CN108069698A - High-strength abrasion-proof ceramic tile and preparation method thereof - Google Patents

High-strength abrasion-proof ceramic tile and preparation method thereof Download PDF

Info

Publication number
CN108069698A
CN108069698A CN201711450862.4A CN201711450862A CN108069698A CN 108069698 A CN108069698 A CN 108069698A CN 201711450862 A CN201711450862 A CN 201711450862A CN 108069698 A CN108069698 A CN 108069698A
Authority
CN
China
Prior art keywords
parts
soil
corundum
ceramic tile
strength abrasion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711450862.4A
Other languages
Chinese (zh)
Inventor
陈楚玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711450862.4A priority Critical patent/CN108069698A/en
Publication of CN108069698A publication Critical patent/CN108069698A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of high-strength abrasion-proof ceramic tiles, are grouped by each group of following parts by weight：5~12 parts of calcite, 10~16 parts of electro-corundum, 4~7 parts of galapectite, 2~5 parts of Topaz, 1~3 part of chromite powder, 3~6 parts of carbon fiber, wide 8~14 parts of city soil, 9~15 parts of vermiculite, high 11~18 parts of Cen soil, 6~10 parts of sandstone, 12~19 parts of sodium porcelain sand, 10~17 parts of sericite, 7~14 parts of Suzhou soil, 5~9 parts of potassium feldspar.The invention further relates to the preparation methods of high-strength abrasion-proof ceramic tile, its cold crushing strength of high-strength abrasion-proof ceramic tile produced by its formula and preparation method is more than 160MPa, high temperature break resistant intensity is more than 28Mpa, wear-resisting property is good, long with good characteristics, service lifes such as anti-erosion, impermeabilisation, anti-strips, manufacturing process is simple, it is easily achieved, suitable for the decorations in the places such as market, toilet, kitchen, has a vast market prospect.

