CN108625026A - A kind of production technology of banana fiber/tencel/viscose blended yarn person's textile fabric - Google Patents

A kind of production technology of banana fiber/tencel/viscose blended yarn person's textile fabric Download PDF

Info

Publication number
CN108625026A
CN108625026A CN201810378444.7A CN201810378444A CN108625026A CN 108625026 A CN108625026 A CN 108625026A CN 201810378444 A CN201810378444 A CN 201810378444A CN 108625026 A CN108625026 A CN 108625026A
Authority
CN
China
Prior art keywords
tencel
banana fiber
fabric
yarn
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810378444.7A
Other languages
Chinese (zh)
Inventor
蔡永东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Textile Vocational Technology College
Original Assignee
Nantong Textile Vocational Technology College
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Textile Vocational Technology College filed Critical Nantong Textile Vocational Technology College
Priority to CN201810378444.7A priority Critical patent/CN108625026A/en
Publication of CN108625026A publication Critical patent/CN108625026A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of production technologies of banana fiber/tencel/viscose blended yarn person's textile fabric.The exploitation of banana fiber/tencel/viscose blended yarn home textile bed necessaries fabric of the present invention is smooth with production, fabric weaving efficiency is up to 90% or more, First Grade Percentage Before Cloth Repairing is up to 85%, and storage top-quality product rate is up to 99%, and product physical properties index reaches high-class product standard to finished product after testing.Banana fiber and tencel, viscose glue are carried out blended resultant yarn by the present invention by a certain percentage, and for developing high-grade home textile bed necessaries fabric, banana fiber blending product can be given full play of with the performances such as persistence antibacterial, moisture absorption be ventilative, the product has a vast market foreground, it applies it in home textile set of bed articles product, meets the life idea that current people pursue " natural, safe and healthy ".

Description

A kind of production technology of banana fiber/tencel/viscose blended yarn person's textile fabric
Technical field
The invention belongs to fabric weaving fields, and in particular to a kind of banana fiber/tencel/viscose blended yarn person's textile fabric Production technology.
Background technology
Current people pursue via warming-type to environment-friendly type and health transition the function of home textile bed necessaries fabric.At present Different kind organism matter functional fibre comes into being, wherein banana fiber is successfully applied to home textile bed by many weaving producers both at home and abroad The exploitation of product fabric.It is raw material, a kind of cellulose fibre made of chemically treated, tool that banana fiber, which is using banana stalk, There are the characteristics such as lighter weight, gloss are good, hygroscopicity is strong, antibiotic property is good, easy degradation.Banana fiber has the spy of bast-fibre Sign, initial modulus is high, and poor flexibility, pure spinning spinnability is relatively poor, to enable banana fiber to be applied very well, it is necessary to by it Blended resultant yarn is carried out with other cellulose fibres, such as tencel, viscose glue, and is applied on home textile bed necessaries fabric, can be given full play to Banana fiber and tencel and the respective advantageous characteristic of viscose rayon.
Invention content
Goal of the invention:In order to solve the deficiencies in the prior art, it is mixed that the present invention provides a kind of banana fiber/tencel/viscose glues The production technology of yarn person's textile fabric.
