CN108672625A - 一种利用径锻机生产多台阶冷轧工作辊坯的加工方法 - Google Patents
一种利用径锻机生产多台阶冷轧工作辊坯的加工方法 Download PDFInfo
- Publication number
- CN108672625A CN108672625A CN201810524010.3A CN201810524010A CN108672625A CN 108672625 A CN108672625 A CN 108672625A CN 201810524010 A CN201810524010 A CN 201810524010A CN 108672625 A CN108672625 A CN 108672625A
- Authority
- CN
- China
- Prior art keywords
- forging
- roll base
- cold roll
- forging machine
- diameter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种利用径锻机生产多台阶冷轧工作辊坯的加工方法，它属于冶金机械制造技术领域。本发明通过电炉冶炼、LF炉精炼、VD真空处理后，进行火切、退火、表面抛丸、煤气烘烤、电渣重熔制得MC6B多台阶冷轧工作辊坯电渣锭，然后进行退火、表面清理、燃气炉加热保温时间≧24h，然后进行弧形镦粗板镦粗、第一次返炉加热、上平、下V型砧子拔长、第二次返炉加热、径锻机锻造后制得MC6B多台阶冷轧工作毛坯辊坯，最后进行热锯切割、水冷后正火、两段式球化退火、无损探伤检验，制得利用径锻机生产多台阶冷轧工作辊坯。本发明使生产的轧辊毛坯锻件锻件余量小，机加工时间减少，进而达到降低锻件工艺重量，节约制造成本。
Description
一种利用径锻机生产多台阶冷轧工作辊坯的加工方法
技术领域
[0001] 本发明属于冶金机械制造技术领域;具体涉及一种利用径锻机生产多台阶冷乳工 作辊坯的加工方法。
背景技术
[0002] 目前小规格辊坯的成形方式主要是采用加大锻造余块的方式在快锻机生产，国内 辊坯的生产技术方案为:将电炉/转炉炼钢+LF炉精炼+VD真空脱气处理后的钢水浇注成尺 寸重量合适的电极坯料，电极坯进行去应力退火，再进行电渣重熔，钢锭退火，退火后的钢 锭加热到锻造变形所需的温度，采用快锻机锻造成毛坯锻件，毛坯锻件经退火后采用车床 等设备加工成成品乳辊。现有锻造工艺生产的乳辊锻件，由于快锻机设备精度及成品形状 台阶较多且台阶差较大的原因，致使生产过程需加大锻造余块，造成成材率的损失，正常采 用快锻机锻造锻件重量在1.755吨左右，成材率在53.8%左右(按成品重量结算计算），原料 消耗多，生产制造成本高:锻造余量大，加工周期长，生产效率低，制造的辊坯毛坯锻件工艺 重量为成品重量的1.48倍，成材率较低，原料投入过多致使生产成本过高，利润空间减小。 针对设备能力原因导致锻造余块过大，导致加工周期长，生产效率低。合金钢锻制冷乳辊在 国内冶金制造行业应用十分广泛，小规格多台阶辊坯的需求提升明显，为进一步节约材料、 降低能耗，需要开发有效的锻造方法，能够降低辊坯锻件的毛坯工艺重量，从而节约辊坯制 造成本，同时减少加工周期，提高生产效率。
发明内容
[0003] 本发明目的是提供了一种利用径锻机生产多台阶冷乳工作辊坯的加工方法。
[0004] 本发明通过以下技术方案实现：
[0005] —种利用径锻机生产多台阶冷乳工作辊坯的加工方法，包括如下步骤：
[0006] 步骤a、通过电炉冶炼、LF炉精炼、VD真空处理后的钢水浇注成MC6B多台阶冷乳工 作辊坯电极锭；
[0007] 步骤b、将步骤a制得的MC6B多台阶冷乳工作辊坯电极锭进行火切、退火、表面抛 丸、煤气烘烤、电渣重熔制得MC6B多台阶冷乳工作辊坯电渣锭；
[0008] 步骤c、将步骤b制得的MC6B多台阶冷乳工作辊坯电渣锭进行退火、表面清理、燃气 炉加热保温时间3 24h，制得MC6B多台阶冷乳工作辊坯钢锭，待用；
