CN107960793A - A kind of mattress is with sponge and preparation method thereof - Google Patents
A kind of mattress is with sponge and preparation method thereof Download PDFInfo
- Publication number
- CN107960793A CN107960793A CN201711066857.3A CN201711066857A CN107960793A CN 107960793 A CN107960793 A CN 107960793A CN 201711066857 A CN201711066857 A CN 201711066857A CN 107960793 A CN107960793 A CN 107960793A
- Authority
- CN
- China
- Prior art keywords
- parts
- sponge
- chinese medicine
- medicine composition
- mattress
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of mattress with sponge, including spongiosum, placing groove is equipped with the spongiosum, the spring mechanism of multiple rectangular arrangements is equipped with the placing groove, the spring mechanism includes the first plastics spring, the second plastics spring and the 3rd plastics spring set gradually from top to bottom, and the elastic force of first plastics spring, the second plastics spring and the 3rd plastics spring is sequentially increased, the spongiosum includes the raw material of following parts by weight：100 120 parts of polyether polyol combination material, 50 70 parts of polyester, 30 50 parts of toluene di-isocyanate(TDI), 9 18 parts of tourmaline powder, 20 40 parts of bamboo and woods fiber powder, 39 parts of graphene, 5 10 parts of carbon black, 1 10 parts of silicones, 20 40 parts of Chinese medicine composition；The invention also provides a kind of mattress preparation method of sponge.Cost of the present invention is low, and supportive coexists with pliability, and metal product is reduced compared with pure sping mattress, strengthens comfort, and manufacture craft is simple, good health care effect, is adapted to promote.
Description
Technical field
The present invention relates to mattress sponge technical field, more particularly to a kind of mattress is with sponge and preparation method thereof.
Background technology
Sponge is named according to algae in ocean, its main feature is that soft and high resilience.We live now
Used in sponge be mostly foamed by chemical products such as rubber, polyester, polyethers and formed.Sponge is widely used, root
According to characteristics such as its insulation, sound insulation, protecting against shocks, largely should in seat, mattress, sofa, medical health care products, decorative product
With.Whole world sponge yield is very big, is a very important industrial field.But the sponge of the prior art mainly plays insulation
Acted on protecting against shock, the demand with people and the raising using standard, it is also proposed sponge the requirement of higher, for example require
More functions and using when the health that is beneficial to.
In addition, existing bed cushion class product is typically pure sping mattress or polyurethane cotton mattress, two kinds of mattresses respectively have quality
Gesture, spring mattress supports are fabulous, but because metal spring there are noise, easy bursting surface, it is long after mattress it is unequal
Problem, the above problem is not present in pure polyurethane mattress, but supportive cannot meet proprietary demand again.
The content of the invention
Based on technical problem existing for background technology, the present invention proposes a kind of mattress with sponge and preparation method thereof.
A kind of mattress proposed by the present invention is equipped with placing groove with sponge, including spongiosum in the spongiosum, described
The spring mechanism of multiple rectangular arrangements is equipped with placing groove, the spring mechanism includes the first modeling set gradually from top to bottom
Expect spring, the second plastics spring and the 3rd plastics spring, and the first plastics spring, the second plastics spring and the 3rd plastics spring
Elastic force is sequentially increased, and the spongiosum includes the raw material of following parts by weight：Polyether polyol combination material 100-120 parts, polyester
50-70 parts, 30-50 parts of toluene di-isocyanate(TDI), 9-18 parts of tourmaline powder, 20-40 parts of bamboo and woods fiber powder, 3-9 parts of graphene, charcoal
5-10 parts black, 1-10 parts of silicones, 20-40 parts of Chinese medicine composition.
Preferably, the polyether polyol combination material includes, polyether polyol 1：Molecular weight 3000, degree of functionality 3；Polymer
Polyalcohol 1：Molecular weight 5000, degree of functionality 3；Catalyst 1：Triethylenediamine；Catalyst 2：Dibutyl tin laurate；Water.
Preferably, the raw material of the Chinese medicine composition include the banksia rose, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean,
Flos Albiziae.
Preferably, the production method of the Chinese medicine composition is：Weigh the banksia rose of equivalent, fennel, windproof, Angelica sinensis, public fourth
Perfume, tealeaves, black soya bean, Flos Albiziae, mallet mix into chip, then mixture are dried 2-4h under conditions of 60-80 DEG C, you can obtain
Chinese medicine composition.
