CN108477719A

CN108477719A - A kind of production technology of layer insulation composite cloth material, down products with penetration resistance structure and layer insulation composite cloth material

Info

Publication number: CN108477719A
Application number: CN201810123758.2A
Authority: CN
Inventors: 罗明
Original assignee: Sheng Xin New Material Technology (jiashan) Co Ltd
Current assignee: Sheng Xin New Material Technology (jiashan) Co Ltd
Priority date: 2018-02-07
Filing date: 2018-02-07
Publication date: 2018-09-04

Abstract

A kind of layer insulation composite cloth material, the production technology of down products with penetration resistance structure and warm composite material-feeding, pass through composite material-feeding on the inside of two point gluing structure composite and outside composite material-feeding, and there are gaps between the first outer fabric cloth and the second inner fabrics cloth, inside composite material-feeding is connect along edge by edge sealing structure with outside composite material-feeding, and it is equipped at least one down-filling mouth in edge, down feather material can be filled by down-filling mouth in the gap between inside composite material-feeding and outside composite material-feeding, it can so solve to bore suede phenomenon and run suede phenomenon, without suture, it is durable.

Description

A kind of layer insulation composite cloth material, down products with penetration resistance structure and layer insulation composite cloth material Production technology

Technical field

The present invention relates to fabric material field, especially a kind of layer insulation composite cloth material, down products with penetration resistance structure and guarantor The production technology of warm composite material-feeding.

Background technology

Natural feather is a kind of heat insulating material that natural lightweight is excellent, and insulation garment and bedding field have extensively in winter Application, but it is very light and easily flows and moves with air, and is very easy to from the gap in fabric yarn or tissue Or slowly drilled out in the pinprick micropore of sewing, that is, it generates and bores suede phenomenon.The natural feather drilled out is liable to stick on other clothings Influence beautiful, it is also possible to cause sensitive group respiratory tract not just as asthma the problems such as.

Chinese patent CN105128442B discloses a kind of DOWN PROOF displacement anti-chiseling down and the structure that maintains fabric elasticity Manufacturing process, it has the two layers of cloth bed of material, natural feather to be filled between two layers of cloth, and natural feather is wrapped with air-permeable elastic film, elasticity Breathable films invest the inner surface of bed of cloth, the inner surface setting tie point or glue point of air-permeable elastic film.To a certain extent The problem of less brill suede.

There is bed of cloth protection on the outside of such air-permeable elastic film, but inside directly contacts friction with natural feather, to the internal layer of film Protection is not very perfect and abundant, and natural feather can quickly flow aggregation with air flowing in film, cause the bulkiness of natural feather compared with Difference there are problems that running suede.

In order to solve to run suede phenomenon, generally suture is carried out in longitude and latitude direction so that villus is limited in one piece one piece In lattice, but suture necessarily leads to pin hole, and villus can be drilled out from pin hole so that bores the aggravation of suede phenomenon.

In addition, being directly arranged at due to glue point on more smooth air-permeable elastic film, glue point is insecure, is easy to slip, make Use short life.

Invention content

In view of this, can solve to bore suede phenomenon the present invention provides one kind and run suede phenomenon, down-filling region without suture, warp The production technology of long durable layer insulation composite cloth material and down products with penetration resistance structure and layer insulation composite cloth material, to solve above-mentioned ask Topic.

A kind of layer insulation composite cloth material, it includes the inside composite material-feeding being mutually bonded and outside composite material-feeding, Yi Jishe to include It is placed in the edge sealing structure of the edge between inside composite material-feeding and outside composite material-feeding, inside composite material-feeding and outside Compound Fabric Edge between material is additionally provided at least one down-filling mouth；The inside composite material-feeding includes that the first moisture-inhibiting is anti-successively from inside to outside The side of wind elasticity PU films and the first outer fabric cloth, the first outer fabric cloth towards windproof elasticity PU films of the first moisture-inhibiting is set There is the first two point to apply plastic structure；The outside composite material-feeding includes the second inner fabrics cloth and the second moisture-inhibiting successively from inside to outside Windproof elasticity PU films, the second inner fabrics cloth apply towards the side of the windproof elasticity PU films of the second moisture-inhibiting equipped with the second two point cementing First outer fabric cloth of structure, the inside composite material-feeding is multiple far from the side of the windproof elasticity PU films of the first moisture-inhibiting or outside The the second inner fabrics cloth for closing cloth is equipped with third two point painting plastic structure towards the side of inside composite material-feeding.

Further, it is irregular distribution that first, second two point, which applies plastic structure, and distribution density is 80-180/ cm2。

Further, the third two point applies bulk or strip distribution of the plastic structure in interval, forms two point coating area, In two point coating area, it is irregular distribution that the third two point, which applies plastic structure, and distribution density is 20-130/cm2.

Further, the windproof elasticity PU films of first moisture-inhibiting and the windproof elasticity PU films of the second moisture-inhibiting are for low ventilated membrane or not Ventilated membrane.

Further, the edge sealing structure has the elastic base fabric of strip, and the both sides of elastic base fabric are respectively equipped with the 4th Two point applies plastic structure, and it is irregular distribution that the 4th two point, which applies plastic structure, and distribution density is 20-130/cm2.

Further, it is additionally provided with the first inner fabrics cloth on the inside of the windproof elasticity PU films of first moisture-inhibiting, described One inner fabrics cloth is equipped with the 5th two point towards the side of the windproof elasticity PU films of the first moisture-inhibiting and applies plastic structure.

Further, it is additionally provided with the second outer fabric cloth on the outside of the windproof elasticity PU films of second moisture-inhibiting, described Two outer fabric clothes are equipped with the 6th two point towards the side of the windproof elasticity PU films of the second moisture-inhibiting and apply plastic structure.

A kind of down products with penetration resistance structure has layer insulation composite cloth material as described above and is filled in layer insulation composite cloth material In down feather material, be stacked in edge between adjacent layer insulation composite cloth material, and sewed up by suture.

Further, the suture is arranged within the scope of the edge sealing of both sides formation of edge sealing structure.

Further, the edge sealing range is equipped with horda chirurgicalis close to the edge of both sides, is set in the middle part of the edge sealing structure There are "the" shape rip out stitches.

Further, it is in U that the edge sealing structure of the first adjacent layer insulation composite cloth material and the second layer insulation composite cloth material, which is bent, The edge sealing structure of type, the edge sealing structure of the first layer insulation composite cloth material and the second layer insulation composite cloth material, which is staggered, colludes with.

A kind of production technology of layer insulation composite cloth material, includes the following steps：

Step S1：Make outside composite material-feeding；

Step S2：Make inside composite material-feeding；

Step S3：Side of the first outer fabric cloth of composite material-feeding far from the windproof elasticity PU films of the first moisture-inhibiting in inside Two point is set and applies plastic structure；

Step S4：Make edge sealing structure；

Step S5：Edge sealing structure is compound in the edge of inside composite material-feeding；

Step S6：Outside composite material-feeding and inside composite material-feeding and edge sealing structure is compound.

Further, above-mentioned steps S1 includes the following steps：

Step S11：Make the second inner fabrics cloth of outside composite material-feeding；

Step S12：Make the second outer fabric cloth of outside composite material-feeding；

Step S13：There is provided the second moisture-inhibiting windproof elasticity PU films；

Step S14：The compound second inner fabrics cloth of hot pressing, the windproof elasticity PU films of the second moisture-inhibiting and the second outer fabric cloth Material.

Further, above-mentioned steps S14 includes the following steps：

Step S141：Set the operating condition of compounding machine；

Step S142：Second inner fabrics cloth is had the one of two point painting plastic structure to face upward and is through work feed lengths On；

Step S143：The windproof elasticity PU films of second moisture-inhibiting are placed on debatching position, and are through in work feed lengths；

Step S144：Second outer fabric cloth is placed on debatching position, and applies the one of plastic structure with two point and faces It is through in work feed lengths downwards；

Step S145：It regulates each section tension, sets speed, start compounding machine, make the second inner fabrics cloth and the The two point painting plastic structure thawing of two outer fabric clothes is simultaneously compound with the both sides of the windproof elasticity PU films of the second moisture-inhibiting.