[0009] 步骤d、将步骤c制得的MC6B多台阶冷乳工作辊坯钢锭进行弧形镦粗板镦粗、第一 次返炉加热、上平、下V型砧子拔长、第二次返炉加热、径锻机锻造后制得MC6B多台阶冷乳工 作毛坯辊坯；
[0010] 步骤e、将步骤d制得的MC6B多台阶冷乳工作毛坯辊坯进行热锯切割、水冷后正火、 两段式球化退火、无损探伤检验，制得利用径锻机生产多台阶冷乳工作辊坯。
[0011] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤a中电 炉冶炼为每炉配入铁水或生铁比例30〜32%，出钢温度1640〜1700°C，出钢过程完成增碳， 当出钢量达到15〜30吨时倒入合金、渣料;步骤a中LF炉精炼中按照2〜4m/t加入铝线，铝豆 与碳粉的混合物用量1〜1.5kg/t，白渣精炼时间20〜25分钟。
[0012] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤a中VD 真空处理前保证温度1600〜1700 °C、VD真空处理前加入Si-Ca线2m/t，VD真空处理时保持真 空度5 67帕，保持时间20〜30min，破真空后取样时，向吊包中加入150kg保温剂均匀覆盖渣 面，软吹时间15〜20分钟。
[0013] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤b中火 切用火切机在线火切，火切后热送退火，热送温度500〜60(TC，表面抛丸处理后煤气烘烤为 电极锭电渣重熔前对MC6B多台阶冷乳工作辊坯电极锭端头进行煤气烘烤，烘烤时间1〜2小 时，电渣重熔的加热温度为1650〜1750°C，加热时间为12〜18h，电渣重熔炉口采用空气干 燥器保护。
[0014] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤c中退 火温度为840〜860 °C，退火时间为20〜22h，燃气炉加热为分段加热，400〜450 °C保温3小时 后按升温速度控制在55〜60°C/小时升温至800〜850°C，保温3小时，随后按升温速度控制 在兰100°C/小时升温至1190〜1210°C，保温时间24小时。进行去应力退火处理能够消除铸 造应力，经电渣重熔成工艺要求的电渣钢锭，电渣钢锭经退火出炉后，将钢锭表面结疤、裂 纹等缺陷清理掉，得到MC6B多台阶冷乳工作辊坯钢锭。
[0015] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤d中弧 形镦粗板镦粗不压钳口，采取按钢锭高度变形方式控制镦粗比，镦粗比1.5，镦粗后返回径 锻机室式加热炉进行第一次返炉加热，加热温度1190〜1210°C，保温时间4h〜6h。采取按钢 锭高度变形方式控制镦粗比，要求镦粗比多1.5，镦粗后钢锭返回加热炉进行加热。钢锭通 过镦粗变形，可提高后续拔长锻比，提高锻件致密度，改善锻件横向性能。
[0016] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤d中上 平、下V型砧子拔长采用轻-重-轻的锻造方式，电渣锭初始阶段轻击，然后用60〜80mm压下 量锻造，锻造温度850〜900°C时修整，拔长锻造比为2.0，锻至直径为400mm然后坯料返回径 锻机室式加热炉进行第二次返炉加热，加热温度1190〜1210°C，保温时间2.5h〜5h。拔长至 工艺要求尺寸返回加热炉进行加热。本发明拔长方式采取轻压-重压-轻压，先初步焊合表 面钢锭缺陷，采取大压下量可有效改善钢锭内部疏松缺陷，充分破碎碳化物，进一步提高产 品内在质量，最后采取小压下量精整表面，减小因钢种塑性不好产生过多的表面裂纹。
