CN108610031A - 一种熔融石英陶瓷搅拌棒的生产方法 - Google Patents

一种熔融石英陶瓷搅拌棒的生产方法 Download PDF

Info

Publication number
CN108610031A
CN108610031A CN201611134663.8A CN201611134663A CN108610031A CN 108610031 A CN108610031 A CN 108610031A CN 201611134663 A CN201611134663 A CN 201611134663A CN 108610031 A CN108610031 A CN 108610031A
Authority
CN
China
Prior art keywords
fused quartz
stirring rod
quartz ceramic
hours
ceramic stirring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611134663.8A
Other languages
English (en)
Inventor
王永江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuzhou Connor Hi-Tech Materials Science And Technology Co Ltd
Original Assignee
Xuzhou Connor Hi-Tech Materials Science And Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xuzhou Connor Hi-Tech Materials Science And Technology Co Ltd filed Critical Xuzhou Connor Hi-Tech Materials Science And Technology Co Ltd
Priority to CN201611134663.8A priority Critical patent/CN108610031A/zh
Publication of CN108610031A publication Critical patent/CN108610031A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种熔融石英陶瓷搅拌棒的生产方法,本发明属于熔融石英陶瓷制品生产领域,生产该产品使用的原料配方按重量百分比计算:200‑210目熔融石英硅微粉55‑57%、250‑260目熔融石英硅微粉40‑42%、碳化硼1%、氮化硅1%、纳米胶0.40%、过硫酸铵0.20%,四甲基乙二胺0.20%,聚乙二醇200 0.20%;该生产方法具有使用设备少、工艺简单、无污染废弃物排放、产品质量好等一系列优点;产品熔融石英陶瓷搅拌棒在1000℃时具有优异的热性能、化学稳定性能和电绝缘性能,可用于多种场合的人工搅拌或机械搅拌,尤其是高温环境。

