CN108432642A - Antibacterial and deodouring pet urine pad and its manufacturing method - Google Patents

Antibacterial and deodouring pet urine pad and its manufacturing method Download PDF

Info

Publication number
CN108432642A
CN108432642A CN201810691658.XA CN201810691658A CN108432642A CN 108432642 A CN108432642 A CN 108432642A CN 201810691658 A CN201810691658 A CN 201810691658A CN 108432642 A CN108432642 A CN 108432642A
Authority
CN
China
Prior art keywords
antibacterial
urine pad
deodouring
pet urine
mass parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810691658.XA
Other languages
Chinese (zh)
Inventor
黄世伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Pioneer Synergy Nanometer Technology Co Ltd
Original Assignee
Nanjing Pioneer Synergy Nanometer Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Pioneer Synergy Nanometer Technology Co Ltd filed Critical Nanjing Pioneer Synergy Nanometer Technology Co Ltd
Priority to CN201810691658.XA priority Critical patent/CN108432642A/en
Publication of CN108432642A publication Critical patent/CN108432642A/en
Pending legal-status Critical Current

Abstract

The present invention relates to antibacterial and deodouring pet urine pad and its manufacturing methods, it is homogenized after hybrid oxidant, organic iron catalyst, antiseptic and adsorbent in proportion, curing process, grinding obtains antibacterial deodorant and is added into high exhaustion, it is pressed in order with wood pulp, toilet paper again, and covering surface layer non-woven fabrics and PE film base fabrics are made.The antibacterial and deodouring pet urine pad antibiosis and deodorization effects of the present invention protrude, while with good stability and durability, and product dispersion effect is good, and processing technology is simply, conveniently.