[0017] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤d中径 锻机锻造过程控制每道次压下量50〜80mm，锻造频次选择180次/分钟，锻造比1.5〜1.6。拔 长后的圆形坯料加热2.5小时以上后，利用奥地利GFM公司1600MN径锻机自带编程软件 BarForge编程软件设计，采用根据成品辊坯的尺寸并结合径锻机锤头的工作面存在10°角 的坡面，将坯料继续锻造至工艺要求的尺寸，得到乳辊毛坯锻件，同时可根据生产需要能够 由一支坯料生产两种不同规格辊坯。本发明根据MC6B钢种特性控制锻造压下量及锻造频 率，控制每道次压下量50〜80mm，锻造频次为180次/分钟，可保证再加工前能够有效避免锻 造裂纹的发生并保证充分锻透。
[0018] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤d中径 锻机自带编程软件BarForge精确控制锻至乳辊毛坯，锻造过程利用一支坯料锻造两种规格 辊坯，首先坯料先全部锻造成最大辊坯辊身规格的圆棒，然后再锻造两个辊坯连接端即中 间凹档处，然后按辊坯工艺形状锻造一种规格辊坯至成品尺寸，最后锻造另一中规格辊至 成品尺寸。
[0019] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤e热锯 切割后单件多台阶冷乳工作辊坯重1.675吨，水冷后正火温度930〜950 °C，保温8小时，采用 两段式球化的方法，球化温度分别是830〜850°C均温加保温12小时、730〜750°C均温加保 温16小时，去氢670〜690°C均温加保温50小时后以25〜30°C/h随炉降温至200°C，出炉空冷 至室温后制得利用径锻机生产多台阶冷乳工作辊坯，将制得的利用径锻机生产多台阶冷乳 工作辊坯用超声波探伤仪进行无损探伤检验，检验合格后用卧室车床加工后再进行超声波 探伤合格后，得到乳辊成品。本发明对辊坯进行正火、球化去氢退火减少锻造应力，降低锻 件硬度，得到球状珠光体组织，便于后续热处理。
[0020] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，MC6B多台阶 冷乳工作辊坯电极锭的合金组成为(：0.85〜0.90、510.90〜1.00、]\1110.25〜0.50、？彡 0.015、S<0.010、Cr5.90〜6.20、Mo0.40〜0.60、V0.10〜0.20、Cu<0.25。
[0021] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，基于径锻机 设计特点，在锻造过程中变形均匀，生产效率高、温降少，经过快锻机镦粗拔长后可直接一 火成材，在对塑性不好且需严格规定锻造变形量的MC6B辊坯生产更能凸显径锻机的优势。 本发明为进一步节约材料、降低能耗，依据成品形状及径锻机设备、锻造方式等特点重新设 计锻造变形工艺，改变锻造方法，有效降低辊坯锻件的毛坯工艺重量，从而节约辊坯制造成 本，同时减少加工周期，提高生产效率。
[0022] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，与国内现有 技术方案相比，现有技术方案乳辊锻件工艺重量为1.755吨，本发明技术方案乳辊锻件工艺 重量为1.675吨，成材率提升2.5%，减少了原料投料量，节约了制造成本;通过一种径锻机 生产两种小规格多台阶冷乳工作辊坯MC6B的锻造工艺生产的乳辊锻件，锻件重量少，加工 时间少，成本低，效率高。本发明的锻造工艺生产的乳辊锻件较快锻机锻造工艺生产的乳辊 锻件成材率提升了近2.5个百分点(按成品重量结算计算)加工周期提升30%。
[0023] 本发明所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，与现有技术 相比，现有技术方案受设备精度制约，锻造锻件余量较大，本发明技术方案根据成品乳辊多 台阶的特点，充分利用径锻机锤头角度锻造成型方式，锤头工作面角度为10°，锤头型号为 SE1708.006改变锻件成型方式，将径锻机锤头坡度与成品锻件各台阶相互结合，使生产的 乳辊毛坯锻件锻件余量小，机加工时间减少，进而达到降低锻件工艺重量，节约制造成本的 目的，生产效率提高，同时利用径锻机编程对锻造过程变形量及温度的精准控制，满足产品 质量要求，制备的MC6B多台阶冷乳工作毛坯辊坯性能突出，Cr含量6 %，球化组织达到2〜3 级，碳化物网状<2.0级，碳化物带状、碳化物液析<2.0级，非金属夹杂物总和<4.0级，探 伤合格率95 %，碳化物分布细小、弥散，使用寿命长。