Description

High-strength abrasion-proof ceramic tile and preparation method thereof
Technical field
The present invention relates to ceramic tile field, more particularly, to a kind of high-strength abrasion-proof ceramic tile and preparation method thereof.
Background technology
World's development of real estate is rapid so that and the production and consumption of world's ceramic tile is all got a larger development, due to Chinese tile product designs and varieties are more, quantity is big, quality is good, low- medium- high level product is complete, choice is big and affordable, generation Chinese tile product is favored many countries and regions on boundary very much, and proportion of the Chinese ceramic tile in international market is growing.And In the current constantly age of seeking change and innovation, requirement of the people to decorating ceramic tile, especially for the intensity and wearability of ceramic tile The requirement of energy is higher and higher, this just forces ceramic tile production firm to accelerate the paces of new product development, constantly puts out a new product, with suitable Answer the different needs of consumer.
The content of the invention
The object of the present invention is to provide a kind of high-strength abrasion-proof ceramic tiles.
It is a further object of the present invention to provide a kind of preparation methods of the high-strength abrasion-proof ceramic tile.
The object of the invention is achieved by the following technical programs：
A kind of high-strength abrasion-proof ceramic tile is provided, is grouped by each group of following parts by weight：5~12 parts of calcite, electro-corundum 10~16 parts, 4~7 parts of galapectite, 2~5 parts of Topaz, 1~3 part of chromite powder, 3~6 parts of carbon fiber, wide 8~14 parts of city soil, 9~15 parts of vermiculite, high 11~18 parts of Cen soil, 6~10 parts of sandstone, 12~19 parts of sodium porcelain sand, 10~17 parts of sericite, Suzhou soil 7~14 parts, 5~9 parts of potassium feldspar.
Preferably, the high-strength abrasion-proof ceramic tile is grouped by each group of following parts by weight：9 parts of calcite, electric smelting is firm It is 14 parts beautiful, 6 parts of galapectite, 4 parts of Topaz, 2 parts of chromite powder, 5 parts of carbon fiber, wide 10 parts of city soil, 12 parts of vermiculite, high Cen soil 15 parts, 8 parts of sandstone, 15 parts of sodium porcelain sand, 14 parts of sericite, 11 parts of Suzhou soil, 7 parts of potassium feldspar.
Further, it is fine and close to include electric smelting plate diamond spar, fused white corundum, fused brown corundum and electric smelting for the electro-corundum Corundum.
The present invention also provides the preparation methods of the high-strength abrasion-proof ceramic tile, comprise the following steps：
S1. raw material are taken by weight ratio, with ball：Water：Material=2：0.7~0.8：1 ratio goal barreling is milled to fineness as 250 ~300 mesh sieves tail over 0.3~0.5%, spare；
S2. 0.05~0.23 part of 0.3~0.5 part of chitosan and wood vinegar, stirring are added in step S1 products therefroms Uniformly, aging 8~13 days, except iron, it is spare to obtain blank；
S3. blank is pressed into adobe, then dried, enter the firing of kiln oxidizing flame, firing temperature is 1200~1350 DEG C, is fired Time is 10~15h, and natural cooling through edging, is packaged to be finished product.
Compared with prior art, the invention has the advantages that：
The present invention provides a kind of high-strength abrasion-proof ceramic tile, cold crushing strength is more than 160MPa, and high temperature break resistant intensity is more than 28Mpa, wear-resisting property is good, has the good characteristics such as anti-erosion, impermeabilisation, anti-strip, and service life is long, and manufacturing process is simple, It is easily achieved, suitable for the decorations in the places such as market, toilet, kitchen, has a vast market prospect.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of high-strength abrasion-proof ceramic tiles, are grouped by each group of following parts by weight：9 parts of calcite, electricity Molten 14 parts of corundum, 6 parts of galapectite, 4 parts of Topaz, 2 parts of chromite powder, 5 parts of carbon fiber, wide 10 parts of city soil, 12 parts of vermiculite are high 15 parts of Cen soil, 8 parts of sandstone, 15 parts of sodium porcelain sand, 14 parts of sericite, 11 parts of Suzhou soil, 7 parts of potassium feldspar.Wherein, the electro-corundum Including electric smelting plate diamond spar, fused white corundum, fused brown corundum and electric smelting dense alumina.
Embodiment 2
Present embodiment discloses a kind of high-strength abrasion-proof ceramic tiles, are grouped by each group of following parts by weight：12 parts of calcite, electricity Molten 10 parts of corundum, 7 parts of galapectite, 2 parts of Topaz, 3 parts of chromite powder, 3 parts of carbon fiber, wide 14 parts of city soil, 9 parts of vermiculite are high 18 parts of Cen soil, 6 parts of sandstone, 19 parts of sodium porcelain sand, 10 parts of sericite, 14 parts of Suzhou soil, 5 parts of potassium feldspar.Wherein, the electro-corundum Including electric smelting plate diamond spar, fused white corundum, fused brown corundum and electric smelting dense alumina.
Embodiment 3
Present embodiment discloses a kind of high-strength abrasion-proof ceramic tiles, are grouped by each group of following parts by weight：5 parts of calcite, electricity Molten 4 parts of plate diamond spar, 4 parts of fused white corundum, 4 parts of fused brown corundum, 4 parts of electric smelting dense alumina, 4 parts of galapectite, Topaz 5 Part, 1 part of chromite powder, 6 parts of carbon fiber, wide 8 parts of city soil, 15 parts of vermiculite, high 11 parts of Cen soil, 10 parts of sandstone, 12 parts of sodium porcelain sand, 17 parts of sericite, 7 parts of Suzhou soil, 9 parts of potassium feldspar.
Embodiment 4
Present embodiment discloses a kind of high-strength abrasion-proof ceramic tiles, are grouped by each group of following parts by weight：6 parts of calcite, electricity Molten 12 parts of corundum, 5 parts of galapectite, 3 parts of Topaz, 1 part of chromite powder, 4 parts of carbon fiber, wide 12 parts of city soil, 10 parts of vermiculite are high 13 parts of Cen soil, 9 parts of sandstone, 14 parts of sodium porcelain sand, 12 parts of sericite, 12 parts of Suzhou soil, 8 parts of potassium feldspar.Wherein, the electro-corundum Including electric smelting plate diamond spar, fused white corundum, fused brown corundum and electric smelting dense alumina.
Embodiment 5
Present embodiment discloses a kind of high-strength abrasion-proof ceramic tiles, are grouped by each group of following parts by weight：11 parts of calcite, electricity Molten 11 parts of corundum, 6 parts of galapectite, 4 parts of Topaz, 2 parts of chromite powder, 5 parts of carbon fiber, wide 10 parts of city soil, 13 parts of vermiculite are high 17 parts of Cen soil, 9 parts of sandstone, 15 parts of sodium porcelain sand, 13 parts of sericite, 9 parts of Suzhou soil, 6 parts of potassium feldspar.Wherein, the electro-corundum Including electric smelting plate diamond spar, fused white corundum, fused brown corundum and electric smelting dense alumina.
Embodiment 6
The components by weight percent of 1~5 any embodiment of Example prepares high-strength abrasion-proof ceramic tile, and preparation process is as follows：
S1. raw material are taken by weight ratio, with ball：Water：Material=2：0.7：1 ratio goal barreling is milled to fineness and is sieved for 300 mesh sieves Remaining 0.3%, it is spare；
S2. 0.05 part of 0.5 part of chitosan and wood vinegar are added in step S1 products therefroms, is stirred evenly, aging 8 My god, except iron, it is spare to obtain blank；
S3. blank is pressed into adobe, then dried, enter the firing of kiln oxidizing flame, firing temperature is 1350 DEG C, and the firing time is 10h, natural cooling through edging, are packaged to be finished product.
Embodiment 7
The components by weight percent of 1~5 any embodiment of Example prepares high-strength abrasion-proof ceramic tile, and preparation process is as follows：
S1. raw material are taken by weight ratio, with ball：Water：Material=2： 0.8：1 ratio goal barreling is milled to fineness as 250 mesh sieves Tail over 0.5%, it is spare；
S2. 0.23 part of 0.3 part of chitosan and wood vinegar are added in step S1 products therefroms, is stirred evenly, aging 13 My god, except iron, it is spare to obtain blank；
S3. blank is pressed into adobe, then dried, enter the firing of kiln oxidizing flame, firing temperature is 1200 DEG C, and the firing time is 15h, natural cooling through edging, are packaged to be finished product.
Embodiment 8
The components by weight percent of 1~5 any embodiment of Example prepares high-strength abrasion-proof ceramic tile, and preparation process is as follows：
S1. raw material are taken by weight ratio, with ball：Water：Material=2：0.75：1 ratio goal barreling is milled to fineness as 280 mesh sieves Tail over 0.4%, it is spare；
S2. 0.15 part of 0.4 part of chitosan and wood vinegar are added in step S1 products therefroms, is stirred evenly, aging 10 My god, except iron, it is spare to obtain blank；
S3. blank is pressed into adobe, then dried, enter the firing of kiln oxidizing flame, firing temperature is 1280 DEG C, and the firing time is 12h, natural cooling through edging, are packaged to be finished product.

