CN108505635B - 具有绝热吸声的毡板 - Google Patents
具有绝热吸声的毡板 Download PDFInfo
- Publication number
- CN108505635B CN108505635B CN201810225121.4A CN201810225121A CN108505635B CN 108505635 B CN108505635 B CN 108505635B CN 201810225121 A CN201810225121 A CN 201810225121A CN 108505635 B CN108505635 B CN 108505635B
- Authority
- CN
- China
- Prior art keywords
- parts
- sound absorption
- heat insulation
- layer
- sound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本案涉及一种具有绝热吸声的毡板,所述绝热吸声毡板包括自上而下依次叠加的第一防火织物层、绝热吸声层和第二防火织物层;其中,所述绝热吸声层包括以下重量份的材料:铜氨纤维40~60份;硅酸铝纤维24~30份;乙烯‑偏二氟乙烯共聚物15~20份;聚对苯二甲酸乙二酯纤维8~14份;硅灰石20~40份;吸声剂10~20份;保温剂6~12份。本发明的绝热吸声的毡板,其结构包括第一防火织物层、绝热吸声层和第二防火织物层,使其具有更优异的防火性能和绝热消音性,其防火等级达到A级。
Description
技术领域
本发明涉及复合材料技术领域,特别是涉及一种具有绝热吸声的毡板。
背景技术
随着经济和技术的发展,人们对建筑物室内声学效果的要求越来越高,比如在宾馆的会议室和大型的体育场馆,为了达到良好的音响效果,对室内的装饰和装修材料就提出了很高的吸声系数要求。随着科技的发展,越来越多同时具有吸声绝热及装饰作用的材料及其复合构件被用于室内的装饰和装修。
目前,市场上的绝热吸声材料主要有岩棉、玻璃棉、硅酸铝棉等矿物纤维产品,另外还有泡沫塑料类的绝热吸声材料,比如柔性橡塑、发泡聚氨酯、酚醛泡沫、聚乙烯泡沫材料等。这些材料普遍存在耐高温性能差,降噪音效果不理想的缺点。
发明内容
针对上述不足之处,本发明的目的在于提供一种具有绝热吸声的毡板,其具有优良的阻燃性能、绝热性能和吸声性能,且使用方便。
一种具有绝热吸声的毡板,其中,所述绝热吸声毡板包括自上而下依次叠加的第一防火织物层、绝热吸声层和第二防火织物层;
其中,所述绝热吸声层包括以下重量份的材料:
铜氨纤维 40~60份;
硅酸铝纤维 24~30份;
乙烯-偏二氟乙烯共聚物 15~20份;
聚对苯二甲酸乙二酯纤维 8~14份;
硅灰石 20~40份;
吸声剂 10~20份;
保温剂 6~12份。
优选的是,所述的具有绝热吸声的毡板,其中,所述吸声剂由如下质量份的组分组成:
膨胀珍珠岩 30~45wt%;
空心玻璃微球 55~70wt%。
优选的是,所述的具有绝热吸声的毡板,其中,所述保温剂包括70~ 80wt%二氧化硅气凝胶、15~20wt%碳化硼和5~10wt%硫化锶。
优选的是,所述的具有绝热吸声的毡板,其中,所述第一防火织物层组份及重量份数为玻璃短纤50~70份、硼砂20~30份、氧化铈10~15份、聚磷酸铵6~12份、四丙氟胶乳3~5份。
优选的是,所述的具有绝热吸声的毡板,其中,所述玻璃短纤直径为10 μm,长度为4~6mm。
