CN108726959A - A kind of preparation method of low smell color tile grout - Google Patents
A kind of preparation method of low smell color tile grout Download PDFInfo
- Publication number
- CN108726959A CN108726959A CN201810600589.7A CN201810600589A CN108726959A CN 108726959 A CN108726959 A CN 108726959A CN 201810600589 A CN201810600589 A CN 201810600589A CN 108726959 A CN108726959 A CN 108726959A
- Authority
- CN
- China
- Prior art keywords
- preparation
- low smell
- cement
- tile grout
- color tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of low smell color tile grout, including mixed fillers 55%, organic emulsified material 20%, antioxidant 15%, mould inhibitor 4.9%, preservative 3%, hydrophober 2%, pigment 0.1%, the mixed fillers include white cement 10-20g, titanium dioxide 7.5-15g, silica flour 22.5-45g, calcium carbonate 7.5-15g, dolomite dust 2.5-5g, high alumina cement 6-12g, portland cement 7-14g, Sodium Polyacrylate 2-4g, lignin fibre 0.8-2g, organic emulsified material includes vinyl acetate powder latex 3-6g, acrylate synthetic resin 4-8g.The present invention ceramic tile gap filler, easy construction, be watered stir evenly i.e. can be used, be easy to fill out connect it is full, it does not shrink, and various ceramic tile intermiscibilities are good, easy drying, not yellowing, cohesive force are strong, antiknock is split, in bright gay color, and it is non-toxic and tasteless, antioxidant effect is good, and use is more environmentally friendly, and overall processing cost of material is low, method is simple, is worthy to be popularized.
Description
Technical field
The present invention relates to building material technical field, especially a kind of preparation method of low smell color tile grout.
Background technology
Ceramic tile, also known as ceramic tile, are metal oxide and half-metal oxide with fire resisting, via grinding, mixing, compacting,
The process of glazing, sintering, and a kind of porcelain of the acid and alkali-resistance formed or stone matter etc., building or ornament materials, referred to as ceramic tile.Its
Raw material are mostly mixed by clay, quartz sand etc..Ceramic tile often will appear gap when being laid with, these gaps are such as
Fruit is not filled up, and ceramic tile loosening is be easy to cause, and more at present on the market to use gap filler, gap filler adhesion is strong, shrinks small, color
Pull-out capacity is strong, the flexibility with Anti-cracking, and decoration texture is good, and compressive resistance is wear-resistant, and antimycotic feature enables it that can perfectly repair
The cracking or breakage, its surface for mending floor surface can also paint, and have good water proofing property, however current gap filler, gas
Taste is heavier, and more gap filler is used for a long time, and oxidation reaction occurs, the phenomenon that nigrescence, influences U.S. of ceramic tile entirety
See effect.Problems above just needs to be improved traditional processing method, for above problem, herein it is proposed that
A kind of preparation method of low smell color tile grout.
Invention content
It is color to provide a kind of low smell for technical deficiencies such as the functional aspects of existing joint filling agent prescription by the present invention
The preparation method of color tile grout.
The present invention is to solve above-mentioned phenomenon, using the technical solution of following modification, a kind of low smell color tile grout
Preparation method, including mixed fillers 55%, organic emulsified material 20%, antioxidant 15%, mould inhibitor 4.9%, preservative 3%,
Hydrophober 2%, pigment 0.1%, the mixed fillers include white cement 10-20g, titanium dioxide 7.5-15g, silica flour 22.5-
45g, calcium carbonate 7.5-15g, dolomite dust 2.5-5g, high alumina cement 6-12g, portland cement 7-14g, Sodium Polyacrylate 2-
4g, lignin fibre 0.8-2g, organic emulsified material include vinyl acetate powder latex 3-6g, acrylate synthetic resin 4-
8g。
As present invention further optimization mode, the mixed fillers include white cement 20g, titanium dioxide 15g, silica flour
45g, calcium carbonate 15g, dolomite dust 5g, high alumina cement 12g, portland cement 14g, Sodium Polyacrylate 4g, lignin fibre 2g,
Organic emulsified material includes vinyl acetate powder latex 6g, acrylate synthetic resin 8g.
As present invention further optimization mode, the mixed fillers include white cement 10g, titanium dioxide 7.5g, quartz
Powder 22.5g, calcium carbonate 7.5g, dolomite dust 2.5g, high alumina cement 6g, portland cement 7g, Sodium Polyacrylate 2g, lignin are fine
0.8g is tieed up, organic emulsified material includes vinyl acetate powder latex 3-6g, acrylate synthetic resin 4-8g.
As present invention further optimization mode, manufacturing process steps are as follows：
A. above-mentioned raw materials are weighed according to weight percent；
B. the alleged mixed fillers obtained are sent into parcher in batches, the parch time exists according to the humid control of different component
4-10 minutes or so, then parch sieved raw material to parching completely, be filtered using 120-180 mesh screens；
C. organic emulsified material, antioxidant, mould inhibitor, hydrophober, pigment are sequentially poured into step b, after impregnating 1-2h
It is mixed, control temperature reaches 65 DEG C, and time control is within 1 hour；
D. after the completion of mixing, stopping stirring, carry out high-temperature sterilization, temperature is controlled at 110-140 DEG C, continues 5-12 minutes,
After high-temperature sterilization, then carry out disinfection by ultraviolet light.