Technical solution:A kind of production technology of banana fiber/tencel/viscose blended yarn person's textile fabric, including walk as follows Suddenly:
(1) raw material designs
It is blended using banana fiber, viscose rayon, tencel fiber progress, blending ratio banana fiber/30/ viscose glue of tencel Blending ratio is 30:30:40, resultant yarn 18.5tex;
(2) product design
For raw yarn feature, in conjunction with the requirement of bedclothes fabric style, product specification design is as follows:
Finished door width:248cm;
Through weft yarn:30/ tencel of banana fiber, 30/ viscose glue 4018.5tex × 30/ tencel of banana fiber, 30/ viscose glue 4018.5tex;
Finished product thread count:420/10cm × 320 piece/10cm;
Fabric tissue:Ground is organized as the block plaid tissue based on 5/2 Warp Satin, and lattice is 1cm × 1cm;For anti-cloth Side crimping, Selvage Stitch are designed as 2/2 cut stuipes;
(3) main weaving process
A. warping process
Select domestic GA121C types warping machine, main knitting technology as follows:Total quantity of warps is 5516 × 2, warping head part 788×7;Speed of beaming 650m/min or so;Using tension pulley adjust tension in Warping, bobbin cradle by upper, middle and lower layer and it is preceding, In, heel row be divided into 9 sections, the weight of each section tension pulley reasonable disposition between 7-10cN;
B. sizing operation
Using domestic GA308 types dual-box slasher, using " high pressure, it is highly concentrated, low glue, small tension receiving coil, be impregnated with again, middle starching, The sizing technique route of height moisture regain ", according to " similar compatibility " principle and raw yarn strength situation, slurry selects the lower denaturation of viscosity Mixing slurry based on starch;Formula of size is:Converted starch 50kg, polyacrylamide 35kg, CMC5kg, smooth agent 4kg;Thereon Sizing process parameter:The rate of sizing is 15 ± 1%, and regain is 8 ± 0.5%, and elongation is less than 1.0%, and size box sizing temperature is 95 DEG C, stock tank viscosity is 8s-9s, preceding squeezing roller pressure 12KN, post jacking roller pressure 20KN, and pre- drying tube temperature is 115 DEG C and closes baking Dry drying tube temperature is 105 DEG C, speed 40m/min;
C. drawing-in process
The block plaid tissue due to the fabric being organized as based on 5/2 Warp Satin, Selvage Stitch are designed as 2/2 variation side Flat tissue, thus must with page 12, wherein organize page 10, Selvage Stitch page 2;When drawing-in, ground through using fly threading method, that is, press 1,3,5,7, 9,2,4,6,8,10 sequences are gaited, friction when can reduce weaving in this way between warp thread;And side is all made of through being through back zone, both sides The threading method of (11,11,12,12) × 16 is entered with the reed that metric system porter is 140 teeth/10cm per dent 3;
D. air-jet weaving
Using ZAX-320 type multi-arm air-jet looms, since raw yarn is 30/ tencel of banana fiber, 30/ viscose glue, 40 18.5tex, Yarn number is thin, and density is big, and comprehensive page is more, therefore when looming weaving, technological parameter must be rationally set, and take related technical measures, specifically It is as follows:
(1) since the fabric is broad fabric, pneumatic picking can Filling Insertion Time angle suitably to increase, to ensure that wefting insertion is suitable Profit carries out, and loom speed is unsuitable too fast, and heald level time is suitably postponed, therefore speed is set as 500r/min, opening time is 290 °;
(2) since the Density is larger, be again in addition be organized as block plaid tissue based on 5/2 Warp Satin, The Warp line that should rationally adjust on loom carrys out opening or cleaning shed open, and suitably reduces warp tension.Because when warp tension is big, though have It conducive to opening or cleaning shed open, but can cause to stop platform rate to increase, and the float such as driving shelves, weft crackiness easily occur;Therefore warp tension answer it is moderate It adjusts, but can be by the reasonable adjustment of Warp line, it, can be by the back rest and warp stop frame to meet the needs of the clear shed open of air-jet weaving Location-appropriate move forward, to shorten front shed length, can reduce break to stopping platform number in this way, and reduce broadwise defect rate Occur;
(3) reasonable pneumatic picking technological parameter, to meet wealthy woven needs of jet;Its major parameter can be in loom electricity It is arranged on brain as follows:Main and auxiliary nozzle supply gas pressure is respectively set to 0.3MPa, 0.35MPa;Main burner opening/closing time be 60 °- 170°;Needle rise and fall the time be 65 ° -190 °;Pilot jet is divided into eight groups and supplies successively, and opening/closing time is respectively looming weaving Process parameters design is:1st group 60 ° -130 °, the 2nd group 80 ° -150 °, the 3rd group 100 ° -170 °, the 4th group 120 ° -190 °, the 5th 140 ° -210 °, the 6th group 150 ° -220 °, the 7th group 160 ° -230 °, the 8th group 170 ° -240 ° of group;Weft yarn angle of arrival is 230 °.