Description

Antibacterial and deodouring pet urine pad and its manufacturing method
Technical field
The present invention relates to pet urine pads;More particularly, it relates to antibacterial and deodouring pet urine pad.In addition, the present invention is also It is related to the manufacturing method of pet urine pad.
Background technology
Currently, with the abundant of people's material life and meet, the spiritual sustenance of more and more people's pursuit, and pet Just filled up we it is spiritual dependence and comfort.Also psychiatrist points out, pet has the mental health of the mankind , there is the irreplaceable effect of the mankind at place.But coming with summer, it is moistening under high temperature, the smell of pet seems More strong protrusion, many pet owners feel put about because of the smell for the unpleasant stimulation that pet brings.And have very much Taste is extremely difficult to be removed, and with soap, washing powder, after liquid detergent etc. is washed soon, unpleasant peculiar smell come out again.These are different Taste is mainly derived from the taste of the taste and pet excrement of pet itself secretion, and the consumption more energy of owner is needed to go to clear up The excrement and its taste of pet.Consider the convenience of the easiness and owner's cleaning of pet life area, increasingly More people have begun or are beginning to use pet urine pad.Nonetheless, ammonia nitrogen and low molecule are contained in pet excrement The chemical substance of the organic or inorganics sulphur such as amine, mercaptan, thioether causes to will produce stink in air and diaper, and easily grows bacterium, Different degrees of influence is caused to pet and owner.In this context, the diaper with antibacterial and deodorization functions is come into being.
Nowadays, though there is the pet urine pad of antibacterial and deodouring function in the market, there are various problems:1. product or it is more or It is few to contain the harmful substance to pet skin with corrosiveness;2. having a single function, less effective, product can only reduce ammonia nitrogen class Irritation taste, or the peculiar smell of sulfydryl class can only be reduced, or only antibiotic effect, deodorizing effect are poor;3. product stability and resistance to Long property is poor;4 product bad dispersibilities, production technology are complicated;5. product has penetrating odor mixed with the fragrance of masking property, Injury is easily caused to pet.
Invention content
For insufficient existing for existing product as described above and defect, the present invention provide it is a kind of it is nontoxic, simple for process, The all good antibacterial and deodouring pet urine pad of antibiosis and deodorization effects and its manufacturing method.
In the first aspect, the present invention relates to a kind of manufacturing method of antibacterial and deodouring pet urine pad, include the following steps:
(1)Weigh 0.5-1 mass parts of oxidant, the organic iron catalyst of 0.5-1 mass parts, 1-2 mass parts antiseptic, 1-3 mass Part adsorbent, is homogenized, after curing process, is ground to 20-100 mesh, obtain antibacterial deodorant A;
(2)0.2-3.5 mass parts antibacterial deodorant A is added in 100 mass parts high exhaustions to obtain after mixing Mixture B;
(3)Mixture B and wood pulp, toilet paper are pressed in order, be absorbed a layer C;
(4)It is covered each by face layer non-woven fabrics and PE film base fabrics above or below absorbed layer C, antibacterial and deodouring pet urine pad is made.
In a preferred embodiment, the oxidant is selected from Na2Fe04 and sodium bismuthate.The oxidant that the present invention uses For strong base-weak acid salt soluble easily in water, redox reaction can occur after being contacted with peculiar smell and excreta, it can will be therein Organic sulfur and organic amino are oxidized to the solable matter of lighter odor ,-complex reaction of finally decomposing under the action of catalyst, Become tasteless macromolecular chemistry substance, be fixed on absorbed layer, avoids the regeneration of pungent odour.
In a preferred embodiment, organic iron catalyst is selected from ironic citrate and ferric acetyl acetonade.The present invention makes Organic iron catalyst can accelerate oxidation reaction, improve the reaction rate and the extent of reaction of decomposition-complexing, and making originally cannot The deodorization of generation is reacted, and plays good catalytic action, ironic citrate and ferric acetyl acetonade can also promote antibacterial, The raising for sterilizing rate, plays the effect of antibacterial and deodouring to a greater extent.
In a preferred embodiment, the antiseptic is selected from Nano-Zinc, zinc gluconate and basic zinc chloride.The present invention The antiseptic used is attracted to via negative electrical charge in bacterial body after being contacted with bacterium, with internal sulfydryl (- SH), hydroxy Deng combination, make bacterial cell because of protein denaturization, other catalysis reactions can not be normally carried out and influence metabolism, up to bacterial death And it completely disappears.
In a preferred embodiment, the adsorbent is selected from attapulgite, white carbon, humic acid and absorption resin.This It invents the absorption carrier itself used and belongs to porous material, there is very high specific surface area, the same of suction-operated can played When, sufficient reaction compartment is provided, reaction is made more to stablize, improves antibiosis and deodorization effects.
In a preferred embodiment, the high exhaustion is selected from Sodium Polyacrylate.
