CN107841675A - A kind of wearable hard alloy - Google Patents
A kind of wearable hard alloy Download PDFInfo
- Publication number
- CN107841675A CN107841675A CN201711063045.3A CN201711063045A CN107841675A CN 107841675 A CN107841675 A CN 107841675A CN 201711063045 A CN201711063045 A CN 201711063045A CN 107841675 A CN107841675 A CN 107841675A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- hard alloy
- wearable hard
- silica flour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses 2~4 parts of 4~10 parts of 3~4 parts of 6~10 parts of 9~14 parts of parts by weight aluminium powder, comminuted steel shot, lead powder, copper powder, the manganese powder and 3~5 parts of silica flour of a kind of wearable hard alloy, including following components.Wearable hard alloy provided by the invention improves the anti-wear performance of hard alloy due to adding aluminium powder, comminuted steel shot, lead powder, copper powder, manganese powder and silica flour, while has excellent thermal fatigue and shock resistance damage capability, has resistance to broken, corrosion resistant performance.
Description
Technical field
The present invention relates to antifriction alloy field, more particularly to a kind of wearable hard alloy.
Background technology
Hard alloy is applied to a variety of occasions as main raw material(s), such as rotary drill hard-metal insert, is using process
In failure mechanism for heat fatigue with abrasion simultaneously effect result, in order to meet such use occasion, it is desirable to hard alloy
There is good thermal fatigue and wearability simultaneously.
Traditional hard alloy is generally homogeneous texture, often wear-resisting to sacrifice its when improving the thermal fatigue resistance of product
Property is cost;Conversely, when needing to improve the wearability of product, again must be such to sacrifice its thermal fatigue resistance as cost
Alloy is difficult to obtain good combination property.
The content of the invention
It is an object of the invention to provide a kind of wearable hard alloy.
The purpose of the present invention is achieved through the following technical solutions:
A kind of wearable hard alloy, include 6~10 parts of 9~14 parts of parts by weight aluminium powder, comminuted steel shot, the lead powder 3~4 of following components
Part, 4~10 parts of copper powder, 2~4 parts of manganese powder and 3~5 parts of silica flour.
The parts by weight of above component are put into crucible furnace, mould is poured into after using temperature as 500~550 DEG C of high temperature melt
It is cooled and shaped in tool.
Wearable hard alloy provided by the invention carries due to adding aluminium powder, comminuted steel shot, lead powder, copper powder, manganese powder and silica flour
The anti-wear performance of high hard alloy, while there is excellent thermal fatigue and shock resistance damage capability, have resistance to broken, corrosion-resistant
Performance.
Embodiment
Embodiment 1:
The wearable hard alloy that the present embodiment provides includes 8 parts of 12 parts of parts by weight aluminium powder, comminuted steel shot, the lead powder 4 of following components
Part, 7 parts of copper powder, 3 parts of manganese powder and 4 parts of silica flour;Said components are put into crucible furnace, use temperature as 550 DEG C of high temperature melt
After pour into mould and be cooled and shaped.
Embodiment 2:
The wearable hard alloy that the present embodiment provides includes 6 parts of 9 parts of parts by weight aluminium powder, comminuted steel shot, the lead powder 3 of following components
Part, 4 parts of copper powder, 2 parts of manganese powder and 3 parts of silica flour;Said components are put into crucible furnace, use temperature as 500 DEG C of high temperature melt
After pour into mould and be cooled and shaped.
Embodiment 3:
The wearable hard alloy that the present embodiment provides includes 10 parts of 14 parts of parts by weight aluminium powder, comminuted steel shot, the lead powder 4 of following components
Part, 10 parts of copper powder, 4 parts of manganese powder and 5 parts of silica flour;Said components are put into crucible furnace, use temperature as 520 DEG C of high temperature melt
After pour into mould and be cooled and shaped.
Described above is only the preferred embodiment of the present invention, but protection scope of the present invention is not limited thereto, any
The transformation and replacement that are carried out based on technical scheme provided by the present invention and inventive concept should all cover the protection model in the present invention
In enclosing.
Claims (2)
- A kind of 1. wearable hard alloy, it is characterised in that:9~14 parts of parts by weight aluminium powder, comminuted steel shot 6~10 including following components Part, 3~4 parts of lead powder, 4~10 parts of copper powder, 2~4 parts of manganese powder and 3~5 parts of silica flour.
- 2. wearable hard alloy according to claim 1, it is characterised in that:The parts by weight of above component are put into crucible furnace In, pour into mould and be cooled and shaped after using temperature as 500~550 DEG C of high temperature melt.