As an optimization:The banana fiber:The banana fiber of selection is the process of fiber of refining processing, fibre fineness For 7dtex, length is not less than 7.5cN in 60mm, ultimate strength.
As an optimization:The tencel fiber:Select 1.67D × 38mm Tencel LF fiber types.
As an optimization:The viscose rayon, specification are 1.67D × 38mm.
Advantageous effect:The exploitation of banana fiber/tencel/viscose blended yarn home textile bed necessaries fabric of the present invention and production are suitable Profit, fabric weaving efficiency is up to 90% or more, and First Grade Percentage Before Cloth Repairing is up to 85%, and up to 99%, finished product produces storage top-quality product rate after testing Product physical properties index reaches high-class product standard.The present invention carries out banana fiber and tencel, viscose glue by a certain percentage Blended resultant yarn, and for developing high-grade home textile bed necessaries fabric, it is anti-with persistence that banana fiber blending product can be given full play of Performances, the products such as bacterium, moisture absorption be ventilative have a vast market foreground, apply it in home textile set of bed articles product, meet Current people pursue the life idea of " natural, safe and healthy ".
Specific implementation mode
The technical scheme in the embodiments of the invention will be clearly and completely described below, so that the technology of this field Personnel can be better understood from advantages and features of the invention, to make apparent boundary to protection scope of the present invention It is fixed.Embodiment described in the invention is only a part of the embodiment of the present invention, instead of all the embodiments, based on the present invention In embodiment, the every other implementation that those of ordinary skill in the art are obtained without making creative work Example, shall fall within the protection scope of the present invention.
Embodiment
1. raw material is selected
A banana fibers
The banana fiber of selection is the process of fiber of refining processing, and fibre fineness is 7dtex or so, and length is on the left sides 60mm The right side, ultimate strength are not less than 7.5cN.
B tencel fibers
Tencel fibers are divided into three kinds of the LF types of the A100 types of non-fibrillating, the G100 types of fibrillation and low fibrillation, Wherein LF types Tencel has the characteristics that high intensity, flatness length, wet modulus are high, dry and wet intensity height.Since this product need to be used Fine count Yarn line, it is necessary to select 1.67D × 38mm Tencel LF fiber types to be carried out with other fibers blended.
C viscose rayons
The dry strength of viscose rayon is lower than cotton, and wet strong 60% or so only done by force, elastic resilience is poor, intolerant to Mill, it is not sun-proof, it is alkaline-resisting without acidproof;But viscose rayon good hygroscopicity, easy to dye, fabric is comfortable and easy to wear.Used in this product Viscose glue is viscose staple fibre, and specification is 1.67D × 38mm, has preferable stretching property by force.
2. the determination of blending ratio
Blended using banana fiber, viscose glue, tencel fiber progress, the performance that can integrate three kinds of cellulose fibre raw materials is special Point is, it can be achieved that have complementary functions.With its manufactured web surface good luster, soft smooth, high resilience.In view of banana fibre Dimension has the characteristic of similar flaxen fiber, dosage to have high-strength low no more than 30%, the in addition wet strong relatively low and tencel of viscose rayon The characteristics of stretching, therefore repetition test compares, and determines that its blending ratio is that 30/ tencel of banana fiber, 30/ viscose glue 40 is more suitable, resultant yarn For 18.5tex.
3. product design
For raw yarn feature, in conjunction with the requirement of bedclothes fabric style, product specification design is as follows:
Finished door width:248cm;
Through weft yarn:30/ tencel of banana fiber, 30/ viscose glue 4018.5tex × 30/ tencel of banana fiber, 30/ viscose glue 4018.5tex;
Finished product thread count:420/10cm × 320 piece/10cm;
Fabric tissue:Ground is organized as the block plaid tissue based on 5/2 Warp Satin, and lattice is 1cm × 1cm;For anti-cloth Side crimping, Selvage Stitch are designed as 2/2 cut stuipes.