附图说明
[0024] 图1为本发明具体实施方式一方法制备的径锻辊坯毛坯锻件示意图；
[0025] 图2为本发明快锻机方法制备的径锻辊坯毛坯锻件示意图；
[0026] 图3为本发明具体实施方式一方法制备的单规格乳辊成品示意图；
[0027] 图4为本发明具体实施方式一方法制备的多规格乳辊成品示意图；
[0028] 图5为本发明径锻机锤头主视图；
[0029] 图6为本发明拔长的上平砧子示意图；
[0030]图7为本发明拔长的下¥站子不意图。
具体实施方式
[0031]
具体实施方式一：
[0032] —种利用径锻机生产多台阶冷乳工作辊坯的加工方法，包括如下步骤：
[0033] 步骤a、通过电炉冶炼、LF炉精炼、VD真空处理后的钢水浇注成MC6B多台阶冷乳工 作辊坯电极锭；
[0034] 步骤b、将步骤a制得的MC6B多台阶冷乳工作辊坯电极锭进行火切、退火、表面抛 丸、煤气烘烤、电渣重熔制得MC6B多台阶冷乳工作辊坯电渣锭；
[0035] 步骤c、将步骤b制得的MC6B多台阶冷乳工作辊坯电渣锭进行退火、表面清理、燃气 炉加热保温时间3 24h，制得MC6B多台阶冷乳工作辊坯钢锭，待用；
[0036] 步骤d、将步骤c制得的MC6B多台阶冷乳工作辊坯钢锭进行弧形镦粗板镦粗、第一 次返炉加热、上平、下V型砧子拔长、第二次返炉加热、径锻机锻造后制得MC6B多台阶冷乳工 作毛坯辊坯；
[0037] 步骤e、将步骤d制得的MC6B多台阶冷乳工作毛坯辊坯进行热锯切割、水冷后正火、 两段式球化退火、无损探伤检验，制得利用径锻机生产多台阶冷乳工作辊坯。
[0038] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤a 中电炉冶炼为每炉配入铁水或生铁比例30%，出钢温度1640,出钢过程完成增碳，当出钢量 达到15〜30吨时倒入合金、渣料;步骤a中LF炉精炼中按照2〜4m/t加入铝线，铝豆与碳粉的 混合物用量lkg/t，白渣精炼时间20分钟。
[0039] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤a 中VD真空处理前保证温度1600°(：、¥0真空处理前加入5^&线2111八，¥0真空处理时保持真空 度5 67帕，保持时间20min，破真空后取样时，向吊包中加入150kg保温剂均匀覆盖渣面，软 吹时间15分钟。
[0040] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤b 中火切用火切机在线火切，火切后热送退火，热送温度500°C，表面抛丸处理后煤气烘烤为 电极锭电渣重熔前对MC6B多台阶冷乳工作辊坯电极锭端头进行煤气烘烤，烘烤时间1小时， 电渣重熔的加热温度为1650〜1750°C，加热时间为12〜18h，电渣重熔炉口采用空气干燥器 保护。
[0041] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤c 中退火温度为840〜860 °C，退火时间为20〜22h，燃气炉加热为分段加热，400〜450 °C保温3 小时后按升温速度控制在60 °C/小时升温至800〜850 °C，保温3小时，随后按升温速度控制 在兰100 °C /小时升温至1190〜1210 °C，保温时间24小时。
[0042] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤d 中弧形镦粗板镦粗不压钳口，采取按钢锭高度变形方式控制镦粗比，镦粗比1.5，镦粗后返 回径锻机室式加热炉进行第一次返炉加热，加热温度1190〜1210 °C，保温时间4h〜6h。
