CN108773116A - 一种具有抗菌快速导湿的面料 - Google Patents

一种具有抗菌快速导湿的面料 Download PDF

Info

Publication number
CN108773116A
CN108773116A CN201810406517.9A CN201810406517A CN108773116A CN 108773116 A CN108773116 A CN 108773116A CN 201810406517 A CN201810406517 A CN 201810406517A CN 108773116 A CN108773116 A CN 108773116A
Authority
CN
China
Prior art keywords
layer
fabric
wetness
base cloth
elastomer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810406517.9A
Other languages
English (en)
Inventor
陈寒煜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Zhou Shi New Material Co Ltd
Original Assignee
Zhejiang Zhou Shi New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Zhou Shi New Material Co Ltd filed Critical Zhejiang Zhou Shi New Material Co Ltd
Priority to CN201810406517.9A priority Critical patent/CN108773116A/zh
Publication of CN108773116A publication Critical patent/CN108773116A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种具有抗菌快速导湿的面料，属于纺织技术领域。本具有抗菌快速导湿的面料，包括基布层以及基布层上依次设有的导湿层和抗菌层，基布层利用罗纹组织的不同调配，使其形成一面为光滑面，另一面为凹凸面，光滑面交织于导湿层，导湿层由经线和纬线的交织而成，经线和纬线在交织时会形成一个个均匀分布透气孔，经线和纬线均采用多功能混纺纱线，多功能混纺纱线由大豆纤维和竹碳涤纶纤维混纺而成，抗菌层由改性聚烯烃弹性体和聚氨酯弹性体复合而成的超细纤维，改性聚烯烃弹性体为由聚烯烃弹性体经N‑(3‑二甲氨基丙基)甲基丙烯酰胺接枝改性并经氯胺化处理制备的产物组成。本发明通过其结构与材料使得面料具有较好的导湿和抗菌效果。

