CN108149874A - Real stone paint decoration surface heat insulation decoration integrated plate and its manufacture craft - Google Patents
Real stone paint decoration surface heat insulation decoration integrated plate and its manufacture craft Download PDFInfo
- Publication number
- CN108149874A CN108149874A CN201711329075.4A CN201711329075A CN108149874A CN 108149874 A CN108149874 A CN 108149874A CN 201711329075 A CN201711329075 A CN 201711329075A CN 108149874 A CN108149874 A CN 108149874A
- Authority
- CN
- China
- Prior art keywords
- heat insulation
- real stone
- stone paint
- panel
- decoration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to real stone paint decoration surface heat insulation decoration integrated plate and its manufacture crafts, include the real stone paint decoration surface of bottom plate, heat insulation core material layer, panel and the panel upper surface that is laid in.Compared with prior art, all planks that the present invention uses are A grades of fire-retardant fireproof materials, whole fire-protection rating reaches the requirement of highest fire-protection rating, the facing of natural real stone paint do not rise rouse, do not fall off, not cracking, is water-fast, is alkaline-resisting, strong adhesive force, impact resistance, can be according to the features such as client's selection different facing colors.
Description
Technical field
The present invention relates to a kind of Side fascias, more particularly, to a kind of real stone paint decoration surface heat insulation decoration integrated plate and its make work
Skill.
Background technology
Current lacquer system is all directly in wall construction, plays decorative effect, do not add in heat insulation effect.Individually
Heat insulation decoration integrated plate play the role of heat preservation and decoration, but cost is excessively high.
Chinese patent CN104947812A discloses a kind of thermal insulation board, includes wall layer successively from inside to outside, styrofoam, resists
Split screed, glass web scrim layer, architectural surface；Styrofoam is connect by nylon anchor bolt with wall layer.It is protected using styrofoam
In the case of warm plate, glass web scrim layer is in addition added, improves the heat insulation effect of wall.But this kind of construction technology is
Decoration function is individually played, easy to fall off, cracking is constructed because of the next many uncertainties of worker, weather, temperature band, and linked network is applied
Work is cumbersome, long in time limit, intensity difference.Finish coat out-of-flatness influences beauty, and service life is general.
Invention content
It is an object of the present invention to overcome the above-mentioned drawbacks of the prior art and provide a kind of good flame retardation effects
Real stone paint decoration surface heat insulation decoration integrated plate and its manufacture craft.
The purpose of the present invention can be achieved through the following technical solutions：
Real stone paint decoration surface heat insulation decoration integrated plate, including bottom plate, heat insulation core material layer, panel and the panel upper surface that is laid in
Real stone paint decoration surface.
The bottom plate is perforated sound-absorbing plate, and as preferred embodiment, perforated sound-absorbing plate is to perforate equipped with groover
Cement base plate.
It is connected between the heat insulation core material layer and bottom plate and panel through adhesive.
As preferred embodiment, adhesive is crosslinked for solvent-free epoxy resin base and polyurethane resin-based two-component
Curing type adhesive.
The heat insulation core material is less than the inorganic heat insulation material layer of 0.048W/ (mK) for thermal conductivity factor, with good day
Right rock is formed through high-temperature calcination high speed centrifugation into the rock wool belt that fibre is formed.
The panel is calcium silicate board or cement fibrolite plate.
The real stone paint decoration surface is natural granite, natural rubble, mountain flour are main stuffing, using synthetic resin emulsion as
Primary bond agent is simultaneously aided with the environment-friendlywater-based water-based paint that waterborne nature vegetalitas auxiliary agent is formulated and forms combination with decorative surfaces.
As preferred embodiment, the natural granite of use, natural rubble, mountain flour grain size be to be chosen meticulously from mountain
The natural colorful ore of choosing, by strictly processing, refined to form, product specification is complete, light that is bright in colour, being filled with the Nature
It is color.The coating of natural colour sand production has many advantages, such as that color and luster is soft, graceful, ageing-resistant, will never fade, and it is more to solve exterior coating
The problem of year colour retention difference, therefore there is high application value.Wherein, the qualitative effects of color sand stone outer after smearing
Type and color effect, and the quality of adhesive and adjuvant then affects the service life of lacquer, it is natural granite, natural broken
Stone, mountain flour grain size be less than 3mm.