[0043] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤d 中上平、下V型砧子拔长采用轻-重-轻的锻造方式，电渣锭初始阶段轻击，然后用60〜80mm 压下量锻造，锻造温度900°C时修整，拔长锻造比为2.0,锻至直径为400mm然后坯料返回径 锻机室式加热炉进行第二次返炉加热，加热温度1190〜1210°C，保温时间2.5h。
[0044] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤d 中径锻机锻造过程控制每道次压下量80mm，锻造频次选择180次/分钟，锻造比1.5。
[0045] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，步骤d 中径锻机自带编程软件BarForge精确控制锻至乳辊毛坯，锻造过程利用一支坯料锻造两种 规格辊坯，首先坯料先全部锻造成最大辊坯辊身规格的圆棒，然后再锻造两个辊坯连接端 即中间凹档处，然后按辊坯工艺形状锻造一种规格辊坯至成品尺寸，最后锻造另一中规格 辊至成品尺寸。
[0046] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，MC6B多 台阶冷乳工作辊坯电极锭的合金组成为(：0.85〜0.90、310.90〜1.00、]\1110.25〜0.50、？ <0.015、S<0.010、Cr5.90〜6.20、Mo0.40〜0.60、V0.10〜0.20、Cu<0.25。
[0047] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，热锯切 割后单件多台阶冷乳工作辊坯重1.675吨，水冷后正火温度950°C，保温8小时，采用两段式 球化的方法，球化温度分别是830 °C均温加保温12小时、730 °C均温加保温16小时，去氢670 °C均温加保温50小时后以30°C/h随炉降温至200°C，出炉空冷至室温后制得利用径锻机生 产多台阶冷乳工作辊坯，将制得的利用径锻机生产多台阶冷乳工作辊坯用超声波探伤仪进 行无损探伤检验，检验合格后用卧室车床加工后再进行超声波探伤合格后，得到乳辊成品。
[0048] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，与目前 采用快锻机锻造辊坯锻件工艺相比，如图1、图2所示：图1为本实施方式方法制备的径锻辊 坯毛坯锻件示意图，图2为快锻机方法制备的径锻辊坯毛坯锻件示意图，从图1和图2的对比 能够看出，径锻机锻造的辊坯毛坯锻件具有梯台结构，并且台阶较少，锻造效率高、与成品 形状更为接近，而快锻机锻造的辊坯毛坯锻件完全是矩形台阶结构，台阶较多、锻造余量较 大，不利于后续的工艺加工过程。
[0049] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，制备的 MC6B多台阶冷乳工作毛坯辊坯性能突出，Cr含量6 %，球化组织达到2〜3级，碳化物网状< 2.0级，碳化物带状、碳化物液析<2.0级，非金属夹杂物总和<4.0级，探伤合格率95 %。本 实施方式制备的MC6B多台阶冷乳工作毛坯辊坯，碳化物分布细小、弥散，使用寿命长。
[0050] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，与目前 采用快锻机锻造辊坯锻件工艺相比，如表1所示，锻件工艺重量降低，节约了制造成本，同时 可由编程软件设计生产不同规格辊坯锻件，辊坯锻件规格为辊身差在80mm以内且辊颈连接 端辊颈差在30_以内同时连体生产乳辊总重量<8吨，锻造余量少，辊身及两端辊颈余量小 使机加工时间大大减少，提尚了棍还的生广效率。
[0051] 表1锻造辊坯锻件工艺效果对比表
[0052]
[0053] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，通过一 种径锻机生产两种小规格多台阶冷乳工作辊坯MC6B的锻造工艺生产的乳辊锻件，锻件重量 少，加工时间少，成本低，效率高。本实施方式锻造工艺生产的乳辊锻件较快锻机锻造工艺 生产的乳辊锻件成材率提升了近2.5个百分点(按成品重量结算计算)加工周期提升30%。