Further, setting two point applies plastic structure and includes the following steps：

Step S151：Prepare prime cement；

Step S152：Prepare thermosol powder；

Step S153：Slurry point coating treatment is carried out in embryo cloth or base fabric with prime cement, forms multiple slurry points, multiple slurry point structures At prime cement coating；

Step S154：Dusting coating treatment is carried out on prime cement coating with thermosol powder, distributes in prime cement coating The thermosol gel coating on surface.

Further, above-mentioned steps S4 includes the following steps：

Step S41：Base fabric is provided；

Step S42：Two point is respectively set in two sides of base fabric and applies plastic structure.

Step S1：Make outside composite material-feeding；

Step S2：Make inside composite material-feeding；

Step S4：Make edge sealing structure；

Step S5：Outside composite material-feeding and inside composite material-feeding is compound；

Step S6：Outside composite material-feeding is detached with inside composite material-feeding 100 along edge, edge sealing structure is put into so that Edge sealing structure is aligned with outside composite material-feeding and inside composite material-feeding along edge；

Step S7：Outside composite material-feeding, edge sealing structure and inside composite material-feeding is compound along edge.

Compared with prior art, layer insulation composite cloth material of the invention and down products with penetration resistance structure and layer insulation composite cloth material Production technology by composite material-feeding on the inside of two point gluing structure composite and outside composite material-feeding, and in the first outer fabric cloth There are gaps, inside composite material-feeding to pass through edge sealing structure along edge with outside composite material-feeding between the second inner fabrics cloth Connection, and at least one down-filling mouth is equipped in edge, down feather material can be filled by down-filling mouth inside composite material-feeding with it is outer In gap between the composite material-feeding of side, it can so solve to bore suede phenomenon and run suede phenomenon, be not necessarily to suture, be durable, there is appropriateness Elasticity, wind-proof warming, anti-chiseling down, air-moisture-permeable, comfort is good.

Description of the drawings

The embodiment of the present invention is described below in conjunction with attached drawing, wherein：

Fig. 1 is the structural schematic diagram of the first embodiment of layer insulation composite cloth material provided by the invention.

Fig. 2 is the enlarged diagram of part A in Fig. 1.

Fig. 3 is the structural schematic diagram of inside composite material-feeding in Fig. 1.

Fig. 4 is the structural schematic diagram of outside composite material-feeding in Fig. 1.

Fig. 5 is the vertical view of the inside composite material-feeding in Fig. 3.

Fig. 6 is the structural schematic diagram of the second embodiment of layer insulation composite cloth material provided by the invention.

Fig. 7 is the enlarged diagram of part A in Fig. 6.

Fig. 8 is the structural schematic diagram of inside composite material-feeding in Fig. 6.

Fig. 9 is the structural schematic diagram of outside composite material-feeding in Fig. 6.

Figure 10 is the side sectional view of edge sealing structure in Fig. 1 or Fig. 6.

Figure 11 is the vertical view of layer insulation composite cloth material provided by the invention.

Figure 12 is the stacking schematic diagram of down products with penetration resistance structure provided by the invention.

Figure 13 is the sewing schematic diagram of down products with penetration resistance structure provided by the invention.

Figure 14 is the flow diagram of the first embodiment of the production technology of layer insulation composite cloth material provided by the invention.

Figure 15 is the flow diagram of the second embodiment of the production technology of layer insulation composite cloth material provided by the invention.

Specific implementation mode

Specific embodiments of the present invention are further elaborated below based on attached drawing.It should be understood that herein The explanation of the embodiment of the present invention is not intended to limit the scope of protection of the present invention.

It please refers to Fig.1 and Fig. 2, is a kind of first embodiment of layer insulation composite cloth material provided by the invention, it is warming compound Cloth includes the inside composite material-feeding 100 being mutually bonded and outside composite material-feeding 200, and for connecting inside composite material-feeding 100 with the edge sealing structure 300 at the edge of outside composite material-feeding 200, after clothing is made, inside composite material-feeding 100 is towards human body flesh Skin.In present embodiment, using the direction residing for inside composite material-feeding 100 as inside, with the direction residing for outside composite material-feeding 200 For outside.

It please also refer to Fig. 3, inside composite material-feeding 100 includes the windproof elasticity PU films of the first moisture-inhibiting 120 successively from inside to outside And the first outer fabric cloth 130, the side of the first outer fabric cloth 130 towards the windproof elasticity PU films of the first moisture-inhibiting 120 are set There is two point to apply plastic structure 150, the first outer fabric cloth 130 applies plastic structure 150 and the windproof elasticity PU of the first moisture-inhibiting by two point Film 120 is bonded.Side of the first outer fabric cloth 130 far from the windproof elasticity PU films of the first moisture-inhibiting 120 also is provided with two point gluing Structure 160.

Fig. 4 is please also refer to, outside composite material-feeding 200 includes the second inner fabrics cloth 210, second successively from inside to outside The side of the windproof elasticity PU films 220 of moisture-inhibiting, the second inner fabrics cloth 210 towards the windproof elasticity PU films of the second moisture-inhibiting 220 is equipped with Two point applies plastic structure 240, and the second inner fabrics cloth 210 applies plastic structure 240 and the windproof elasticity PU films of the second moisture-inhibiting by two point 220 bondings.In other embodiment, two point applies plastic structure 160 and may also set up the second inner fabrics in outside composite material-feeding 200 Cloth 210 is towards on the side of inside composite material-feeding 100.

Inside composite material-feeding 100 is Nian Jie with outside composite material-feeding 200 by two point painting plastic structure 160.

Inside composite material-feeding 100 is connect along edge by edge sealing structure 300 with outside composite material-feeding 200, and at edge Place is equipped at least one down-filling mouth 400.

It is irregular distribution that two point, which applies plastic structure 150,240, and distribution density is 80-180/cm2.So that the first inside is knitted Object cloth 110, the first outer fabric cloth 130 are close to connect with the both sides of the windproof elasticity PU films of the first moisture-inhibiting 120 respectively, and second Inner fabrics cloth 210, the second outer fabric cloth 230 are close to connect with the both sides of the windproof elasticity PU films of the second moisture-inhibiting 220 respectively It connects.

Referring to FIG. 5, two point applies bulk or strip distribution of the plastic structure 160 in interval, forms the two point being spaced apart and apply Glue area 170 forms felting channel 180 so between adjacent two point coating area 170, and down feather material 500 can pass through down-filling mouth 400 are filled into the felting channel 180 between inside composite material-feeding 100 and outside composite material-feeding 200.In two point coating area 170, It is irregular distribution that the two point, which applies plastic structure 160, and distribution density is 20-130/cm2.One kind provided by the invention is warming multiple In the first embodiment for closing cloth, elastic PU films can be directly in the most inner side or outermost of layer insulation composite cloth material, have corium Texture, it is easy to clean.

Fig. 6 to Fig. 9 is please referred to, is a kind of second embodiment of layer insulation composite cloth material provided by the invention, it is warming compound Cloth includes the inside composite material-feeding 100 being mutually bonded and outside composite material-feeding 200, and for connecting inside composite material-feeding 100 with the edge sealing structure 300 at the edge of outside composite material-feeding 200, after clothing is made, inside composite material-feeding 100 is towards human body flesh Skin.In present embodiment, using the direction residing for inside composite material-feeding 100 as inside, with the direction residing for outside composite material-feeding 200 For outside.

Fig. 7 and Fig. 8 is please also refer to, inside composite material-feeding 100 includes the first inner fabrics cloth successively from inside to outside 110, the windproof elasticity PU films 120 of the first moisture-inhibiting and the first outer fabric cloth 130, the first inner fabrics cloth 110 towards first The side of the windproof elasticity PU films of moisture-inhibiting 120 is equipped with two point and applies plastic structure 140, and the first outer fabric cloth 130 is towards the first moisture-inhibiting The side of windproof elasticity PU films 120 is equipped with two point and applies plastic structure 150, the first inner fabrics cloth 110 and the first outer fabric cloth Material 130 applies two side bonds of the plastic structure 140,150 respectively with the windproof elasticity PU films of the first moisture-inhibiting 120 by two point.First outside Side of the fabric material 130 far from the windproof elasticity PU films of the first moisture-inhibiting 120 also is provided with two point and applies plastic structure 160.