Using synthetic resin emulsion as base-material, form with the configuration of pigment, extender pigment and various auxiliary agents, can be formed after applying Tu
The exterior coating of the thin matter coating of surfacing.Play decoration and protective action.Synthetic resin emulsion by monomer, emulsifier, draw
It is 51 in mass ratio to send out agent:1-2:The high molecular polymer that 0.2-0.7 is polymerized, the monomer are methyl methacrylate
Ester, methacrylic acid styrene or styrene, the emulsifier are answered for anionic emulsifier and nonionic emulsifier
With object, the initiator is water soluble persulfates class, including ammonium persulfate or potassium peroxydisulfate.
Waterborne nature vegetalitas auxiliary agent is using polysiloxanes as the organic silicon defoamer of primary raw material, is being slowly added into naturally
Colored stone sand stirs evenly.
The manufacture craft of real stone paint decoration surface heat insulation decoration integrated plate, using following steps：
(1) it is 4 by weight by epoxy resin based cross-linker and polyurethane resin based cross-linker：1 carries out being mixed to get glue
Glutinous agent；
(2) adhesive being configured is placed in the glue spreader of rolling by mixing machine；
(3) glue spreader that is sent to of perforated sound-absorbing plate balance is carried out gluing, the glue-spread of single side is 300-400g/m2；
(4) heat insulation core material is neatly placed on glue-coated perforated sound-absorbing plate；
(5) panel balance was sent to glue spreader gluing, the glue-spread of single side is 300-400g/m2；
(6) glue-coated panel is placed on heat insulation core material；
(7) compound good plank is controlled with cold pressing 4-6h, pressure in cold press is placed in 3-4MPa；
(8) after the completion of being cold-pressed, required specification is cut into；
(9) it after the completion of cutting, drills on panel, every square no less than 6；
(10) lacquer is sprayed in panel surface when using, that is, makes and obtains real stone paint decoration surface heat insulation decoration integrated plate.
Compared with prior art, all planks that the present invention uses are A grades of fire-retardant fireproof materials, and whole fire-protection rating reaches
The requirement of highest fire-protection rating, the natural real stone paint of use have that fire prevention, waterproof, acid and alkali-resistance, nontoxic, tasteless, bonding force is strong, forever
The features such as colour-fast, can effectively stop extraneous adverse circumstances and building is corroded, extends the service life of building, due to lacquer
Have good adhesive force and freeze-thaw resistance property, therefore be suitble to use in cold district.In order to the uses such as architect, designer
The decorative colour series and layout of personnel matches, and can be mixed colours according to specific demand, can also be according to client's
The product that intention offer is made to measure, and the facing of natural real stone paint does not rise and rouses, do not fall off, not cracking, is water-fast, is alkaline-resisting, is attached
The features such as putting forth effort strong, impact resistance, can different facing colors being selected according to client.
Description of the drawings
Fig. 1 is the structural diagram of the present invention.
In figure, 1- real stone paint decoration surfaces, 2- panels, 3- adhesives, 4- heat insulation core materials layer, 5- bottom plates.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail.Following embodiment will be helpful to the technology of this field
Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the ordinary skill to this field
For personnel, without departing from the inventive concept of the premise, various modifications and improvements can be made.These belong to the present invention
Protection domain.
Embodiment 1
Real stone paint decoration surface heat insulation decoration integrated plate, structure is as shown in Figure 1, including bottom plate 5, heat insulation core material layer 4, panel 2
And the real stone paint decoration surface 1 for the panel upper surface that is laid in.The bottom plate 5 used is perforated sound-absorbing plate, is directly prepared through factory lines
Cement base plate in thermal insulation board bottom surface, risen in thermal insulation board bottom surface enhancing, waterproof, fire retardation techonosphere.By directly sticking
Patch perforation, fluting cement base plate are formed.It is connected between heat insulation core material layer 4 and bottom plate 5 and panel 2 through adhesive 3.