Claims (4)

1. a kind of high-strength abrasion-proof ceramic tile, which is characterized in that be grouped by each group of following weight percent：Calcite 5~12 Part, 10~16 parts of electro-corundum, 4~7 parts of galapectite, 2~5 parts of Topaz, 1~3 part of chromite powder, 3~6 parts of carbon fiber are wide 8~14 parts of city soil, 9~15 parts of vermiculite, high 11~18 parts of Cen soil, 6~10 parts of sandstone, 12~19 parts of sodium porcelain sand, sericite 10 ~17 parts, 7~14 parts of Suzhou soil, 5~9 parts of potassium feldspar.
2. high-strength abrasion-proof ceramic tile according to claim 1, which is characterized in that be grouped by each group of following parts by weight Into：9 parts of calcite, 14 parts of electro-corundum, 6 parts of galapectite, 4 parts of Topaz, 2 parts of chromite powder, 5 parts of carbon fiber, wide city soil 10 Part, 12 parts of vermiculite, high 15 parts of Cen soil, 8 parts of sandstone, 15 parts of sodium porcelain sand, 14 parts of sericite, 11 parts of Suzhou soil, 7 parts of potassium feldspar.
3. high-strength abrasion-proof ceramic tile according to claim 1 or 2, which is characterized in that the electro-corundum includes electric smelting plate Shape corundum, fused white corundum, fused brown corundum and electric smelting dense alumina.
4. according to the preparation method of the 1 or 2 or 3 high-strength abrasion-proof ceramic tile of claim, which is characterized in that including following step Suddenly：
S1. raw material are taken by weight ratio, with ball：Water：Material=2：0.7~0.8：1 ratio goal barreling is milled to fineness as 250 ~300 mesh sieves tail over 0.3~0.5%, spare；
S2. 0.05~0.23 part of 0.3~0.5 part of chitosan and wood vinegar, stirring are added in step S1 products therefroms Uniformly, aging 8~13 days, except iron, it is spare to obtain blank；
S3. blank is pressed into adobe, then dried, enter the firing of kiln oxidizing flame, firing temperature is 1200~1350 DEG C, is fired Time is 10~15h, and natural cooling through edging, is packaged to be finished product.
CN201711450862.4A 2017-12-27 2017-12-27 High-strength abrasion-proof ceramic tile and preparation method thereof Pending CN108069698A (en)