CN108005299A - A kind of assembled architecture interior wall wallboard and its processing method - Google Patents
A kind of assembled architecture interior wall wallboard and its processing method Download PDFInfo
- Publication number
- CN108005299A CN108005299A CN201711315438.9A CN201711315438A CN108005299A CN 108005299 A CN108005299 A CN 108005299A CN 201711315438 A CN201711315438 A CN 201711315438A CN 108005299 A CN108005299 A CN 108005299A
- Authority
- CN
- China
- Prior art keywords
- interior wall
- processing method
- assembled architecture
- weight
- wallboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to interior wall wallboard technical field for building, and in particular to a kind of assembled architecture interior wall wallboard and its processing method, the processing method include:(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric;(2) thermal insulation board is laid with the superstructure of step (1), then proceedes to be laid with layer of glass cloth and pour second layer mortar mixture on it, smooth out and stand, treat its setting and hardening;(3) perforative through hole is drilled with step (2) molding structure using drilling machine, binding sand slurry is poured into through hole, 12d is conserved after standing solidification, up to the inner wall of building wallboard;Assembled architecture provided by the invention interior wall wallboard, using thermal insulation board as agent structure, glass fabric and screed are set in its both sides, then are linked using perforative adhesive mortar column as communication, while its heat insulation effect is taken into account, improve its structural strength.
Description
Technical field
The present invention relates to interior wall wallboard technical field for building, and in particular to a kind of assembled architecture with interior wall wallboard and its
Processing method.
Background technology
In the prior art, our common several building types have:Brick mix structure, cast-in-place concrete shear wall structure are existing
Pouring concrete frame structure, steel construction;Wherein, brick mix structure is most widely used, and history is also more remote, but be in order at guarantor
The needs in retaining ring border, national law-making stipulation is phased out and forbids using clay brick, thus brick mix structure will be eliminated, other
Several construction methods are also because technics comparing is complicated, therefore rate of progress of the construction is slow, and long in time limit, building industrialization level is low.Especially
In the case of frame structure such as concrete frame or steel construction, the very big duration is wasted in the construction of wall for it.
In recent years, many building research mechanisms or construction unit are one after another using the novel wall building for being capable of industrialized construction
The use of material, such as various light thermal insulation boards, accelerates the speed of construction to a certain extent, and heat-insulating and cold effect is good, but this
A little improved wall body building material structural strength deficiencies, limit the application of assembled architecture interior wall wallboard.
The content of the invention
For the problems of the prior art, it is an object of the invention to provide in a kind of assembled architecture use easy to process
The processing method of wall wallboard, the interior wall wallboard processed can be used for the quick splicing installation of inner wall of building wall, improve building and apply
Work efficiency rate.
To achieve these goals, the present invention is achieved by the following scheme:A kind of assembled architecture interior wall wall
The processing method of plate, comprises the following steps:
(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes
It is immersed in first layer mortar mixture;
(2) thermal insulation board is laid with the superstructure of step (1), then proceedes to be laid with layer of glass cloth and pour on it
Second layer mortar mixture is built, smoothes out and stands, treat its setting and hardening;
(3) perforative through hole is drilled with step (2) molding structure using drilling machine, adhesive mortar is poured into through hole
Material, 12d is conserved after standing solidification, up to the inner wall of building wallboard.
In the present invention, by setting screed, and perforative adhesive mortar master in the both sides of conventional vacuum plate, improve
The overall construction intensity of interior wall wallboard.
According to the present invention, the present invention does not do particular/special requirement to the concrete composition of first, second layer of mortar mixture,
It is the mixture that cement, quartz sand and water reconcile in proportion.It can be the common harmonic ratio of one of ordinary skill in the art
Example, specifically, for example, cement, quartz sand and water are pressed 1:3:0.6 ratio is reconciled, and the cement can select 425
Number, No. 525, one kind in No. 625 portland cements, the quartz sand selects 40~70 mesh.
Further, according to the present invention, the spacing of adhesive mortar column directly affects the bonding strength of each layer, therefore, lead to
The spacing in hole is smaller, pours that the intensity of overall interior wall wallboard after adhesive mortar is higher, and still, through hole spacing is too small, causes to drill
Quantity is excessive so that the production cycle is long;In addition, the aperture of through hole can also directly affect the thickness of adhesive mortar column, so that shadow
Ring the integral strength to interior wall wallboard.In the present invention, the spacing of the through hole is 0.5~1m, and the aperture of through hole is 2~5cm.