Description

一种熔融石英陶瓷搅拌棒的生产方法
技术领域
本发明属于熔融石英陶瓷制品生产领域,尤其涉及一种以熔融石英硅微粉为原料生产熔融石英陶瓷搅拌棒的方法。
背景技术
熔融石英陶瓷是一种以熔融石英为原料,采用陶瓷生产工艺制成的熔融石英材料,其特点是:热膨胀系数小、热稳定性好、电绝缘性好、耐化学侵蚀性好;石英陶瓷最大的优点是在l1O0℃ 以下时,其强度随着温度的升高而增加,从室温至1100 ℃时,其强度可增加33%,在1250℃时产品仍可正常使用。熔融石英陶瓷的主要产品种类繁多,如玻璃水平钢化炉用石英陶瓷辊、浮法玻璃窑用闸板砖、浮法玻璃退火炉用空心辊、铸钢用水口、金属带材热处理炉用空心辊、玻璃及冶金窑炉用水口、冲头、坩埚、炉体、科硫、匀科筒、搅拌棒、料盆、旋转管、焦炉炉门及上升管内衬以及绝缘插件、微波屏、灭弧罩、高效间歇炉用热绝缘器、激光反射器和其它光学零件、石英光源用光反射和吸收零件等.此外,在导弹、火箭、雷达等方面也有少量应用。这些产品使用的主要原料都是熔融石英硅微粉,不同点仅是硅微粉的粒度不同、辅料不同、产品的形状不同而已。本发明是一种熔融石英陶瓷搅拌棒,搅拌棒种类繁多,短到长度几厘米,长达几米,直径有几毫米到十几厘米,可用于多种场合的人工搅拌或机械搅拌,尤其是高温环境,该产品要求强度高、耐高温,具有高温性能稳定不变形、热膨胀小、化学稳定性好、表面光滑细腻、耐磨性好,经长期使用不易磨损等特点。本发明产品在生产中拟解决的关键技术问题有,一是熔融石英陶瓷粉的颗粒度的最佳配比;二是辅料的最佳组合,辅料的组合将直接影响到熔融石英陶瓷粉颗粒的结合度,对减小空隙,提高产品的质量至关重要。
发明内容
本发明主要解决的问题是提供一种熔融石英陶瓷搅拌棒的生产方法,生产该产品使用的原料重量配比为:200-210目熔融石英硅微粉55-57%、250-260目熔融石英硅微粉40-42%、碳化硼1%、氮化硅1%、纳米胶0.40%、过硫酸铵0.20%,四甲基乙二胺0.20%,聚乙二醇2000.20%。
本发明可以通过以下技术方案来实现:
(1)在搅拌罐中先将配方量的纳米胶、过硫酸铵、四甲基乙二胺、聚乙二醇200加入搅拌罐中,常温下搅拌混合均匀,再将配方量的200-210目熔融石英硅微粉、250-260目熔融石英硅微粉、碳化硼、氮化硅送入球磨机球磨2.8-3.0小时,将搅拌罐中的混合物加热至30-35℃后加入球磨机,掺混均匀;
(2)将球磨机中的物料加注入熔融石英陶瓷搅拌棒模具,采用边浇铸边震动的方法浇铸成型,然后加压放置25-27小时后脱去模具,再自然晾干32-34小时;
(3)将晾干的熔融石英陶瓷搅拌棒送入窑炉开始加热升温,先经4.2-4.4小时的时间将烧结温度缓慢的从0℃升至400℃后,再在5小时时间内将烧结温度从400℃升至1190-1200℃,维持此温度36-37小时后停止加热,逐步降温至常温后得到熔融石英陶瓷搅拌棒的毛坯料;
(4)将熔融石英陶瓷搅拌棒的毛坯料送入外圆磨床,将外圆磨至规定尺寸即得成品。
本发明的进一步技术方案是:
步骤(3)所述的窑炉为煤气发生梭式窑炉。
步骤(3)所述的窑炉内的烧结温度为1195℃,烧结的总时间为36.5小时。
本发明的有益效果是:提供了一种熔融石英陶瓷搅拌棒的生产方法,该生产方法具有使用设备少、工艺简单、无污染废弃物排放、产品质量好等一系列优点;产品熔融石英陶瓷搅拌棒在1000℃以下具有优异的热性能、化学稳定性能和电绝缘性能,主要作为各种人工或机械搅拌工具使用。
具体实施方式
通过以下实施例进一步描述本发明。
实施例1:
在搅拌罐中先将将占总量为0.40%的纳米胶、0.20%的过硫酸铵,0.20%的四甲基乙二胺,0.20%的聚乙二醇200加入搅拌罐中,常温下搅拌混合均匀,再将占总量为55%的200-210目熔融石英硅微粉、占总量为42%的250-260目熔融石英硅微粉、占总量为1%的碳化硼、占总量为1%的氮化硅送入球磨机球磨2.8小时,将搅拌罐中的混合物加热至30℃后加入球磨机,掺混均匀;将球磨机中的物料加注入熔融石英陶瓷搅拌棒模具,采用边浇铸边震动的方法浇铸成型,然后加压放置25小时后脱去模具,再自然晾干34小时;将晾干的熔融石英陶瓷搅拌棒送入窑炉开始加热升温,先经4.2小时的时间将烧结温度缓慢的从0℃升至400℃后,再在5小时时间内将烧结温度从400℃升至1190℃,维持此温度37小时后停止加热,逐步降温至常温后得到熔融石英陶瓷搅拌棒的毛坯料;将熔融石英陶瓷搅拌棒的毛坯料送入外圆磨床,将外圆磨至规定尺寸即得成品。
实施例2:
在搅拌罐中先将将占总量为0.40%的纳米胶、0.20%的过硫酸铵,0.20%的四甲基乙二胺,0.20%的聚乙二醇200加入搅拌罐中,常温下搅拌混合均匀,再将占总量为56%的200-210目熔融石英硅微粉、占总量为41%的250-260目熔融石英硅微粉、占总量为1%的碳化硼、占总量为1%的氮化硅送入球磨机球磨2.9小时,将搅拌罐中的混合物加热至32.5℃后加入球磨机,掺混均匀;将球磨机中的物料加注入熔融石英陶瓷搅拌棒模具,采用边浇铸边震动的方法浇铸成型,然后加压放置26小时后脱去模具,再自然晾干33小时;将晾干的熔融石英陶瓷搅拌棒送入窑炉开始加热升温,先经4.3小时的时间将烧结温度缓慢的从0℃升至400℃后,再在5小时时间内将烧结温度从400℃升至1195℃,维持此温度36.5小时后停止加热,逐步降温至常温后得到熔融石英陶瓷搅拌棒的毛坯料;将熔融石英陶瓷搅拌棒的毛坯料送入外圆磨床,将外圆磨至规定尺寸即得成品。
实施例3:
在搅拌罐中先将将占总量为0.40%的纳米胶、0.20%的过硫酸铵,0.20%的四甲基乙二胺,0.20%的聚乙二醇200加入搅拌罐中,常温下搅拌混合均匀,再将占总量为57%的200-210目熔融石英硅微粉、占总量为40%的250-260目熔融石英硅微粉、占总量为1%的碳化硼、占总量为1%的氮化硅送入球磨机球磨3.0小时,将搅拌罐中的混合物加热至35℃后加入球磨机,掺混均匀;将球磨机中的物料加注入熔融石英陶瓷搅拌棒模具,采用边浇铸边震动的方法浇铸成型,然后加压放置27小时后脱去模具,再自然晾干32小时;将晾干的熔融石英陶瓷搅拌棒送入窑炉开始加热升温,先经4.4小时的时间将烧结温度缓慢的从0℃升至400℃后,再在5小时时间内将烧结温度从400℃升至1200℃,维持此温度36小时后停止加热,逐步降温至常温后得到熔融石英陶瓷搅拌棒的毛坯料;将熔融石英陶瓷搅拌棒的毛坯料送入外圆磨床,将外圆磨至规定尺寸即得成品。