Fig. 9 is please also refer to, outside composite material-feeding 200 includes the second inner fabrics cloth 210, second successively from inside to outside The windproof elasticity PU films 220 of moisture-inhibiting and the second outer fabric cloth 230, the second inner fabrics cloth 210 are windproof towards the second moisture-inhibiting The side of elastic PU films 220 is equipped with two point and applies plastic structure 240, and the second outer fabric cloth 230 is towards the windproof elasticity of the second moisture-inhibiting The side of PU films 220 is equipped with two point and applies plastic structure 250, and the second inner fabrics cloth 210 and the second outer fabric cloth 230 pass through Two point applies two side bonds of the plastic structure 240,250 respectively with the windproof elasticity PU films of the second moisture-inhibiting 220.It is double in other embodiment Spot printing plastic structure 160 may also set up the second inner fabrics cloth 210 in outside composite material-feeding 200 towards inside composite material-feeding On 100 side.

It is irregular distribution that two point, which applies plastic structure 140,150,240,250, and distribution density is 80-180/cm2.So that the One inner fabrics cloth 110, the first outer fabric cloth 130 are close to the both sides of the windproof elasticity PU films of the first moisture-inhibiting 120 respectively Connection, the second inner fabrics cloth 210, the second outer fabric cloth 230 respectively with the windproof elasticity PU films of the second moisture-inhibiting 220 two It is close to connect in side.

Referring to FIG. 5, two point applies bulk or strip distribution of the plastic structure 160 in interval, forms the two point being spaced apart and apply Glue area 170 forms felting channel 180 so between adjacent two point coating area 170, and down feather material 500 can pass through down-filling mouth 400 are filled into the felting channel 180 between inside composite material-feeding 100 and outside composite material-feeding 200.In two point coating area 170, It is irregular distribution that the two point, which applies plastic structure 160, and distribution density is 80-180/cm2.

In other embodiment, the first inner fabrics cloth 110 and the second outer fabric cloth can not also be set simultaneously 230, i.e., be only equipped with the first inner fabrics cloth 110 in the inside of the windproof elasticity PU films of the first moisture-inhibiting 120, or only second thoroughly The outside of wet windproof elasticity PU films 220 is equipped with the second outer fabric cloth 230.

Referring to FIG. 10, edge sealing structure 300 has the elastic base fabric 310 of strip, divide inside and outside elastic base fabric 310 Not She You two point apply plastic structure 320 and 330, two point applies plastic structure 320 for the first outer fabric with inside composite material-feeding 100 A side bonds of the cloth 130 far from the windproof elasticity PU films of the first moisture-inhibiting 120, two point apply plastic structure 330 and are used for and outside Compound Fabric A side bonds of the second inner fabrics cloth 210 of material 200 far from the windproof elasticity PU films of the second moisture-inhibiting 220.

It is irregular distribution that two point, which applies plastic structure 320 and 330, and distribution density is 20-130/cm2, realizes that inside is compound In the connection of edge between cloth 100 and outside composite material-feeding 200, prevent down feather material 500 from revealing.It is applied in adjacent two point Between plastic structure 320 or adjacent two point apply plastic structure 330 between form gas channel 340, in such layer insulation composite cloth material Air-flow can be connected to outside by the gas channel 340 of edge sealing structure 300, realize preferable gas permeability；Elastic base fabric simultaneously 310 warp thread and weft yarn intersect after between form " well " font gap, warp thread and weft yarn are made of several monofilament, monofilament it Between also form certain gap, can further improve permeability.

The windproof elasticity PU films 120 of first moisture-inhibiting and the windproof elasticity PU films of the second moisture-inhibiting 220 can be low ventilated membrane or airtight Film has better warming effect.But gas permeability is poor compared with high ventilated membrane, in present embodiment, permeability is main It is addressed by edge sealing structure 300, so reduces vapor permeation area, improve warming effect, realize preferable warming effect Fruit simultaneously maintains certain airing function.

Please refer to Fig.1 1 to Figure 13, down products with penetration resistance structure provided by the invention includes several above-mentioned warming compound Cloth, the down feather material being filled in layer insulation composite cloth material.In edge, stacking is set between several adjacent layer insulation composite cloth material It sets, and is sewed up by suture.In order to solve the problems, such as to bore suede, suture is arranged at the edge sealing model that the both sides of edge sealing structure 300 are formed It encloses in d.

Specifically, as shown in figure 11, monolithic layer insulation composite cloth material forms cut-parts, and circumferential direction is equipped with edge sealing structure 300.

As shown in the top of Figure 12, by the edge sealing structure 300 of the first layer insulation composite cloth material and the second layer insulation composite cloth material Edge sealing structure 300 is parallel to be overlapped, and is adopted close to the edge of both sides in the edge sealing range d that the both sides of edge sealing structure 300 are formed It is sewed up with horda chirurgicalis, the middle part of edge sealing structure 300 is sewed up using "the" shape rip out stitches.So sewing mode, it is warming first Composite material-feeding and the second layer insulation composite cloth material junction have preferable elasticity and reliability.

As shown in the lower part of Figure 12, the envelope of the edge sealing structure 300 of the first layer insulation composite cloth material and the second layer insulation composite cloth material Side structure 300 is bent U-shaped, the edge sealing knot of the edge sealing structure 300 of the first layer insulation composite cloth material and the second layer insulation composite cloth material Structure 300, which is staggered, colludes with, i.e. the end of the edge sealing structure 300 of the first layer insulation composite cloth material extend into the envelope of the second layer insulation composite cloth material In the U-type groove of side structure 300, the end of the edge sealing structure 300 of the second layer insulation composite cloth material extend into the first layer insulation composite cloth material Edge sealing structure 300 U-type groove in, then the both sides of edge sealing structure 300 formed edge sealing range d in sewed, sew Using the mode as shown in being easy 13, i.e., sewed up using horda chirurgicalis close to the edge of both sides in edge sealing range d, edge sealing structure It is sewed up using "the" shape rip out stitches at 300 middle part.Since the first layer insulation composite cloth material and the second layer insulation composite cloth material are mutually curved Song is colluded with so that it can prevent water from entering layer insulation composite cloth from the section of edge sealing structure 300 with preferable water resistance The inside of material.

Please refer to Fig.1 4, the first embodiment of the production technology of layer insulation composite cloth material provided by the invention, including following step Suddenly：

Step S1：Make outside composite material-feeding 200.

Step S2：Make inside composite material-feeding 100.

Step S3：In inside, the first outer fabric cloth 130 of composite material-feeding 100 is far from the windproof elasticity PU films of the first moisture-inhibiting 120 side setting two point applies plastic structure 160.

The setting up procedure that two point applies plastic structure is as follows：

Step S151：Prepare prime cement, after polyacrylate dispersion and water allotment are stirred evenly, thickener appropriate is added It stirs, is deployed into the prime cement of certain viscosity.

Step S152：Prepare thermosol powder.

Step S153：Slurry point coating treatment is carried out on cloth with prime cement, forms multiple slurry points, multiple slurry points constitute prime cement Coating.Specially：Prime cement in spot distribution and is bonded on cloth by pump and cylinder.

Step S154：By blowing device for inhaling powdery substances thermosol powder is subjected to dusting coating treatment on prime cement coating, is formed It is distributed in the thermosol gel coating of prime cement coating surface.It uses later and blows device for inhaling powdery substances by thermosol powder pressure-vaccum extra between slurry point Totally, hot setting is then carried out in drying chamber.Prime cement first dries out to heat up and quickly be carried out at 130 DEG C or more in drying chamber Heat cross-linking reacts, while the heated thawing of hot-melt adhesive powder is covered in the slurry point of prime cement above.This bonding prime cement slurry point and thermosol The dotted coating process that powder is combined into one is known as double-dot coating technique.

Step S4：Make edge sealing structure 300.

Step S5：Edge sealing structure 300 is saturating far from first in the first outer fabric cloth 130 of inside composite material-feeding 100 The side of wet windproof elasticity PU films 120 is compound along edge.

Step S6：By the first outer fabric cloth 130 and edge sealing of outside composite material-feeding 200 and inside composite material-feeding 100 Structure 300 is compound.

Below to be described in detail for making the second embodiment of layer insulation composite cloth material：

Step S1：Make outside composite material-feeding 200.It is specific as follows：

Step S11：Make the second inner fabrics cloth 210 of outside composite material-feeding 200.

Step S12：Make the second outer fabric cloth 230 of outside composite material-feeding 200.