According to the present invention, pour play each layer of interior wall wallboard after adhesive mortar setting and hardening in through-holes link work
With, the present invention in, the binding sand slurry by cement, quartz sand, hypromellose, glass fibre yarn cutting mixing and
Into specifically, being counted by 100 parts by weight of the weight of quartz sand, the binding sand slurry includes the material of following parts by weight:Water
20~34 parts by weight of mud, 100 parts by weight of quartz sand, 5~15 parts by weight of hypromellose, 12~20 weight of glass fibre yarn cutting
Measure part.
Glass fibre yarn cutting has the advantages that high, non-ignitable, the anti-corruption of heatproof, sound insulation, heat-insulated, tensile strength is high, and powdered
Hypromellose mixing after be filled in binding sand slurry, improve adhesive mortar column bonding strength;Meanwhile hydroxypropyl first
Base cellulose is also used as the water-retaining agent of cement mortar, avoids adhesive mortar column dehydration is too fast from causing cracking, enhancing solidification is hard
Intensity after change.
Further, according to the present invention, the length of the glass fibre yarn cutting is 20~100mm.
According to the present invention, glass fabric is formed by glass fiber yarn weaving, by the setting of glass fabric,
Improve the interlaminar shear strength and antibody Monoclonal tolerance limit of interior wall wallboard.Heretofore described glass fabric is plain, yarn
Number warp-wise broadwise 50~100Tex, 50~100g/m2。
According to the present invention, the agent structure of interior wall wallboard provided in the present invention is thermal insulation board, and the thermal insulation board can be with
Select in the market common, such as XPS thermal insulation boards, EPS thermal insulation boards, or one kind in polyurethane thermal insulation board.
Specifically, the XPS thermal insulation boards are to add other supplementary materials and polymer by raw material of polystyrene resin,
By heating mixing injecting catalyst at the same time, then extrusion molding extrusion molding and the rigid foam plate that manufactures, it has perfection
Closed honeycomb structure, extremely low water imbibition is made it have, the advantages of low thermal conductivity coefficient, high pressure resistance;
After the heated prefoam of EPS thermal insulation board expandable polystyrenes in a mold hot briquetting prepared by have
There is the polystyrene foam plastics of hole-closing structure, compared to traditional molded polystyrene foams plate, it, which has not only continued low-heat, leads and be
The advantages of number, high pressure resistance, it also compensate for the advantages of flame retardant effect is poor;
The polyurethane thermal insulation board is that thermal conductivity factor is minimum in existing thermal insulation material, just corresponds to EPS thermal insulation boards
Half, but its unit price it is comparatively also higher.The present invention does not do special requirement to the material of thermal insulation board, according to tool
The demand of the inner wall of building wall of body makes choice use.
According to the present invention, complete in through hole after the pouring of binding sand slurry, to treat its setting and hardening, be conserved, it is described
Maintenance be to ensure concrete strength, prevent the important step in crack, maintenance of the present invention need to carry out 12d, wherein, preceding 3
My god, wallboard need to be carried out when 4 is small watering wetting once, in 5 days, when 6 is small watering wetting once, latter 4 days, every 12
Hour watering wetting once, using this maintenance method, can not only reach the effect of maintenance, prevent crack, while can be most
The using water wisely of limits.
The present invention also provides a kind of assembled architecture interior wall wallboard, process to obtain by above-mentioned processing method.
Assembled architecture of the present invention interior wall wallboard, including it is arranged on the glass fabric and sand of thermal insulation board both sides
Pulp layer, and the adhesive mortar column through above layers;Wherein, the thickness of the screed is 3~10cm.
Compared with prior art, the present invention has following technique effect:
1st, assembled architecture provided by the invention interior wall wallboard, using thermal insulation board as agent structure, sets in its both sides
Glass fabric and screed are put, then is linked using perforative adhesive mortar column as communication, while its heat insulation effect is taken into account,
Improve its structural strength;
2nd, assembled architecture provided by the invention interior wall wallboard, industrialized production is realized in factory, is then transported to applying
Work scene carries out assembling construction, has evaded existing architectural mode and dirt is easily produced in the work progress of inner wall of building body
The drawbacks of dye, noise;
3rd, assembled architecture provided by the invention interior wall wallboard, it is reusable, reduce waste.