Preferably, the raw material of following parts by weight is included：105-115 parts of polyether polyol combination material, 55-65 parts of polyester, first
35-45 parts of phenylene diisocyanate, 12-15 parts of tourmaline powder, 25-35 parts of bamboo and woods fiber powder, 5-7 parts of graphene, 7-8 parts of carbon black,
3-8 parts of silicones, 25-35 parts of Chinese medicine composition.
Preferably, the raw material of following parts by weight is included：110 parts of polyether polyol combination material, 60 parts of polyester, toluene diisocyanate
40 parts of acid esters, 13.5 parts of tourmaline powder, 30 parts of bamboo and woods fiber powder, 6 parts of graphene, 7.5 parts of carbon black, 5.5 parts of silicones, Chinese medicine group
30 parts of compound.
Preferably, the polyether polyol combination material, polyester, the weight ratio of toluene di-isocyanate(TDI) are 105-115：55-
65：35-45.
The invention also provides a kind of mattress preparation method of sponge, comprise the following steps：
S1, weigh polyether polyol combination material 100-120 parts, 50-70 parts of polyester, 9-18 parts of tourmaline powder, bamboo and woods fiber powder
20-40 parts, 3-9 parts of graphene, 5-10 parts of carbon black, 1-10 parts of silicones, above-mentioned raw materials are stirred at a temperature of 50-70 DEG C mixed
1-2h is closed, obtains mixture；
S2, weighs 20-40 parts of Chinese medicine composition, Chinese medicine composition is put into pot, adds the 5-9 times of water measured, and decocts 2-4h, mistake
Filter, obtains filter residue and filtrate；
S3, grinds after filter residue drying in S2 are put into the mixture into S1,2-3h are sufficiently stirred, then by after stirring
Mixture pours into foam box, accurately weighs 30-50 parts of toluene di-isocyanate(TDI) and is mixed into S3 high-speed stirreds 10S（≥3000rpm）,
Wait mixture to be foamed into cavernous body, stand 40-100min so that sponge body-shaping；
S4, is uniformly sprayed at the cavernous body surface after shaping in S3 by the filtrate in S2, is baked to using baking oven, finally carried out
I.e. can obtain mattress uses sponge for assembling.
Preferably, in the S3, the sponge body-shaping curing time is 50-70min.
The present invention not only has the characteristics that traditional sponge, but also has incorporated the characteristic of tourmaline, can discharge anion, and purification is empty
Gas, additionally it is possible to radiation infrared, acting on human body can promote blood circulation, and active cell metabolism, improves immunity, in
The component contained in drug composition can support member and consolidate, warming kidney for dispelling cold, strengthening the spleen and stomach, human body often with the sea containing traditional Chinese medicine ingredients
Silk floss contact, has good health-care effect, uses the plastics spring of three kinds of different hardness so that and comfort is greatly enhanced,
Cost of the present invention is low, and supportive coexists with pliability, and metal product is reduced compared with pure sping mattress, strengthens comfort, makes
Technique is simple, good health care effect, is adapted to promote.
Brief description of the drawings
Fig. 1 is the structure diagram of spongiosum in the present invention；
Fig. 2 is the structure diagram of spring mechanism in the present invention.
In figure：1 spongiosum, 2 spring mechanisms, 21 first plastics springs, 22 second plastics springs, 23 the 3rd plastics bullets
Spring, 3 placing grooves.
Embodiment
The present invention is made with reference to specific embodiment further to explain.
Embodiment one
With reference to Fig. 1-2, a kind of mattress proposed by the present invention is put with sponge, including spongiosum 1, interior be equipped with of the spongiosum 1
Put groove 3, be equipped with the spring mechanism 2 of multiple rectangular arrangements in the placing groove 3, the spring mechanism 2 include from top to bottom according to
The first plastics spring 21, the second plastics spring 22 and the 3rd plastics spring 23 of secondary setting, and the first plastics spring 21, second is moulded
The elastic force of material 22 and the 3rd plastics spring 23 of spring is sequentially increased, and the spongiosum 1 includes the raw material of following parts by weight：Polyethers
100 parts of polyhydric alcohol conjugate material, 50 parts of polyester, 30 parts of toluene di-isocyanate(TDI), 9 parts of tourmaline powder, 20 parts of bamboo and woods fiber powder, graphite
3 parts of alkene, 5 parts of carbon black, 1 part of silicones, 20 parts of Chinese medicine composition.
