CN108648729A - Environment-friendly type sound hole PVC film piece production technology for mouth organ - Google Patents

Environment-friendly type sound hole PVC film piece production technology for mouth organ Download PDF

Info

Publication number
CN108648729A
CN108648729A CN201810733928.9A CN201810733928A CN108648729A CN 108648729 A CN108648729 A CN 108648729A CN 201810733928 A CN201810733928 A CN 201810733928A CN 108648729 A CN108648729 A CN 108648729A
Authority
CN
China
Prior art keywords
diaphragm
epiphragma
mouth organ
sound hole
overlay film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810733928.9A
Other languages
Chinese (zh)
Inventor
张敏
Original Assignee
张敏
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 张敏 filed Critical 张敏
Priority to CN201810733928.9A priority Critical patent/CN108648729A/en
Publication of CN108648729A publication Critical patent/CN108648729A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of environment-friendly type sound hole PVC film piece production technologies for mouth organ.Diaphragm includes overlay film and epiphragma, and wherein overlay film is the ultrathin white PVC films of 0.1mm;Epiphragma is made of DBL divalent ester, benzoic acid isooctyl acid diethylene glycol (DEG) ester, FRB 126, polyvinyl chloride, nano silicon dioxide, titanium dioxide and organic gel.The mouth organ diaphragm produced using this technique so that chromatic harmonica air-tightness is good, and when playing wind instruments, cross-talk, diaphragm will not ensure that the voice quality of chromatic harmonica to player with mouth organ seat board adhesion.

Description

Environment-friendly type sound hole PVC film piece production technology for mouth organ
Technical field
The present invention relates to a kind of environment-friendly type sound hole PVC film piece production technologies for mouth organ.Belong to musical instrument technical field.
Background technology
Mouth organ, (English Harmonica), with mouth blowing or inhaling gas, make more reed musical instruments of metal spring leaf vibration sounding;In pleasure Belong to the blowing instrument of free spring in device classification.
Mouth organ is broadly divided into solo mouth organ and instrumental ensembles mouth organ, respectively has variety classes again.Its range is different according to type, tonality And slightly difference.As melody musical instrument, mouth organ can play wind instruments at least two chords, and high-caliber musician can abide by mouth organ Under the premise of following mouth organ structure while blowing out two relatively independent parts.Because its small and exquisite volume is referred to as the " steel in pocket Qin ".
Mouth organ diaphragm is the important component of mouth organ, especially chromatic harmonica, and mouth organ diaphragm can effectively improve semitone The sound quality of rank mouth organ.Existing mouth organ diaphragm cannot ensure the air-tightness of chromatic harmonica well so that player is playing wind instruments Shi Zaocheng cross-talks;The gas that player blows into is hot, and hot gas sweats naturally in mouth organ, and such diaphragm and plate are sticked to Together, it will can just be spoken energetically with very when player plays wind instruments, and influence playing effect.
Invention content
The purpose of the present invention is to overcome the above shortcomings and to provide a kind of environment-friendly type sound hole PVC film piece lifes for mouth organ Production. art.
The object of the present invention is achieved like this:
A kind of environment-friendly type sound hole PVC film piece production technology for mouth organ, its main feature is that:Diaphragm includes overlay film and epiphragma, wherein Overlay film is the ultrathin white PVC films of 0.1mm;Epiphragma is by DBL divalent ester, benzoic acid isooctyl acid diethylene glycol (DEG) ester, FRB-126, poly- Vinyl chloride, nano silicon dioxide, titanium dioxide and organic gel composition.
The production technology of diaphragm includes the following steps:
Step 1: first pouring into polyvinyl chloride and nano silicon dioxide in vessel, adds 10-12ml DBL divalent esters and fully stir The stirring of 1-2ml benzoic acid isooctyl acid diethylene glycol (DEG) esters is added after mixing uniformly, it is uniformly rear that 1-2ml FRB-126 are added, continue stirring 5 Minute, polyvinyl chloride 2-3g and nano silicon dioxide 1-2g are sequentially added, titanium dioxide is eventually adding and organic gel mixing is mixed well;
Step 2: the mixed liquor in step 1 is coated uniformly on preprepared 0.1mm red pigments, 5- is then used 304 stainless steel plates of 6mm are held as pallet is put into baking oven, and 80 degree of heated at constant temperature 20 minutes, are made epiphragma in baking oven;
Step 3: according to chromatic harmonica seat board sound hole length, the epiphragma in step 2 is cut into item;
Step 4: the size of overlay film is adjusted to 2/3rds of epiphragma, after overlay film and epiphragma strength glue bond one, It is laid flat pressure 24 hours with thick every layer of 304 stainless steel flat plates of 5-6mm, is then placed in baking oven and is taken out certainly within one hour with 80 degree of heated at constant temperature It is so cooling, it finally places into baking oven and is taken out within two hours with 60 degree of heated at constant temperature, diaphragm is made after natural cooling;
Step 5: into strips by diaphragm shearing, the wherein width of diaphragm is wider 0.1mm than chromatic harmonica seat board sound hole mouth organ, film The length of piece is longer 5mm than chromatic harmonica seat board sound hole, and the strip diaphragm after shearing is bonded in chromatic harmonica seat with seccotine The reverse side of plate sound hole completes bonding after placing 48 hours, is finally assembled into finished product mouth organ.
Compared with prior art, the beneficial effects of the invention are as follows:
A kind of environment-friendly type sound hole PVC film piece production technology for mouth organ of the invention, the mouth organ diaphragm produced using this technique So that chromatic harmonica air-tightness is good, when playing wind instruments, cross-talk, diaphragm will not ensure that half to player with mouth organ seat board adhesion The voice quality of scale mouth organ.
Specific implementation mode
The present invention relates to a kind of environment-friendly type sound hole PVC film piece production technology for mouth organ, diaphragm includes overlay film and epiphragma, Wherein overlay film is the ultrathin white PVC films of 0.1mm;Epiphragma is by DBL divalent esters(Ring copper), benzoic acid isooctyl acid diethylene glycol (DEG) ester (Dibutyl ester)、FRB-126(Third bronze medal), polyvinyl chloride, nano silicon dioxide, titanium dioxide, organic gel composition.
The production technology of diaphragm includes the following steps:
Step 1: first pouring into polyvinyl chloride and nano silicon dioxide in vessel, adds 10-12ml DBL divalent esters and fully stir The stirring of 1-2ml benzoic acid isooctyl acid diethylene glycol (DEG) esters is added after mixing uniformly, it is uniformly rear that 1-2ml FRB-126 are added, continue stirring 5 Minute, polyvinyl chloride 2-3g and nano silicon dioxide 1-2g are sequentially added, Cornstarch is eventually adding and organic gel mixing is mixed well;
Step 2: the mixed liquor in step 1 is coated uniformly on preprepared 0.1mm red pigments, 5- is then used 304 stainless steel plates of 6mm are held as pallet is put into baking oven, and 80 degree of heated at constant temperature 20 minutes, are made epiphragma in baking oven.
Step 3: according to chromatic harmonica seat board sound hole length, the epiphragma in step 2 is cut into item.
Step 4: the size of overlay film is adjusted to 2/3rds of epiphragma, by overlay film and epiphragma strength glue bond one After head, pressure is laid flat 24 hours with thick every layer of 304 stainless steel flat plates of 5-6mm, is then placed in baking oven 80 degree of heated at constant temperature one hour Natural cooling is taken out, baking oven is finally placed into and is taken out within two hours with 60 degree of heated at constant temperature, diaphragm is made after natural cooling.
Step 5: into strips by diaphragm shearing, the wherein width of diaphragm is wider than chromatic harmonica seat board sound hole mouth organ The length of 0.1mm, diaphragm are longer 5mm than chromatic harmonica seat board sound hole, and the strip diaphragm after shearing is bonded in semitone with seccotine The reverse side of rank mouth organ seat board sound hole completes bonding after placing 48 hours, is finally assembled into finished product mouth organ.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.