4. main weaving process and its technical measures
A. warping process
Select domestic GA121C types warping machine.To ensure that sizing quality, when warping must reduce the elongation of yarn as far as possible, And to accomplish that warping piece yarn tension is uniform, therefore using the unsuitable excessively high and moderate Process configuration of tension in Warping of speed when warping.It is main Want knitting technology as follows:Total quantity of warps is 5516 × 2, warping head part 788 × 7;Speed of beaming 650m/min or so;Using Power disk adjust tension in Warping, bobbin cradle by upper, middle and lower layer and before, during and after row be divided into 9 sections, each section tension pulley Weight reasonable disposition between 7-10cN.
B. sizing operation
Using domestic GA308 types dual-box slasher.Due to 30/ viscose glue of banana fiber, 30/ tencel 40 that warp thread is ramuscule Mixed yarn, pck count is extra-high, and fabric compactness is also up to 89%, the total quantity of warps of single loom beam more than 5000, and in jet It is weaved on loom, the appropriate to the occasion starching using " high pressure, highly concentrated, low glue, small tension receiving coil, be impregnated with, middle starching, high getting damp again " again of sizing thus Process route reaches to be impregnated with and lay equal stress on coating, to improve sizing wear resistant performance, preferably patch volt Yarn filoplume, and ensures sizing With extensibility.
Since banana fiber, viscose rayon, the tencel fiber in raw yarn belong to cellulosic fibre, according to " similar compatibility " Principle and raw yarn strength situation, slurry preferably select the mixing based on the lower converted starch of viscosity to starch.Formula of size is:Denaturation is formed sediment Powder 50kg, polyacrylamide 35kg, CMC5kg, smooth agent 4kg;Its Technological Parameters of Sizing:The rate of sizing is 15 ± 1%, regain It is 8 ± 0.5%, elongation is less than 1.0%, and size box sizing temperature is 95 DEG C, and stock tank viscosity is 8s-9s, preceding squeezing roller pressure 12KN, post jacking roller pressure 20KN, pre- drying tube temperature be 115 DEG C and close drying drying tube temperature be 105 DEG C, speed 40m/ min。
C. drawing-in process
The block plaid tissue due to the fabric being organized as based on 5/2 Warp Satin, Selvage Stitch are designed as 2/2 variation side Flat tissue, thus must with page 12, wherein organize page 10, Selvage Stitch page 2.When drawing-in, ground through using fly threading method, that is, press 1,3,5,7, 9,2,4,6,8,10 sequences are gaited, friction when can reduce weaving in this way between warp thread;And side is all made of through being through back zone, both sides The threading method of (11,11,12,12) × 16.With the reed that metric system porter is 140 teeth/10cm, enter per dent 3.
D. air-jet weaving
Using ZAX-320 type multi-arm air-jet looms.Since raw yarn is 30/ viscose glue of banana fiber, 30/ tencel 40
18.5tex, yarn number is thin, and density is big, and comprehensive page is more, therefore when looming weaving, technological parameter must be rationally set, and take phase Technical measures are answered, it is specific as follows:
(1) since the fabric is broad fabric, pneumatic picking can Filling Insertion Time angle suitably to increase, to ensure that wefting insertion is suitable Profit carries out, and loom speed is unsuitable too fast, and heald level time is suitably postponed, therefore speed is set as 500r/min, opening time is 290 ° It is advisable.