In second aspect, the present invention relates to the antibacterial and deodouring pet urine pads obtained by method as described above manufacture.
The antibacterial and deodouring pet urine pad of acquisition constructed in accordance has the advantages that:
1, selection has no toxic side effect, or corrosiveness non-stimulated to pet skin belongs to environment-friendly type antibiotic deodorant;
2, antibiosis and deodorization effects protrude, while with good stability and durability;
3, product dispersion effect is good, and processing technology is simply, conveniently;
4, dote on for owner and love and a pure and fresh, clean, comfortable, healthy living environment is provided.
Specific implementation mode
The embodiment of the present invention will be hereafter further described, wherein each embodiment is only that the present invention is exemplary Embodiment, it is not intended to constitute limiting the scope of the invention.Those skilled in the art can according to explanation above with And following description of the embodiments make a variety of different improvement and deformations, without departing from spirit and substance of the present invention. Accordingly, the scope of the present invention is intended merely to be defined by every claim range claimed.
In following examples, odorous gas detection is carried out according to GB/T14679-93, GB/T14678-93;According to GB15979-2002 carries out antibacterial detection.
Embodiment 1
Antibacterial and deodouring pet urine pad is manufactured in accordance with the following steps:
(1)Weigh 0.5 mass parts Na2Fe04,0.5 mass parts ironic citrate, 1 mass parts zinc gluconate, 1 mass parts humic Acid is homogenized, after curing process, is ground to 80 mesh, obtains antibacterial deodorant A;
(2)0.2 mass parts antibacterial deodorant A is added in 100 mass parts polyacrylic resins to be mixed after mixing Close object B;
(3)Mixture B and wood pulp, toilet paper are pressed in order, be absorbed a layer C;
(4)It is covered each by face layer non-woven fabrics and PE film base fabrics above or below absorbed layer C, antibacterial and deodouring pet urine pad is made.
Following detection experiment is carried out to the antibiosis and deodorization effects of thus obtained antibacterial and deodouring pet urine pad:
Common diaper and antibacterial and deodouring diaper of the present invention are made into 20cm × 20cm specifications, pave respectively be put into it is different can be close It closes in container, after the pet excrement 200ml gathered is divided equally, pours into closed container, closing carries out stink after standing 5min Gas detection and antibacterial detection.Common diaper testing result:Ammonia density 85mg/m3, mercaptan, thioether and other sulfur-containing compounds 25mg/m3;Antibiotic rate:Substantially do not have for staphylococcus aureus, Escherichia coli, Candida albicans antibacterial effect. Antibacterial and deodouring diaper testing result of the present invention:Ammonia density 0.5mg/m3, mercaptan, thioether and other sulfur-containing compound 0.1mg/m3;It is anti- Bacterium rate:Staphylococcus aureus 99.5%, Escherichia coli 99.6%, Candida albicans 99.5%.
Embodiment 2
(1)Weigh 1.0 mass parts sodium bismuthates, 1.0 mass parts ferric acetyl acetonades, 1.5 mass parts Nano-Zincs, 2.5 mass parts hard charcoals It is black, it is homogenized, after curing process, is ground to 60 mesh, obtain antibacterial deodorant A;
(2)0.2 mass parts antibacterial deodorant A is added in 100 mass parts polyacrylic resins to be mixed after mixing Close object B;
(3)Mixture B and wood pulp, toilet paper are pressed in order, be absorbed a layer C;
(4)It is covered each by face layer non-woven fabrics and PE film base fabrics above or below absorbed layer C, antibacterial and deodouring pet urine pad is made.
Following detection experiment is carried out to the antibiosis and deodorization effects of thus obtained antibacterial and deodouring pet urine pad:
Common diaper and antibacterial and deodouring diaper of the present invention are made into 20cm × 20cm specifications, pave respectively be put into it is different can be close It closes in container, after the pet excrement 200ml gathered is divided equally, pours into closed container, closing carries out stink after standing 5min Gas detection and antibacterial detection.Common diaper testing result:Ammonia density 86mg/m3, mercaptan, thioether and other sulfur-containing compounds 23mg/m3;Antibiotic rate:Substantially do not have for staphylococcus aureus, Escherichia coli, Candida albicans antibacterial effect. Antibacterial and deodouring diaper testing result of the present invention:Ammonia density 0.57mg/m3, mercaptan, thioether and other sulfur-containing compound 0.12mg/m3; Antibiotic rate:Staphylococcus aureus 99.4%, Escherichia coli 99.5%, Candida albicans 99.6%.
Embodiment 3
(1)Weigh 1.0 mass parts sodium bismuthates, 1.0 mass parts ferric acetyl acetonades, 2 mass parts basic zinc chlorides, 2 mass parts bumps Stick soil, is homogenized, after curing process, is ground to 20 mesh, obtain antibacterial deodorant A;
(2)2.5 mass parts antibacterial deodorant A are added in 100 mass parts polyacrylic resins to be mixed after mixing Close object B;
(3)Mixture B and wood pulp, toilet paper are pressed in order, be absorbed a layer C;
(4)It is covered each by face layer non-woven fabrics and PE film base fabrics above or below absorbed layer C, antibacterial and deodouring pet urine pad is made.
Following detection experiment is carried out to the antibiosis and deodorization effects of thus obtained antibacterial and deodouring pet urine pad:
Common diaper and antibacterial and deodouring diaper of the present invention are made into 20cm × 20cm specifications, pave respectively be put into it is different can be close It closes in container, after the pet excrement 200ml gathered is divided equally, pours into closed container, closing carries out stink after standing 5min Gas detection and antibacterial detection.Common diaper testing result:Ammonia density 82mg/m3, mercaptan, thioether and other sulfur-containing compounds 26mg/m3;Antibiotic rate:Substantially do not have for staphylococcus aureus, Escherichia coli, Candida albicans antibacterial effect. Antibacterial and deodouring diaper testing result of the present invention:Ammonia density 0.61mg/m3, mercaptan, thioether and other sulfur-containing compound 0.11mg/m3; Antibiotic rate:Staphylococcus aureus 99.7%, Escherichia coli 99.8%, Candida albicans 99.8%.
Embodiment 4
(1)Weighing 1.0 mass parts Na2Fe04s, 1.0 mass parts ironic citrates, 2 mass parts Nano-Zincs, 3 mass parts adsorb resin, It is homogenized, after curing process, is ground to 100 mesh, obtain antibacterial deodorant A;
(2)3.5 mass parts antibacterial deodorant A are added in 100 mass parts polyacrylic resins to be mixed after mixing Close object B;
(3)Mixture B and wood pulp, toilet paper are pressed in order, be absorbed a layer C;
(4)It is covered each by face layer non-woven fabrics and PE film base fabrics above or below absorbed layer C, antibacterial and deodouring pet urine pad is made.
Following detection experiment is carried out to the antibiosis and deodorization effects of thus obtained antibacterial and deodouring pet urine pad:
Common diaper and antibacterial and deodouring diaper of the present invention are made into 20cm × 20cm specifications, pave respectively be put into it is different can be close It closes in container, after the pet excrement 200ml gathered is divided equally, pours into closed container, closing carries out stink after standing 5min Gas detection and antibacterial detection.Common diaper testing result:Ammonia density 87mg/m3, mercaptan, thioether and other sulfur-containing compounds 26mg/m3;Antibiotic rate:Substantially do not have for staphylococcus aureus, Escherichia coli, Candida albicans antibacterial effect. Antibacterial and deodouring diaper testing result of the present invention:Ammonia density 0.31mg/m3, mercaptan, thioether and other sulfur-containing compound 0.08mg/m3; Antibiotic rate:Staphylococcus aureus 99.8%, Escherichia coli 99.9%, Candida albicans 99.9%.
Embodiment 5
(1)Weigh 0.6 mass parts Na2Fe04,0.8 mass parts ferric acetyl acetonade, 1.1 mass parts zinc gluconates, 1.3 mass Part white carbon, is homogenized, after curing process, is ground to 40 mesh, obtain antibacterial deodorant A;
(2)1.2 mass parts antibacterial deodorant A are added in 100 mass parts polyacrylic resins to be mixed after mixing Close object B;
(3)Mixture B and wood pulp, toilet paper are pressed in order, be absorbed a layer C;
(4)It is covered each by face layer non-woven fabrics and PE film base fabrics above or below absorbed layer C, antibacterial and deodouring pet urine pad is made.
Following detection experiment is carried out to the antibiosis and deodorization effects of thus obtained antibacterial and deodouring pet urine pad:
Common diaper and antibacterial and deodouring diaper of the present invention are made into 20cm × 20cm specifications, pave respectively be put into it is different can be close It closes in container, after the pet excrement 200ml gathered is divided equally, pours into closed container, closing carries out stink after standing 5min Gas detection and antibacterial detection.Common diaper testing result:Ammonia density 83mg/m3, mercaptan, thioether and other sulfur-containing compounds 24mg/m3;Antibiotic rate:Substantially do not have for staphylococcus aureus, Escherichia coli, Candida albicans antibacterial effect. Antibacterial and deodouring diaper testing result of the present invention:Ammonia density 0.56mg/m3, mercaptan, thioether and other sulfur-containing compound 0.12mg/m3; Antibiotic rate:Staphylococcus aureus 99.6%, Escherichia coli 99.7%, Candida albicans 99.9%.
Embodiment 6
(1)Weigh 0.7 mass parts sodium bismuthate, 0.9 mass parts ferric acetyl acetonade, 1.6 mass parts Nano-Zincs, 1.9 mass parts humics Acid is homogenized, after curing process, is ground to 70 mesh, obtains antibacterial deodorant A;
(2)1.3 mass parts antibacterial deodorant A are added in 100 mass parts polyacrylic resins to be mixed after mixing Close object B;
(3)Mixture B and wood pulp, toilet paper are pressed in order, be absorbed a layer C;
(4)It is covered each by face layer non-woven fabrics and PE film base fabrics above or below absorbed layer C, antibacterial and deodouring pet urine pad is made.
Following detection experiment is carried out to the antibiosis and deodorization effects of thus obtained antibacterial and deodouring pet urine pad:
Common diaper and antibacterial and deodouring diaper of the present invention are made into 20cm × 20cm specifications, pave respectively be put into it is different can be close It closes in container, after the pet excrement 200ml gathered is divided equally, pours into closed container, closing carries out stink after standing 5min Gas detection and antibacterial detection.Common diaper testing result:Ammonia density 81mg/m3, mercaptan, thioether and other sulfur-containing compounds 23mg/m3;Antibiotic rate:Substantially do not have for staphylococcus aureus, Escherichia coli, Candida albicans antibacterial effect. Antibacterial and deodouring diaper testing result of the present invention:Ammonia density 0.7mg/m3, mercaptan, thioether and other sulfur-containing compound 0.14mg/m3; Antibiotic rate:Staphylococcus aureus 99.5%, Escherichia coli 99.4%, Candida albicans 99.4%.