Claims (1)

1. a kind of environment-friendly type sound hole PVC film piece production technology for mouth organ, it is characterised in that:Diaphragm includes overlay film and epiphragma, Wherein overlay film is the ultrathin white PVC films of 0.1mm;Epiphragma is by DBL divalent ester, benzoic acid isooctyl acid diethylene glycol (DEG) ester, FRB- 126, polyvinyl chloride, nano silicon dioxide, titanium dioxide and organic gel composition;
The production technology of diaphragm includes the following steps:
Step 1: first pouring into polyvinyl chloride and nano silicon dioxide in vessel, adds 10-12ml DBL divalent esters and fully stir The stirring of 1-2ml benzoic acid isooctyl acid diethylene glycol (DEG) esters is added after mixing uniformly, it is uniformly rear that 1-2ml FRB-126 are added, continue stirring 5 Minute, polyvinyl chloride 2-3g and nano silicon dioxide 1-2g are sequentially added, titanium dioxide is eventually adding and organic gel mixing is mixed well;
Step 2: the mixed liquor in step 1 is coated uniformly on preprepared 0.1mm red pigments, 5- is then used 304 stainless steel plates of 6mm are held as pallet is put into baking oven, and 80 degree of heated at constant temperature 20 minutes, are made epiphragma in baking oven;
Step 3: according to chromatic harmonica seat board sound hole length, the epiphragma in step 2 is cut into item;
Step 4: the size of overlay film is adjusted to 2/3rds of epiphragma, after overlay film and epiphragma strength glue bond one, It is laid flat pressure 24 hours with thick every layer of 304 stainless steel flat plates of 5-6mm, is then placed in baking oven and is taken out certainly within one hour with 80 degree of heated at constant temperature It is so cooling, it finally places into baking oven and is taken out within two hours with 60 degree of heated at constant temperature, diaphragm is made after natural cooling;
Step 5: into strips by diaphragm shearing, the wherein width of diaphragm is wider 0.1mm than chromatic harmonica seat board sound hole mouth organ, film The length of piece is longer 5mm than chromatic harmonica seat board sound hole, and the strip diaphragm after shearing is bonded in chromatic harmonica seat with seccotine The reverse side of plate sound hole completes bonding after placing 48 hours, is finally assembled into finished product mouth organ.
CN201810733928.9A 2018-07-06 2018-07-06 Environment-friendly type sound hole PVC film piece production technology for mouth organ Pending CN108648729A (en)