The adhesive used be solvent-free epoxy resin base or polyurethane resin-based, two-component crosslinking curing type gluing material
Material bonds for panel and thermal insulation board, bottom plate.Heat insulation core material layer 4 is less than the inorganic heat preservation of 0.048W/ (mK) by thermal conductivity factor
Material is mainly formed (hereinafter referred to as with good natural rock through high-temperature calcination high speed centrifugation into fibre：Rock wool belt (RWS)),
The techonosphere of insulation effect is played in thermal insulation board.Panel 2 is calcium silicate board or cement fibrolite plate, and decoration is played in heat insulating decorative board
With the techonosphere of protective effect.Real stone paint decoration surface 1 is based on natural granite, natural rubble, mountain flour of certain granules degree etc.
Material is wanted, the environment-friendly type that a variety of waterborne nature vegetalitas auxiliary agents are formulated as main bonding agent and is aided with using synthetic resin emulsion
Water paint.It is the one kind belonged in coating for internal and external wall.
The present embodiment is using the calcium silicate board of no facing, cement fibrolite plate by adhesive and heat insulation core material, bottom plate in work
Factory's assembly line is combined, and is fixed on outer plinth course using the mode that adhesive mortar bonds, formula is being directed through using panel
Anchorage style anchored, at the seam crossing of plank and anchoring with profession sealing material do water-proofing treatment, integrally carry out
After waterproof and cracking resistance processing, spraying alkali-resistant primer, spraying lacquer, finishing varnish.
The manufacture craft of real stone paint decoration surface heat insulation decoration integrated plate, using following steps：
(1) it is 4 by weight by epoxy resin based cross-linker and polyurethane resin based cross-linker：1 carries out being mixed to get glue
Glutinous agent；
(2) adhesive being configured is placed in the glue spreader of rolling by mixing machine；
(3) glue spreader that is sent to of perforated sound-absorbing plate balance is carried out gluing, the glue-spread of single side is 320g/m2；
(4) heat insulation core material is neatly placed on glue-coated perforated sound-absorbing plate；
(5) panel balance was sent to glue spreader gluing, the glue-spread of single side is 320g/m2；
(6) glue-coated panel is placed on heat insulation core material；
(7) compound good plank is controlled with cold pressing 5h, pressure in cold press is placed in 3.5MPa；
(8) after the completion of being cold-pressed, required specification is cut into；
(9) it after the completion of cutting, drills on panel, every square no less than 6；
(10) lacquer is sprayed in panel surface when using, that is, makes and obtains real stone paint decoration surface heat insulation decoration integrated plate, have
Body construction process is as follows：
Pacify base course wall inspection → snap the line lattice → composite plate bottom surface point type Tu adhesive mortar → composite plate anchor bolt is fixed →
It installs into and professional encapsulation process → exterior wall is done at rear plank seam and anchoring integrally to do waterproof sealing leveling → roller coating special
Alkali-resistant primer → spraying lacquer → spraying finishing varnish → final acceptance of construction.
Embodiment 2
Real stone paint decoration surface heat insulation decoration integrated plate, including bottom plate, heat insulation core material layer, panel and the panel upper surface that is laid in
Real stone paint decoration surface.Wherein, the bottom plate used is perforated sound-absorbing plate, to be equipped with the cement base plate of groover perforation.Heat insulation core material
Between layer and bottom plate and panel through solvent-free epoxy resin base and polyurethane resin-based two-component crosslinking curing type adhesive into
Row bonds.The heat insulation core material used is less than the inorganic heat insulation material layer of 0.048W/ (mK) for thermal conductivity factor, with good natural
Rock is formed through high-temperature calcination high speed centrifugation into the rock wool belt that fibre is formed.Panel is calcium silicate board.