Embodiment
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention easy to understand, tie below
Specific embodiment is closed, the present invention is furture elucidated.
Embodiment 1
A kind of processing method of assembled architecture interior wall wallboard:
(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes
It is immersed in first layer mortar mixture;
(2) XPS thermal insulation boards (thickness 100mm) are laid with the superstructure of step (1), then proceed to be laid with one layer of glass fibers
Wei Bu simultaneously pours second layer mortar mixture on it, smoothes out and stands, treats its setting and hardening;
(3) using drilling machine perforative through hole (through hole specification is drilled with step (2) molding structure:Spacing 0.8m, hole
Footpath 3cm), binding sand slurry is poured into through hole, 12d is conserved after standing solidification, up to the inner wall of building wallboard;
The first, second floor mortar mixture presses 1 by portland cement 425, quartz sand (60 mesh) and water:3:
0.6 ratio reconciles and forms;
The thickness that pours of first, second mortar mixture is 8cm;
The glass fabric is plain, yarn number warp-wise broadwise 80Tex, 60g/m2。
The binding sand slurry includes the material of following parts by weight:
Cement (No. 425) 28 parts by weight
Quartz sand (60 mesh) 100 parts by weight
10 parts by weight of hypromellose
16 parts by weight of glass fibre yarn cutting (length 60mm).
Embodiment 2
A kind of processing method of assembled architecture interior wall wallboard:
(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes
It is immersed in first layer mortar mixture;
(2) XPS thermal insulation boards (thickness 100mm) are laid with the superstructure of step (1), then proceed to be laid with one layer of glass fibers
Wei Bu simultaneously pours second layer mortar mixture on it, smoothes out and stands, treats its setting and hardening;
(3) using drilling machine perforative through hole (through hole specification is drilled with step (2) molding structure:Spacing 0.6m, hole
Footpath 4cm), binding sand slurry is poured into through hole, 12d is conserved after standing solidification, up to the inner wall of building wallboard;
The first, second floor mortar mixture presses 1 by portland cement 425, quartz sand (50 mesh) and water:3:
0.6 ratio reconciles and forms;
The thickness that pours of first, second mortar mixture is 6cm;
The glass fabric is plain, yarn number warp-wise broadwise 60Tex, 80g/m2。
The binding sand slurry includes the material of following parts by weight:
Cement (No. 425) 25 parts by weight
Quartz sand (60 mesh) 100 parts by weight
8 parts by weight of hypromellose
14 parts by weight of glass fibre yarn cutting (length 40mm).
Embodiment 3
A kind of processing method of assembled architecture interior wall wallboard:
(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes
It is immersed in first layer mortar mixture;
(2) XPS thermal insulation boards (thickness 100mm) are laid with the superstructure of step (1), then proceed to be laid with one layer of glass fibers
Wei Bu simultaneously pours second layer mortar mixture on it, smoothes out and stands, treats its setting and hardening;
(3) using drilling machine perforative through hole (through hole specification is drilled with step (2) molding structure:Spacing 0.8m, hole
Footpath 4cm), binding sand slurry is poured into through hole, 12d is conserved after standing solidification, up to the inner wall of building wallboard;
The first, second floor mortar mixture presses 1 by portland cement 425, quartz sand (60 mesh) and water:3:
0.6 ratio reconciles and forms;
The thickness that pours of first, second mortar mixture is 8cm;
The glass fabric is plain, yarn number warp-wise broadwise 90Tex, 90g/m2。
The binding sand slurry includes the material of following parts by weight:
Cement (No. 425) 30 parts by weight
Quartz sand (60 mesh) 100 parts by weight
13 parts by weight of hypromellose
18 parts by weight of glass fibre yarn cutting (length 80mm)
Embodiment 4
A kind of processing method of assembled architecture interior wall wallboard:
(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes
It is immersed in first layer mortar mixture;
(2) XPS thermal insulation boards (thickness 100mm) are laid with the superstructure of step (1), then proceed to be laid with one layer of glass fibers
Wei Bu simultaneously pours second layer mortar mixture on it, smoothes out and stands, treats its setting and hardening;
(3) using drilling machine perforative through hole (through hole specification is drilled with step (2) molding structure:Spacing 0.5m, hole
