pre-setting when 180 DEG C of temperature of pre-setting, 25 m/ of speed
Min, overfeeding is than 25%.
In above-mentioned technical proposal, it is preferred that when the opposite step F material base cloth carries out ring baking, ring dries temperature at 98 DEG C, and ring dries
Time is in 16min.
In above-mentioned technical proposal, it is preferred that when the opposite step I material base cloth carries out hot light, hot light temperature is controlled 160
℃。
It is added with spandex in fabric of the present invention, makes cloth cover compact by spandex, there is good elasticity, while fabric table
Face uses big bright-polyester synthetic fibre, to guarantee the reflecting feel of cloth cover.The present invention obtains rationally mainly then by adjusting dyeing and finishing technology
Thermal finalization technical parameter, to guarantee final gloss and cloth cover quality；And temperature, time are dried by suitable ring, it is specific
High temperature hot light mode physics polishing carried out to surface fiber increase cloth cover smooth feeling and reflecting feel.In terms of dyeing and finishing, if warm
Height is spent, the gloss of flannelette can damage；Temperature is too low, then fixed effect is bad, and final to shrink, grammes per square metre can be unstable.Our roots
According to the glass transition temperature of polyester fiber, melting temperature, the temperature of most reasonable thermal finalization is obtained by experimental exploration, time etc. closes
Key technology parameter, with this come guarantee flannelette gloss smooth feeling and excellent cloth cover quality.In high temperature hot light, using 150
DEG C -180 DEG C of degree hot lights carry out high temperature hot light to flannelette, so that velvet surface is more smooth glossy.
Compared with prior art, the beneficial effects of the invention are as follows：It is smooth glossy by the woven web surface of this method,
Solve the problems, such as that previous imitation velvet fabric reflecting feel is universal bad and not smooth compact enough.
Specific embodiment
Present invention is further described in detail With reference to embodiment.
Embodiment 1, a kind of high light sensation, silk like fabric velvet are knitted the preparation method of fabric, including following steps, step
Rapid A：It chooses 75D/36F (DTY has greatly light) (S) and is used as looped pile, 100D/36F (DTY) * 40D spandex thread (Lycra 562B) is as ground
Yarn opens cloth weaving into the fabric fabric of suede structure by stop mechanism for towel machine.Step B：Fabric fabric is subjected to pre-setting, pre-setting temperature
Degree is at 170 DEG C, and speed is in 10m/min, and overfeeding is than 10%.Step C：Opposite material base cloth surface carries out repairing hair, by fabric fabric surface
Villus be trimmed to by shearing machine it is consistent with natural velvet height of naps.Step D：Opposite material base cloth is dyed；Fabric
Fabric needs to be immersed in dyeing liquor, the bath raio 1 of fabric fabric and dyeing liquor:10, dyeing temperature be 90 DEG C, processing the time be
50min further includes that 0.1g/L glacial acetic acid, 0.1g/L sodium acetate, 1g/L chelating agent, 1g/L anhydrous sodium sulphate, 1g/L dispersion are even in dyeing
Stain, 1% (owf) softening agent and 1% (owf) KY dye of positive ion.Step E：Opposite material base cloth is dehydrated.Step F：Opposite
Material base cloth carries out ring baking, and ring dries temperature at 70 DEG C when ring dries, and ring dries the time in 10min.Step G：Opposite material base cloth carries out reverse side
Cropping.Step H：Opposite material base cloth carries out shaking grain.Step I：Opposite material base cloth carries out hot light, and temperature control is at 150 DEG C when hot light
And only the flannelette of opposite material base cloth carries out hot light.Step J：Opposite material base cloth carries out multiple sizing, obtains one kind after the completion of multiple sizing
High light sensation, silk like fabric velvet are knitted fabric.Fabric fabric is formed in open-width forming machine, and 100 DEG C of setting temperature, speed 10m/
Min, overfeeding is than 25%, air quantity 100%, and softening agent is added while sizing.