[0054]
具体实施方式二：
[0055] —种利用径锻机生产多台阶冷乳工作辊坯的加工方法，包括如下步骤：
[0056] 步骤a、通过电炉冶炼、LF炉精炼、VD真空处理后的钢水浇注成MC6B多台阶冷乳工 作辊坯电极锭；
[0057] 步骤b、将步骤a制得的MC6B多台阶冷乳工作辊坯电极锭进行火切、退火、表面抛 丸、煤气烘烤、电渣重熔制得MC6B多台阶冷乳工作辊坯电渣锭；
[0058] 步骤c、将步骤b制得的MC6B多台阶冷乳工作辊坯电渣锭进行退火、表面清理、燃气 炉加热保温时间3 24h，制得MC6B多台阶冷乳工作辊坯钢锭，待用；
[0059] 步骤d、将步骤c制得的MC6B多台阶冷乳工作辊坯钢锭进行弧形镦粗板镦粗、第一 次返炉加热、上平、下V型砧子拔长、第二次返炉加热、径锻机锻造后制得MC6B多台阶冷乳工 作毛坯辊坯；
[0060] 步骤e、将步骤d制得的MC6B多台阶冷乳工作毛坯辊坯进行热锯切割、水冷后正火、 两段式球化退火、无损探伤检验，制得利用径锻机生产多台阶冷乳工作辊坯。
[0061] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，与目前 采用快锻机锻造辊坯锻件工艺相比，如表1所示，锻件工艺重量降低，节约了制造成本，同时 可由编程软件设计生产不同规格辊坯锻件，辊坯锻件规格为辊身差在80mm以内且辊颈连接 端辊颈差在30_以内同时连体生产乳辊总重量<8吨，锻造余量少，辊身及两端辊颈余量小 使机加工时间大大减少，提尚了棍还的生广效率。
[0062] 本实施方式所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，通过一 种径锻机生产两种小规格多台阶冷乳工作辊坯MC6B的锻造工艺生产的乳辊锻件，锻件重量 少，加工时间少，成本低，效率高。本实施方式的锻造工艺生产的乳辊锻件较快锻机锻造工 艺生产的乳辊锻件成材率提升了近2.5个百分点（按成品重量结算计算）加工周期提升 30% 〇
[0063]
具体实施方式三：
[0064] 根据具体实施方式二所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方 法，步骤a中电炉冶炼为每炉配入铁水或生铁比例30〜32%，出钢温度1640〜1700°C，出钢 过程完成增碳，当出钢量达到15〜30吨时倒入合金、渣料;步骤a中LF炉精炼中按照2〜4m/t 加入铝线，铝豆与碳粉的混合物用量1〜1.5kg/t，白渣精炼时间20〜25分钟。
[0065]
具体实施方式四：
[0066] 根据具体实施方式二所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方 法，步骤a中VD真空处理前保证温度1600〜1700°C、VD真空处理前加入Si-Ca线2m/t，VD真空 处理时保持真空度=67帕，保持时间20〜30min，破真空后取样时，向吊包中加入150kg保温 剂均匀覆盖渣面，软吹时间15〜20分钟。
[0067]
具体实施方式五：
[0068] 根据具体实施方式二所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方 法，步骤b中火切用火切机在线火切，火切后热送退火，热送温度500〜600°C，表面抛丸处理 后煤气烘烤为电极锭电渣重熔前对MC6B多台阶冷乳工作辊坯电极锭端头进行煤气烘烤，烘 烤时间1〜2小时，电渣重熔的加热温度为1650〜1750°C，加热时间为12〜18h，电渣重熔炉 口采用空气干燥器保护。
[0069]
具体实施方式六：
[0070] 根据具体实施方式二所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方 法，步骤c中退火温度为840〜860°C，退火时间为20〜22h，燃气炉加热为分段加热，400〜 450 °C保温3小时后按升温速度控制在55〜60 °C/小时升温至800〜850°C，保温3小时，随后 按升温速度控制在兰l〇〇°C/小时升温至1190〜1210°C，保温时间24小时。