优选的是,所述的具有绝热吸声的毡板,其中,所述聚磷酸铵的数均分子量为1600~1800g/mol。
优选的是,所述的具有绝热吸声的毡板,其中,所述第一防火织物层、绝热吸声层和第二防火织物层之间均通过胶粘剂粘连。
优选的是,所述的具有绝热吸声的毡板,其中,所述胶粘剂为聚氨酯。
优选的是,所述的具有绝热吸声的毡板,其中,所述第二防火织物层为气相二氧化硅和多晶莫来石纤维。
本发明的有益效果是:
(1)本发明所述的绝热吸声的砧板,其结构包括第一防火织物层、绝热吸声层和第二防火织物层,使其具有更优异的防火性能和绝热消音性,其防火性能达到A级,导热系数为0.03-0.07w/m.k,隔音指数≥52dB,抗压强度≥ 8.2Mpa。
(2)本发明以铜氨纤维作为绝热吸声层的主体;通过加入硅酸铝纤维提高其绝热特性,耐化学稳定性、和吸声性好;通过加入乙烯-偏二氟乙烯共聚物,提高其耐化学腐蚀性能、耐氧化性、柔韧性和耐冲击性强度;通过加入聚对苯二甲酸乙二酯纤维提高其耐高温、耐低温性能、耐水性能、耐抗疲劳性、提高其稳定性和韧性;通过加入硅灰石提高其耐高温性和机械性能;膨胀珍珠岩和空心玻璃微球协同作为绝热吸声毡板的吸声剂,提高其吸声性能,并可提高其保温、隔热性能;通过二氧化硅气凝胶、碳化硼和硫化锶共同作为保温剂,强化其绝热效果。
(3)本发明玻璃短纤作为第一防火织物层的主体,其具有抗冲击强度大、弹性系数高、不燃和耐化学性能佳的优点;通过加入硼砂、氧化铈和聚磷酸铵进一步提高其耐火性能;通过加入四丙氟胶乳提高其耐酸碱性能、耐侯性和耐辐射性能和柔软性。
(4)本发明第二防火织物层为气相二氧化硅和多晶莫来石纤维,多晶莫来石纤维具有高温尺寸稳定性,大分子结构不易降解(长期使用温度在200℃以上),具有良好的耐水解和耐化学药剂等性能,通过气相二氧化硅可提高其耐热性能。
具体实施方式
下面结合实施例对本发明做进一步的详细说明,以令本领域技术人员参照说明书文字能够据以实施。
本案提供一种具有绝热吸声的毡板,其中,所述绝热吸声毡板包括自上而下依次叠加的第一防火织物层、绝热吸声层和第二防火织物层;
其中,所述绝热吸声层包括以下重量份的材料:
铜氨纤维 40~60份;
硅酸铝纤维 24~30份;
乙烯-偏二氟乙烯共聚物 15~20份;
聚对苯二甲酸乙二酯纤维 8~14份;
硅灰石 20~40份;
吸声剂 10~20份;
保温剂 6~12份。
铜氨纤维作为绝热吸声层的主体,其具有较高的耐热性能和耐腐蚀性能;硅酸铝纤维具有优良的绝热特性,耐酸、碱腐蚀性好,具有优良化学稳定性、电绝缘性、吸声性好,对500Hz以上中、高度波可吸收80%以上,通过加入硅酸铝纤维提高其绝热性能和吸声性能;通过加入乙烯-偏二氟乙烯共聚物,提高其耐化学腐蚀性能、耐氧化性、柔韧性和耐冲击性强度;通过加入聚对苯二甲酸乙二酯纤维提高其耐高温、耐低温性能、耐水性能、耐抗疲劳性、提高其稳定性和韧性;通过加入硅灰石提高其耐高温性和机械性能。
优选的是,所述的具有绝热吸声的毡板,其中,所述吸声剂由如下质量份的组分组成:
膨胀珍珠岩 30~45wt%;
空心玻璃微球 55~70wt%。
膨胀珍珠岩和空心玻璃微球协同作为绝热吸声毡板的吸声剂,提高其吸声性能,并可提高其保温、隔热性能。