Real stone paint decoration surface is natural granite, natural rubble, mountain flour are main stuffing, using synthetic resin emulsion to be main viscous
It connects agent and is aided with the environment-friendlywater-based water-based paint that waterborne nature vegetalitas auxiliary agent is formulated and form combination with decorative surfaces.Natural flowers hilllock
Rock, natural rubble, mountain flour grain size be less than 3mm, synthetic resin emulsion by monomer, emulsifier, initiator in mass ratio be 51:1:
0.2 high molecular polymer being polymerized, monomer are methyl methacrylate, and emulsifier is anionic emulsifier and nonionic
The compound of type emulsifier, initiator are ammonium persulfate, and waterborne nature vegetalitas auxiliary agent is using polysiloxanes as primary raw material
Organic silicon defoamer.
The manufacture craft of real stone paint decoration surface heat insulation decoration integrated plate, using following steps：
(1) it is 4 by weight by epoxy resin based cross-linker and polyurethane resin based cross-linker：1 carries out being mixed to get glue
Glutinous agent；
(2) adhesive being configured is placed in the glue spreader of rolling by mixing machine；
(3) glue spreader that is sent to of perforated sound-absorbing plate balance is carried out gluing, the glue-spread of single side is 300g/m2；
(4) heat insulation core material is neatly placed on glue-coated perforated sound-absorbing plate；
(5) panel balance was sent to glue spreader gluing, the glue-spread of single side is 300g/m2；
(6) glue-coated panel is placed on heat insulation core material；
(7) compound good plank is controlled with cold pressing 4h, pressure in cold press is placed in 4MPa；
(8) after the completion of being cold-pressed, required specification is cut into；
(9) it after the completion of cutting, drills on panel, every square no less than 6；
(10) lacquer is sprayed in panel surface when using, that is, makes and obtains real stone paint decoration surface heat insulation decoration integrated plate.
Embodiment 3
Real stone paint decoration surface heat insulation decoration integrated plate, including bottom plate, heat insulation core material layer, panel and the panel upper surface that is laid in
Real stone paint decoration surface.Wherein, the bottom plate used is perforated sound-absorbing plate, to be equipped with the cement base plate of groover perforation.Heat insulation core material
Between layer and bottom plate and panel through solvent-free epoxy resin base and polyurethane resin-based two-component crosslinking curing type adhesive into
Row bonds.The heat insulation core material used is less than the inorganic heat insulation material layer of 0.048W/ (mK) for thermal conductivity factor, with good natural
Rock is formed through high-temperature calcination high speed centrifugation into the rock wool belt that fibre is formed.Panel is cement fibrolite plate.
Real stone paint decoration surface is natural granite, natural rubble, mountain flour are main stuffing, using synthetic resin emulsion to be main viscous
It connects agent and is aided with the environment-friendlywater-based water-based paint that waterborne nature vegetalitas auxiliary agent is formulated and form combination with decorative surfaces.Natural flowers hilllock
Rock, natural rubble, mountain flour grain size be less than 3mm, synthetic resin emulsion by monomer, emulsifier, initiator in mass ratio be 51:2:
0.7 high molecular polymer being polymerized, monomer be methacrylic acid styrene, emulsifier for anionic emulsifier and it is non-from
The compound of subtype emulsifier, initiator are potassium peroxydisulfate, and waterborne nature vegetalitas auxiliary agent is using polysiloxanes as primary raw material
Organic silicon defoamer.
The manufacture craft of real stone paint decoration surface heat insulation decoration integrated plate, using following steps：
(1) it is 4 by weight by epoxy resin based cross-linker and polyurethane resin based cross-linker：1 carries out being mixed to get glue
Glutinous agent；
(2) adhesive being configured is placed in the glue spreader of rolling by mixing machine；
(3) glue spreader that is sent to of perforated sound-absorbing plate balance is carried out gluing, the glue-spread of single side is 400g/m2；
(4) heat insulation core material is neatly placed on glue-coated perforated sound-absorbing plate；
(5) panel balance was sent to glue spreader gluing, the glue-spread of single side is 400g/m2；
(6) glue-coated panel is placed on heat insulation core material；
(7) compound good plank is controlled with cold pressing 6h, pressure in cold press is placed in 3MPa；
(8) after the completion of being cold-pressed, required specification is cut into；
(9) it after the completion of cutting, drills on panel, every square no less than 6；
(10) lacquer is sprayed in panel surface when using, that is, makes and obtains real stone paint decoration surface heat insulation decoration integrated plate.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (10)
1. real stone paint decoration surface heat insulation decoration integrated plate, which is characterized in that the integrated board include bottom plate, heat insulation core material layer, panel and
Be laid in the real stone paint decoration surface of panel upper surface.