E. raw material is packed：The solution sterilized is fitted into bottled packing machine, by being packed into Packaging Bottle according to fixed weight
In, after the completion of loading, preservative is added, is integrally sealed processing, completes production.
As present invention further optimization mode, the antioxidant is set as antioxidant 1010, antioxidant DNP, antioxygen
Agent 164 is one such or the mixture of a variety of compositions.
As present invention further optimization mode, the pigment is set as the mixture that iron oxide or titanium oxide are constituted.
As present invention further optimization mode, the hydrophober is set as polysiloxanes powder hydrophober.
As present invention further optimization mode, the mould inhibitor is set as 2- methylols ethyl alcohol, 2- methyl -2- hydroxyls
Methyl aminopropyl alcohol, tetramethyl disulfide thiuram it is one or more.
Compared with prior art：The present invention ceramic tile gap filler, easy construction, be watered stir evenly i.e. can be used, be easy to fill out
It connects full, does not shrink, and various ceramic tile intermiscibilities are good, easy drying, not yellowing, cohesive force are strong, antiknock is split, in bright gay color, and
Non-toxic and tasteless, antioxidant effect is good, and use is more environmentally friendly, and overall processing cost of material is low, and method is simple, is worthy to be popularized.
Specific implementation mode
Below in conjunction in the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
The present invention provides a kind of technical solution：A kind of preparation method of low smell color tile grout, including mixing are filled out
Material 55%, organic emulsified material 20%, antioxidant 15%, mould inhibitor 4.9%, preservative 3%, hydrophober 2%, pigment 0.1%, institute
It includes white cement 10-20g, titanium dioxide 7.5-15g, silica flour 22.5-45g, calcium carbonate 7.5-15g, dolomite to state mixed fillers
Powder 2.5-5g, high alumina cement 6-12g, portland cement 7-14g, Sodium Polyacrylate 2-4g, lignin fibre 0.8-2g, it is described to have
Machine emulsified material includes vinyl acetate powder latex 3-6g, acrylate synthetic resin 4-8g.
The mixed fillers include white cement 20g, titanium dioxide 15g, silica flour 45g, calcium carbonate 15g, dolomite dust 5g, height
Aluminum water mud 12g, portland cement 14g, Sodium Polyacrylate 4g, lignin fibre 2g, organic emulsified material includes vinyl acetate powder
Last latex 6g, acrylate synthetic resin 8g.
The mixed fillers include white cement 10g, titanium dioxide 7.5g, silica flour 22.5g, calcium carbonate 7.5g, dolomite dust
2.5g, high alumina cement 6g, portland cement 7g, Sodium Polyacrylate 2g, lignin fibre 0.8g, organic emulsified material includes acetic acid
Ethylene powder latex 3-6g, acrylate synthetic resin 4-8g.
Manufacturing process steps are as follows：
A. above-mentioned raw materials are weighed according to weight percent；
B. the alleged mixed fillers obtained are sent into parcher in batches, the parch time exists according to the humid control of different component
4-10 minutes or so, then parch sieved raw material to parching completely, be filtered using 120-180 mesh screens；
C. organic emulsified material, antioxidant, mould inhibitor, hydrophober, pigment are sequentially poured into step b, after impregnating 1-2h
It is mixed, control temperature reaches 65 DEG C, and time control is within 1 hour；
D. after the completion of mixing, stopping stirring, carry out high-temperature sterilization, temperature is controlled at 110-140 DEG C, continues 5-12 minutes,
After high-temperature sterilization, then carry out disinfection by ultraviolet light.
E. raw material is packed：The solution sterilized is fitted into bottled packing machine, by being packed into Packaging Bottle according to fixed weight
In, after the completion of loading, preservative is added, is integrally sealed processing, completes production.
The antioxidant is set as that antioxidant 1010, antioxidant DNP, antioxidant 164 is one such or a variety of compositions
Mixture.
The pigment is set as the mixture that iron oxide or titanium oxide are constituted.
The hydrophober is set as polysiloxanes powder hydrophober.
The mould inhibitor is set as 2- methylols ethyl alcohol, 2- methyl -2- methylols propyl alcohol, tetramethyl curing autumn
Blue nurse it is one or more.