Claims (3)

1.一种熔融石英陶瓷搅拌棒的生产方法,其原料配方按重量百分比计算:200-210目熔融石英硅微粉55-57%、250-260目熔融石英硅微粉40-42%、碳化硼1%、氮化硅1%、纳米胶0.40%、过硫酸铵0.20%,四甲基乙二胺0.20%,聚乙二醇200 0.20%;其特征是:
(1)在搅拌罐中先将配方量的纳米胶、过硫酸铵、四甲基乙二胺、聚乙二醇200加入搅拌罐中,常温下搅拌混合均匀,再将配方量的200-210目熔融石英硅微粉、250-260目熔融石英硅微粉、碳化硼、氮化硅送入球磨机球磨2.8-3.0小时,将搅拌罐中的混合物加热至30-35℃后加入球磨机,掺混均匀;
(2)将球磨机中的物料加注入熔融石英陶瓷搅拌棒模具,采用边浇铸边震动的方法浇铸成型,然后加压放置25-27小时后脱去模具,再自然晾干32-34小时;
(3)将晾干的熔融石英陶瓷搅拌棒送入窑炉开始加热升温,先经4.2-4.4小时的时间将烧结温度缓慢的从0℃升至400℃后,再在5小时时间内将烧结温度从400℃升至1190-1200℃,维持此温度36-37小时后停止加热,逐步降温至常温后得到熔融石英陶瓷搅拌棒的毛坯料;
(4)将熔融石英陶瓷搅拌棒的毛坯料送入外圆磨床,将外圆磨至规定尺寸即得成品。
2.根据权利要求1所述的一种熔融石英陶瓷搅拌棒的生产方法,其特征是:步骤(3)所述的窑炉为煤气发生梭式窑炉。
3.根据权利要求1所述的一种熔融石英陶瓷搅拌棒的生产方法,其特征是:步骤(3)所述的窑炉内的烧结温度为1195℃,烧结的总时间为36.5小时。
CN201611134663.8A 2016-12-11 2016-12-11 一种熔融石英陶瓷搅拌棒的生产方法 Pending CN108610031A (zh)