Step S13：The windproof elasticity PU films of second moisture-inhibiting 220 are provided.The characteristic of film determines the windproof, saturating of joint product The key performances such as wet, waterproof all have a major impact the elasticity of joint product, feel and the friction sound.In present embodiment, choosing The windproof elasticity PU films of another day this DIC companies moisture-inhibiting, Key Performance Indicator such as following table：

The name of an article	Thickness	Square grammes per square metre	Water vapour permeability	Water resistance	Elongation at break
						KH‐13	0.02mm	10‐12	>4200g/m2x24h	>10000mm	>300%

The windproof elasticity PU films 220 of second moisture-inhibiting are hermetically sealable film, have better warming effect.But gas permeability is poor.

Step S14：The compound second inner fabrics cloth 210 of hot pressing, windproof 220 and second outside of elasticity PU films of the second moisture-inhibiting Fabric material 230.

Wherein, step S11, the second inner fabrics cloth 210 for making outside composite material-feeding 200 include the following steps：

Step S111：Fabric is weaved, and selects to weave on 210 type weaving machine with water spraying, 1/1 plain weave is all selected through weft yarn Polyester DTY 20D/24F, upper gate width 205cm, upper machine weft density：29.5x19.5 roots/cm, lower machine-processed rice grow 1000 meters/volume.

Step S112：Washing oil removing and overflow dyeing, the fabric that woven fabric is got off need, by debatching process, to fall back on Bu Cheli Facilitate overflow dyeing machine cloth feeding.

If it is white fabric is made, technique is as follows：

The cloth feeding in 84-92 DEG C of hot water.Polyester DTY material can discharge texturing craft in 78 DEG C or more of hot water and leave The internal stress come, yarn meeting acutely puffing contraction, filament contraction form many microcosmic bendings, and such fabric will produce lateral and vertical To contraction, cloth cover becomes close and thickens, and generates elasticity.The anti-hook silk splitting parameter of cloth cover greatly increases simultaneously.Cloth feeding finishes, and runs 10 points Zhong Rangbu cycles are smooth, then are cooled to 80 DEG C of additions and remove oil assistant.

Go the formula of oil assistant as follows：Multi-function refining flux BL-806 (Bi Ning companies of upper Taiwan Strait Exchange Association produce) 1.2g/l, deoils Clever TF101 (development of evil in febrile disease company product) 1.5g/l, NaOH piece alkali 0.5g/l.Above-mentioned formula is primarily to refining oil removing.

Addition is warming up to 120-125 DEG C after removing oil assistant, keeps the temperature 15-20 minutes, is then cooled to according to 2 DEG C/min speed 80 DEG C of drainings, reinject 60 DEG C of hot water, circulating water wash 15 minutes, then draining reinjects 35-40 DEG C of hot water and is added 0.5g/l's Glacial acetic acid, 15 minutes cloth outputtings of pickling.

If necessary to dye, the technique for washing oil removing and overflow dyeing is as follows：

If fabric yarn finish comparision contents are high, (product of less demanding can not also remove for preferably first oil removing before dyeing Oily direct staining), except oil formula is as follows in water inlet：The 2g/l development of evil in febrile disease is deoiled clever TF101,4g/l soda ash NaCO3；At 84-92 DEG C Cloth feeding in hot water, after be warming up to 94 DEG C keep the temperature 15 minutes.Then 80 DEG C or less drainings are cooled to.Then water inlet is warming up to 60 DEG C dyestuff and auxiliary agent is added.Dyeing assistant formula is as follows：The level dyeing dispersion of 1.5-2g/l chelates three-in-one multiple-effect coloring agent, Shanghai Xie Bining companies BL106；The dolantin company dyeing acid DA of 0.6-0.8g/l.According to the heating speed of 1.5 DEG C/min after addition auxiliary agent Rate is warming up to 130 DEG C, keeps the temperature 30 minutes, is then cooled to 80 DEG C according to 1.5 DEG C/min, the reduction cleaner of 1-2g/l is added The piece alkali NaOH of DS-1559 (production of dolantin company) and 1g/l, then be warming up to 85-90 DEG C and carry out reduction cleaning and keep the temperature 25 points Then clock is cooled to 70 DEG C of drains.Then it is warming up to 60 DEG C into hot water to wash 15 minutes, drain.Then it is added again into warm water The glacial acetic acid pickling of 0.5g/l 15 minutes, then cloth outputting, which is placed in cloth vehicle, enters next process.

Step S113：It is dehydrated open-width, the base fabric for refining or dyeing by overflow preshrunk is carried out dehydrating, using Open-width process is placed on the medium undetermined type of cloth vehicle.

Step S114：Sizing arranges, and embryo cloth is sent into sizing padding machine by cloth vehicle, and the interior configuration sizing of groove for padding machine of shaping helps The formula of agent, sizing aids is as follows：The development of evil in febrile disease company silicone oil TF-438 of 15g/l；The antistatic agent of the development of evil in febrile disease company of 0.8g/l 480；The glacial acetic acid of 0.5-1g/l.

The speed of sizing padding machine is 40-50m/min, cloth outputting door width 148cm, 190-198 DEG C of setting temperature, through latitude after sizing Close 40.8x26.7 roots/cm, square grammes per square metre is in 20.5g/m2 or so after sizing, and sizing yield rate is 73%；Water repellent degree in 70-80, After sizing under tension-free state, 180 DEG C xeothermic through broadwise shrinking percentage<2%.Fabric appearance wants smooth after sizing, soft cunning Refreshing, elasticity is good.

Preferably, it is contemplated that natural feather is a kind of protein fibre, humidity etc. some under the conditions of, may be mouldy or thin Bacterium is decomposed, and peculiar smell is generated, unhygienic；Therefore fabric can be processed into antibiosis anti-acarien characteristic, allows down products to have and preferably defends Raw and snugness of fit guarantee.Antiseptic or anti-mite auxiliary agent are added i.e. in the formula of sizing aids, prevents eiderdown quilt bacterium Or acarid is grown, it is much cleaner.

Step S115：Two point is set in embryo cloth and applies plastic structure.

Embryo cloth after sizing handles the second inner fabrics that can serve as outside composite material-feeding 200 using double-dot coating Cloth 210 uses, and the setting up procedure that two point applies plastic structure is as follows：

Step S151：Prepare prime cement, polyacrylate dispersion is deployed according to solid content 20-25% with water, it is stirred After mixing uniformly, thickener appropriate is added and stirs, is deployed into the prime cement of certain viscosity.Polyacrylate dispersion is selected The polyacrylic acid fat liquor YD-368 trades mark of Shanghai crowd Yi Da companies, solid content 30-33%.

Step S152：Prepare thermosol powder, the M1276 trades mark PA produced using Shanghai Ah's Kerma (unit of kinetic energy) hot melt adhesive Co., Ltd Thermosol, grain size 80-170um.

Step S153：Slurry point coating treatment is carried out in embryo cloth with prime cement.Prepare random disorderly point cylinder, a prime cement to pass through Pump and the random disorderly point cylinder are in random spot distribution and are bonded in the side of embryo cloth, form multiple slurry points, multiple slurries Point constitutes prime cement coating 171.It is random disorderly point cylinder use by Computer Design it is random disorderly point cylinder cp130, i.e., 130 A hole point/cm2, aperture 0.15-0.16mm, wall thickness 0.16-0.17mm.

Step S154：Dusting coating treatment is carried out on prime cement coating 171 with thermosol powder, distributes in prime cement painting The thermosol gel coating 172 on 171 surface of layer.Specially：Appropriate thermosol powder is added in the powder hopper of duster, opens two point machine Device for inhaling powdery substances is blown, waits for that drying chamber is warming up to 170-185 DEG C or so, there is bottom by blowing device for inhaling powdery substances and spreading thermosol powder to embryo cloth The side of coating, speed 20-30m/min are starched, the control of prime cement coating is controlled in 1.5-2g/m2, thermosol gel coating in 4.5-6.0g/ M2, coating amount total in this way are 6-8g/m2.Here our preferred 7g/m2 of total coating amount.Door width in this way after coating is in 147- 148cm, square grammes per square metre is in 28g/m2 or so.