Embodiment 2, a kind of high light sensation, silk like fabric velvet are knitted the preparation method of fabric, including following steps, step
Rapid A：It chooses 75D/36F (DTY has greatly light) (S) and is used as looped pile, 100D/36F (DTY) * 40D spandex thread (Lycra 562B) is as ground
Yarn opens cloth weaving into the fabric fabric of suede structure by stop mechanism for towel machine.Step B：Fabric fabric is subjected to pre-setting, pre-setting temperature
180 DEG C of degree, 25 m/min of speed, overfeeding is than 25%.Step C：Opposite material base cloth surface carries out repairing hair, by fabric fabric surface
Villus is trimmed to consistent with natural velvet height of naps by shearing machine.Step D：Opposite material base cloth is dyed；Fabric base
Cloth needs to be immersed in dyeing liquor, the bath raio 1 of fabric fabric and dyeing liquor:10, dyeing temperature is 95 DEG C, and the processing time is 60
Min further includes 0.5g/L glacial acetic acid, 0.5g/L sodium acetate, 1.5g/L chelating agent, 2.5g/L anhydrous sodium sulphate, 2g/L dispersion in dyeing
Levelling agent, 3% (owf) softening agent and 4% (owf) KY dye of positive ion.Step E：Opposite material base cloth is dehydrated.Step F：
Opposite material base cloth carries out ring baking, and ring dries temperature at 98 DEG C, and ring dries the time in 16min.Step G：Opposite material base cloth carries out reverse side and cuts
Hair.Step H：Opposite material base cloth carries out shaking grain.Step I：Opposite material base cloth carries out hot light, and the control of hot light temperature is at 160 DEG C and only
The flannelette of opposite material base cloth carries out hot light.Step J：Opposite material base cloth carries out multiple sizing, obtains a kind of bloom after the completion of multiple sizing
Sense, silk like fabric velvet are knitted fabric.When the rapid opposite J material base cloth carries out multiple sizing, fabric fabric is default in open-width forming machine
Type, 1300 DEG C of setting temperature, speed 20m/min, overfeeding is than 30%, air quantity 100%, and softening agent is added while sizing.
Embodiment 3, a kind of high light sensation, silk like fabric velvet are knitted the preparation method of fabric, including following steps, step
Rapid A：It chooses 75D/36F (DTY has greatly light) (S) and is used as looped pile, 100D/36F (DTY) * 40D spandex thread (Lycra 562B) is as ground
Yarn opens cloth weaving into the fabric fabric of suede structure by stop mechanism for towel machine.Step B：Fabric fabric is subjected to pre-setting, pre-setting temperature
Degree is at 200 DEG C, and speed is in 30 m/min, and overfeeding is than 40%.Step C：Opposite material base cloth surface carries out repairing hair, by fabric fabric table
The villus in face is trimmed to consistent with natural velvet height of naps by shearing machine.Step D：Opposite material base cloth is dyed；Face
Material base cloth needs to be immersed in dyeing liquor, the bath raio 1 of fabric fabric and dyeing liquor:10, dyeing temperature is 100 DEG C, handles the time
It further include that 1g/L glacial acetic acid, 1g/L sodium acetate, 2g/L chelating agent, 4g/L anhydrous sodium sulphate, 3g/L dispersion are even in dyeing for 70 min
Stain, 5% (owf) softening agent and 7% (owf) KY dye of positive ion.Step E：Opposite material base cloth is dehydrated.Step F：It is right
Fabric fabric carries out ring baking, and ring dries temperature at 110 DEG C when ring dries, and ring dries the time in 30min.Step G：Opposite material base cloth carries out anti-
Face cropping.Step H：Opposite material base cloth carries out shaking grain.Step I：Opposite material base cloth carries out hot light, and temperature control is 180 when hot light
DEG C and only opposite material base cloth flannelette carry out hot light.Step J：Opposite material base cloth carries out multiple sizing, obtains one after the completion of multiple sizing
The high light sensation of kind, silk like fabric velvet are knitted fabric.When the rapid opposite J material base cloth carries out multiple sizing, fabric fabric is formed in open-width
Sizing in machine, 150 DEG C of setting temperature, speed 30m/min, overfeeding is than 35%, air quantity 100%, and softening agent is added while sizing.