The polyether polyol combines material：30 parts of 60 parts of PPG3000, POP2045,0.2 part of 1 part of A-33, T-12,
8.8 parts of water.
The raw material of the Chinese medicine composition includes the banksia rose, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae.
Its production method is：The banksia rose of equivalent, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae are weighed, mallet is mixed into chip
With, then mixture dried into 2h under conditions of 60 DEG C, you can obtain Chinese medicine composition.
The invention also provides a kind of mattress preparation method of sponge, comprise the following steps：
S1, weighs 100 parts of polyether polyol combination material, 50 parts of polyester, 9 parts of tourmaline powder, 20 parts of bamboo and woods fiber powder, graphene 3
Above-mentioned raw materials are stirred 1h at a temperature of 50 DEG C, obtain mixture by part, 5 parts of carbon black, 1 part of silicones；
S2, weighs 20 parts of Chinese medicine composition, Chinese medicine composition is put into pot, adds the 5-9 times of water measured, and decocts 2-4h, filters,
Obtain filter residue and filtrate；
S3, grinds after filter residue drying in S2 are put into the mixture into S1, are sufficiently stirred 2h, then will be mixed after stirring
Compound pours into foam box, accurately weighs 30 parts of toluene di-isocyanate(TDI) and is mixed into S3 high-speed stirreds 10S（≥3000rpm）, wait
Mixture is foamed into cavernous body, stands 40min so that sponge body-shaping；
S4, is uniformly sprayed at the cavernous body surface after shaping in S3 by the filtrate in S2, is baked to using baking oven, finally carried out
I.e. can obtain mattress uses sponge for assembling.
Embodiment two
With reference to Fig. 1-2, a kind of mattress proposed by the present invention is put with sponge, including spongiosum 1, interior be equipped with of the spongiosum 1
Put groove 3, be equipped with the spring mechanism 2 of multiple rectangular arrangements in the placing groove 3, the spring mechanism 2 include from top to bottom according to
The first plastics spring 21, the second plastics spring 22 and the 3rd plastics spring 23 of secondary setting, and the first plastics spring 21, second is moulded
The elastic force of material 22 and the 3rd plastics spring 23 of spring is sequentially increased, and the spongiosum 1 includes the raw material of following parts by weight：Polyethers
105 parts of polyhydric alcohol conjugate material, 55 parts of polyester, 35 parts of toluene di-isocyanate(TDI), 12 parts of tourmaline powder, 25 parts of bamboo and woods fiber powder, stone
Black 5 parts of alkene, 7 parts of carbon black, 3 parts of silicones, 25 parts of Chinese medicine composition.
The polyether polyol combines material：20 parts of 70 parts of PPG3000, POP2045,0.8 part of A-33, T-12 0.2
Part, 9 parts of water.
The raw material of the Chinese medicine composition includes the banksia rose, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae.
Its production method is：The banksia rose of equivalent, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae are weighed, mallet is mixed into chip
With, then mixture dried into 2.5h under conditions of 65 DEG C, you can obtain Chinese medicine composition.
The invention also provides a kind of mattress preparation method of sponge, comprise the following steps：
S1, weighs 105 parts of polyether polyol combination material, 55 parts of polyester, 12 parts of tourmaline powder, 25 parts of bamboo and woods fiber powder, graphene 5
Above-mentioned raw materials are stirred 1.2h at a temperature of 55 DEG C, obtain mixture by part, 6 parts of carbon black, 3 parts of silicones；
S2, weighs 25 parts of Chinese medicine composition, Chinese medicine composition is put into pot, adds the water of 6 times of amounts, decocts 2.5h, filtering, obtains
To filter residue and filtrate；
S3, grinds after filter residue drying in S2 are put into the mixture into S1,2.2h are sufficiently stirred, then by after stirring
Mixture pours into foam box, accurately weighs 35 parts of toluene di-isocyanate(TDI) and is mixed into S3 high-speed stirreds 10S（≥3000rpm）, etc.