Claims (7)

1. a kind of manufacturing method of antibacterial and deodouring pet urine pad, it is characterised in that:Described method includes following steps:
(1)Weigh 0.5-1 mass parts of oxidant, the organic iron catalyst of 0.5-1 mass parts, 1-2 mass parts antiseptic, 1-3 mass Part adsorbent, is homogenized, after curing process, is ground to 20-100 mesh, obtain antibacterial deodorant A;
(2)0.2-3.5 mass parts antibacterial deodorant A is added in 100 mass parts high exhaustions to obtain after mixing Mixture B;
(3)Mixture B and wood pulp, toilet paper are pressed in order, be absorbed a layer C;
(4)It is covered each by face layer non-woven fabrics and PE film base fabrics above or below absorbed layer C, antibacterial and deodouring pet urine pad is made.
2. the manufacturing method of antibacterial and deodouring pet urine pad according to claim 1, it is characterised in that:The oxidant is selected from Na2Fe04 and sodium bismuthate.
3. the manufacturing method of antibacterial and deodouring pet urine pad according to claim 1 or 2, it is characterised in that:The Organic Iron Catalyst is selected from ironic citrate and ferric acetyl acetonade.
4. the manufacturing method of antibacterial and deodouring pet urine pad according to any one of claims 1 to 3, it is characterised in that:It is described Antiseptic is selected from Nano-Zinc, zinc gluconate and basic zinc chloride.
5. the manufacturing method of antibacterial and deodouring pet urine pad according to any one of claims 1 to 4, it is characterised in that:It is described Adsorbent is selected from attapulgite, white carbon, humic acid and absorption resin.
6. the manufacturing method of antibacterial and deodouring pet urine pad according to any one of claims 1 to 5, it is characterised in that:It is described High exhaustion is selected from Sodium Polyacrylate.
7. a kind of antibacterial and deodouring pet urine pad, it is characterised in that:Using according to claim 1-6 any one of them method systems .
CN201810691658.XA 2018-06-28 2018-06-28 Antibacterial and deodouring pet urine pad and its manufacturing method Pending CN108432642A (en)