CN107841814A - Environment-friendlyfabric fabric that a kind of Lyocell long filaments interweave with spun yarn and preparation method thereof - Google Patents
Environment-friendlyfabric fabric that a kind of Lyocell long filaments interweave with spun yarn and preparation method thereof Download PDFInfo
- Publication number
- CN107841814A CN107841814A CN201711078128.XA CN201711078128A CN107841814A CN 107841814 A CN107841814 A CN 107841814A CN 201711078128 A CN201711078128 A CN 201711078128A CN 107841814 A CN107841814 A CN 107841814A
- Authority
- CN
- China
- Prior art keywords
- long filaments
- lyocell
- spun yarn
- lyocell long
- interweave
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Environment-friendlyfabric fabric to interweave the present invention relates to a kind of Lyocell long filaments and spun yarn and preparation method thereof, the environment-friendlyfabric fabric that Lyocell long filaments interweave with spun yarn is that one kind makees warp thread by Lyocell long filaments, cellulose fibre spun yarn makees weft yarn, through the woven green interwoven fabric being process.Its preparation method includes：(1) raw material is made from Lyocell FDY full-drawn yarns and cellulose fibre spun yarn；(2) warping processing is carried out to Lyocell long filaments；(3) starching processing is carried out to Lyocell long filaments；(4) Lyocell long filaments are carried out and axle is handled；(5) leasing processing is carried out to Lyocell long filaments；(6) the plug in reed processing of silk of gaiting is carried out to Lyocell long filaments；(7) it is woven into fabric on.The degradable degree of fabric of the present invention is high, has superior water imbibition, drapability and wearability；Pilling is not easy, fastness is good, and changes of shade is small；And warp thread is long filament, spinning process is eliminated, saves the energy and manpower, preparation cost is low, and method is simple, is suitable for industrialized production.
Description
Technical field
The present invention relates to a kind of fabric of field of textiles and preparation method thereof, more particularly, to a kind of Lyocell long filaments with
Environment-friendlyfabric fabric that spun yarn interweaves and preparation method thereof.
Background technology
Lyocell fiber utilizes the cellulose fibre of patent solvent method preparation based on planned plantation forest.Its
Solvent in manufacturing process belongs to Closed Cycle, and the pollution such as waste water, waste gas and discarded object will not be produced in manufacturing process, is mesh
Preceding green fiber the most safe and environment-friendly, therefore Lyocell short fine fabric is rapidly progressed.But the short fine fabrics of Lyocell
Because of the fibrillation of fiber, in the case of hygrometric state, after by mechanical friction, fibrous outer is easily broken for it, forms length about 1~4
The young pilose antler of micron, can also tangle into cotton grain when serious.Therefore, the short fine fabrics of Lyocell in use easily fluffing, balling-up,
Changes of shade, and fabric can be hardened under damp and hot environment, clothes is produced strong old sense.
The content of the invention
The present invention is directed to the deficiency of the short fine fabrics of existing Lyocell, there is provided one kind makees warp thread with Lyocell long filaments, fine
Cellulose fiber spun yarn makees weft yarn, and through woven green interwoven fabric being process and preparation method thereof, this method is simple,
It is suitable for industrialized production；Pilling is not easy, fastness is good, and changes of shade is small；The more aobvious green of product, environmental protection, practicality, meet and disappear
The purchasing demand of the person of expense.
The present invention be addressed by following technical proposals, a kind of Lyocell long filaments interweave with spun yarn it is green
Fabric, it is interweaved and is formed by warp thread and weft yarn, and the Lyocell long filaments are warp thread, the cellulose fibre spun yarn is weft yarn.
Further, the Lyocell long filaments are 75D~150D full-drawn yarn (FDY).
Further, the cellulose fibre spun yarn is modal spun yarn, spun viscose, cuprammonium spun yarn, pure cotton
Yarn etc..
Further, the fineness of the cellulose fibre spun yarn is 7.4tex~29.5tex.
The environment-friendlyfabric fabric preparation method that a kind of Lyocell long filaments of the present invention interweave with spun yarn, including step：
(1) raw material is made from Lyocell full-drawn yarns and cellulose fibre spun yarn；
(2) warping is carried out to the Lyocell long filaments by beam warper, is processed into warp beam；
(3) starching is carried out to the Lyocell long filaments in warp beam by starching silk machine, is processed into slurry axle；
(4) simultaneously axle is carried out to the Lyocell long filaments on slurry axle by warp rebeaming machine, is processed into and does not wear beam of a loom；
(5) it is divided into two layers up and down by root by odevity to not wearing the Lyocell long filaments on beam of a loom by splitting machine, is penetrated point
Twisted wire；
(6) the plug in reed of silk of gaiting is carried out to the Lyocell long filaments do not worn on beam of a loom through leasing by drawing-in machine, be processed into
Wear beam of a loom；
(7) by loom to have worn the Lyocell long filaments of beam of a loom as warp thread, the cellulose fibre spun yarn is weft yarn, is knitted
The green interwoven fabric to interweave into Lyocell long filaments and spun yarn.