优选的是,所述的具有绝热吸声的毡板,其中,所述保温剂包括70~ 80wt%二氧化硅气凝胶、15~20wt%碳化硼和5~10wt%硫化锶。当相邻两根纤维互相接触时,热量会沿着接触点流走,形成“热桥”。如果形成纤维+二氧化硅气凝胶+纤维的结构,二氧化硅气凝胶在这里充当了热阻的作用,因为其优良的绝热性能,热量很难沿着二氧化硅气凝胶传递过去,形成“位隔”效应。同时二氧化硅气凝胶填充了纤维之间的间隙,阻止了空气的对流。这两种效应联合作用,有效提高了纤维的绝热性能。碳化硼和硫化锶作为遮光剂,降低辐射传热,以达到更好的隔热效果。通过二氧化硅气凝胶、碳化硼和硫化锶共同作为保温剂,强化其绝热效果。
优选的是,所述的具有绝热吸声的毡板,其中,所述第一防火织物层组份及重量份数为玻璃短纤50~70份、硼砂20~30份、氧化铈10~15份、聚磷酸铵6~12份、四丙氟胶乳3~5份。玻璃短纤作为第一防火织物层的主体,其具有抗冲击强度大、弹性系数高、不燃和耐化学性能佳的优点;通过加入硼砂、氧化铈和聚磷酸铵进一步提高其耐火性能;通过加入四丙氟胶乳提高其耐酸碱性能、耐侯性和耐辐射性能和柔软性。
优选的是,所述的具有绝热吸声的毡板,其中,所述玻璃短纤直径为10 μm,长度为4~6mm。
优选的是,所述的具有绝热吸声的毡板,其中,所述聚磷酸铵的数均分子量为1600~1800g/mol。
优选的是,所述的具有绝热吸声的毡板,其中,所述第一防火织物层、绝热吸声层和第二防火织物层之间均通过胶粘剂粘连。
优选的是,所述的具有绝热吸声的毡板,其中,所述胶粘剂为聚氨酯。聚氨酯胶粘剂主链柔性很好,其耐受冲击震动和弯曲疲劳,剥离强度很高,特别是耐低温性能极其优异。
优选的是,所述的具有绝热吸声的毡板,其中,所述第二防火织物层为气相二氧化硅和多晶莫来石纤维。多晶莫来石纤维具有高温尺寸稳定性,大分子结构不易降解(长期使用温度在200℃以上),具有良好的耐水解和耐化学药剂等性能。通过气相二氧化硅可提高其耐热性能。
下表列出一些具体的实施例:
下表是实施例和对比例的测试结果:
尽管本发明的实施方案已公开如上,但其并不仅仅限于说明书和实施方式中所列运用,它完全可以被适用于各种适合本发明的领域,对于熟悉本领域的人员而言,可容易地实现另外的修改,因此在不背离权利要求及等同范围所限定的一般概念下,本发明并不限于特定的细节。
Claims (7)
1.一种具有绝热吸声的毡板,其特征在于,所述具有绝热吸声的毡板包括自上而下依次叠加的第一防火织物层、绝热吸声层和第二防火织物层;
其中,所述绝热吸声层包括以下重量份的材料:
铜氨纤维 40~60份;
硅酸铝纤维 24~30份;
乙烯-偏二氟乙烯共聚物 15~20份;
聚对苯二甲酸乙二酯纤维 8~14份;
硅灰石 20~40份;
吸声剂 10~20份;
保温剂 6~12份;
所述吸声剂由如下质量份的组分组成:
膨胀珍珠岩 30~45wt%;
空心玻璃微球 55~70wt%;
所述第一防火织物层组份及重量份数为玻璃短纤50~70份、硼砂20~30份、氧化铈10~15份、聚磷酸铵6~12份、四丙氟胶乳3~5份。
2.如权利要求1所述的具有绝热吸声的毡板,其特征在于,所述保温剂包括70~80wt%二氧化硅气凝胶、15~20wt%碳化硼和5~10wt%硫化锶。
3.如权利要求1所述的具有绝热吸声的毡板,其特征在于,所述玻璃短纤直径为10μm,长度为4~6mm。
4.如权利要求1所述的具有绝热吸声的毡板,其特征在于,所述聚磷酸铵的数均分子量为1600~1800g/mol。
5.如权利要求1所述的具有绝热吸声的毡板,其特征在于,所述第一防火织物层、绝热吸声层和第二防火织物层之间均通过胶粘剂粘连。
6.如权利要求5所述的具有绝热吸声的毡板,其特征在于,所述胶粘剂为聚氨酯。
7.如权利要求1所述的具有绝热吸声的毡板,其特征在于,所述第二防火织物层为气相二氧化硅和多晶莫来石纤维。