It is with device for inhaling powdery substances is blown that thermosol powder pressure-vaccum extra between slurry point is clean again later, then carried out in drying chamber Hot setting.Prime cement first dries out to heat up in drying chamber quickly carries out heat cross-linking reaction, while hot melt adhesive at 130 DEG C or more The heated thawing of powder is covered in the slurry point of prime cement above.

Similarly, step S12, the second outer fabric cloth 230 for making outside composite material-feeding 200 include the following steps：

Step S121：Fabric is weaved, and selects to weave on 210 type weaving machine with water spraying, 1/1 plain weave is all selected through weft yarn Polyester DTY 30D/24F x 30D/36F, upper gate width 205cm, upper machine weft density：36x29 roots/cm, lower 1000 meters of machine-processed rice length/ Volume.

Step S122：Washing oil removing and overflow dyeing, the fabric that woven fabric is got off need, by debatching process, to fall back on Bu Cheli Facilitate overflow dyeing machine cloth feeding.

If it is white fabric is made, technique is as follows：

Step S123：It is dehydrated open-width, the base fabric for refining or dyeing by overflow preshrunk is carried out dehydrating, using Open-width process is placed on the medium undetermined type of cloth vehicle.

Step S124：Sizing arranges, and embryo cloth is sent into sizing padding machine by cloth vehicle, and the interior configuration sizing of groove for padding machine of shaping helps The formula of agent, sizing aids is as follows：The German Dr.PETRY companies fluorin environment protection waterproofing agent PERIGUARD ZP of 15-25g/l conc；1.0-1.2g/l development of evil in febrile disease company non-ionic antistatic agent 480；The glacial acetic acid of 0.5g/l.

The speed of sizing padding machine is 40-50m/min, cloth outputting door width 148cm, 190-198 DEG C of setting temperature, through latitude after sizing Close (49-50) x (39-40) root/cm, square grammes per square metre is in 40g/m2 or so after sizing, and sizing yield rate is in 73-74%；Water repellent degree After 75-80, sizing under tension-free state, 180 DEG C xeothermic through broadwise shrinking percentage<2%.Fabric appearance wants smooth after sizing, hand Sense is soft smooth, and elasticity is good.

Step S125：Two point is set in embryo cloth and applies plastic structure.

Embryo cloth after sizing handles the second outer fabric that can serve as outside composite material-feeding 200 using double-dot coating Cloth 230 uses, and the setting up procedure that two point applies plastic structure is as follows：

Step S152：Prepare thermosol powder, using the M1276 trade mark heat of Shanghai Ah's Kerma (unit of kinetic energy) hot melt adhesive Co., Ltd production Colloidal sol, grain size 80-170um.

Step S153：Slurry point coating treatment is carried out in embryo cloth with prime cement.Prepare random disorderly point cylinder, a prime cement to pass through Pump and the random disorderly point cylinder are in random spot distribution and are bonded in the side of embryo cloth, form multiple slurry points, multiple slurries Point constitutes prime cement coating.Random disorderly point cylinder uses the random disorderly point cylinder cp80 by Computer Design, i.e. 80 holes Point/cm2, aperture 0.26-0.28mm, wall thickness 0.17-0.20mm.

Step S154：Dusting coating treatment is carried out on prime cement coating with thermosol powder, distributes in prime cement coating The thermosol gel coating on surface.Specially：Appropriate thermosol powder is added in the powder hopper of duster, opens two point machine pressure-vaccum powder dress It sets, waits for that drying chamber is warming up to 170-185 DEG C or so, there is prime cement coating by blowing device for inhaling powdery substances and spreading thermosol powder to embryo cloth Side, speed 20-30m/min, the control of prime cement coating are controlled in 3-4g/m2, thermosol gel coating in 6-7g/m2, coating total in this way Amount is 9-11g/m2.Here our preferred 10g/m2 of total coating amount.In 147cm, a square grammes per square metre exists door width in this way after coating 51-52g/m2 or so.

In above-mentioned steps S14, the compound second inner fabrics cloth 210 of compounding machine hot pressing, the windproof elasticity of the second moisture-inhibiting are utilized PU films 220 and the second outer fabric cloth 230, include the following steps：

Step S141：The condition for setting compounding machine is as follows：Interior heater temperature makes roller surface temperature at 240-250 DEG C Degree reaches 135-138 DEG C, and air pressure is set in precompressed 2kg/cm2, and rear platen pressure is 2.5kg/cm2.

Step S142：After roller surface temperature reaches 135-138 DEG C, the second inner fabrics cloth 210 is applied with two point The one of plastic structure upwardly and is through in work feed lengths, starts the suction ventilator under lengths and to regulate appropriate suction air volume smooth The second inner fabrics cloth 210 is gently sucked in ground；

Step S143：Then the windproof elasticity PU films of the second moisture-inhibiting 220 are placed on debatching position, and are through work feed lengths On, it paves whole；

Step S144：Then the second outer fabric cloth 230 is placed on debatching position, and plastic structure is applied with two point One is through under in work feed lengths, paves whole；

Step S145：After regulating each section tension, compounding machine is started, setting speed 8-12m/min makes the second inside knit The two point of object cloth 210 and the second outer fabric cloth 230 applies plastic structure and melts and be firmly compounded in the windproof elasticity of the second moisture-inhibiting The both sides of PU films 220 form outside composite material-feeding 200, composite material-feeding 200 width in outside are in 147- after being fully cooled winding 148cm。

Outside composite material-feeding 200 is cleaved except the intensity for meeting conventional cloth, wearability, anti-hook silk, outside color fastness index, outside It sees outside flatness and feel smooth degree, other main performance index are as follows：

Step S2：Inside composite material-feeding 100 is made, method is similar with outside composite material-feeding 200 is made, specific as follows：

Step S21：Make the first inner fabrics cloth 110 of inside composite material-feeding 100.

Step S22：Make the first outer fabric cloth 130 of inside composite material-feeding 100.

Step S23：The windproof elasticity PU films of first moisture-inhibiting 120 are provided.The characteristic of film determines the windproof, saturating of joint product The key performances such as wet, waterproof all have a major impact the elasticity of joint product, feel and the friction sound.In present embodiment, choosing The windproof elasticity PU films of another day this DIC companies moisture-inhibiting.

Step S24：The compound first inner fabrics cloth 110 of hot pressing, windproof 120 and first outside of elasticity PU films of the first moisture-inhibiting Fabric material 130.

Wherein, step S21, the first inner fabrics cloth 110 for making inside composite material-feeding 100 include the following steps：

Step S211：Fabric is weaved, and selects to weave on 210 type weaving machine with water spraying, 1/1 plain weave is all selected through weft yarn Polyester DTY 15D/12F, upper gate width 196cm, upper machine weft density：31.5x21.5 roots/cm, lower machine-processed rice grow 1000 meters/volume.

Step S212：Washing oil removing and overflow dyeing, the fabric that woven fabric is got off need, by debatching process, to fall back on Bu Cheli Facilitate overflow dyeing machine cloth feeding.

If it is white fabric is made, technique is as follows：

Step S213：It is dehydrated open-width, the base fabric for refining or dyeing by overflow preshrunk is carried out dehydrating, using Open-width process is placed on the medium undetermined type of cloth vehicle.

Step S214：Sizing arranges, and embryo cloth is sent into sizing padding machine by cloth vehicle, and the interior configuration sizing of groove for padding machine of shaping helps The formula of agent, sizing aids is as follows：The development of evil in febrile disease company silicone oil TF-438 of 15g/l；The antistatic agent of the development of evil in febrile disease company of 0.8g/l 480；The glacial acetic acid of 0.5-1g/l.

The speed of sizing padding machine is 40-50m/min, cloth outputting door width 148cm, 190-198 DEG C of setting temperature, through latitude after sizing Close 41.7x29.5 roots/cm, square grammes per square metre is in 16g/m2 or so after sizing, and sizing yield rate is 73%；Water repellent degree is determined in 70-80 After type under tension-free state, 180 DEG C xeothermic through broadwise shrinking percentage<2%.Fabric appearance wants smooth after sizing, soft smooth, It is elastic good.

Step S215：Two point is set in embryo cloth and applies plastic structure.