(2) since the Density is larger, be again in addition be organized as block plaid tissue based on 5/2 Warp Satin, The Warp line that should rationally adjust on loom carrys out opening or cleaning shed open, and suitably reduces warp tension.Because when warp tension is big, though have It conducive to opening or cleaning shed open, but can cause to stop platform rate to increase, and the float such as driving shelves, weft crackiness easily occur.Therefore warp tension answer it is moderate It adjusts, but can be by the reasonable adjustment of Warp line, it, can be by the back rest and warp stop frame to meet the needs of the clear shed open of air-jet weaving Location-appropriate move forward, to shorten front shed length, can reduce break to stopping platform number in this way, and reduce broadwise defect rate Occur.
(3) reasonable pneumatic picking technological parameter, to meet wealthy woven needs of jet.Its major parameter can be in loom electricity It is arranged on brain as follows:Main and auxiliary nozzle supply gas pressure is respectively set to 0.3MPa, 0.35MPa;Main burner opening/closing time be 60 °- 170°;Needle rise and fall the time be 65 ° -190 °;Pilot jet is divided into eight groups and supplies successively, and opening/closing time is respectively looming weaving Process parameters design is:1st group 60 ° -130 °, the 2nd group 80 ° -150 °, the 3rd group 100 ° -170 °, the 4th group 120 ° -190 °, the 5th 140 ° -210 °, the 6th group 150 ° -220 °, the 7th group 160 ° -230 °, the 8th group 170 ° -240 ° of group;Weft yarn angle of arrival is 230 °.
The present invention due to after each above-mentioned main weaving process takes series of process and measure, banana fiber/viscose glue/ The exploitation of tencel blended yarn home textile bed necessaries fabric is smooth with production, and fabric weaving efficiency is up to 90% or more, First Grade Percentage Before Cloth Repairing Up to 85%, storage top-quality product rate is up to 99%, and product physical properties index reaches high-class product standard to finished product after testing.
Banana fiber and tencel, viscose glue are carried out blended resultant yarn by the present invention by a certain percentage, and for developing high-grade home textile Bed necessaries fabric, can giving full play of banana fiber blending product, performances, the product have with persistence antibacterial, moisture absorption be ventilative etc. Vast market prospect applies it in home textile set of bed articles product, meets current people and pursues " natural, safe and healthy " Life idea.

Claims (4)

1. a kind of production technology of banana fiber/tencel/viscose blended yarn person's textile fabric, it is characterised in that:Including walking as follows Suddenly:
(1) raw material designs
Blended, the blending ratio of blending ratio banana fiber/tencel/viscose glue is carried out using banana fiber, tencel, viscose rayon fiber It is 30:30:40, resultant yarn 18.5tex;
(2) product design
For raw yarn feature, in conjunction with the requirement of bedclothes fabric style, product specification design is as follows:
Finished door width:248cm;
Through weft yarn:30/ tencel of banana fiber, 30/ viscose glue 4018.5tex × 30/ tencel of banana fiber, 30/ viscose glue 40 18.5tex;
Finished product weft density:420/10cm × 320 piece/10cm;
Fabric tissue:Ground is organized as the block plaid tissue based on 5/2 Warp Satin, and lattice is 1cm × 1cm;It is rolled up for anti-selvedge Side, Selvage Stitch are designed as 2/2 cut stuipes;
(3) main weaving process
A. warping process
Select domestic GA121C types warping machine, main knitting technology as follows:Total quantity of warps be 5516 × 2, warping head part 788 × 7;Speed of beaming 650m/min or so;Using tension pulley adjust tension in Warping, bobbin cradle by upper, middle and lower layer and before, during and after Row is divided into 9 sections, the weight of each section tension pulley reasonable disposition between 7-10cN;
B. sizing operation