In above-mentioned technical proposal, it is preferred that in described step (2), warp beam surface smoothness is less than 2.5mm.
In above-mentioned technical proposal, it is preferred that in the step (3), by weight percentage, sizing material is 98%~99%
's
Polyvinyl alcohol and 1%~2% antistatic additive.
In above-mentioned technical proposal, it is preferred that in the step (3), by weight percentage, the Lyocell long filaments being somebody's turn to do it is upper
Slurry rate is 4%~6%, preferably 4%~5.6%.
In above-mentioned technical proposal, it is preferred that in the step (3), the slurry silk elongation of Lyocell long filaments is 1~3%, excellent
Elect 1~2.5% as.
Compared with prior art, the beneficial effects of the invention are as follows：
(1) warp thread of fabric of the present invention uses Lyocell long filaments, eliminates spinning each operation, the effectively save energy of energy, drop
Low machine material consumption, it is low to prepare cost.
(2) warp thread of fabric of the present invention uses Lyocell long filaments, and its strength is high, is not easy to break end in production, can effectively improve
Production efficiency.
(3) weft yarn of fabric of the present invention uses cellulose fibre spun yarn, not easily fibrillable, and fastness is good, is not easy to fluff
Ball, changes of shade is small, effectively improves the wearability of fabric.
(4) fabric of the present invention is green fiber through weft yarn, biodegradable, has very strong security and environmental protection
Property.
Specific embodiment
The principles and features of the present invention are described below, and the given examples are served only to explain the present invention, is not intended to limit
Determine the scope of the present invention.
The present invention is described in further detail with reference to embodiment.
Embodiment 1：A kind of preparation method of Lyocell long filaments environment-friendlyfabric fabric, includes following steps：
(1) raw material is selected, and chooses the 150D long yarn packages of Lyocell as warp thread and weft yarn；
(2) warping, warping is carried out to the Lyocell long filaments by beam warper, is processed into warp beam, warping radical is
1026；
(3) silk is starched, starching is carried out to the Lyocell long filaments in warp beam by starching silk machine, is processed into slurry axle；The formula of slurry
For：By weight percentage, major ingredient is 98% PVA-205MB (alcoholysis degree 86.5-89%, the degree of polymerization 500), and auxiliary material is
2% antistatic additive；The rate of sizing is 4.5%, and slurry silk elongation is 1.6%, and slurry silk locomotive speed is 50m/min；
(4) and axle, by warp rebeaming machine the Lyocell long filaments on slurry axle are carried out and axle, are processed into and do not wear beam of a loom, and axle
During need on the warp rebeaming machine every slurry axle move back solution uniform tension in order；
(5) leasing, it is divided into two layers up and down by root by odevity to not wearing the Lyocell long filaments on beam of a loom by splitting machine,
Penetrate leased line；
(6) pass, the plug in reed of silk of gaiting is carried out to the Lyocell long filaments do not worn on beam of a loom through leasing by drawing-in machine, added
Work is into having worn beam of a loom；
(7) looming weaving, by air-jet loom to have worn the Lyocell long filaments of beam of a loom as warp thread, the Lyocell long filament cylinders
Sub- yarn is weft yarn, and it is 385/10cm to be made into warp count, and weft yarn is the Lyocell long filament green rings that density is 298/10cm
Friendly fabric.
Embodiment 2：A kind of preparation method of Lyocell long filaments environment-friendlyfabric fabric, includes following steps：
(1) raw material is selected, and chooses the 120D long yarn packages of Lyocell as warp thread and weft yarn；
(2) warping, warping is carried out to the Lyocell long filaments by beam warper, is processed into warp beam, warping radical is
1100；
(3) silk is starched, starching is carried out to the Lyocell long filaments in warp beam by starching silk machine, is processed into slurry axle；The formula of slurry
For：By weight percentage, major ingredient is 99% PVA-205MB, and auxiliary material is 1% antistatic additive；The rate of sizing is 5%, starches silk
Elongation is 1.6%, and slurry silk locomotive speed is 50m/min；
(4) and axle, by warp rebeaming machine the Lyocell long filaments on slurry axle are carried out and axle, are processed into and do not wear beam of a loom, and axle
During need on the warp rebeaming machine every slurry axle move back solution uniform tension in order；
(5) leasing, it is divided into two layers up and down by root by odevity to not wearing the Lyocell long filaments on beam of a loom by splitting machine,
Penetrate leased line；
(6) pass, the plug in reed of silk of gaiting is carried out to the Lyocell long filaments do not worn on beam of a loom through leasing by drawing-in machine, added
Work is into having worn beam of a loom；
(7) looming weaving, by air-jet loom to have worn the Lyocell long filaments of beam of a loom as warp thread, the Lyocell long filament cylinders
Sub- yarn is weft yarn, and it is 550/10cm to be made into warp count, and weft yarn is the Lyocell long filament green rings that density is 340/10cm
Friendly fabric.