Claims (6)
1. a kind of high light sensation, silk like fabric velvet is knitted the preparation method of fabric, it is characterized in that include following steps,
Step A：It chooses 75D/36F (DTY has greatly light) (S) and is used as looped pile, 100D/36F (DTY) * 40D spandex thread (Lycra 562B)
Cloth weaving is opened into the fabric fabric of suede structure by stop mechanism for towel machine as wire gauze；
Step B：Fabric fabric is subjected to pre-setting, pre-setting temperature is between 170 DEG C -200 DEG C, and speed is in 10m/min ~ 30
Between m/min, overfeeding is than 10% ~ 40%；
Step C：Opposite material base cloth surface carries out repairing hair, and the villus on fabric fabric surface is trimmed to and natural day by shearing machine
Goose down height of naps is consistent；
Step D：Opposite material base cloth is dyed；
Step E：Opposite material base cloth is dehydrated；
Step F：Opposite material base cloth carries out ring baking, and ring dries temperature between 70 DEG C -110 DEG C when ring dries, and ring dries the time in 10min-
Between 30min；
Step G：Opposite material base cloth carries out reverse side cropping；
Step H：Opposite material base cloth carries out shaking grain；
Step I：Opposite material base cloth carries out hot light, temperature control at 150 DEG C -180 DEG C and only flannelette of opposite material base cloth when hot light
Carry out hot light；
Step J：Opposite material base cloth carries out multiple sizing, obtains a kind of high light sensation, silk like fabric velvet knitted side after the completion of multiple sizing
Material.
2. a kind of high light sensation according to claim 1, silk like fabric velvet is knitted the preparation method of fabric, it is characterized in that,
In step D：When opposite material base cloth is dyed, fabric fabric needs to be immersed in dyeing liquor, the bath of fabric fabric and dyeing liquor
Than 1:10, dyeing temperature is 90 DEG C ~ 100 DEG C, and it further includes 0.1g/L ~ 1g/L ice in dyeing that the processing time, which is the min of 50min ~ 70,
Acetic acid, 0.1g/L ~ 1g/L sodium acetate, 1g/L ~ 2g/L chelating agent, 1g/L ~ 4g/L anhydrous sodium sulphate, 1g/L ~ 3g/L Disperse Leveler,
1% (owf) ~ 5% (owf) softening agent and 1% (owf) ~ 7% (owf) KY dye of positive ion.
3. a kind of high light sensation according to claim 1, silk like fabric velvet is knitted the preparation method of fabric, it is characterized in that,
When the rapid opposite J material base cloth carries out multiple sizing, fabric fabric is formed in open-width forming machine, and 100 DEG C ~ 150 DEG C of setting temperature, vehicle
Softening agent is added while sizing in fast 10m/min ~ 30m/min, overfeeding ratio 25%-35%, air quantity 100%.
4. a kind of high light sensation according to claim 1, silk like fabric velvet is knitted the preparation method of fabric, it is characterized in that,
By 180 DEG C of temperature of pre-setting when fabric fabric progress pre-setting, 25 m/min of speed, overfeeding is than 25%.
5. a kind of high light sensation according to claim 1, silk like fabric velvet is knitted the preparation method of fabric, it is characterized in that,
When the opposite step F material base cloth carries out ring baking, ring dries temperature at 98 DEG C, and ring dries the time in 16min.
6. a kind of high light sensation according to claim 1, silk like fabric velvet is knitted the preparation method of fabric, it is characterized in that,
When the opposite step I material base cloth carries out hot light, hot light temperature is controlled at 160 DEG C.