[0071]
具体实施方式七：
[0072] 根据具体实施方式二所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方 法，步骤d中弧形镦粗板镦粗不压钳口，采取按钢锭高度变形方式控制镦粗比，镦粗比1.5， 镦粗后返回径锻机室式加热炉进行第一次返炉加热，加热温度1190〜1210°C，保温时间4h 〜6h〇
[0073]
具体实施方式八：
[0074] 根据具体实施方式二所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方 法，步骤d中上平、下V型砧子拔长采用轻-重-轻的锻造方式，电渣锭初始阶段轻击，然后用 60〜80mm压下量锻造，锻造温度850〜900 °C时修整，拔长锻造比为2.0，锻至直径为400mm然 后坯料返回径锻机室式加热炉进行第二次返炉加热，加热温度1190〜1210°C，保温时间 2.5h~5h〇
[0075]
具体实施方式九：
[0076] 根据具体实施方式二所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方 法，步骤d中径锻机锻造过程控制每道次压下量50〜80mm，锻造频次选择180次/分钟，锻造 比 1.5 〜1.6〇
[0077]
具体实施方式十：
[0078] 根据具体实施方式二所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方 法，步骤d中径锻机自带编程软件BarForge精确控制锻至乳辊毛坯，锻造过程利用一支坯料 锻造两种规格辊坯，首先坯料先全部锻造成最大辊坯辊身规格的圆棒，然后再锻造两个辊 坯连接端即中间凹档处，然后按辊坯工艺形状锻造一种规格辊坯至成品尺寸，最后锻造另 一中规格辊至成品尺寸。
[0079]具体实施方式^ :
[0080]根据具体实施方式二所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方 法，热锯切割后单件多台阶冷乳工作辊坯重1.675吨，水冷后正火温度930〜950°C，保温8小 时，采用两段式球化的方法，球化温度分别是830〜850°C均温加保温12小时、730〜750 °C均 温加保温16小时，去氢670〜690°C均温加保温50小时后以25〜30°C/h随炉降温至200°C，出 炉空冷至室温后制得利用径锻机生产多台阶冷乳工作辊坯，将制得的利用径锻机生产多台 阶冷乳工作辊坯用超声波探伤仪进行无损探伤检验，检验合格后用卧室车床加工后再进行 超声波探伤合格后，得到乳辊成品。
Claims (10)
1. 一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特征在于:包括如下步骤： 步骤a、通过电炉冶炼、LF炉精炼、VD真空处理后的钢水浇注成MC6B多台阶冷乳工作辊 还电极锭； 步骤b、将步骤a制得的MC6B多台阶冷乳工作辊坯电极锭进行火切、退火、表面抛丸、煤 气烘烤、电渣重熔制得MC6B多台阶冷乳工作辊坯电渣锭； 步骤c、将步骤b制得的MC6B多台阶冷乳工作辊坯电渣锭进行退火、表面清理、燃气炉加 热保温时间3 24h，制得MC6B多台阶冷乳工作辊坯钢锭，待用； 步骤d、将步骤c制得的MC6B多台阶冷乳工作辊坯钢锭进行弧形镦粗板镦粗、第一次返 炉加热、上平、下V型砧子拔长、第二次返炉加热、径锻机锻造后制得MC6B多台阶冷乳工作毛 坯辊坯； 步骤e、将步骤d制得的MC6B多台阶冷乳工作毛坯辊坯进行热锯切割、水冷后正火、两段 式球化退火、无损探伤检验，制得利用径锻机生产多台阶冷乳工作辊坯。