Embryo cloth after sizing handles the first inner fabrics that can serve as inside composite material-feeding 100 using double-dot coating Cloth 110 uses, and the setting up procedure that two point applies plastic structure is as follows：

Step S153：Slurry point coating treatment is carried out in embryo cloth with prime cement.Prepare random disorderly point cylinder, a prime cement to pass through Pump and the random disorderly point cylinder are in random spot distribution and are bonded in the side of embryo cloth, form multiple slurry points, multiple slurries Point constitutes prime cement coating.It is random disorderly point cylinder use by Computer Design it is random disorderly point cylinder cp130, i.e., 130 Hole point/cm2, aperture 0.15-0.16mm, wall thickness 0.17-0.18mm.

Step S154：Dusting coating treatment is carried out on prime cement coating with thermosol powder, distributes in prime cement coating The thermosol gel coating on surface.Specially：Appropriate thermosol powder is added in the powder hopper of duster, opens two point machine pressure-vaccum powder dress It sets, waits for that drying chamber is warming up to 170-185 DEG C or so, there is prime cement coating by blowing device for inhaling powdery substances and spreading thermosol powder to embryo cloth Side, speed 20-30m/min, in 1.5-2.5g/m2, thermosol gel coating is controlled in 4.5-5.5g/m2 the control of prime cement coating, this The total coating amount of sample is 6-8g/m2.Here our preferred 7g/m2 of total coating amount.Door width in this way after coating in 147-148cm, Square grammes per square metre is in 23g/m2 or so.

Similarly, step S22, the first outer fabric cloth 130 for making inside composite material-feeding 100 include the following steps：

Step S221：Fabric is weaved, and selects to weave on 210 type weaving machine with water spraying, 1/1 plain weave, is washed through weft yarn selection Synthetic fibre DTY 20D/24F x 20D/24F, upper gate width 205cm, upper machine weft density：36x29 roots/cm, lower 1000 meters of machine-processed rice length/ Volume.

Step S222：Washing oil removing and overflow dyeing, the fabric that woven fabric is got off need, by debatching process, to fall back on Bu Cheli Facilitate overflow dyeing machine cloth feeding.

If it is white fabric is made, technique is as follows：

Step S223：It is dehydrated open-width, the base fabric for refining or dyeing by overflow preshrunk is carried out dehydrating, using Open-width process is placed on the medium undetermined type of cloth vehicle.

Step S224：Sizing arranges, and embryo cloth is sent into sizing padding machine by cloth vehicle, and the interior configuration sizing of groove for padding machine of shaping helps The formula of agent, sizing aids is as follows：The fluffy softening agent of the development of evil in febrile disease company of 20-25g/l 480；The development of evil in febrile disease company of 1.0-1.2g/l is non- Ionic antistatic agent 480；The glacial acetic acid of 0.5-0.8/l.

The speed of sizing padding machine is 40-50m/min, cloth outputting door width 148cm, 185-190 DEG C of setting temperature, through latitude after sizing Close (49-50) x (39-40) root/cm, square grammes per square metre is in 27g/m2 or so after sizing, and sizing yield rate is in 73-74%；Water repellent degree After 75-80, sizing under tension-free state, 180 DEG C xeothermic through broadwise shrinking percentage<2%.Fabric appearance wants smooth after sizing, hand Sense is soft smooth, and elasticity is good.

Step S225：Two point is set in embryo cloth and applies plastic structure.

Embryo cloth after sizing handles the first outer fabric that can serve as inside composite material-feeding 100 using double-dot coating Cloth 130 uses, and the setting up procedure that two point applies plastic structure is as follows：

Step S153：Slurry point coating treatment is carried out in embryo cloth with prime cement.Prepare random disorderly point cylinder, a prime cement to pass through Pump and the random disorderly point cylinder are in random spot distribution and are bonded in the side of embryo cloth, form multiple slurry points, multiple slurries Point constitutes prime cement coating.It is random disorderly point cylinder use by Computer Design it is random disorderly point cylinder cp180, i.e., 180 Hole point/cm2, aperture 0.20-0.22mm, wall thickness 0.16-0.17mm.

Step S154：Dusting coating treatment is carried out on prime cement coating with thermosol powder, distributes in prime cement coating The thermosol gel coating on surface.Specially：Appropriate thermosol powder is added in the powder hopper of duster, opens two point machine pressure-vaccum powder dress It sets, waits for that drying chamber is warming up to 170-185 DEG C or so, there is prime cement coating by blowing device for inhaling powdery substances and spreading thermosol powder to embryo cloth Side, speed 20-30m/min, for the control of prime cement coating in 2-2.5g/m2, the control of thermosol gel coating is total in this way in 4-5.5g/m2 Coating amount is 6-8g/m2.Here our preferred 7g/m2 of total coating amount.Door width in this way after coating is in 147cm, square grammes per square metre In 33-34g/m2 or so.

In above-mentioned steps S24, the compound first inner fabrics cloth 110 of compounding machine hot pressing, the windproof elasticity of the first moisture-inhibiting are utilized PU films 120 and the first outer fabric cloth 130, include the following steps：

Step S241：The condition for setting compounding machine is as follows：Interior heater temperature makes roller surface temperature at 240-250 DEG C Degree reaches 135-138 DEG C, and air pressure is set in precompressed 2kg/cm2, and rear platen pressure is 2.5kg/cm2.

Step S242：After roller surface temperature reaches 135-138 DEG C, the first inner fabrics cloth 110 is applied with two point The one of plastic structure upwardly and is through in work feed lengths, starts the suction ventilator under lengths and to regulate appropriate suction air volume smooth The first inner fabrics cloth 110 is gently sucked in ground；Then the windproof elasticity PU films of the first moisture-inhibiting 120 are placed on debatching position, and It is through in work feed lengths, paves whole；Then the first outer fabric cloth 130 is placed on debatching position, and is applied with two point The one of plastic structure is through under in work feed lengths, is paved whole；After regulating each section tension, compounding machine is started, is set Speed 8-12m/min makes the two point of the first inner fabrics cloth 110 and the first outer fabric cloth 130 apply plastic structure thawing and jail Jail is compounded in the both sides of the windproof elasticity PU films of the first moisture-inhibiting 120, after being fully cooled winding, forms inside composite material-feeding 100, interior Composite material-feeding 100 width in side are in 147-148cm.

Step S3：In inside, the first outer fabric cloth 130 of composite material-feeding 100 is far from the windproof elasticity PU films of the first moisture-inhibiting 120 side setting two point applies plastic structure 160.Specially：

Step S153：With prime cement in side of the first outer fabric cloth 130 far from the windproof elasticity PU films of the first moisture-inhibiting 120 On carry out slurry point a coating treatment.Prepare a regular pattern cylinder or random disorderly point cylinder, a prime cement passes through pump and the rule Then pattern cylinder or random disorderly point cylinder in spot distribution and are bonded on the first outer fabric cloth 130, form multiple slurries Point, multiple slurry points constitute prime cement coating.In present embodiment, the circular hole distribution of regular pattern cylinder or random disorderly point cylinder is close Degree is 20-130/cm2, aperture 0.5-1.0mm, wall thickness 0.3-0.5mm.

Step S154：Dusting coating treatment is carried out on prime cement coating with thermosol powder, distributes in prime cement coating The thermosol gel coating on surface.Specially：Appropriate thermosol powder is added in the powder hopper of duster, opens two point machine pressure-vaccum powder dress It sets, waits for that drying chamber is warming up to 170-185 DEG C or so, spread thermosol powder to the first outer fabric cloth by blowing device for inhaling powdery substances On 130 sides with prime cement coating, speed 20-30m/min, the control of prime cement coating is in 1-2.5g/m2, the control of thermosol gel coating In 3-6.5g/m2, coating amount total in this way is 4-9g/m2.Here our preferred 6g/m2 of total coating amount.Door in this way after coating Width is in 147cm, and square grammes per square metre is in 74-76g/m2 or so.

Step S4：Make edge sealing structure 300.Include the following steps：

Step S41：One base fabric is provided, can be the lining item woven or the lining item woven by loom, the thickness of the base fabric For 0.2-1mm, there is good airing function.

Base fabric is woven by loom：210 type weaving machine with water spraying, twill 2/2 are selected to organize, warp-wise material is polyester DTY Microgrid 30D/24F, weft material are polyester DTY 30D/24F, upper machine weft density：27.5x17 roots/cm, upper gate width 165cm.