Material to be mixed is foamed into cavernous body, stands 50min so that sponge body-shaping；
S4, is uniformly sprayed at the cavernous body surface after shaping in S3 by the filtrate in S2, is baked to using baking oven, finally carried out
I.e. can obtain mattress uses sponge for assembling.
Embodiment three
With reference to Fig. 1-2, a kind of mattress proposed by the present invention is put with sponge, including spongiosum 1, interior be equipped with of the spongiosum 1
Put groove 3, be equipped with the spring mechanism 2 of multiple rectangular arrangements in the placing groove 3, the spring mechanism 2 include from top to bottom according to
The first plastics spring 21, the second plastics spring 22 and the 3rd plastics spring 23 of secondary setting, and the first plastics spring 21, second is moulded
The elastic force of material 22 and the 3rd plastics spring 23 of spring is sequentially increased, and the spongiosum 1 includes the raw material of following parts by weight：Polyethers
110 parts of polyhydric alcohol conjugate material, 60 parts of polyester, 40 parts of toluene di-isocyanate(TDI), 13.5 parts of tourmaline powder, 30 parts of bamboo and woods fiber powder,
6 parts of graphene, 7.5 parts of carbon black, 5.5 parts of silicones, 30 parts of Chinese medicine composition.
The polyether polyol combines material：20 parts of 70 parts of PPG3000, POP2045,0.8 part of A-33, T-12 0.2
Part, 9 parts of water.
The raw material of the Chinese medicine composition includes the banksia rose, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae.
Its production method is：The banksia rose of equivalent, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae are weighed, mallet is mixed into chip
With, then mixture dried into 2.5h under conditions of 65 DEG C, you can obtain Chinese medicine composition.
The invention also provides a kind of mattress preparation method of sponge, comprise the following steps：
S1, weigh polyether polyol combination material 110 parts, 60 parts of polyester, 13.5 parts of tourmaline powder, 30 parts of bamboo and woods fiber powder, graphite
Above-mentioned raw materials are stirred 1.5h at a temperature of 60 DEG C, obtain mixture by 6 parts of alkene, 7.5 parts of carbon black, 5.5 parts of silicones；
S2, weighs 30 parts of Chinese medicine composition, Chinese medicine composition is put into pot, adds the water of 7 times of amounts, decocts 3h, filtering, obtains
Filter residue and filtrate；
S3, grinds after filter residue drying in S2 are put into the mixture into S1,2.5h are sufficiently stirred, then by after stirring
Mixture pours into foam box, accurately weighs 40 parts of toluene di-isocyanate(TDI) and is mixed into S3 high-speed stirreds 10S（≥3000rpm）, etc.
Material to be mixed is foamed into cavernous body, stands 70min so that sponge body-shaping；
S4, is uniformly sprayed at the cavernous body surface after shaping in S3 by the filtrate in S2, is baked to using baking oven, finally carried out
I.e. can obtain mattress uses sponge for assembling.
Example IV
With reference to Fig. 1-2, a kind of mattress proposed by the present invention is put with sponge, including spongiosum 1, interior be equipped with of the spongiosum 1
Put groove 3, be equipped with the spring mechanism 2 of multiple rectangular arrangements in the placing groove 3, the spring mechanism 2 include from top to bottom according to
The first plastics spring 21, the second plastics spring 22 and the 3rd plastics spring 23 of secondary setting, and the first plastics spring 21, second is moulded
The elastic force of material 22 and the 3rd plastics spring 23 of spring is sequentially increased, and the spongiosum 1 includes the raw material of following parts by weight：Polyethers
115 parts of polyhydric alcohol conjugate material, 65 parts of polyester, 45 parts of toluene di-isocyanate(TDI), 15 parts of tourmaline powder, 35 parts of bamboo and woods fiber powder, stone
Black 7 parts of alkene, 8 parts of carbon black, 8 parts of silicones, 35 parts of Chinese medicine composition.
The polyether polyol combines material：20 parts of 70 parts of PPG3000, POP2045,0.8 part of A-33, T-12 0.2
Part, 9 parts of water.
The raw material of the Chinese medicine composition includes the banksia rose, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae.