Using domestic GA308 types dual-box slasher, using again " high pressure highly concentrated, low glued, small tension receiving coil, is impregnated with, middle starching, high returns The sizing technique route of tide ", according to " similar compatibility " principle and raw yarn strength situation, slurry selects the lower converted starch of viscosity Based on mixing slurry;Formula of size is:Converted starch 50kg, polyacrylamide 35kg, CMC5kg, smooth agent 4kg;Its starching work Skill parameter:The rate of sizing is 15 ± 1%, and regain is 8 ± 0.5%, and elongation is less than 1.0%, and size box sizing temperature is 95 DEG C, slurry Slot viscosity is 8s-9s, preceding squeezing roller pressure 12KN, post jacking roller pressure 20KN, and pre- drying tube temperature is 115 DEG C and closes drying baking Cylinder temperature is 105 DEG C, speed 40m/min;
C. drawing-in process
The block plaid tissue due to the fabric being organized as based on 5/2 Warp Satin, Selvage Stitch are designed as 2/2 variation Fang Ping groups Knit, thus must with page 12, wherein organize page 10, Selvage Stitch page 2;When drawing-in, ground through using fly threading method, that is, press 1,3,5,7,9,2, 4,6,8,10 sequences are gaited, friction when can reduce weaving in this way between warp thread;And side is through being through back zone, both sides be all made of (11, 11,12,12) threading method × 16 is entered with the reed that metric system porter is 140 teeth/10cm per dent 3;
D. air-jet weaving
Using ZAX-320 type multi-arm air-jet looms, since raw yarn is 30/ viscose glue of banana fiber, 30/ tencel 4018.5tex, yarn number Carefully, density is big, and comprehensive page is more, thus when looming weaving, technological parameter must be rationally set, and take related technical measures, it is specific as follows:
(1) since the fabric is broad fabric, pneumatic picking can Filling Insertion Time angle suitably to increase, for ensure wefting insertion smoothly into Row, loom speed is unsuitable too fast, and heald level time is suitably postponed, therefore speed is set as 500r/min, opening time is 290 °;
(2) since the Density is larger, be again in addition be organized as block plaid tissue based on 5/2 Warp Satin, Ying He The Warp line that reason is adjusted on loom carrys out opening or cleaning shed open, and suitably reduces warp tension.Because when warp tension is big, though be conducive to Opening or cleaning shed open, but can cause to stop platform rate to increase, and easily there are the float such as driving shelves, weft crackiness;Therefore warp tension answers moderate adjusting, But can be by the reasonable adjustment of Warp line, to meet the needs of the clear shed open of air-jet weaving, it can be by the position of the back rest and warp stop frame Appropriate forward movement is set, to shorten front shed length, can reduce break to stopping platform number in this way, and reduce going out for broadwise defect rate It is existing;
(3) reasonable pneumatic picking technological parameter, to meet wealthy woven needs of jet;Its major parameter can be on loom computer Setting is as follows:Main and auxiliary nozzle supply gas pressure is respectively set to 0.3MPa, 0.35MPa;Main burner opening/closing time is 60 ° -170 °; Needle rise and fall the time be 65 ° -190 °;Pilot jet is divided into eight groups and supplies successively, and opening/closing time is respectively looming weaving technique Parameter designing is:1st group 60 ° -130 °, the 2nd group 80 ° -150 °, the 3rd group 100 ° -170 °, the 4th group 120 ° -190 °, the 5th group 140 ° -210 °, the 6th group 150 ° -220 °, the 7th group 160 ° -230 °, the 8th group 170 ° -240 °;Weft yarn angle of arrival is 230 °.
2. the production technology of banana fiber/tencel according to claim 1/viscose blended yarn person's textile fabric, feature It is:The banana fiber:The banana fiber of selection is the process of fiber of refining processing, fibre fineness 7dtex, length In 60mm, ultimate strength is not less than 7.5cN.
3. the production technology of banana fiber/tencel according to claim 1/viscose blended yarn person's textile fabric, feature It is:The tencel fiber:Select 1.67D × 38mm Tencel LF fiber types.
4. the production technology of banana fiber/tencel according to claim 1/viscose blended yarn person's textile fabric, feature It is:The viscose rayon is viscose staple fibre, and specification is 1.67D × 38mm.
CN201810378444.7A 2018-04-25 2018-04-25 A kind of production technology of banana fiber/tencel/viscose blended yarn person's textile fabric Pending CN108625026A (en)