Footpath 2cm), binding sand slurry is poured into through hole, 12d is conserved after standing solidification, up to the inner wall of building wallboard;
The first, second floor mortar mixture presses 1 by portland cement 425, quartz sand (40 mesh) and water:3:
0.6 ratio reconciles and forms;
The thickness that pours of first, second mortar mixture is 3cm;
The glass fabric is plain, yarn number warp-wise broadwise 50Tex, 100g/m2。
The binding sand slurry includes the material of following parts by weight:
Cement (No. 425) 20 parts by weight
Quartz sand (60 mesh) 100 parts by weight
5 parts by weight of hypromellose
12 parts by weight of glass fibre yarn cutting (length 20mm)
Embodiment 5
A kind of processing method of assembled architecture interior wall wallboard:
(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes
It is immersed in first layer mortar mixture;
(2) XPS thermal insulation boards (thickness 100mm) are laid with the superstructure of step (1), then proceed to be laid with one layer of glass fibers
Wei Bu simultaneously pours second layer mortar mixture on it, smoothes out and stands, treats its setting and hardening;
(3) using drilling machine perforative through hole (through hole specification is drilled with step (2) molding structure:Spacing 1m, aperture
5cm), binding sand slurry is poured into through hole, 12d is conserved after standing solidification, up to the inner wall of building wallboard;
The first, second floor mortar mixture presses 1 by portland cement 425, quartz sand (70 mesh) and water:3:
0.6 ratio reconciles and forms;
The thickness that pours of first, second mortar mixture is 10cm;
The glass fabric is plain, yarn number warp-wise broadwise 100Tex, 100g/m2。
The binding sand slurry includes the material of following parts by weight:
Cement (No. 425) 34 parts by weight
Quartz sand (60 mesh) 100 parts by weight
15 parts by weight of hypromellose
20 parts by weight of glass fibre yarn cutting (length 100mm)
Embodiment 6
A kind of processing method of assembled architecture interior wall wallboard:
(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes
It is immersed in first layer mortar mixture;
(2) EPS thermal insulation boards (thickness 100mm) are laid with the superstructure of step (1), then proceed to be laid with one layer of glass fibers
Wei Bu simultaneously pours second layer mortar mixture on it, smoothes out and stands, treats its setting and hardening;
(3) using drilling machine perforative through hole (through hole specification is drilled with step (2) molding structure:Spacing 0.8m, hole
Footpath 3cm), binding sand slurry is poured into through hole, 12d is conserved after standing solidification, up to the inner wall of building wallboard;
The first, second floor mortar mixture presses 1 by portland cement 425, quartz sand (60 mesh) and water:3:
0.6 ratio reconciles and forms;
The thickness that pours of first, second mortar mixture is 8cm;
The glass fabric is plain, yarn number warp-wise broadwise 80Tex, 60g/m2。
The binding sand slurry includes the material of following parts by weight:
Cement (No. 425) 28 parts by weight
Quartz sand (60 mesh) 100 parts by weight
10 parts by weight of hypromellose
16 parts by weight of glass fibre yarn cutting (length 60mm).
Embodiment 7
A kind of processing method of assembled architecture interior wall wallboard:
(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes
It is immersed in first layer mortar mixture;
(2) polyurethane thermal insulation board (thickness 100mm) is laid with the superstructure of step (1), then proceedes to be laid with one layer of glass
Glass fiber cloth simultaneously pours second layer mortar mixture on it, smoothes out and stands, treats its setting and hardening;
(3) using drilling machine perforative through hole (through hole specification is drilled with step (2) molding structure:Spacing 0.8m, hole
Footpath 3cm), binding sand slurry is poured into through hole, 12d is conserved after standing solidification, up to the inner wall of building wallboard;
The first, second floor mortar mixture presses 1 by portland cement 425, quartz sand (60 mesh) and water:3:
0.6 ratio reconciles and forms;
The thickness that pours of first, second mortar mixture is 8cm;
The glass fabric is plain, yarn number warp-wise broadwise 80Tex, 60g/m2。
The binding sand slurry includes the material of following parts by weight:
Cement (No. 425) 28 parts by weight
Quartz sand (60 mesh) 100 parts by weight
10 parts by weight of hypromellose
16 parts by weight of glass fibre yarn cutting (length 60mm).