Wash oil removing and overflow dyeing：Base fabric after drying is washed and further into oil removing is refined in overflow dyeing machine Preshrunk is puffing.Except oil refinement formula：The Zhejiang development of evil in febrile disease company high temperature of 1g/l deoils spirit, the BL-106 pre-treatments chelating point of 1.2g/l Powder, the DM-1320 desizing agents of 1.2g/l, the soda ash of 2.5g/l.Base fabric enters overflow dyeing machine at 90 degree, in 1.5 degree/min It is warming up to 115 degree under rate, keeps the temperature 25 minutes.Then 60 degree of drains are cooled to, under 45 degree in pickling and drain in 15 minutes, then Cloth outputting of 40 degree of washings.

Coloured product is dyed if necessary, by the base fabric after above-mentioned desizing refining according still further to dacron dyer Skill, with disperse dyeing, reduction, cloth outputting after cleaning.

It is dehydrated open-width, the base fabric for refining or dyeing by overflow preshrunk is carried out dehydrating, using open-width process It is placed on the medium undetermined type of cloth vehicle.

Sizing arranges, and base fabric is sent into sizing padding machine by cloth vehicle, and sizing aids are configured in the groove for padding machine of shaping, and sizing helps The formula of agent is as follows：The high fluffy silicone oil 438 of the development of evil in febrile disease of 15g/l, the soft and slender elements of small molecule silicone oil CST of 10g/l, 0.5g/l's is anti-quiet Electric agent, the glacial acetic acid of 1g/l.195 degree, speed 35-38m/min of setting temperature, shape back door width 123cm, yield rate of shaping 73%, through filling density 36x23.2 roots/cm, 25 grams of square grammes per square metre, water repellent degree 90-95 after sizing (by international standard measurement).After sizing The fluffy softness of base fabric feel, elasticity fully.140 degree of lower measurement are through broadwise pyrocondensation：Warp-wise<2%, broadwise<1.4%.

Step S151：Prepare prime cement, polyaminoester emulsion is deployed according to solid content 20-25% with water, it is stirred After even, thickener appropriate is added and stirs, is deployed into the prime cement of certain viscosity.Polyaminoester emulsion selects Shanghai east farsighted 506 trade mark of polyaminoester emulsion, this aromatic urethane prime cement have extraordinary bonding intensity and durable performance.

Step S153：Slurry point coating treatment is carried out in base fabric with prime cement.Prepare a random disorderly point cylinder, random unrest The hole dot density of point cylinder is 20-130/cm2, and prime cement is in random spot distribution by pump and the random disorderly point cylinder And it is bonded in the side of embryo cloth, multiple slurry points are formed, multiple slurry points constitute prime cement coating.In present embodiment, random unrest point Cylinder uses the random disorderly point cylinder cp80, i.e. 80 hole point/cm2, aperture 0.28mm by Computer Design, wall thickness 0.18mm。

Step S154：Dusting coating treatment is carried out on prime cement coating with thermosol powder, distributes in prime cement coating The thermosol gel coating on surface.Specially：Appropriate thermosol powder is added in the powder hopper of duster, opens two point machine pressure-vaccum powder dress It sets, waits for that drying chamber is warming up to 180 DEG C or so, spread thermosol powder to one of embryo cloth with prime cement coating by blowing device for inhaling powdery substances Side, speed 20m/min, total coating amount are 8-10g/m2.Door width in this way after coating is in 122cm, and square grammes per square metre is in 33-35g/ m2。

Then go 45 degree of beveling at 6-8mm according to 50 meters/volume cloth-inspecting rolling the good two-sided lining of 30D twills of coated on both sides Wide both-sided adhesive check rod sabot is used for above-mentioned direct down-filling garment piece hot-pressing, edge-sealing.

Step S5：Edge sealing structure 300 is saturating far from first in the first outer fabric cloth 130 of inside composite material-feeding 100 The side of wet windproof elasticity PU films 120 is compound along edge, and edge sealing structure 300 passes through with the compound of inside composite material-feeding 100 Flatiron is completed.

Step S5 includes the following steps：

Step S51：There is the first outer fabric cloth 130 and two point to apply the one of plastic structure 160 inside composite material-feeding 100 It upwardly and is through in work feed lengths, starts the suction ventilator under lengths and regulate appropriate suction air volume and be entirely gently sucked Inside composite material-feeding 100；

Step S52：Edge sealing structure 300 is smooth along the laying of the edge of inside composite material-feeding 100；

Step S53：The running parameter for setting flatiron makes the first outer fabric cloth by flatiron hot-pressing, edge-sealing structure 300 The two point of material 130 applies plastic structure 160 and the two point of edge sealing structure 300 applies the thawing of plastic structure 320 and makes the first outer fabric cloth Material 130 is firmly compound with edge sealing structure 300.

Step S6：By the first outer fabric cloth 130 and edge sealing of outside composite material-feeding 200 and inside composite material-feeding 100 Structure 300 is compound, includes the following steps：

Step S61：The condition for setting compounding machine is as follows：Interior heater temperature makes roller surface temperature at 240-250 DEG C Reach 135-138 DEG C, air pressure is set in precompressed 2.5kg/cm2, and rear platen pressure is 3.5kg/cm2.

Step S62：After roller surface temperature reaches 135-138 DEG C, outside composite material-feeding 200 had into the second inner fabrics The one of cloth 210 is placed on downwards on debatching position, and is through in work feed lengths, with inside composite material-feeding 100 and edge sealing knot The edge of structure 300 is aligned, and is laid with smooth；

Step S63：After regulating each section tension, compounding machine is started, sets speed 6-10m/min, the first outside is made to knit The two point of object cloth 130 applies plastic structure 160 and the two point of edge sealing structure 300 applies the thawing of plastic structure 330 and makes outside Compound Fabric Material 200 is firmly compound with inside composite material-feeding 100 and edge sealing structure 300.

Edge sealing structure 300 not fully closes all edges of inside composite material-feeding 100 and outside composite material-feeding 200, and It is to have reserved a down-filling mouth 400 in an edge of inside composite material-feeding 100 and outside composite material-feeding 200.

When making down products with penetration resistance structure using above-mentioned layer insulation composite cloth material, need down feather material through down-filling machine 500 are filled by down-filling mouth 400 in the gap between inside composite material-feeding 100 and outside composite material-feeding 200.Suture should later Down-filling mouth 400.

When several layer insulation composite cloth material connections, need to be sewed up by suture, specially：

The edge sealing structure 300 of first layer insulation composite cloth material and the edge sealing structure 300 of the second layer insulation composite cloth material is parallel heavy The setting that acts in collusion is folded or be bent, is sewed up using horda chirurgicalis at the both sides of the edge of edge sealing structure 300, in edge sealing structure 300 It is sewed up using "the" shape rip out stitches in portion.The width of edge sealing structure 300 is about 10mm, and the width between two horda chirurgicalis is about For 8mm, "the" shape rip out stitches are serrated, and width is about 4mm.

In this way, two panels layer insulation composite cloth material is all by two vertical elastic sewing threads and intermediate zigzag sewing thread, Yi Gongsan Road suture sewing is secured, has elasticity, and beautiful.It is important to note that the region of these sewing sewers is all envelope The region of side structure 300, rather than down-filling region, that is to say, that the cloth in down-filling region is not destroyed by pin hole, also just not There are the brill suede risks caused by sewing thread pin hole.

5 are please referred to Fig.1, is the second embodiment of the production technology of layer insulation composite cloth material provided by the invention.

The maximum difference of the present embodiment and first embodiment is：Edge sealing structure 300 and outside composite material-feeding 200 and inside The complex method of composite material-feeding 100, in the present embodiment：

Step S1：Make outside composite material-feeding 200.

Step S2：Make inside composite material-feeding 100.

Step S4：Make edge sealing structure 300.

Step S5：By the second inner fabrics cloth 210 and the first of inside composite material-feeding 100 of outside composite material-feeding 200 Outer fabric cloth 130 is compound.Specially：

Step S52：The condition for setting compounding machine is as follows：Interior heater temperature makes roller surface temperature at 240-250 DEG C Reach 135-138 DEG C, air pressure is set in precompressed 2.5kg/cm2, and rear platen pressure is 3.5kg/cm2.