Its production method is：The banksia rose of equivalent, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae are weighed, mallet is mixed into chip
With, then mixture dried into 3.5h under conditions of 75 DEG C, you can obtain Chinese medicine composition.
The invention also provides a kind of mattress preparation method of sponge, comprise the following steps：
S1, weigh polyether polyol combination material 115 parts, 65 parts of polyester, 15 parts of tourmaline powder, 35 parts of bamboo and woods fiber powder, graphene
7 parts, 8 parts of carbon black, 8 parts of silicones, above-mentioned raw materials are stirred 1.8h at a temperature of 65 DEG C, obtain mixture；
S2, weighs 35 parts of Chinese medicine composition, Chinese medicine composition is put into pot, adds the water of 8 times of amounts, decocts 3.5h, filtering, obtains
To filter residue and filtrate；
S3, grinds after filter residue drying in S2 are put into the mixture into S1,2.8h are sufficiently stirred, then by after stirring
Mixture pours into foam box, accurately weighs 45 parts of toluene di-isocyanate(TDI) and is mixed into S3 high-speed stirreds 10S（≥3000rpm）, etc.
Material to be mixed is foamed into cavernous body, stands 80min so that sponge body-shaping；
S4, is uniformly sprayed at the cavernous body surface after shaping in S3 by the filtrate in S2, is baked to using baking oven, finally carried out
I.e. can obtain mattress uses sponge for assembling.
Embodiment five
With reference to Fig. 1-2, a kind of mattress proposed by the present invention is put with sponge, including spongiosum 1, interior be equipped with of the spongiosum 1
Put groove 3, be equipped with the spring mechanism 2 of multiple rectangular arrangements in the placing groove 3, the spring mechanism 2 include from top to bottom according to
The first plastics spring 21, the second plastics spring 22 and the 3rd plastics spring 23 of secondary setting, and the first plastics spring 21, second is moulded
The elastic force of material 22 and the 3rd plastics spring 23 of spring is sequentially increased, and the spongiosum 1 includes the raw material of following parts by weight：Polyethers
120 parts of polyhydric alcohol conjugate material, 70 parts of polyester, 50 parts of toluene di-isocyanate(TDI), 18 parts of tourmaline powder, 40 parts of bamboo and woods fiber powder, stone
Black 9 parts of alkene, 10 parts of carbon black, 10 parts of silicones, 40 parts of Chinese medicine composition.
The polyether polyol combines material：20 parts of 70 parts of PPG3000, POP2045,0.8 part of A-33, T-12 0.2
Part, 9 parts of water.
The raw material of the Chinese medicine composition includes the banksia rose, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae.
Its production method is：The banksia rose of equivalent, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae are weighed, mallet is mixed into chip
With, then mixture dried into 4h under conditions of 80 DEG C, you can obtain Chinese medicine composition.
The invention also provides a kind of mattress preparation method of sponge, comprise the following steps：
S1, weighs 120 parts of polyether polyol combination material, 70 parts of polyester, 18 parts of tourmaline powder, 40 parts of bamboo and woods fiber powder, graphene 9
Above-mentioned raw materials are stirred 2h at a temperature of 70 DEG C, obtain mixture by part, 10 parts of carbon black, 10 parts of silicones；
S2, weighs 40 parts of Chinese medicine composition, Chinese medicine composition is put into pot, adds the water of 9 times of amounts, decocts 4h, filtering, obtains
Filter residue and filtrate；
S3, grinds after filter residue drying in S2 are put into the mixture into S1, are sufficiently stirred 3h, then will be mixed after stirring
Compound pours into foam box, accurately weighs 50 parts of toluene di-isocyanate(TDI) and is mixed into S3 high-speed stirreds 10S（≥3000rpm）, wait
Mixture is foamed into cavernous body, stands 100min so that sponge body-shaping；
S4, is uniformly sprayed at the cavernous body surface after shaping in S3 by the filtrate in S2, is baked to using baking oven, finally carried out
I.e. can obtain mattress uses sponge for assembling.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (9)
1. a kind of mattress is with sponge, it is characterised in that including spongiosum（1）, the spongiosum（1）It is interior to be equipped with placing groove
（3）, the placing groove（3）The interior spring mechanism equipped with multiple rectangular arrangements（2）, the spring mechanism（2）Including on to
Under the first plastics spring for setting gradually（21）, the second plastics spring（22）With the 3rd plastics spring（23）, and the first plastics bullet
Spring（21）, the second plastics spring（22）With the 3rd plastics spring（23）Elastic force be sequentially increased, the spongiosum（1）Including with
The raw material of lower parts by weight：100-120 parts of polyether polyol combination material, 50-70 parts of polyester, 30-50 parts of toluene di-isocyanate(TDI), electricity
9-18 parts of gas mountain flour, 20-40 parts of bamboo and woods fiber powder, 3-9 parts of graphene, 5-10 parts of carbon black, 1-10 parts of silicones, Chinese medicine composition
20-40 parts.