Comparative example 1
The present embodiment is identical with the processing method of the inner wall of building wallboard of embodiment 1, unlike, in molding structure
Without drilling and pouring adhesive mortar, specific processing method is:
A kind of processing method of assembled architecture interior wall wallboard:
(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes
It is immersed in first layer mortar mixture;
(2) XPS thermal insulation boards (thickness 100mm) are laid with the superstructure of step (1), then proceed to be laid with one layer of glass fibers
Wei Bu simultaneously pours second layer mortar mixture on it, smoothes out and stands, treats its setting and hardening;12d is conserved in the same way, i.e.,
Obtain the inner wall of building wallboard.
Comparative example 2
The present embodiment is identical with the processing method of the inner wall of building wallboard of embodiment 1, unlike, in the binding sand
Glass fibre yarn cutting is not contained in slurry, remaining is constant, and processing obtains the inner wall of building wallboard.
The inner wall of building wallboard performance obtained in above-described embodiment is detected, it is as shown in table 1 below:
Table 1:
Thermal conductivity factor/W/ (mk) | Compression strength/Mpa | Water absorption rate/% | |
Embodiment 1 | 0.168 | 7.8 | 0.3 |
Embodiment 2 | 0.154 | 7.6 | 0.4 |
Embodiment 3 | 0.162 | 7.5 | 0.5 |
Embodiment 4 | 0.148 | 7.6 | 0.4 |
Embodiment 5 | 0.169 | 7.7 | 0.5 |
Embodiment 6 | 0.167 | 7.8 | 0.4 |
Embodiment 7 | 0.084 | 8.3 | 0.3 |
Comparative example 1 | 0.169 | 3.6 | 0.3 |
Comparative example 2 | 0.169 | 5.8 | 0.4 |
Basic principle, main feature and the features of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement is both fallen within the range of claimed invention.The scope of protection of present invention is by appended claims
And its equivalent thereof.
Claims (8)
- A kind of 1. assembled architecture processing method of interior wall wallboard, it is characterised in that:Comprise the following steps:(1) first layer mortar mixture is poured into mould, smoothes out and is laid with glass fabric, rolled glass fiber cloth makes its leaching Enter in first layer mortar mixture;(2) thermal insulation board is laid with the superstructure of step (1), then proceedes to be laid with layer of glass cloth and pour the on it Two layers of mortar mixture, smooth out and stand, treat its setting and hardening;(3) perforative through hole is drilled with step (2) molding structure using drilling machine, binding sand slurry is poured into through hole, 12d is conserved after standing solidification, up to the inner wall of building wallboard.
- 2. the assembled architecture according to claim 1 processing method of interior wall wallboard, it is characterised in that:The through hole Spacing is 0.5~1m;And/or the aperture of the through hole is 2~5cm.
- 3. the assembled architecture according to claim 1 processing method of interior wall wallboard, it is characterised in that:The bonding Mortar is mixed by cement, quartz sand, hypromellose, glass fibre yarn cutting;Counted by 100 parts by weight of the weight of quartz sand, the binding sand slurry includes the material of following parts by weight:Cement 20~ 34 parts by weight, 100 parts by weight of quartz sand, 5~15 parts by weight of hypromellose, 12~20 parts by weight of glass fibre yarn cutting.
- 4. the assembled architecture according to claim 3 processing method of interior wall wallboard, it is characterised in that:The glass The length of fiber yarn cutting is 20~100mm.
- 5. the assembled architecture according to claim 1 processing method of interior wall wallboard, it is characterised in that:The glass Fiber cloth is plain, yarn number warp-wise broadwise 50~100Tex, 50~100g/m2。
- 6. the assembled architecture according to claim 1 processing method of interior wall wallboard, it is characterised in that:The insulation Plate is XPS thermal insulation boards, one kind in EPS thermal insulation boards, polyurethane thermal insulation board.
- A kind of 7. assembled architecture interior wall wallboard, it is characterised in that:The interior wall wallboard is any one by claim 1~6 The item processing method processes to obtain.
- 8. assembled architecture according to claim 7 interior wall wallboard, it is characterised in that:Including being arranged on thermal insulation board both sides Glass fabric and screed, and the adhesive mortar column through above layers, wherein, the thickness of the screed for 3~ 10cm。