Description

一种具有抗菌快速导湿的面料
技术领域
本发明属于纺织技术领域，涉及一种具有抗菌快速导湿的面料。
背景技术
面料是用来制作服装的材料，它不仅可以诠释服装的风格和特性，而且直接左右着服装的色彩、造型的表现效果。随着时代的发展，人们对服装面料的品质及功能性要求越来越高，现在市场上的面料一般只有遮体、保暖、防护等实用性，而不具有功能性，但是生活水平的提高，人对服装面料的要求越来越高。随着全名健身口号的推广，运动的人越来越多，而且很多运动都属于室外运动，这样人们在穿着普通的的服装面料时，会产生两大问题，服装面料导湿性差会影响人们运动时的舒适性，服装面料抗菌差会影响人们的健康，因此亟需一种服装面料解决该问题。
发明内容
本发明的目的是针对现有的技术存在上述问题，提出了一种具有抗菌快速导湿的面料。
本发明的目的可通过下列技术方案来实现：一种具有抗菌快速导湿的面料，包括基布层以及基布层上依次设有的导湿层和抗菌层，其特征在于，所述基布层利用罗纹组织的不同调配，使其形成一面为光滑面，另一面为凹凸面，凹凸面部分与身体接触，光滑面交织于导湿层，导湿层由经线和纬线的交织而成，经线和纬线在交织时会形成一个个均匀分布透气孔，所述经线和纬线均采用多功能混纺纱线，多功能混纺纱线由大豆纤维和竹碳涤纶纤维混纺而成，抗菌层由改性聚烯烃弹性体和聚氨酯弹性体复合而成的超细纤维，所述改性聚烯烃弹性体为由聚烯烃弹性体经N-(3-二甲氨基丙基)甲基丙烯酰胺接枝改性并经氯胺化处理制备的产物组成。
进一步，所述基布层的厚度为30～45μm。
进一步，所述导湿层的厚度为20～35μm。
进一步，竹碳涤纶纤维的单纤维线密度为2-3D，大豆纤维和竹碳涤纶纤维混纺的质量份数比为60-40～70-30。
进一步，所述抗菌层的厚度为25～35μm，所述抗菌层中，改性聚烯烃弹性体和聚氨酯弹性体的质量份数比为35：65～50：50。
与现有技术相比，本具有抗菌快速导湿的面料的优点具有以下几点：
1、本具有抗菌快速导湿的面料通过凹凸面的设计使得身体与凹凸面的凹部隔开有利于空气的导入，起到散热导湿作用，另外凸部与身体接触能快速的将湿气通过导湿层导出，导湿层上的若干小孔能快速的将湿气导出。
2、本具有抗菌快速导湿的面料中采用多功能混纺纱线的经线和纬线在交织形成导湿层后不但具有吸附、消除异味功能，具有远红外、负离子发射、抗菌保健功能外，而且织物吸湿性好，手感柔软，舒适功能佳的特点
3、本具有抗菌快速导湿的面料中抗菌层由改性聚烯烃弹性体和聚氨酯弹性体复合而成的超细纤维具备较好的抑菌率，细菌阻隔率，反复使用氯酸钠氯胺化处理，可避免抗菌能力的减弱。
附图说明
图1是本具有抗菌快速导湿的面料的剖视图。
图中，1、基布层；2、导湿层；3、抗菌层。
具体实施方式
以下是本发明的具体实施例并结合附图，对本发明的技术方案作进一步的描述，但本发明并不限于这些实施例。
如图1所示，本具有抗菌快速导湿的面料，包括基布层1以及基布层1上依次设有的导湿层2和抗菌层3，基布层1利用罗纹组织的不同调配，使其形成一面为光滑面，另一面为凹凸面，凹凸面部分与身体接触，光滑面交织于导湿层2，导湿层2由经线和纬线的交织而成，经线和纬线在交织时会形成一个个均匀分布透气孔，经线和纬线均采用多功能混纺纱线，多功能混纺纱线由大豆纤维和竹碳涤纶纤维混纺而成，抗菌层3由改性聚烯烃弹性体和聚氨酯弹性体复合而成的超细纤维，改性聚烯烃弹性体为由聚烯烃弹性体经N-(3-二甲氨基丙基)甲基丙烯酰胺接枝改性并经氯胺化处理制备的产物组成。
其中抗菌层3由改性聚烯烃弹性体和聚氨酯弹性体复合而成的超细纤维具备较好的抑菌率，细菌阻隔率，反复使用氯酸钠氯胺化处理，可避免抗菌能力的减弱。
基布层1的厚度为35μm。导湿层2的厚度为30μm。基布层1对导湿层2具有一定的引导作用，基布层1一面为为光滑面，另一面为凹凸面，凹凸面部分与身体接触，这样使得基布层1不是全部贴附在身体上，由于凹凸面的设计使得身体与凹凸面的凹部隔开有利于空气的导入，起到散热导湿作用，另外凸部与身体接触能快速的将湿气通过导湿层2导出，导湿层2上的若干小孔能快速的将湿气导出。
竹碳涤纶纤维的单纤维线密度为2D，大豆纤维和竹碳涤纶纤维混纺的质量份数比为70-30。采用多功能混纺纱线的经线和纬线在交织形成导湿层2后不但具有吸附、消除异味功能，具有远红外、负离子发射、抗菌保健功能外，而且织物吸湿性好，手感柔软，舒适功能佳的特点。
抗菌层3的厚度为30μm，抗菌层3中，改性聚烯烃弹性体和聚氨酯弹性体的质量份数比为45：55。
基布层1、导湿层2和抗菌层3的厚度均不能太薄不然导湿与抗菌效果会降低，但也不能过厚，不然会影响面料对身体舒适性，因此基布层1的厚度为35μm，导湿层2的厚度为30μm，抗菌层3的厚度为30μm为最佳参数。
本文中所描述的具体实施例仅仅是对本发明精神作举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。
尽管本文较多地使用了基布层1、导湿层2、抗菌层3等术语，但并不排除使用其它术语的可能性。使用这些术语仅仅是为了更方便地描述和解释本发明的本质；把它们解释成任何一种附加的限制都是与本发明精神相违背的。

Claims (5)

1.一种具有抗菌快速导湿的面料，包括基布层以及基布层上依次设有的导湿层和抗菌层，其特征在于，所述基布层利用罗纹组织的不同调配，使其形成一面为光滑面，另一面为凹凸面，凹凸面部分与身体接触，光滑面交织于导湿层，导湿层由经线和纬线的交织而成，经线和纬线在交织时会形成一个个均匀分布透气孔，所述经线和纬线均采用多功能混纺纱线，多功能混纺纱线由大豆纤维和竹碳涤纶纤维混纺而成，抗菌层由改性聚烯烃弹性体和聚氨酯弹性体复合而成的超细纤维，所述改性聚烯烃弹性体为由聚烯烃弹性体经N-(3-二甲氨基丙基)甲基丙烯酰胺接枝改性并经氯胺化处理制备的产物组成。
2.根据权利要求1所述的一种具有抗菌快速导湿的面料，其特征在于，所述基布层的厚度为30～45μm。
3.根据权利要求2所述的一种具有抗菌快速导湿的面料，其特征在于，所述导湿层的厚度为20～35μm。
4.根据权利要求3所述的一种具有抗菌快速导湿的面料，其特征在于，竹碳涤纶纤维的单纤维线密度为2-3D，大豆纤维和竹碳涤纶纤维混纺的质量份数比为60-40～70-30。
5.根据权利要求4所述的一种具有抗菌快速导湿的面料，其特征在于，所述抗菌层的厚度为25～35μm，所述抗菌层中，改性聚烯烃弹性体和聚氨酯弹性体的质量份数比为35：65～50：50。
CN201810406517.9A 2018-04-30 2018-04-30 一种具有抗菌快速导湿的面料 Pending CN108773116A (zh)