2. a kind of mattress according to claim 1 is with sponge, it is characterised in that the polyether polyol combination material includes,
Polyether polyol 1：Molecular weight 3000, degree of functionality 3；Polymer polyatomic alcohol 1：Molecular weight 5000, degree of functionality 3；Catalyst 1：Sanya
Ethyldiamine；Catalyst 2：Dibutyl tin laurate；Water.
3. a kind of mattress according to claim 1 is with sponge, it is characterised in that the raw material of the Chinese medicine composition includes wood
Perfume, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae.
4. a kind of mattress according to claim 3 is with sponge, it is characterised in that the production method of the Chinese medicine composition
For：The banksia rose of equivalent, fennel, windproof, Angelica sinensis, flos caryophylli, tealeaves, black soya bean, Flos Albiziae are weighed, mallet is mixed into chip, then will be mixed
Compound dries 2-4h under conditions of 60-80 DEG C, you can obtains Chinese medicine composition.
5. a kind of mattress according to claim 1 is with sponge, it is characterised in that includes the raw material of following parts by weight：Polyethers
105-115 parts of polyhydric alcohol conjugate material, 55-65 parts of polyester, 35-45 parts of toluene di-isocyanate(TDI), 12-15 parts of tourmaline powder, bamboo and wood
25-35 parts of fiber powder, 5-7 parts of graphene, 7-8 parts of carbon black, 3-8 parts of silicones, 25-35 parts of Chinese medicine composition.
6. a kind of mattress according to claim 1 is with sponge, it is characterised in that includes the raw material of following parts by weight：Polyethers
110 parts of polyhydric alcohol conjugate material, 60 parts of polyester, 40 parts of toluene di-isocyanate(TDI), 13.5 parts of tourmaline powder, 30 parts of bamboo and woods fiber powder,
6 parts of graphene, 7.5 parts of carbon black, 5.5 parts of silicones, 30 parts of Chinese medicine composition.
7. a kind of mattress according to claim 1 is with sponge, it is characterised in that the polyether polyol combination material, polyester,
The weight ratio of toluene di-isocyanate(TDI) is 105-115：55-65：35-45.
8. a kind of mattress preparation method of sponge, it is characterised in that comprise the following steps：
S1, weigh polyether polyol combination material 100-120 parts, 50-70 parts of polyester, 9-18 parts of tourmaline powder, bamboo and woods fiber powder
20-40 parts, 3-9 parts of graphene, 5-10 parts of carbon black, 1-10 parts of silicones, above-mentioned raw materials are stirred at a temperature of 50-70 DEG C mixed
1-2h is closed, obtains mixture；
S2, weighs 20-40 parts of Chinese medicine composition, Chinese medicine composition is put into pot, adds the 5-9 times of water measured, and decocts 2-4h, mistake
Filter, obtains filter residue and filtrate；
S3, grinds after filter residue drying in S2 are put into the mixture into S1,2-3h are sufficiently stirred, then by after stirring
Mixture pours into foam box, accurately weighs 30-50 parts of toluene di-isocyanate(TDI) and is mixed into S3 high-speed stirreds 10S（≥3000rpm）,
Wait mixture to be foamed into cavernous body, stand 40-100min so that sponge body-shaping；
S4, is uniformly sprayed at the cavernous body surface after shaping in S3 by the filtrate in S2, is baked to using baking oven, finally carried out
I.e. can obtain mattress uses sponge for assembling.
A kind of 9. mattress according to claim 8 preparation method of sponge, it is characterised in that in the S3, the sea
The continuous body-shaping curing time is 50-70min.