Step S53：After roller surface temperature reaches 135-138 DEG C, outside composite material-feeding 200 had into the second inner fabrics The one of cloth 210 is placed on downwards on debatching position, and is through in work feed lengths, the edge pair with inside composite material-feeding 100 Together, it is laid with smooth；

Step S54：After regulating each section tension, compounding machine is started, sets speed 6-10m/min, the first outside is made to knit The two point of object cloth 130 applies plastic structure 160 and melts and make outside composite material-feeding 200 and inside composite material-feeding 100 compound.

Step S6：By the first of the second inner fabrics cloth 210 of outside composite material-feeding 200 and inside composite material-feeding 100 Outer fabric cloth 130 is raised along edge so that the two is detached in edge, is put into edge sealing structure 300 so that edge sealing structure 300 with the second inner fabrics cloth 210 of outside composite material-feeding 200 and the first outer fabric cloth of inside composite material-feeding 100 130 are aligned along edge.

Step S7：Outside composite material-feeding 200, edge sealing structure 300 and inside composite material-feeding 100 is compound along edge, it is multiple It is compound that flatiron hot pressing can be used in conjunction mode.

Compared with prior art, layer insulation composite cloth material of the invention and down products with penetration resistance structure and warming compound The production technology of cloth applies 160 compound inside composite material-feeding 100 of plastic structure and outside composite material-feeding 200 by two point, and the There are gap between one outer fabric cloth 130 and the second inner fabrics cloth 210, inside composite material-feeding 100 and outside are compound Cloth 200 is connected along edge by edge sealing structure 300, and is equipped at least one down-filling mouth 400, down feather material in edge 500 can be filled by down-filling mouth 400 in the gap between inside composite material-feeding 100 and outside composite material-feeding 200, can so be solved It certainly bores suede phenomenon and runs suede phenomenon, without suture, durable, there is appropriate elasticity, wind-proof warming, anti-chiseling down, air-moisture-permeable, Comfort is good.

The foregoing is merely a prefered embodiment of the invention, is not used to limitation protection scope of the present invention, any in the present invention Modification, equivalent replacement or improvement in spirit etc., all cover in scope of the presently claimed invention.

Claims

1. a kind of layer insulation composite cloth material, it is characterised in that：The layer insulation composite cloth material includes the inside composite material-feeding being mutually bonded And outside composite material-feeding, and be set to inside composite material-feeding and outside composite material-feeding between edge edge sealing structure, it is interior Edge between side composite material-feeding and outside composite material-feeding is additionally provided at least one down-filling mouth；The inside composite material-feeding is from interior Include the windproof elasticity PU films of the first moisture-inhibiting and the first outer fabric cloth successively outward, the first outer fabric cloth is saturating towards first The side of wet windproof elasticity PU films is equipped with the first two point and applies plastic structure；The outside composite material-feeding includes second successively from inside to outside Inner fabrics cloth and the windproof elasticity PU films of the second moisture-inhibiting, the second inner fabrics cloth direction windproof elasticity PU films of the second moisture-inhibiting Side is equipped with the second two point and applies plastic structure, and the first outer fabric cloth of the inside composite material-feeding is far from the windproof bullet of the first moisture-inhibiting Property PU films side or the second inner fabrics cloth of outside composite material-feeding towards the side of inside composite material-feeding to be equipped with third double Spot printing plastic structure.

2. layer insulation composite cloth material as described in claim 1, it is characterised in that：First, second two point applies plastic structure Irregular distribution, distribution density are 80-180/cm2.

3. layer insulation composite cloth material as described in claim 1, it is characterised in that：The third two point applies block of the plastic structure in interval Shape or strip distribution, form two point coating area, and in two point coating area, it is irregular distribution that the third two point, which applies plastic structure, Distribution density is 20-130/cm2.

4. layer insulation composite cloth material as described in claim 1, it is characterised in that：The windproof elasticity PU films and second of first moisture-inhibiting The windproof elasticity PU films of moisture-inhibiting are low ventilated membrane or hermetically sealable film.

5. layer insulation composite cloth material as described in claim 1, it is characterised in that：The edge sealing structure has the elastic base of strip Cloth, the both sides of elastic base fabric are respectively equipped with the 4th two point and apply plastic structure, and it is irregular distribution that the 4th two point, which applies plastic structure, and distribution is close Degree is 20-130/cm2.

6. layer insulation composite cloth material as described in claim 1, it is characterised in that：The inside of the windproof elasticity PU films of first moisture-inhibiting It is additionally provided with the first inner fabrics cloth, the side of the first inner fabrics cloth towards the windproof elasticity PU films of the first moisture-inhibiting is equipped with 5th two point applies plastic structure.

7. layer insulation composite cloth material as described in claim 1 or 6, it is characterised in that：The windproof elasticity PU films of second moisture-inhibiting Outside is additionally provided with the second outer fabric cloth, the side of the second outer fabric cloth direction windproof elasticity PU films of the second moisture-inhibiting Plastic structure is applied equipped with the 6th two point.

8. a kind of down products with penetration resistance structure, it is characterised in that：Including several as claim 1-7 any one of them is warming Composite material-feeding and the down feather material being filled in layer insulation composite cloth material, in edge, stacking is set between adjacent layer insulation composite cloth material It sets, and is sewed up by suture.

9. down products with penetration resistance structure as claimed in claim 8, it is characterised in that：The suture is arranged at edge sealing structure Both sides formed edge sealing within the scope of.

10. down products with penetration resistance structure as claimed in claim 9, it is characterised in that：The edge sealing range is close to both sides Edge is equipped with horda chirurgicalis, and the middle part of the edge sealing structure is equipped with "the" shape rip out stitches.

11. down products with penetration resistance structure as claimed in claim 8, it is characterised in that：The first adjacent layer insulation composite cloth material And second the edge sealing structure of layer insulation composite cloth material be bent U-shaped, the edge sealing structure and second of the first layer insulation composite cloth material The edge sealing structure of layer insulation composite cloth material, which is staggered, colludes with.

12. a kind of production technology of layer insulation composite cloth material, special for producing layer insulation composite cloth material as described in claim 1 Sign is：Include the following steps：

Step S1：Make outside composite material-feeding；

Step S2：Make inside composite material-feeding；

Step S3：Side setting of the first outer fabric cloth of composite material-feeding far from the windproof elasticity PU films of the first moisture-inhibiting in inside Two point applies plastic structure；

Step S4：Make edge sealing structure；

13. the production technology of layer insulation composite cloth material as claimed in claim 12, it is characterised in that：Above-mentioned steps S1 includes following Step：

Step S14：The compound second inner fabrics cloth of hot pressing, the windproof elasticity PU films of the second moisture-inhibiting and the second outer fabric cloth.

14. the production technology of layer insulation composite cloth material as claimed in claim 13, it is characterised in that：Above-mentioned steps S14 include with Lower step：

Step S141：Set the operating condition of compounding machine；

Step S142：Have the one of two point painting plastic structure to face upward and be through in work feed lengths the second inner fabrics cloth；

Step S144：Second outer fabric cloth is placed on debatching position, and with two point apply plastic structure one under It is through in work feed lengths；

Step S145：Each section tension is regulated, speed is set, starts compounding machine, make outside the second inner fabrics cloth and second The two point painting plastic structure thawing of side fabric material is simultaneously compound with the both sides of the windproof elasticity PU films of the second moisture-inhibiting.

15. the production technology of layer insulation composite cloth material as claimed in claim 12, it is characterised in that：Two point is set and applies plastic structure packet Include following steps：

Step S151：Prepare prime cement；

Step S152：Prepare thermosol powder；

Step S153：Slurry point coating treatment is carried out in embryo cloth or base fabric with prime cement, forms multiple slurry points, multiple slurry points constitute bottom Starch coating；

Step S154：Dusting coating treatment is carried out on prime cement coating with thermosol powder, distributes in prime cement coating surface Thermosol gel coating.

16. the production technology of layer insulation composite cloth material as claimed in claim 12, it is characterised in that：Above-mentioned steps S4 includes following Step：

Step S41：Base fabric is provided；

17. a kind of production technology of layer insulation composite cloth material, special for producing layer insulation composite cloth material as described in claim 1 Sign is：Include the following steps：

Step S1：Make outside composite material-feeding；

Step S2：Make inside composite material-feeding；

Step S4：Make edge sealing structure；

Step S6：Outside composite material-feeding is detached with inside composite material-feeding 100 along edge, is put into edge sealing structure so that edge sealing Structure is aligned with outside composite material-feeding and inside composite material-feeding along edge；