Embodiment 3：A kind of preparation method of Lyocell long filaments environment-friendlyfabric fabric, includes following steps：
(1) raw material is selected, and chooses the 75D long yarn packages of Lyocell as warp thread and weft yarn；
(2) warping, warping is carried out to the Lyocell long filaments by beam warper, is processed into warp beam, warping radical is
1172；
(3) silk is starched, starching is carried out to the Lyocell long filaments in warp beam by starching silk machine, is processed into slurry axle；The formula of slurry
For：By weight percentage, major ingredient is 99% PVA-205MB, and auxiliary material is 1% antistatic additive；The rate of sizing is 5.5%, slurry
Silk elongation is 1.8%, and slurry silk locomotive speed is 50m/min；
(4) and axle, by warp rebeaming machine the Lyocell long filaments on slurry axle are carried out and axle, are processed into and do not wear beam of a loom, and axle
During need on the warp rebeaming machine every slurry axle move back solution uniform tension in order；
(5) leasing, it is divided into two layers up and down by root by odevity to not wearing the Lyocell long filaments on beam of a loom by splitting machine,
Penetrate leased line；
(6) pass, the plug in reed of silk of gaiting is carried out to the Lyocell long filaments do not worn on beam of a loom through leasing by drawing-in machine, added
Work is into having worn beam of a loom；
(7) looming weaving, by air-jet loom to have worn the Lyocell long filaments of beam of a loom as warp thread, the Lyocell long filament cylinders
Sub- yarn is weft yarn, and it is 700/10cm to be made into warp count, and weft yarn is the Lyocell long filament green rings that density is 436/10cm
Friendly fabric.
Some preferred embodiments of invention have shown and described in described above, but it has been observed that it should be understood that the present invention is not
Form disclosed herein is confined to, is not to be taken as the exclusion to other embodiment, and available for various other combinations, modification
And environment, and in the invented the scope of the idea, can be changed herein by the technology or knowledge of above-mentioned teaching or association area
It is dynamic., then all should be in power appended by the present invention and the change and change that those skilled in the art are carried out do not depart from the spirit and scope of invention
In the protection domain that profit requires.
Claims (9)
1. the environment-friendlyfabric fabric that a kind of Lyocell long filaments interweave with spun yarn, is interweaved by warp thread and weft yarn and formed, it is special
Sign is：The warp thread is Lyocell long filaments, and the weft yarn is cellulose fibre spun yarn.
2. the environment-friendlyfabric fabric that a kind of Lyocell long filaments according to claim 1 interweave with spun yarn, its feature exist
In：The Lyocell long filaments are 75D~150D full-drawn yarn.
3. the environment-friendlyfabric fabric that a kind of Lyocell long filaments according to claim 1 interweave with spun yarn, its feature exist
In：The cellulose fibre spun yarn is tencel spun yarn, spun viscose, modal spun yarn, cuprammonium spun yarn etc..
4. the environment-friendlyfabric fabric that a kind of Lyocell long filaments according to claim 1 interweave with spun yarn, its feature exist
In：The fineness of the cellulose fibre spun yarn is 7.4tex~29.5tex.
5. the environment-friendlyfabric fabric preparation method that a kind of Lyocell long filaments interweave with spun yarn, including：
(1) raw material is made from Lyocell full-drawn yarns and cellulose fibre spun yarn；
(2) warping is carried out to described Lyocell long filaments by beam warper, is processed into warp beam；
(3) starching is carried out to the Lyocell long filaments in warp beam by starching silk machine, is processed into slurry axle；
(4) simultaneously axle is carried out to the Lyocell long filaments on slurry axle by warp rebeaming machine, is processed into and does not wear beam of a loom；
(5) it is divided into two layers up and down by root by odevity to not wearing the Lyocell long filaments on beam of a loom by splitting machine, penetrates leasing
Line；
(6) the plug in reed of silk of gaiting is carried out to the Lyocell long filaments do not worn on beam of a loom through leasing by drawing-in machine, is processed into have worn and knits
Axle；
(7) by loom to have worn the Lyocell long filaments of beam of a loom as warp thread, described cellulose fibre spun yarn is as latitude
Yarn, it is made into the environment-friendlyfabric fabric that Lyocell long filaments interweave with spun yarn.
6. the environment-friendlyfabric fabric preparation method that a kind of Lyocell long filaments according to claim 5 interweave with spun yarn, its
It is characterized as, in described step (2), warp beam surface smoothness is less than 2.5mm.
7. the environment-friendlyfabric fabric preparation method that a kind of Lyocell long filaments according to claim 5 interweave with spun yarn, its
Be characterized as, in described step (3), by weight percentage, sizing material be 98%~99% polyvinyl alcohol and 1%~
2% antistatic additive.
8. the environment-friendlyfabric fabric preparation method that a kind of Lyocell long filaments according to claim 5 interweave with spun yarn, its
It is characterized as, in described step (3), by weight percentage, the rate of sizing of Lyocell long filaments is 4~6%.
9. the environment-friendlyfabric fabric preparation method that a kind of Lyocell long filaments according to claim 5 interweave with spun yarn, its
It is characterized as, in described step (3), the slurry silk elongation of Lyocell long filaments is 1~3%.