2. 根据权利要求1所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特 征在于：步骤a中电炉冶炼为每炉配入铁水或生铁比例30〜32%，出钢温度1640〜1700°C， 出钢过程完成增碳，当出钢量达到15〜30吨时倒入合金、渣料;步骤a中LF炉精炼中按照2〜 4m/t加入铝线，铝豆与碳粉的混合物用量1〜1.5kg/t，白渣精炼时间20〜25分钟。
3. 根据权利要求1所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特 征在于:步骤a中VD真空处理前保证温度1600〜1700 °C、VD真空处理前加入Si-Ca线2m/t，VD 真空处理时保持真空度5 67帕，保持时间20〜30min，破真空后取样时，向吊包中加入150kg 保温剂均匀覆盖渣面，软吹时间15〜20分钟。
4. 根据权利要求1所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特 征在于:步骤b中火切用火切机在线火切，火切后热送退火，热送温度500〜600°C，表面抛丸 处理后煤气烘烤为电极锭电渣重熔前对MC6B多台阶冷乳工作辊坯电极锭端头进行煤气烘 烤，烘烤时间1〜2小时，电渣重熔的加热温度为1650〜1750 °C，加热时间为12〜18h，电渣重 熔炉口采用空气干燥器保护。
5. 根据权利要求1所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特 征在于:步骤c中退火温度为840〜860°C，退火时间为20〜22h，燃气炉加热为分段加热，400 〜450°C保温3小时后按升温速度控制在55〜60°C/小时升温至800〜850°C，保温3小时，随 后按升温速度控制在兰l〇〇°C/小时升温至1190〜1210°C，保温时间24小时。
6. 根据权利要求1所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特 征在于:步骤d中弧形镦粗板镦粗不压钳口，采取按钢锭高度变形方式控制镦粗比，镦粗比 1.5,镦粗后返回径锻机室式加热炉进行第一次返炉加热，加热温度1190〜1210°C，保温时 间4h〜6h。
7. 根据权利要求1所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特 征在于:步骤d中上平、下V型砧子拔长采用轻-重-轻的锻造方式，电渣锭初始阶段轻击，然 后用60〜80mm压下量锻造，锻造温度850〜900 °C时修整，拔长锻造比为2.0，锻至直径为 400mm然后坯料返回径锻机室式加热炉进行第二次返炉加热，加热温度1190〜121(TC，保温 时间2.5h〜5h。
8. 根据权利要求1所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特 征在于：步骤d中径锻机锻造过程控制每道次压下量50〜80mm，锻造频次选择180次/分钟， 锻造比1.5〜1.6。
9. 根据权利要求1所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特 征在于:步骤d中径锻机自带编程软件BarForge精确控制锻至乳辊毛坯，锻造过程利用一支 坯料锻造两种规格辊坯，首先坯料先全部锻造成最大辊坯辊身规格的圆棒，然后再锻造两 个辊坯连接端即中间凹档处，然后按辊坯工艺形状锻造一种规格辊坯至成品尺寸，最后锻 造另一中规格辊至成品尺寸。
10. 根据权利要求1所述的一种利用径锻机生产多台阶冷乳工作辊坯的加工方法，其特 征在于：步骤e中热锯切割后单件多台阶冷乳工作辊坯重1.675吨，水冷后正火温度930〜 950°C，保温8小时，采用两段式球化的方法，球化温度分别是830〜850°C均温加保温12小 时、730〜750°C均温加保温16小时，去氢670〜690°C均温加保温50小时后以25〜30°C/h随 炉降温至200°C，出炉空冷至室温后制得利用径锻机生产多台阶冷乳工作辊坯，将制得的利 用径锻机生产多台阶冷乳工作辊坯用超声波探伤仪进行无损探伤检验，检验合格后用卧室 车床加工后再进行超声波探伤合格后，得到乳辊成品。