2. real stone paint decoration surface heat insulation decoration integrated plate according to claim 1, which is characterized in that the bottom plate is perforation
Abatvoix.
3. real stone paint decoration surface heat insulation decoration integrated plate according to claim 2, which is characterized in that the perforated sound-absorbing plate
To be equipped with the cement base plate of groover perforation.
4. real stone paint decoration surface heat insulation decoration integrated plate according to claim 1, which is characterized in that the heat insulation core material layer
It is connect between bottom plate and panel through adhesive.
5. real stone paint decoration surface heat insulation decoration integrated plate according to claim 4, which is characterized in that the adhesive is nothing
Solvent epoxy resin-matrix and polyurethane resin-based two-component crosslinking curing type adhesive.
6. real stone paint decoration surface heat insulation decoration integrated plate according to claim 1, which is characterized in that the heat insulation core material is
Thermal conductivity factor is less than the inorganic heat insulation material layer of 0.048W/ (mK), with good natural rock through high-temperature calcination high speed centrifugation
The rock wool belt formed into fibre is formed.
7. real stone paint decoration surface heat insulation decoration integrated plate according to claim 1, which is characterized in that the panel is silicic acid
Calcium plate or cement fibrolite plate.
8. real stone paint decoration surface heat insulation decoration integrated plate according to claim 1, which is characterized in that the real stone paint decoration surface
It is main stuffing for natural granite, natural rubble, mountain flour, waterborne nature as main bonding agent and is aided with using synthetic resin emulsion
The environment-friendlywater-based water-based paint that vegetalitas auxiliary agent is formulated forms combination with decorative surfaces.
9. real stone paint decoration surface heat insulation decoration integrated plate according to claim 8, which is characterized in that
The natural granite, natural rubble, mountain flour grain size be less than 3mm,
The synthetic resin emulsion is 51 in mass ratio by monomer, emulsifier, initiator:1-2:What 0.2-0.7 was polymerized
High molecular polymer, the monomer be methyl methacrylate, methacrylic acid styrene or styrene, the emulsifier
For anionic emulsifier and the compound of nonionic emulsifier, the initiator is water soluble persulfates class, including
Ammonium persulfate or potassium peroxydisulfate,
The waterborne nature vegetalitas auxiliary agent is using polysiloxanes as the organic silicon defoamer of primary raw material.
10. the manufacture craft of real stone paint decoration surface heat insulation decoration integrated plate as described in claim 1, which is characterized in that the technique
Using following steps：
(1) it is 4 by weight by epoxy resin based cross-linker and polyurethane resin based cross-linker：1 carries out being mixed to get adhesive；
(2) adhesive being configured is placed in the glue spreader of rolling by mixing machine；
(3) glue spreader that is sent to of perforated sound-absorbing plate balance is carried out gluing, the glue-spread of single side is 300-400g/m2；
(4) heat insulation core material is neatly placed on glue-coated perforated sound-absorbing plate；
(5) panel balance was sent to glue spreader gluing, the glue-spread of single side is 300-400g/m2；
(6) glue-coated panel is placed on heat insulation core material；
(7) compound good plank is controlled with cold pressing 4-6h, pressure in cold press is placed in 3-4MPa；
(8) after the completion of being cold-pressed, required specification is cut into；
(9) it after the completion of cutting, drills on panel, every square no less than 6；
(10) lacquer is sprayed in panel surface when using, that is, makes and obtains real stone paint decoration surface heat insulation decoration integrated plate.