Embodiment
Mixed fillers select white cement 20g, titanium dioxide 15g, silica flour 45g, calcium carbonate 15g, dolomite dust 5g, high aluminum water
Mud 12g, portland cement 14g, Sodium Polyacrylate 4g, lignin fibre 2g, organic emulsified material include vinyl acetate powder breast
Glue 6g, acrylate synthetic resin 8g,
A. above-mentioned raw materials are weighed according to weight percent；
B. the alleged mixed fillers obtained are sent into parcher in batches, the parch time exists according to the humid control of different component
4-10 minutes or so, then parch sieved raw material to parching completely, be filtered using 120-180 mesh screens；
C. organic emulsified material, antioxidant, mould inhibitor, hydrophober, pigment are sequentially poured into step b, after impregnating 1-2h
It is mixed, control temperature reaches 65 DEG C, and time control is within 1 hour；
D. after the completion of mixing, stopping stirring, carry out high-temperature sterilization, temperature is controlled at 110-140 DEG C, continues 5-12 minutes,
After high-temperature sterilization, then carry out disinfection by ultraviolet light.
E. raw material is packed：The solution sterilized is fitted into bottled packing machine, by being packed into Packaging Bottle according to fixed weight
In, after the completion of loading, preservative is added, is integrally sealed processing, completes production.
It is as follows to obtain product parameters table：Table 1
。
Traditional joint filling agent parameter is as follows：Table 2
。
It to sum up states, the gap filler energy rapid draing that comparison is evident that the present invention is carried out by Tables 1 and 2 data, and
And easy construction, it is watered to stir evenly and can be used, be easy to fill out and connect full, do not shrink, and various ceramic tile intermiscibilities are good, easy drying, no
Yellowing, cohesive force are strong, antiknock is split, and in bright gay color and non-toxic and tasteless, antioxidant effect is good, and use is more environmentally friendly, overall processing
Cost of material is low, and method is simple, is worthy to be popularized.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from the present invention spirit or
In the case of essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that come within the meaning and range of equivalency of the claims in the present invention
It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (8)
1. a kind of preparation method of low smell color tile grout, including it is mixed fillers 55%, organic emulsified material 20%, anti-oxidant
Agent 15%, mould inhibitor 4.9%, preservative 3%, hydrophober 2%, pigment 0.1%, it is characterised in that：The mixed fillers include
White cement 10-20g, titanium dioxide 7.5-15g, silica flour 22.5-45g, calcium carbonate 7.5-15g, dolomite dust 2.5-5g, high aluminum water
Mud 6-12g, portland cement 7-14g, Sodium Polyacrylate 2-4g, lignin fibre 0.8-2g, organic emulsified material includes acetic acid
Ethylene powder latex 3-6g, acrylate synthetic resin 4-8g.
2. a kind of preparation method of low smell color tile grout according to claim 1, which is characterized in that described mixed
It includes white cement 20g, titanium dioxide 15g, silica flour 45g, calcium carbonate 15g, dolomite dust 5g, high alumina cement 12g, silicic acid to close filler
Salt cement 14g, Sodium Polyacrylate 4g, lignin fibre 2g, organic emulsified material include vinyl acetate powder latex 6g, acrylic acid
Lipase absobed resin 8g.
3. a kind of preparation method of low smell color tile grout according to claim 1, which is characterized in that described mixed
It includes white cement 10g, titanium dioxide 7.5g, silica flour 22.5g, calcium carbonate 7.5g, dolomite dust 2.5g, high alumina cement to close filler
6g, portland cement 7g, Sodium Polyacrylate 2g, lignin fibre 0.8g, organic emulsified material include vinyl acetate powder latex
3-6g, acrylate synthetic resin 4-8g.
4. a kind of preparation method of low smell color tile grout according to claim 1, which is characterized in that make work
Steps are as follows for skill：
A. above-mentioned raw materials are weighed according to weight percent；
B. the alleged mixed fillers obtained are sent into parcher in batches, the parch time is according to the humid control of different component in 4-10
Minute or so, then parch sieves raw material to parching completely, be filtered using 120-180 mesh screens；
C. organic emulsified material, antioxidant, mould inhibitor, hydrophober, pigment are sequentially poured into step b, are carried out after impregnating 1-2h
It is mixed, control temperature reaches 65 DEG C, and time control is within 1 hour；
D. after the completion of mixing, stop stirring, carry out high-temperature sterilization, temperature is controlled at 110-140 DEG C, continues 5-12 minutes, high temperature
After disinfection, then carry out disinfection by ultraviolet light.
E. raw material is packed：The solution sterilized is fitted into bottled packing machine, by being fitted into Packaging Bottle according to fixed weight, is filled
After the completion of entering, preservative is added, is integrally sealed processing, completes production.
5. a kind of preparation method of low smell color tile grout according to claim 1, which is characterized in that described anti-
Oxidant is set as that antioxidant 1010, antioxidant DNP, antioxidant 164 is one such or the mixture of a variety of compositions.
6. a kind of preparation method of low smell color tile grout according to claim 1, which is characterized in that the face
Material is set as the mixture that iron oxide or titanium oxide are constituted.
7. a kind of preparation method of low smell color tile grout according to claim 1, which is characterized in that described to hate
Aqua is set as polysiloxanes powder hydrophober.
8. a kind of preparation method of low smell color tile grout according to claim 1, which is characterized in that described anti-
Mould dose of one kind or more for being set as 2- methylols ethyl alcohol, 2- methyl -2- methylols propyl alcohol, tetramethyl disulfide thiuram
Kind.